JP2011214030A - 溶融亜鉛系めっき鋼板の製造方法 - Google Patents
溶融亜鉛系めっき鋼板の製造方法 Download PDFInfo
- Publication number
- JP2011214030A JP2011214030A JP2010080878A JP2010080878A JP2011214030A JP 2011214030 A JP2011214030 A JP 2011214030A JP 2010080878 A JP2010080878 A JP 2010080878A JP 2010080878 A JP2010080878 A JP 2010080878A JP 2011214030 A JP2011214030 A JP 2011214030A
- Authority
- JP
- Japan
- Prior art keywords
- steel sheet
- rolling
- roll
- dip galvanized
- galvanized steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】鋼板に溶融亜鉛めっきを施し、調質圧延を施した後pH緩衝作用を有する酸性溶液に接触させ、接触終了後1〜60秒保持した後に水洗することによりめっき表面に酸化物層を形成する亜鉛系めっき鋼板の製造方法において、調質圧延は、Raが2μm以上のダルロールを用いて圧下率5%以下で圧延し、次にRaが0.1μm以下のブライトロールを用いて圧下率3%以下で圧延する、又は、Raが0.1μm以下のブライトロールを用いて圧下率3%以下で圧延し、次にRaが2μm以上のダルロールを用いて圧下率5%以下で圧延する。
【選択図】なし
Description
Raが2.0μm以上のダルロールを用いて圧下率5%以下で圧延し、次にRaが0.1μm以下のブライトロールを用いて圧下率3%以下で圧延する、
又は、
Raが0.1μm以下のブライトロールを用いて圧下率3%以下で圧延し、次にRaが2.0μm以上のダルロールを用いて圧下率5%以下で圧延する、
ことを特徴とする溶融亜鉛系めっき鋼板の製造方法である。
酸化物層の厚さ測定方法、酸化物生成面積率の測定方法、摺動特性、ハンドリング性の評価方法は以下の通りである。
酸化物層の厚さの測定には蛍光X線分析装置を使用した。測定時の管球の電圧および電流は30kVおよび100mAとし、分光結晶はTAPに設定してO−Kα線を検出した。O−Kα線の測定に際しては、そのピーク位置に加えてバックグラウンド位置での強度も測定し、O−Kα線の正味の強度が算出できるようにした。なお、ピーク位置およびバックグラウンド位置での積分時間は、それぞれ20秒とした。また、適当な大きさに劈開した膜厚96nm、54nmおよび24nmの酸化シリコン皮膜を形成したシリコンウエハーも同時に測定し、測定したO−Kα線の強度と酸化シリコン膜厚から、亜鉛系酸化物層の厚さを算出した。
極低加速SEMで表面を35μm×45μmの視野を任意の10点観察し、得られたSEM像の酸化物が生成している部分と、生成していない部分の明度差から酸化物が生成している部分の面積率を測定し、その平均値を酸化物生成面積率とした。
プレス成形性を評価するために、各供試材の摩擦係数を以下のようにして測定した。
図1は、摩擦係数測定装置を示す概略正面図である。同図に示すように、供試材から採取した摩擦係数測定用試料1が試料台2に固定され、試料台2は、水平移動可能なスライドテーブル3の上面に固定されている。スライドテーブル3の下面には、これに接したローラ4を有する上下動可能なスライドテーブル支持台5が設けられ、これを押上げることにより、ビード6による摩擦係数測定用試料1への押付荷重Nを測定するための第1ロードセル7が、スライドテーブル支持台5に取付けられている。上記押付力を作用させた状態でスライドテーブル3を水平方向へ移動させるための摺動抵抗力Fを測定するための第2ロードセル8が、スライドテーブル3の一方の端部に取付けられている。なお、潤滑油として、スギムラ化学工業(株)製の防錆洗浄油(プレトンR352L、プレトンは登録商標)を試料1の表面に塗布して試験を行った。
[条件1]
図2に示すビードを用い、押し付け荷重N:400kgf、試料の引き抜き速度(スライドテーブル3の水平移動速度):100cm/minとした。
[条件2]
図3に示すビードを用い、押し付け荷重N:400kgf、試料の引き抜き速度(スライドテーブル3の水平移動速度):20cm/minとした。
供試材とビードとの間の摩擦係数μは、式:μ=F/Nで算出した。
GIは、摺動距離が長い部位において金型へめっきが付着し摺動抵抗が増加する型かじりが問題となる。そこで、GIについて、図1に示した摩擦係数測定装置を用いて、摩擦係数の測定とは別に、摺動試験を50回繰り返し実施し、摩擦係数が0.01以上増加したときの繰り返し数を調査し、この繰り返し数を型かじり発生の限界繰り返し数として、型カジリ性を評価した。ここで、50回繰り返し摺動試験を実施しても0.01以上の摩擦係数の増加が認められない場合には、50回以上とした。試験条件は上記[3]摩擦係数の測定方法と同様に上記の条件1および条件2で実施した。
コイルのハンドリング性をシミュレートするための評価方法として、引張り試験機にロードセルにより一定の押し付け荷重を負荷したビードで供試材を挟み、引き抜き荷重を測定し摩擦係数を算出した。なお、このとき供試材と同一のサンプルをビードに貼り付け、供試材と供試材が接触する部分の摩擦係数を測定した。30mm(幅)×35mm(長さ)の形状のビードを用いて、接触面圧を0.5MPaに設定し、50mm/minの速度で引き抜いた。過去の知見から、摩擦係数が0.08以上であれば、コイルのハンドリング性に問題がないことが知られているので、摩擦係数が0.08未満を×(不良)、0.08以上を○(良好)と判定した。
調質圧延を、ダルロールによる圧延とブライトロールによる圧延を本発明法で行った後、酸性溶液と接触させて酸化物形成処理を行った本発明例は、ダルロールによる調質圧延、ブライトロールによる調質圧延のいずれか一方だけを行いその後酸化物形成処理を行わなかった比較例、ダルロールによる圧延とブライトロールによる圧延を、いずれか一方が本発明範囲を外れる条件で行った後、酸性溶液と接触させて酸化物形成処理を行った比較例、ダルロールによる調質圧延、ブライトロールによる調質圧延のいずれか一方を行った後、酸性溶液と接触させて酸化物形成処理を行った比較例に比べて、酸化物生成面積率が高く、酸化物膜厚が厚く、そのため、摩擦係数が低く、型カジリ発生の限界繰り返し数が大きく、比較例に比べて、摺動特性が向上している。また、ハンドリング性の評価が良好であることから、コイルつぶれの問題もない。
調質圧延を、ダルロールによる圧延とブライトロールによる圧延を本発明法で行った後、酸性溶液と接触させて酸化物形成処理を行った本発明例は、酸化物生成面積率が高く、ダルロールによる圧延とブライトロールによる圧延を、いずれか一方が本発明範囲を外れる条件で行った後、酸性溶液と接触させて酸化物形成処理を行った比較例、ダルロールによる調質圧延、ブライトロールによる調質圧延のいずれか一方を行った後、酸性溶液と接触させて酸化物形成処理を行った比較例に比べて、酸化物膜厚が厚いため、摩擦係数が低い。また、ハンドリング性の評価が良好であることから、コイルつぶれの問題もない。
2 試料台
3 スライドテーブル
4 ローラ
5 スライドテーブル支持台
6 ビード
7 第1ロードセル
8 第2ロードセル
9 レール
N 押付荷重
F 摺動抵抗力
Claims (4)
- 鋼板に溶融亜鉛めっきを施し、調質圧延を施した後pH緩衝作用を有する酸性溶液に接触させ、接触終了後1〜60秒保持した後に水洗することによりめっき表面に亜鉛系酸化物層を形成する溶融亜鉛系めっき鋼板の製造方法において、調質圧延は、
Raが2.0μm以上のダルロールを用いて圧下率5%以下で圧延し、次にRaが0.1μm以下のブライトロールを用いて圧下率3%以下で圧延する、
又は、
Raが0.1μm以下のブライトロールを用いて圧下率3%以下で圧延し、次にRaが2.0μm以上のダルロールを用いて圧下率5%以下で圧延する、
ことを特徴とする溶融亜鉛系めっき鋼板の製造方法。 - 前記pH緩衝作用を有する酸性溶液は、酢酸塩、フタル酸塩、クエン酸塩、コハク酸塩、乳酸塩、酒石酸塩、ホウ酸塩、リン酸塩、硫酸塩のうちの少なくとも1種以上を含有し、pHが1.0〜5.0の範囲にある酸性溶液であることを特徴とする請求項1に記載の溶融亜鉛系めっき鋼板の製造方法。
- pH緩衝作用を有する酸性溶液に接触終了時のめっき鋼板表面の液膜量を15g/m2以下にすることを特徴とする請求項1又は2に記載の溶融亜鉛系めっき鋼板の製造方法。
- 溶融亜鉛めっきを施した後めっき層の合金化処理を行い、その後請求項1記載の調質圧延を施すことを特徴とする請求項1〜3のいずれかの項に記載の溶融亜鉛系めっき鋼板の製造方法。