JP2013152941A - 燃料電池用金属セパレータの製造方法および製造装置 - Google Patents
燃料電池用金属セパレータの製造方法および製造装置 Download PDFInfo
- Publication number
- JP2013152941A JP2013152941A JP2013052065A JP2013052065A JP2013152941A JP 2013152941 A JP2013152941 A JP 2013152941A JP 2013052065 A JP2013052065 A JP 2013052065A JP 2013052065 A JP2013052065 A JP 2013052065A JP 2013152941 A JP2013152941 A JP 2013152941A
- Authority
- JP
- Japan
- Prior art keywords
- base plate
- metal base
- forming
- roll set
- fuel cell
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】
燃料電池用セパレータの外面形状に対応する凹凸部が形成された成形ロールセットの間に、燃料電池用セパレータの金属素板202を通し、金属素板202に形成されているガイド穴203を利用して、金属素板202を位置決めしながら、成形ロールセットの凹凸部によって、金属素板202に連続的に幅方向の成形加工を施し、前記外面形状を形成する。そして、成形ロールセットによる成形加工によってソリが生じた金属素板202を、矯正ロールセット262,272の間に通し、矯正ロールセット262,272によって前記ソリを矯正する。
【選択図】図10
Description
20 スタック部、
30,40 集電板、
35,45 出力端子、
50,60 絶縁板、
70,80 エンドプレート、
71 燃料ガス導入口、
72 燃料ガス排出口、
74 酸化剤ガス導入口、
75 酸化剤ガス排出口、
77 冷媒導入口、
78 冷媒排出口、
90 タイロッド、
100 電極集成体、
110 膜電極接合体、
120,130 ガス拡散層、
141,142,144,145,147,148 マニホールド部、
150 セパレータ、
152 モニタータブ、
161,162,164,165,167,168 マニホールド部、
169 凹凸部、
170 セパレータ、
172 モニタータブ、
181,182,184,185,187,188 マニホールド部、
189 凹凸部、
202 コイル材(金属素板)、
203 ガイド穴、
204 母材、
205 被膜、
210 フィーダ、
220 成形装置(成形手段)、
222,232 成形ロール(成形ロールセット)、
223,233 外周面、
225 支持構造部、
226,236 軸支部、
234 突起部(位置決め手段)、
260 矯正装置(矯正手段)、
262,272 矯正ロール(矯正ロールセット)、
263,273 外周面、
264 突起部(位置決め手段)、
265 支持構造部、
266,276 軸支部、
280 凹凸部
302 コイル材(第2の金属素板)、
303 ガイド穴、
310 フィーダ(第2の投入手段)、
320 成形装置(第2の成形手段)、
322,332 成形ロール(成形ロールセット)、
360 矯正装置(第2の矯正手段)、
362,372 矯正ロール(矯正ロールセット)、
400 シーム溶接機(溶接手段)、
402,412 ガイドロール、
404,414 支持構造部、
406,416 軸支部、
422,432 電極ロール(電極ロールセット)、
423,433 外周面、
424,434 電極部、
425 突起部(位置決め手段)、
465 支持構造部、
466,476 軸支部、
500 さい断機、
600 圧延装置(圧延手段)、
622,632 圧延ロール(圧延ロールセット)、
625 支持構造部、
626,636 軸支部、
S1,S2,S3 空間。
Claims (8)
- 燃料電池用セパレータの外面形状に対応する凹凸部が形成された成形ロールセットの間に、前記燃料電池用セパレータの金属素板を通し、前記金属素板に形成されているガイド穴を利用して、前記金属素板を位置決めしながら、前記成形ロールセットの前記凹凸部によって、前記金属素板に連続的に幅方向の成形加工を施し、前記外面形状を形成し、
前記成形ロールセットによる成形加工によってソリが生じた前記金属素板を、矯正ロールセットの間に通し、前記矯正ロールセットによって前記ソリを矯正することを特徴とする燃料電池用セパレータの製造方法。 - 前記金属素板に、導電性を有する耐食被膜を配置した後、圧延することなく前記成形ロールセットの間を通らせることを特徴とする請求項1に記載の燃料電池用セパレータの製造方法。
- 前記金属素板に、導電性を有する耐食被膜を配置し、圧延した後、前記成形ロールセットの間に通し、前記成形ロールセットによって成形加工された前記金属素板を、圧延ロールセットの間に通し、前記金属素板を圧延することを特徴とする請求項1に記載の燃料電池用セパレータの製造方法。
- 前記金属素板は、コイル材であり、
巻きほぐして投入され、かつ前記成形ロールセットによる成形加工および前記矯正ロールセットによる矯正が施された前記金属素板と、
巻きほぐして投入され、かつ第2の成形ロールセットによる成形加工および第2の矯正ロールセットによる矯正が施された第2の金属素板とが、重ねられ、
電極ロールセットの間に通され、前記電極ロールセットによって連続的な抵抗溶接が施され、その後、切断されることを特徴とする請求項1に記載の燃料電池用セパレータの製造方法。 - 燃料電池用セパレータの外面形状に対応する凹凸部が形成された成形ロールセットを有する成形手段と、
前記燃料電池用セパレータの金属素板に形成されているガイド穴を利用して、前記金属素板を位置決めするための位置決め手段と、
矯正ロールセットを有する矯正手段と、を有しており、
前記成形ロールセットの間に前記金属素板を通す際、前記位置決め手段によって前記金属素板を位置決めしながら、前記成形ロールセットの前記凹凸部によって、前記金属素板に連続的に幅方向の成形加工を施し、前記外面形状を形成し、
前記成形ロールセットによる成形加工によってソリが生じた前記金属素板は、前記矯正ロールセットの間に通され、前記矯正ロールセットによる矯正によって前記ソリが矯正されることを特徴とする記載の燃料電池用セパレータの製造装置。 - 前記成形ロールセットの間に通される前記金属素板は、導電性を有する耐食被膜が配置されており、かつ、前記耐食被膜が配置された後に圧延されていない
ことを特徴とする請求項5に記載のセパレータの製造装置。 - 圧延ロールセットを有する圧延手段を、さらに有し、
前記成形ロールセットの間に通される前記金属素板は、導電性を有する耐食被膜が配置されており、かつ、前記耐食被膜が配置された後に圧延されており、
前記成形ロールセットによって成形加工された前記金属素板は、前記圧延ロールセットの間に通され、前記圧延ロールセットによって圧延されることを特徴とする請求項5に記載の燃料電池用セパレータの製造装置。 - 前記金属素板は、コイル材であり、
前記燃料電池用セパレータの製造装置は、
前記金属素板を巻きほぐして投入するための投入手段、
第2の金属素板を巻きほぐして投入するための第2の投入手段、
第2の成形ロールセットを有する第2の成形手段、
第2の矯正ロールセットを有する第2の矯正手段、
電極ロールセットを有する溶接手段、および、
切断手段
を、さらに有しており、
巻きほぐして投入され、かつ前記成形ロールセットによる成形加工および矯正ロールセットによる矯正が施された前記金属素板と、
巻きほぐして投入され、かつ、第2の前記成形ロールセットによる成形加工および第2の前記矯正ロールセットによる矯正が施された第2の前記金属素板とが、重ねられ、
前記電極ロールセットの間に通され、前記電極ロールセットによって連続的な抵抗溶接が施され、その後、前記切断手段によって切断される
ことを特徴とする請求項5に記載の燃料電池用セパレータの製造装置。