JP2012197542A - キャストコート紙及びその製造方法 - Google Patents
キャストコート紙及びその製造方法 Download PDFInfo
- Publication number
- JP2012197542A JP2012197542A JP2011063877A JP2011063877A JP2012197542A JP 2012197542 A JP2012197542 A JP 2012197542A JP 2011063877 A JP2011063877 A JP 2011063877A JP 2011063877 A JP2011063877 A JP 2011063877A JP 2012197542 A JP2012197542 A JP 2012197542A
- Authority
- JP
- Japan
- Prior art keywords
- cast
- coated paper
- ink
- coat layer
- coated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】本発明に係るキャストコート紙は、基材上に無機顔料及びバインダーを主体として含有するキャストコート層をリウェット法で形成したキャストコート紙において、キャストコート層が、更に界面活性剤を含有し、界面活性剤がアセチレンアルコール化合物、アセチレングリコール化合物又はアセチレン系ジアルコールのポリエーテル化合物の少なくとも1種であり、キャストコート層の乾燥塗工量が、8〜30g/m2であり、表面のJIS Z8741:1997「鏡面光沢度−測定方法」に従って測定した60°における光沢度が、50%以上である。
【選択図】なし
Description
LBKP100部(カナディアンスタンダードフリーネス:CSF=500ml)のパルプスラリーに、カチオン澱粉(ネオタック40T、日本NSC社製)1.0部と、タルク(太平タルク、太平タルク社製)5.0部と、酸性ロジンサイズ剤(AL1200、星光PMC社製)0.2部と、液体硫酸バンド1.0部と、ポリアミド・エピクロルヒドリン樹脂0.2部とを配合して紙料を調製した。この紙料を長網式抄紙機で抄造して坪量70g/m2の原紙を得た。原紙の両面に、酸化澱粉(王子エースA、王子コーンスターチ社製)6%をサイズプレスによって乾燥塗工量が片面当たり1.5g/m2となるように塗工し、乾燥して基材を得た。
クエン酸ナトリウム0.15%と、蟻酸0.8%と、離型剤として脂肪酸誘導体(R‐053D、日新化学研究所社製)0.05%とを分散機にて水中に分散及び溶解させ、再湿潤液Aを調製した。なお、再湿潤液Aの固形分濃度は、1.0%であった。
無機顔料としてクレー(KAMINGLOSS、KaMin社製、体積平均粒子径0.9μm)70部及び炭酸カルシウム(TP‐123、奥多摩工業社製、体積平均粒子径1.0μm)30部と助剤としてポリオキシエチレンポリオキシプロピレングリコール(PE‐61、三洋化成工業社製)0.3部とを分散機にて水中に分散し、顔料スラリーAを調製した。
顔料スラリーA100部と、バインダーとしてカゼイン(ALACID LACTIC CASEIN、Fonterra社製)8部及びスチレン‐ブタジエンラテックス(E‐1974、旭化成社製)20部と、界面活性剤として2,4,7,9‐テトラメチル‐5‐デシン‐4,7‐ジオール‐ジ(ポリオキシエチレン)エーテル(オルフィンE1010、日信化学社製)3部と、助剤として複合ワックス(DKワックスNo.18、大京化学社製)2部とを配合し、水で固形分濃度43%に調製して、キャストコート用塗料Aを得た。
基材の上に、キャストコート用塗料Aを乾燥塗工量で16g/m2となるようにエアーナイフコーターでオフコートした。塗工面を、エアードライヤーにて、所定水分を維持するような条件で、半乾燥させた。半乾燥させた塗工面に、再湿潤液Aを塗布して、再湿潤処理した後に、120℃に加熱したキャストドラムに圧着して乾燥後、ドラム表面から剥離させ、リワインドしてキャストコート紙を得た。
実施例1において、キャストコート用塗料Aの界面活性剤を、2,4,7,9‐テトラメチル‐5‐デシン‐4,7‐ジオール‐ジ(ポリオキシエチレン)エーテルに替えて、2,4,7,9‐テトラメチル‐5‐デシン‐4,7‐ジオール(オルフィンPD001、日信化学社製)とした以外は、実施例1と同様にしてキャストコート紙を得た。
実施例1において、キャストコート用塗料Aの界面活性剤を2,4,7,9‐テトラメチル‐5‐デシン‐4,7‐ジオール‐ジ(ポリオキシエチレン)エーテルに替えて、2,5,8,11‐テトラメチル‐6‐ドデシン‐5,8‐ジオールのポリエトキシレート(ダイノール604、エアープロダクツジャパン社製)とした以外は、実施例1と同様にしてキャストコート紙を得た。
実施例1において、キャストコート用塗料Aの界面活性剤を2,4,7,9‐テトラメチル‐5‐デシン‐4,7‐ジオール‐ジ(ポリオキシエチレン)エーテルに替えて、2,4,7,9‐テトラメチル‐5‐デシン‐4,7‐ジオール及びそのポリエトキシレートの混合物(サーフィノール485、エアープロダクツジャパン社製)とした以外は、実施例1と同様にしてキャストコート紙を得た。
実施例1において、キャストコート用塗料Aの界面活性剤を2,4,7,9‐テトラメチル‐5‐デシン‐4,7‐ジオール‐ジ(ポリオキシエチレン)エーテルに替えて、3,5‐ジメチル‐1‐ヘキシン‐3‐オール(サーフィノール61、エアープロダクツジャパン社製)とした以外は、実施例1と同様にしてキャストコート紙を得た。
無機顔料として、クレー(KAMINGLOSS、KaMin社製)64.5部、炭酸カルシウム(TP‐123、奥多摩工業社製)27部及び合成非晶質シリカ(サイロイド72W、グレースデビソン社製、体積平均粒子径3μm)8部と助剤としてポリオキシエチレンポリオキシプロピレングリコール(PE‐61、三洋化成工業社製)0.3部とを分散機にて水中に分散し、顔料スラリーBを調製した。
実施例1において、顔料スラリーAを顔料スラリーBに変更した以外は、実施例1と同様にしてキャストコート紙を得た。
無機顔料としてクレー(KAMINGLOSS、KaMin社製)58.0部、炭酸カルシウム(TP‐123、奥多摩工業社製)24部及び合成非晶質シリカ(サイロイド72W、グレースデビソン社製、体積平均粒子径3μm)18.0部と助剤としてポリオキシエチレンポリオキシプロピレングリコール(PE‐61、三洋化成工業社製)0.3部とを分散機にて水中に分散し、顔料スラリーCを調製した。
実施例1において、顔料スラリーAを顔料スラリーCに変更し、キャストコート用塗料の乾燥塗工量を18.5g/m2に変更した以外は、実施例1と同様にしてキャストコート紙を得た。
再湿潤液A(1%液)100部に、界面活性剤として2,4,7,9‐テトラメチル‐5‐デシン‐4,7‐ジオール‐ジ(ポリオキシエチレン)エーテル(オルフィンE1010、日信化学社製)を1.5部配合した以外は、再湿潤液Aと同様にして再湿潤液Bを調製した。再湿潤液Bの固形分濃度は、1.1%であった。
実施例1において、キャストコート用塗料Aの界面活性剤を配合せず、再湿潤液Aを再湿潤液Bに変更した以外は、実施例1と同様にしてキャストコート紙を得た。
実施例1において、再湿潤液Aを再湿潤液Bに変更した以外は、実施例1と同様にしてキャストコート紙を得た。
無機顔料としてクレー(KAMINGLOSS、KaMin社製)67.5部、炭酸カルシウム(TP‐123、奥多摩工業社製)29部及び合成非晶質シリカ(サイロイド72W、グレースデビソン社製、体積平均粒子径3μm)3.5部と助剤としてポリオキシエチレンポリオキシプロピレングリコール(PE‐61、三洋化成工業社製)0.3部とを分散機にて水中に分散し、顔料スラリーDを調製した。
実施例1において、顔料スラリーAを顔料スラリーDに変更し、キャストコート用塗料の乾燥塗工量を9g/m2に変更した以外は、実施例1と同様にしてキャストコート紙を得た。
実施例10において、キャストコート用塗料の乾燥塗工量を28g/m2に変更した以外は、実施例10と同様にしてキャストコート紙を得た。
無機顔料としてクレー(KAMINGLOSS、KaMin社製)67.5部、炭酸カルシウム(TP‐123、奥多摩工業社製)29部及び合成非晶質シリカ(サイロイド74x4500、グレースデビソン社製、体積平均粒子径9μm)3.5部と助剤としてポリオキシエチレンポリオキシプロピレングリコール(PE‐61、三洋化成工業社製)0.3部とを分散機にて水中に分散し、顔料スラリーEを調製した。
実施例1において、顔料スラリーAを顔料スラリーEに変更した以外は、実施例1と同様にしてキャストコート紙を得た。
実施例1において、界面活性剤を配合しなかった以外は、実施例1と同様にしてキャストコート紙を得た。
実施例6において、界面活性剤を配合しなかった以外は、実施例6と同様にしてキャストコート紙を得た。
実施例10において、キャストコート用塗料の乾燥塗工量を5g/m2に変更した以外は、実施例10と同様にしてキャストコート紙を得た。
実施例6において、キャストコート用塗料の乾燥塗工量を35g/m2に変更した以外は、実施例6と同様にしてキャストコート紙を得た。
無機顔料としてクレー(KAMINGLOSS、KaMin社製)52.5部、炭酸カルシウム(TP‐123、奥多摩工業社製)21部及び合成非晶質シリカ(サイロイド72W、グレースデビソン社製、体積平均粒子径3μm)26.5部と助剤としてポリオキシエチレンポリオキシプロピレングリコール(PE‐61、三洋化成工業社製)0.3部とを分散機にて水中に分散し、顔料スラリーFを調製した。
実施例1において、顔料スラリーAを顔料スラリーFに変更した以外は、実施例1と同様にしてキャストコート紙を得た。
実施例1において、キャストコート用塗料Aの界面活性剤を2,4,7,9‐テトラメチル‐5‐デシン‐4,7‐ジオール‐ジ(ポリオキシエチレン)エーテル(オルフィンE1010、日信化学社製)に替えて、ジメチル,メチル(ポリエチレンオキサイトアセテートシロキサン)(57ADDITIVE、東レ・ダウコーニング社製)とした以外は、実施例1と同様にしてキャストコート紙を得た。
実施例1において、キャストコート用塗料Aの界面活性剤を2,4,7,9‐テトラメチル‐5‐デシン‐4,7‐ジオール‐ジ(ポリオキシエチレン)エーテル(オルフィンE1010、日信化学社製)に替えて、ジメチルポリシロキサンポリオキシアルキレン共重合体(SN−8X 3200、サンノプコ社製)とした以外は、実施例1と同様にしてキャストコート紙を得た。
無機顔料としてクレー(KAMINGLOSS、KaMin社製)64.5部、炭酸カルシウム(TP‐123、奥多摩工業社製)27部及びコロイダルシリカ(サイロジェット4000A、グレースデビソン社製、体積平均粒子径30〜40nm)8部と助剤としてポリオキシエチレンポリオキシプロピレングリコール(PE‐61、三洋化成工業社製)0.3部とを分散機にて水中に分散し、顔料スラリーGを調製した。コロイダルシリカの含有量は、キャストコート層の乾燥質量に対して、6.0%であった。
実施例1において、顔料スラリーAを顔料スラリーGに変更した以外は、実施例1と同様にしてキャストコート紙を得た。
無機顔料としてクレー(KAMINGLOSS、KaMin社製)64.5部、炭酸カルシウム(TP‐123、奥多摩工業社製)27部及び合成非晶質シリカ(サイロジェットP‐616、グレースデビソン社製、体積平均粒子径16μm)8部と助剤としてポリオキシエチレンポリオキシプロピレングリコール(PE‐61、三洋化成工業社製)0.3部とを分散機にて水中に分散し、顔料スラリーHを調製した。
実施例1において、顔料スラリーAを顔料スラリーHに変更した以外は、実施例1と同様にしてキャストコート紙を得た。
キャストコート層側の表面に、インクジェットプリンター(HP DeskJet560J、ヒューレットパッカード社製)のインクカートリッジにUVインク(ブラックインク 型番SPC−0516、ミマキエンジニアリング社製)を注入し、テスト印字パターン(罫線及びベタ)を印字し、紫外線ランプ(メタルハライドタイプMB−250N、GSユアサ社製)を80W/cmで2秒間照射して、硬化させた後、画像のムラ感及び均一性を視感で評価した。評価基準は、次のとおりである。
◎:ムラがなく、均一性が優れている(実用レベル)、
○:ムラがなく、均一性が良好である(実用レベル)、
△:ムラがなく、均一性がある(実用下限レベル)、
×:ムラが著しい(実用不適レベル)。
キャストコート層側の表面に、溶剤インクジェットプリンター(JV‐3、ミマキエンジニアリング社製)を用いて、ヒーター温度40℃にてテスト印字パターン(罫線及びベタ)を印字し、印字終了後30秒経過後、1分経過後又は2分経過後に、罫線印字部を指で擦り、乾燥性を視感で評価した。評価基準は、次のとおりである。
◎:印字終了後、30秒経過後に擦って印字がカスれない(実用レベル)、
○:印字終了後、1分経過後に擦って印字がカスれない(実用レベル)、
△:印字終了後、2分経過後に擦って印字がカスれない(実用下限レベル)、
×:印字終了後、2分経過した後に印字部を擦っても印字にカスレを生じる(実用不適レベル)。
キャストコート層側の表面に、溶剤インクジェットプリンター(JV‐3、ミマキエンジニアリング社製)を用いて、ヒーター温度40℃にてテスト印字パターン(罫線及びベタ)を印字し、画像のムラ感及び均一性を視感で評価した。評価基準は、次のとおりである。
◎:ムラがなく、均一性が優れている(実用レベル)、
○:ムラがなく、均一性が良好である(実用レベル)、
△:ムラがなく、均一性がある(実用下限レベル)、
×:ムラが著しい(実用不適レベル)。
紫外線硬化インクジェットインク適性又は溶剤インクジェトインク適性試験で得られた印字画像部を指で擦り、印字画像の擦れ落ち易さを評価した。
◎:画像及びキャスト光沢面の密着性が非常に良く、擦れ落ち難い(実用レベル)、
○:画像及びキャスト光沢面の密着性が良く、擦れ落ち難い(実用レベル)、
△:画像及びキャスト光沢面の密着性があり、擦れ落ち難い(実用下限レベル)、
×:画像及びキャスト光沢面の密着性が劣り、擦れ落ちる(実用不適レベル)。
RI印刷適性試験機(RI‐3型、明製作所社製)を使用して印刷強さを評価した。印刷速度は30rpm、印圧は8.5mmとし、インクは、プロセスインキ(SMX、東洋インキ社製)タック値15 0.4mlを使用し、1回刷りで評価を行った。評価は、200mm×250mmのキャストコート紙表面のピック数に基づいて、次に示す評価基準で視感評価した。
◎:ピックが無い(実用レベル)、
○:ピック数が1〜2個である(実用レベル)、
△:ピック数が3〜4個である(実用下限レベル)、
×:ピック数が5個以上である(実用不適レベル)。
キャストコート層側の表面の面質及び均一性の程度を目視評価した。
◎:極めて良好である(実用レベル)、
○:良好である(実用レベル)、
△:若干劣る(実用下限レベル)、
×1:光沢が不均一で面質及び均一性が劣る(実用不適レベル)。
×2:ドラムピックによって、面質及び均一性が劣る(実用不適レベル)。
JIS Z8741:1997「鏡面光沢度−測定方法」に従って、キャストコート層表面の60°光沢度を測定した。60°光沢度が、50%以上を実用レベルとし、50%未満を実用不適レベルとした。
JIS Z8741:1997「鏡面光沢度−測定方法」に従って、キャストコート層表面の20°光沢度を測定した。
Claims (4)
- 基材上に無機顔料及びバインダーを主体として含有するキャストコート用塗料を塗工した塗工面を乾燥後、該塗工面を再湿潤液で再湿潤した後、鏡面状に研磨された加熱ドラムに圧着して乾燥するリウェット法でキャストコート層を形成したキャストコート紙において、
前記キャストコート層が、更に界面活性剤を含有し、該界面活性剤がアセチレンアルコール化合物、アセチレングリコール化合物又はアセチレン系ジアルコールのポリエーテル化合物の少なくとも1種であり、
前記キャストコート層の乾燥塗工量が、8〜30g/m2であり、
表面のJIS Z8741:1997「鏡面光沢度−測定方法」に従って測定した60°における光沢度が、50%以上であることを特徴とするキャストコート紙。 - 前記界面活性剤が、前記アセチレンアルコール化合物として(1)3,5‐ジメチル‐1‐ヘキシン‐3‐オール、前記アセチレングリコール化合物として(2)2,4,7,9‐テトラメチル‐5‐デシン‐4,7‐ジオール、(3)2,4,7,9‐テトラメチル‐5‐デシン‐4,7‐ジオールのポリエトキシレート、(4)2,5,8,11‐テトラメチル‐6‐ドデシン‐5,8‐ジオールのポリエトキシレート、前記アセチレン系ジアルコールのポリエーテル化合物として(5)2,4,7,9‐テトラメチル‐5‐デシン‐4,7‐ジオール‐ジ(ポリオキシエチレン)エーテルの(1)〜(5)のうち少なくとも1種を含有することを特徴とする請求項1に記載のキャストコート紙。
- 前記無機顔料として、レーザー回折・散乱法で測定した体積平均粒子径が0.5〜10μmの合成非晶質シリカを含み、
該合成非晶質シリカの含有量が、前記キャストコート層の乾燥質量に対して、0.1〜15質量%であることを特徴とする請求項1又は2に記載のキャストコート紙。 - 基材上に無機顔料及びバインダーを主体として含有するキャストコート用塗料を塗工した塗工面を乾燥後、該塗工面を再湿潤液で再湿潤した後、鏡面状に研磨された加熱ドラムに圧着して乾燥するリウェット法でキャストコート層を形成するキャストコート紙の製造方法において、
前記キャストコート用塗料若しくは前記再湿潤液のいずれか一方又は両方が、界面活性剤を含有し、
該界面活性剤がアセチレンアルコール化合物、アセチレングリコール化合物又はアセチレン系ジアルコールのポリエーテル化合物の少なくとも1種であることを特徴とするキャストコート紙の製造方法。