JP2013181146A - 硬化性樹脂組成物 - Google Patents
硬化性樹脂組成物 Download PDFInfo
- Publication number
- JP2013181146A JP2013181146A JP2012047425A JP2012047425A JP2013181146A JP 2013181146 A JP2013181146 A JP 2013181146A JP 2012047425 A JP2012047425 A JP 2012047425A JP 2012047425 A JP2012047425 A JP 2012047425A JP 2013181146 A JP2013181146 A JP 2013181146A
- Authority
- JP
- Japan
- Prior art keywords
- component
- agent
- curable resin
- meth
- resin composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】下記(A)〜(C)成分を含有する硬化性樹脂組成物。(A)ジエン系又は水素添加されたジエン系の骨格を有するオリゴマー、(B)ノニルフェノキシポリエチレングリコール(メタ)アクリレート等の芳香族基を有する(メタ)アクリレート、(C)光重合開始剤。熱重合開始剤、還元剤、(A)成分や(B)成分以外の(メタ)アクリレート、シランカップリング剤を含有してもよい。接着剤組成物として使用してもよい。
【選択図】なし
Description
(A)ジエン系又は水素添加されたジエン系の骨格を有するオリゴマー
(B)ノニルフェノキシポリエチレングリコール(メタ)アクリレート、ノニルフェノキシポリプロピレンレングリコール(メタ)アクリレート、ベンジル(メタ)アクリレート、エトキシ化フェニル(メタ)アクリレート、ネオペンチルグリコールベンゾエート(メタ)アクリレート、ECH変性フェノキシ(メタ)アクリレート,フェノキシジエチレングリコール(メタ)アクリレート、フェノキシヘキサエチレングリコール(メタ)アクリレート、フェノキシテトラエチレングリコール(メタ)アクリレート、及び2-ヒドロキシ-3-フェノキシプロピル(メタ)アクリレートからなる群より選ばれる1種以上からなる、芳香族基を有する(メタ)アクリレート
(C)光重合開始剤
更に(D)成分として、熱重合開始剤、(E)成分として、還元剤を含有する該硬化性樹脂組成物であり、更に、(F)成分として、(A)成分や(B)成分以外の(メタ)アクリレートを含有する該硬化性樹脂組成物であり、(F)成分の(A)成分や(B)成分以外の(メタ)アクリレートが水酸基含有(メタ)アクリレートである該硬化性樹脂組成物であり、更に、(G)成分として、シランカップリング剤を含有する該硬化性樹脂組成物であり、(A)成分のジエン系又は水素添加されたジエン系の骨格が、ポリブタジエン、ポリイソプレン、ポリブタジエンの水素添加物、及びポリイソプレンの水素添加物からなる群から選ばれる1種以上の骨格である該硬化性樹脂組成物であり、(A)成分のジエン系又は水素添加されたジエン系の骨格を有するオリゴマーの分子量が500〜70000である該硬化性樹脂組成物であり、(D)熱重合開始剤が、有機過酸化物である該硬化性樹脂組成物であり、(E)還元剤が、チオ尿素誘導体、β−ジケトンキレート、及びβ−ケトエステルからなる群より選ばれる1種以上である該硬化性樹脂組成物であり、二剤型であり、第一剤が少なくとも(D)熱重合開始剤を含有してなり、第二剤が少なくとも(E)還元剤を含有してなる該硬化性樹脂組成物であり、二剤型であり、第一剤が少なくとも(D)熱重合開始剤を含有してなり、第二剤が少なくとも(E)還元剤と溶剤を含有してなるプライマーである該硬化性樹脂組成物であり、該硬化性樹脂組成物からなる接着剤組成物であり、該接着剤組成物の硬化体であり、該硬化体により被着体が被覆又は接合された複合体であり、該被着体がトリアセチルセルロース、フッ素系ポリマー、ポリエステル、ポリカーボネート、ポリオレフィン、ガラス、及び金属からなる群から選ばれる1種以上である複合体であり、該接着剤組成物により被着体を貼り合わせたタッチパネル積層体であり、該接着剤組成物により被着体を貼り合わせた液晶パネル積層体であり、該タッチパネル積層体を用いたディスプレイであり、該液晶パネル積層体を用いたディスプレイであり、第一剤と第二剤を予め混合した二剤型硬化性樹脂組成物を被着体に塗布することにより、被着体を接合又は被覆する該二剤型の硬化性樹脂組成物の接合又は被覆方法であり、第二剤からなるプライマーを一方の被着体に塗布した後、第二剤からなるプライマーの表面に第一剤を塗布することにより、被着体を被覆又は接合する該二剤型の硬化性樹脂組成物の被覆又は接合方法であり、第一剤を一方の被着体に塗布し、第二剤からなるプライマーをもう一方の被着体に塗布した後、被着体同士を貼り合わせることにより、被着体を接合する該二剤型の硬化性樹脂組成物の接合方法である。
特記しない限り、23℃で、実験した。表1〜3に示す組成の硬化性樹脂組成物を調製し、評価した。結果を表1〜3に示した。実験例16と実験例17は第二剤をプライマーとして使用した。
(A−1)1,2−ポリブタジエンオリゴマー(日本曹達社製「TE−2000」)(GPCによるポリスチレン換算の数平均分子量2000)
(A−2)イソプレンオリゴマー(クラレ社製「LIR−30」)(GPCによるポリスチレン換算の数平均分子量28000)
(A−3)ブタジエンオリゴマー(クラレ社製「LBR−307」)(GPCによるポリスチレン換算の数平均分子量8000)
(A−4)イソプレンオリゴマー(クラレ社製「UC−203」)(GPCによるポリスチレン換算の数平均分子量36000)
(B)成分の、フェノキシ基若しくはノニルフェノキシ基を有する(メタ)アクリレートとして、以下の化合物を選択した。
(B−1)ノニルフェノキシポリエチレングリコールアクリレート(n=1)(東亜合成社製「M−111」)
(B−2)2−ヒドロキシ−3−フェノキシプロピルアクリレート(東亜合成社製「アロニックスM−5700」)
(B)成分の比較例として、フェノキシエチルアクリレート(共栄社化学社製「POA」)
(C)成分の光開始剤として、以下の化合物を選択した。
(C−1)1−ヒドロキシシクロヘキシルフェニルケトン(チバスペシャリティケミカル社製「Irgacure184」)
(C−2)2,4,6−トリメチルベンゾイル−ジフェニル−フォスフィンオキサイド(チバスペシャリティケミカル社製「DarocurTPO」)
(D)成分の熱重合開始剤として、以下の化合物を選択した。
(D−1)クメンハイドロパーオキサイド
(E)成分の還元剤として、以下の化合物を選択した。
(E−1)トリメチルチオ尿素
(E−2)バナジルアセチルアセトネート
(F)成分の(A)成分や(B)成分以外の(メタ)アクリレートとして、以下の化合物を選択した。
(F−1)2−ヒドロキシブチルアクリレート(共栄社化学社製「ライトエステルHOBA」)
(G)成分の、シランカップリング剤として、以下の化合物を選択した。
(G−1)γ−グリシドキシプロピルトリメトキシシラン
フェノキシエチルアクリレートを使用した場合、本発明の効果を有しない(実験例12)。
Claims (22)
- 下記(A)〜(C)成分を含有する硬化性樹脂組成物。
(A)ジエン系又は水素添加されたジエン系の骨格を有するオリゴマー
(B)ノニルフェノキシポリエチレングリコール(メタ)アクリレート、ノニルフェノキシポリプロピレンレングリコール(メタ)アクリレート、ベンジル(メタ)アクリレート、エトキシ化フェニル(メタ)アクリレート、ネオペンチルグリコールベンゾエート(メタ)アクリレート、ECH変性フェノキシ(メタ)アクリレート,フェノキシジエチレングリコール(メタ)アクリレート、フェノキシヘキサエチレングリコール(メタ)アクリレート、フェノキシテトラエチレングリコール(メタ)アクリレート、及び2-ヒドロキシ-3-フェノキシプロピル(メタ)アクリレートからなる群より選ばれる1種以上からなる、芳香族基を有する(メタ)アクリレート
(C)光重合開始剤 - 更に(D)成分として、熱重合開始剤、(E)成分として、還元剤を含有する請求項1に記載の硬化性樹脂組成物。
- 更に、(F)成分として、(A)成分や(B)成分以外の(メタ)アクリレートを含有する請求項1又は2に記載の硬化性樹脂組成物。
- (F)成分の(A)成分や(B)成分以外の(メタ)アクリレートが水酸基含有(メタ)アクリレートである請求項1〜3に記載の硬化性樹脂組成物。
- 更に、(G)成分として、シランカップリング剤を含有する請求項1〜4のうちのいずれか1項に記載の硬化性樹脂組成物。
- (A)成分のジエン系又は水素添加されたジエン系の骨格が、ポリブタジエン、ポリイソプレン、ポリブタジエンの水素添加物、及びポリイソプレンの水素添加物からなる群から選ばれる1種以上の骨格である請求項1〜5のうちのいずれか1項に記載の硬化性樹脂組成物。
- (A)成分のジエン系又は水素添加されたジエン系の骨格を有するオリゴマーの分子量が500〜70000である請求項1〜6のうちのいずれか1項に記載の硬化性樹脂組成物。
- (D)熱重合開始剤が、有機過酸化物である請求項2〜7のうちのいずれか1項に記載の硬化性樹脂組成物。
- (E)還元剤が、チオ尿素誘導体、β−ジケトンキレート、及びβ−ケトエステルからなる群より選ばれる1種以上である請求項2〜8のうちのいずれか1項に記載の硬化性樹脂組成物。
- 二剤型であり、第一剤が少なくとも(D)熱重合開始剤を含有してなり、第二剤が少なくとも(E)還元剤を含有してなる請求項2〜9のうちの1項に記載の硬化性樹脂組成物。
- 二剤型であり、第一剤が少なくとも(D)熱重合開始剤を含有してなり、第二剤が少なくとも(E)還元剤と溶剤を含有してなるプライマーである請求項2〜9のうちの1項に記載の硬化性樹脂組成物。
- 請求項1〜11のうちのいずれか1項に記載の硬化性樹脂組成物からなる接着剤組成物。
- 請求項12記載の接着剤組成物の硬化体。
- 請求項13記載の硬化体により被着体が被覆又は接合された複合体。
- 請求項14記載の被着体がトリアセチルセルロース、フッ素系ポリマー、ポリエステル、ポリカーボネート、ポリオレフィン、ガラス、及び金属からなる群から選ばれる1種以上である複合体。
- 請求項12に記載の接着剤組成物により被着体を貼り合わせたタッチパネル積層体。
- 請求項12に記載の接着剤組成物により被着体を貼り合わせた液晶パネル積層体。
- 請求項16に記載のタッチパネル積層体を用いたディスプレイ。
- 請求項17に記載の液晶パネル積層体を用いたディスプレイ。
- 第一剤と第二剤を予め混合した二剤型硬化性樹脂組成物を被着体に塗布することにより、被着体を接合又は被覆する請求項10記載の二剤型の硬化性樹脂組成物の接合又は被覆方法。
- 第二剤からなるプライマーを一方の被着体に塗布した後、第二剤からなるプライマーの表面に第一剤を塗布することにより、被着体を被覆又は接合する請求項11記載の二剤型の硬化性樹脂組成物の被覆又は接合方法。
- 第一剤を一方の被着体に塗布し、第二剤からなるプライマーをもう一方の被着体に塗布した後、被着体同士を貼り合わせることにより、被着体を接合する請求項11記載の二剤型の硬化性樹脂組成物の接合方法。