JP2012057149A - 被覆体 - Google Patents
被覆体 Download PDFInfo
- Publication number
- JP2012057149A JP2012057149A JP2011172449A JP2011172449A JP2012057149A JP 2012057149 A JP2012057149 A JP 2012057149A JP 2011172449 A JP2011172449 A JP 2011172449A JP 2011172449 A JP2011172449 A JP 2011172449A JP 2012057149 A JP2012057149 A JP 2012057149A
- Authority
- JP
- Japan
- Prior art keywords
- coating
- filler
- weight
- resin
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】本発明の被覆体は、下地の上に被膜が設けられた被覆体であって、当該被膜は、結合材(a)、着色顔料(b)、及び平均粒子径1μm以上80μm未満の微粒充填材(c)を含むものであり、前記微粒充填材(c)は、吸油量50ml/100g未満の微粒充填材(c−1)、及び吸油量50ml/100g以上の微粒充填材(c−2)からなり、前記結合材(a)の固形分100重量部に対し、前記着色顔料(b)を1〜300重量部、前記微粒充填材(c)を50〜500重量部含み、前記微粒充填材(c)中に、前記吸油量50ml/100g以上の微粒充填材(c−2)を10〜90重量%含む。
【選択図】図1
Description
このような被覆材の一例として、特許文献1(特開平11−21514号公報)には、カルボニル基含有共重合体のエマルジョン及びポリヒドラジド化合物を含む樹脂分散液に、艶消し剤を含む顔料分を顔料体積濃度が25〜40%となるように含有せしめてなる水性被覆材が記載されている。
1.下地の上に被膜が設けられた被覆体であって、当該被膜は、
結合材(a)、着色顔料(b)、及び平均粒子径1μm以上80μm未満の微粒充填材(c)を含むものであり、
前記微粒充填材(c)は、
吸油量50ml/100g未満の微粒充填材(c−1)、及び
吸油量50ml/100g以上の微粒充填材(c−2)からなり、
前記結合材(a)の固形分100重量部に対し、前記着色顔料(b)を1〜300重量部、前記微粒充填材(c)を50〜500重量部含み、
前記微粒充填材(c)中に、前記吸油量50ml/100g以上の微粒充填材(c−2)を10〜90重量%含むことを特徴とする被覆体。
2.前記被膜が、さらに、平均粒子径80μm以上の粗粒充填材(d)を、前記結合材(a)の固形分100重量部に対し50〜1000重量部含むものである1.記載の被覆体。
3.前記結合材(a)が、架橋反応型有機質樹脂を含むものである1.または2.記載の被覆体。
4.前記下地が、凹凸模様を有するものである1.〜3.のいずれかに記載の被覆体。
5.前記下地が、有機質樹脂を結合材とする既存被膜を有するものである1.〜4.のいずれかに記載の被覆体。
このような結合材としては、架橋反応型有機質樹脂が好適である。架橋反応型有機質樹脂とは、被膜形成過程ないし被膜形成後に架橋反応を生じる有機質樹脂を総称するものである。
架橋反応型有機質樹脂における架橋反応性は、例えば、カルボキシル基とカルボジイミド基、カルボキシル基とエポキシ基、カルボキシル基とアジリジン基、カルボキシル基とオキサゾリン基、水酸基とイソシアネート基、カルボニル基とヒドラジノ基、エポキシ基とヒドラジノ基、エポキシ基とアミノ基、アルコキシシリル基どうし等の反応性官能基を組み合わせることによって付与することができる。これらの組み合わせは1種または2種以上で使用することができる。
架橋反応型有機質樹脂の形態としては、水溶性樹脂、水分散性樹脂、非水分散形樹脂、溶剤可溶形樹脂、無溶剤形樹脂等が挙げられる。このうち、本発明では水分散性樹脂(樹脂エマルション)が好適である。
本発明では、結合材(a)の固形分100重量部に対し、微粒充填材(c)を50〜500重量部(好ましくは100〜400重量部、より好ましくは150〜350重量部)含み、かつ、微粒充填材(c)中に、吸油量50ml/100g以上の微粒充填材(c−2)を10〜90重量%(好ましくは20〜60重量%、より好ましくは25〜50重量%)含む構成とする。
一般に、微粒充填材(c)が、低吸油量の微粒充填材(c−1)のみで構成される場合、(c−1)の量を増やすことにより、艶消し感は改善される。しかしこの場合、十分な艶消し効果が得られるまで(c−1)を増やすと、被膜が割れやすくなったり、また被膜のシール性が不十分となるといった不具合が生じるおそれがある。これに対し、本発明では、低吸油量の微粒充填材(c−1)と高吸油量の微粒充填材(c−2)を併用することにより、実用的な被膜物性が確保できる範囲内で、優れた艶消し感を得ることが可能となる。
なお、吸油量(ml/100g)とは、JIS K 5101−13−2:2004に規定されている方法によって求められる値であり、粉粒体100gに対する煮アマニ油のmlで表されるものである。
繊維状物質の吸油量は、低吸油量の微粒充填材(c−1)、高吸油量の微粒充填材(c−2)のいずれかと同程度であってもよいが、好ましくは35ml/100g以上90ml/100g以下、より好ましくは40ml/100g以上80ml/100g以下である。
本発明では、微粒子充填材として、非繊維状の微粒充填材(c−1)と、非繊維状の微粒充填材(c−2)と、上記繊維状物質とを組合わせて用いることができる。繊維状物質の含有割合は、微粒充填材(c)中に、好ましくは0.1〜20重量%、より好ましくは0.5〜10重量%である。
このような粗粒充填材(d)の吸油量は、好ましくは50ml/100g以下、より好ましくは1ml/100g以上40ml/100g以下、より好ましくは3ml/100g以上30ml/100g以下である。
一般に、凹凸模様を有する下地に塗装を行う場合、被膜の膜厚は一定になり難い傾向がある。このような膜厚の不均一化は、光沢ムラ等を引き起こすおそれがある。これに対し、本発明では、被膜の膜厚が不均一であっても、均質な艶消し感を得ることができる。
本発明では、既存被膜を除去せずに塗り替えを行っても、被膜膨れ等の不具合が抑制でき、新設被膜による美観性を長期に亘り保持することが可能となる。すなわち、塗り替え時の作業が軽減できる。
有機系被覆材における有機質樹脂の含有量は特に限定されないが、有機系塗料の固形分中に好ましくは5重量%以上、より好ましくは20〜80重量%程度である。
下地1における凹凸模様は、基材3自体に形成されたものであってもよいし、既存被膜4によって形成されたものであってもよい。図3では、既存被膜4によって凹凸模様が形成され、その凹凸模様が残存するように被膜2が設けられている。
・結合材2:カルボキシル基・エポキシ基含有アクリル樹脂エマルション(固形分50重量%、ガラス転移温度10℃)
・結合材3:カルボキシル基含有アクリル樹脂エマルション(固形分50重量%、ガラス転移温度10℃)
・着色顔料:酸化チタン(平均粒子径0.3μm、吸油量13ml/100g)
・微粒充填材1:炭酸カルシウム(平均粒子径18μm、吸油量20ml/100g)
・微粒充填材2:炭酸カルシウム(平均粒子径10μm、吸油量22ml/100g)
・微粒充填材3:シリカ粉(平均粒子径12μm、吸油量28ml/100g)
・微粒充填材4:珪藻土(平均粒子径10μm、吸油量180ml/100g)
・微粒充填材5:珪藻土(平均粒子径35μm、吸油量210ml/100g)
・微粒充填材6:シリカゲル(平均粒子径20μm、吸油量195ml/100g)
・微粒充填材7:珪灰石(平均粒子径20μm、吸油量68ml/100g、アスペクト比16)
・微粒充填材8:珪灰石(平均粒子径5μm、吸油量56ml/100g、アスペクト比12)
・造膜助剤:2,2,4−トリメチル−1,3−ペンタンジオールモノイソブチレート
・分散剤:ポリカルボン酸系分散剤
・増粘剤:セルロース系増粘剤
・消泡剤:シリコン系消泡剤
・粗粒充填材:炭酸カルシウム(平均粒子径180μm、吸油量12ml/100g)
なお微粒充填材1〜6は、いずれもアスペクト比3未満の非繊維状物質である。
(実施例1−1)
結合材1を200重量部用意し、これに対し、着色顔料を32重量部、微粒充填材1を143重量部、微粒充填材4を50重量部、造膜助剤を18重量部、水を60重量部、分散剤を2重量部、増粘剤を1重量部、消泡剤を3重量部、粗粒充填材を230重量部均一に混合することにより、被覆材を製造した。
表1〜2に示す配合の被覆材を用いた以外は、実施例1−1と同様の方法で試験を行った。結果を表1〜2に示す。
表2に示す配合の被覆材を用いた以外は、実施例1−1と同様の方法で試験を行った。結果を表2に示す。なお、比較例1−4及び1−5については、被膜に割れ発生が認められたため、他の評価は行っていない。
試験例1と同様の下地に対し、実施例1−2、1−10、及び1−11の被覆材を、それぞれ塗付け量1.8kg/m2でローラー塗装し、温度30℃、相対湿度50%、風速3m/Sの環境下で24時間乾燥させた。以上の方法で得られた試験体について、その被膜外観を観察し、割れ発生の有無の状態を評価した。その結果、実施例1−10では割れ発生は認められなかった。実施例1−11、実施例1−2では、それぞれ一部割れが認められたが、その程度は実施例1−11のほうが軽微であった。
(実施例2−1)
結合材2を200重量部用意し、これに対し、着色顔料を32重量部、微粒充填材1を143重量部、微粒充填材4を50重量部、造膜助剤を18重量部、水を60重量部、分散剤を2重量部、増粘剤を1重量部、消泡剤を3重量部、粗粒充填材を230重量部均一に混合することにより、被覆材を製造した。
この既存被膜に対し、上記方法にて得られた被覆材を、塗付け量0.8kg/m2でローラー塗装し、標準状態(温度23℃、相対湿度50%)で168時間乾燥させた。以上の方法で得られた試験体について、その被膜外観を観察し、割れ発生の有無、及び艶消し感の状態を評価した。被膜の割れについては、割れ発生が認められなかったものを「○」、割れ発生が認められたものを「×」として評価を行った。艶消し感の状態については、艶消し感に優れるものを「A」とする4段階(優:A>B>C>D:劣)で評価を行った。結果を表3に示す。
表3に示す配合の被覆材を用いた以外は、実施例2−1と同様の方法で試験を行った。結果を表3に示す。
表3に示す配合の被覆材を用いた以外は、実施例2−1と同様の方法で試験を行った。結果を表3に示す。なお、比較例2−4及び2−5については、被膜に割れ発生が認められたため、他の評価は行っていない。
試験例2で得られた試験体について、温冷繰返し試験を合計10サイクル行った後、被膜外観を確認し、膨れ発生の状態を評価した。評価は、膨れ発生が認められないものを「A」とする4段階(優:A>B>C>D:劣)で行った。その結果、実施例2−1〜2−7は「A」、実施例2−8〜2−10は「B」、実施例2−11及び比較例2−1〜2−3は「D」であった。
2:被膜
3:基材
4:既存被膜
Claims (5)
- 下地の上に被膜が設けられた被覆体であって、当該被膜は、
結合材(a)、着色顔料(b)、及び平均粒子径1μm以上80μm未満の微粒充填材(c)を含むものであり、
前記微粒充填材(c)は、
吸油量50ml/100g未満の微粒充填材(c−1)、及び
吸油量50ml/100g以上の微粒充填材(c−2)からなり、
前記結合材(a)の固形分100重量部に対し、前記着色顔料(b)を1〜300重量部、前記微粒充填材(c)を50〜500重量部含み、
前記微粒充填材(c)中に、前記吸油量50ml/100g以上の微粒充填材(c−2)を10〜90重量%含むことを特徴とする被覆体。 - 前記被膜が、さらに、平均粒子径80μm以上の粗粒充填材(d)を、前記結合材(a)の固形分100重量部に対し50〜1000重量部含むものである請求項1記載の被覆体。
- 前記結合材(a)が、架橋反応型有機質樹脂を含むものである請求項1または2記載の被覆体。
- 前記下地が、凹凸模様を有するものである請求項1〜3のいずれかに記載の被覆体。
- 前記下地が、有機質樹脂を結合材とする既存被膜を有するものである請求項1〜4のいずれかに記載の被覆体。