JP2011026560A - 塗料用水性樹脂 - Google Patents
塗料用水性樹脂 Download PDFInfo
- Publication number
- JP2011026560A JP2011026560A JP2010138421A JP2010138421A JP2011026560A JP 2011026560 A JP2011026560 A JP 2011026560A JP 2010138421 A JP2010138421 A JP 2010138421A JP 2010138421 A JP2010138421 A JP 2010138421A JP 2011026560 A JP2011026560 A JP 2011026560A
- Authority
- JP
- Japan
- Prior art keywords
- aqueous resin
- coating film
- meth
- mass
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】アミノ基を有するエチレン性不飽和モノマー(a)と、アルコキシシリル基を有するエチレン性不飽和モノマー(b)と、カルボキシル基を有するエチレン性不飽和モノマー(c)を含有するモノマー混合物を共重合して得られる塗料用水性樹脂であって、前記アミノ基を有するエチレン性不飽和モノマー(a)の含有量が、前記モノマー混合物100質量%中、5.00〜95.00質量%であることを特徴とする塗料用水性樹脂。
【選択図】なし
Description
しかし、疎水性の塗料が塗布された外壁などは、車の排気ガス等による油性の汚れや土埃などの汚染物が付着したり、付着した汚染物が雨で流され、その跡が雨筋汚れとして目立ったりしやすかった。特に、建築物の形状により雨筋汚れが付きやすいと、建築物の外観や価値を低下させることとなる。そのため、定期的な洗浄や塗料の塗り替えなどの作業が欠かせなかった。
塗膜に耐汚染性を付与する方法としては、塗膜の表面を親水化する方法が知られている。塗膜の表面が親水性を帯びることで、親和性の異なる油性の汚れが付着しにくくなる。しかも雨が降った際には雨滴が親水性の塗膜表面を洗い流し、油性の汚れや土埃などの汚染物を容易に除去でき、雨筋汚れの付着をも防止できる。
このように、疎水性を帯びた塗膜は耐水性や耐候性に優れるものの耐汚染性に劣り、一方、親水性を帯びた塗膜は耐汚染性に優れるものの耐水性や耐候性に劣り、これら相反する性能を両立するための検討がなされてきた。
また、特許文献2には、親水基を含有する化合物で表面処理されたコロイダルシリカを含有する水性塗料組成物が開示されている。該水性塗料組成物によれば、耐汚染性、耐水性、耐候性等に優れた塗膜を形成できる。
さらに、耐汚染性、耐候性等に優れた塗膜を形成できる塗料として、特許文献4には、フッ素系樹脂に、2−アクリルアミド−2−メチルプロパンスルホン酸などのスルホン酸基を有する単量体を共重合してなる低汚染化剤を配合した塗料用組成物が開示されている。
また、コロイダルシリカは顔料結合力を有さないため、塗料の臨界顔料容積濃度(臨界PVC)が低下してチョーキングが発生したり、塗料の流動安定性が低下したりしやすかった。
特許文献4に記載の塗料用組成物では、耐汚染性に優れる塗膜を形成することはできるものの、塗膜の耐水性を満足することはできなかった。
また、前記アルコキシシリル基を有するエチレン性不飽和モノマー(b)の含有量が、前記モノマー混合物100質量%中、0.01〜5.00質量%であることが好ましい。
さらに、前記カルボキシル基を有するエチレン性不飽和モノマー(c)の含有量が、前記モノマー混合物100質量%中、0.50〜20.00質量%であることが好ましい。
本発明の塗料用水性樹脂(以下、「水性樹脂」という。)は、アミノ基を有するエチレン性不飽和モノマー(a)と、アルコキシシリル基を有するエチレン性不飽和モノマー(b)と、カルボキシル基を有するエチレン性不飽和モノマー(c)を含有するモノマー混合物を共重合して得られる樹脂である。
なお、本発明において、「(メタ)アクリル酸」とは、メタクリル酸とアクリル酸の両方を示し、「(メタ)アクリロキシ」とは、メタクリロキシとアクリロキシの両方を示すものとする。
アミノ基を有するエチレン性不飽和モノマー(a)(以下、「(a)成分」という。)は、得られる水性樹脂を塗料に用いることで、形成される塗膜を親水化して耐汚染性を付与すると共に、塗膜の耐水性をも向上させることを目的として用いる。
これら(a)成分は1種単独で用いてもよく、2種以上を併用してもよい。
アルコキシシリル基を有するエチレン性不飽和モノマー(b)(以下、「(b)成分」という。)は、水性樹脂を架橋することを目的として用いる。架橋した水性樹脂を塗料に用いることで、塗膜に耐水性、耐候性、耐汚染性を付与できる。
水性樹脂が架橋すると、光、熱、水、酸、アルカリなどの外的要因に起因したポリマー鎖の切断が緩和される。従って、架橋した水性樹脂を添加剤として用いた塗料より形成される塗膜は耐候性が向上する。
また、塗膜において造膜界面(すなわち、塗膜形成時の粒子融着部分)は、親水基が局在化するため最も水を吸収しやすい部分であるが、架橋により補強された水性樹脂を添加剤として塗料に用いると、それより形成される塗膜に水が浸水しても塗膜中の水分局在化が抑制されるため、塗膜の白化を抑制できる。さらに、架橋により水性樹脂が補強されることで、油性の汚れや土埃などの汚染物の水性樹脂への付着を防止でき、その結果、塗膜の耐汚染性が向上する。
これら(b)成分は1種単独で用いてもよく、2種以上を併用してもよい。
カルボキシル基を有するエチレン性不飽和モノマー(c)(以下、「(c)成分」という。)は、水性樹脂の安定性を維持することを目的として用いる。
しかし、本発明では(c)成分を併用することで、得られる水性樹脂に適度な電荷が付与されるので、水性樹脂が水に分散または溶解した際に、樹脂同士の電荷の反発により水中で安定した状態を維持できる。
モノマー混合物には、上述した(a)成分、(b)成分、および(c)成分以外のその他のモノマーが含まれていてもよい。
その他のモノマーとしては、(a)成分、(b)成分、および(c)成分と共重合可能なエチレン性不飽和モノマーが挙げられ、具体的には以下に示す化合物が挙げられる。
メチル(メタ)アクリレート、エチル(メタ)アクリレート、n−プロピル(メタ)アクリレート、イソプロピル(メタ)アクリレート、n−ブチル(メタ)アクリレート、イソブチル(メタ)アクリレート、sec−ブチル(メタ)アクリレート、tert−ブチル(メタ)アクリレート、n−ペンチル(メタ)アクリレート、n−ヘキシル(メタ)アクリレート、2−エチル−n−ヘキシル(メタ)アクリレート、n−オクチル(メタ)アクリレート、n−ノニル(メタ)アクリレート、ラウリル(メタ)アクリレート、ステアリル(メタ)アクリレート、シクロヘキシル(メタ)アクリレート、2−ヒドロキシエチル(メタ)アクリレート、2−ヒドロキシプロピル(メタ)アクリレート、ベンジル(メタ)アクリレート、グリシジル(メタ)アクリレート、テトラヒドロフルフリル(メタ)アクリレート、フェノキシエチル(メタ)アクリレート、イソボルニル(メタ)アクリレート、メトキシポリエチレングリコール(メタ)アクリレート等の(メタ)アクリル酸エステル類。
(メタ)アクロレイン、クロトンアルデヒド、ビニルメチルケトン、ビニルエチルケトン、ジアセトンアクリルアミド、2−アセトアセトキシエチル(メタ)アクリレート等のカルボニル基を有するモノマー。
2−アクリルアミド−2−メチルプロパンスルホン酸、スチレンスルホン酸、アリルスルホン酸、スルホエトキシ(メタ)アクリレート等のスルホ基を有するモノマー。
ジビニルベンゼン、ジビニルエーテル、アリル(メタ)アクリレート、フタル酸ジアリル、エチレングリコールジ(メタ)アクリレート、ジエチレングリコールジ(メタ)アクリレート、トリメチロールプロパントリ(メタ)アクリレート、ペンタエリスリトールテトラ(メタ)アクリレート等の多官能重合性モノマー。
(メタ)アクリロニトリル、(メタ)アクリルアミド、N−ヒドロキシメチル(メタ)アクリルアミド等のビニル化合物。
本発明の水性樹脂は、例えば以下のようにして調製できる。
反応容器に、(a)成分、(b)成分、(c)成分と、必要に応じてその他のモノマーを含むモノマー混合物と、重合開始剤と、有機溶媒とを投入し、攪拌しながら70〜80℃に加熱して3〜4時間保持し、重合反応を行う。反応が終了した後、冷却し、中和剤を添加して中和する。その後、水を加え、さらに有機溶媒をエバポレーター等で除去し、水性樹脂を得る。なお、このようにして得られる水性樹脂の状態は、微細なポリマー粒子(水性樹脂)が水に分散したエマルジョンの状態である。
これら有機溶媒は1種単独で用いてもよく、2種以上を併用してもよい。
これら重合開始剤は1種単独で用いてもよく、2種以上を併用してもよい。また、還元剤と組み合わせることで、重合反応の速度を速める場合もある。
これら連鎖移動剤は1種単独で用いてもよく、2種以上を併用してもよい。
本発明の水性樹脂は、バインダー樹脂との質量比(固形分比)がバインダー樹脂:水性樹脂=100:5〜100:15となるように用いるのが好ましい。
市販の塗料に添加する場合、その添加量は、塗料に含まれるバインダー樹脂との質量比(固形分比)が、上述した範囲内となるように適宜決定すればよい。
攪拌機を備えた内容量2Lのセパラブルフラスコに、(a)成分としてメタクリル酸ジメチルアミノエチルを140部、(b)成分として3−アクリロキシプロピルトリメトキシシランを2部、(c)成分としてメタクリル酸を16部、およびその他のモノマーとしてメチルメタクリレートを42部と、有機溶媒として2−プロパノールを600部と、連鎖移動剤としてn−ドデシルメルカプタン2部を仕込み、攪拌しながら70℃まで昇温した。その後70℃にて、重合開始剤として2,2’−アゾビスイソブチロニトリルを2部添加し、内温75℃にて4時間保持し、重合反応を行った。その後、40℃まで冷却し、25%アンモニア水20部および水780部を加え、均一になるまで攪拌を続け、固形分12.5%の液体を得た。ついで、ロータリーエバポレーターで2−プロパノールを留去し、固形分20%の水性樹脂(A)を得た。
各成分の種類および量を表1、2に示す値に変更した以外は、水性樹脂(A)と同様にして固形分20%の水性樹脂(B〜R)を得た。
水12部、ノプコスパース44Cを1部、プロピレングリコールを2部、SNデフォーマー1320を0.1部、ヒドロキシエチルセルロースSP400を0.2部混合し、さらに25%アンモニア水を0.1部と、ベンゾチアゾール系防腐剤を0.1部加えて混合した後、ガラスビーズと共に高速ディスパーで攪拌しつつ、酸化チタン30部を徐々に添加して、白ペーストを得た。
得られた白ペーストを45.5部、アクリルシリコーン系エマルジョン(固形分45%、最低造膜温度0℃、粒子径0.1μm、pH8.5)を150部、テキサノールを4部、SNシックナー641を1部混合し、白ベース塗料Aを調製した。
アクリルシリコーン系エマルジョン(固形分45%、最低造膜温度0℃、粒子径0.1μm、pH8.5)を100部と、テキサノールを2部混合し、クリアベース塗料Aを調製した。
白ベース塗料Aの調製で得た白ペーストを45.5部、フッ素系エマルジョン(固形分50%、最低造膜温度30℃、粒子径0.2μm、pH8.0)を67.5部、アクリルエマルジョン(固形分50%、最低造膜温度0℃、粒子径0.2μm、pH8.0)を67.5部、テキサノールを6部、SNシックナー641を1部混合し、白ベース塗料Bを調製した。
フッ素系エマルジョン(固形分50%、最低造膜温度30℃、粒子径0.2μm、pH8.0)を50部と、アクリルエマルジョン(固形分50%、最低造膜温度0℃、粒子径0.2μm、pH8.0)を50部混合し、これにテキサノールを4部添加して、クリアベース塗料Bを調製した。
<白塗料Aの調製>
白ベース塗料A100部(樹脂固形分:34部)に、水性樹脂(A)17部(樹脂固形分:3.4部)を添加し、白塗料Aを調製した。
クリアベース塗料A100部(樹脂固形分:44部)に、水性樹脂(A)22部(樹脂固形分:4.4部)を添加し、クリア塗料Aを調製した。
(造膜性の評価)
ポリエチレン製の板(100×100×5mm)に、乾燥膜厚が0.5mmになるように白塗料Aを塗布した。その後、温度23℃、湿度65%RHの条件下で1日間乾燥させて塗膜を形成した。塗膜の状態を目視にて観察し、以下に示す評価基準にて評価した。結果を表3に示す。
○:連続膜が形成された。
△:塗膜表面に僅かにクラックが発生した。
×:塗膜表面に深いクラックが発生した。
ガラス板に、アプリケータを用いて乾燥膜厚が0.25mmになるように白塗料Aを塗布した。その後、温度23℃、湿度65%RHの条件下で1日間乾燥させて塗膜を形成した。
形成した塗膜について、60度の鏡面光沢度をJIS Z8741に準拠して、鏡面光沢計(BYK−Gardner社製)を用いて測定した。結果を表3に示す。なお、鏡面光沢度は数値が大きいほど光沢が高いことを示す。
スレート板(70×150×3mm)に、溶剤ウレタン系下塗り塗料(2液)を塗布した。室温下で1日間乾燥させた後、水系下塗り塗料(1液)をさらに塗布し、室温下で4時間乾燥させた。その後、乾燥膜厚が0.5mmになるように白塗料Aを塗布し、室温下で1週間乾燥させて試験片を作製した。得られた試験片について、Lab値をJIS Z8741に準拠して、測色計(コニカミノルタセンシング株式会社製)を用いて測定した。
ついで、70℃で石油を燃焼させたススが舞う煤煙試験機内に試験片を1時間放置し、煤煙処理を施した。その後、エアブローでススを払い、スポンジで水洗した。煤煙処理後の試験片について、先と同様にしてLab値を測定し、下記式(1)よりΔEを求めた。結果を表3に示す。なお、ΔEは数値が小さいほど耐汚染性に優れることを意味する。
ΔE=煤煙処理前の試験片のLab値−煤煙処理後の試験片のLab値 ・・・(1)
ポリエチレン製の板(100×100×5mm)に、乾燥膜厚が0.5mmになるようにクリア塗料Aを塗布した。その後、温度23℃、湿度65%RHの条件下で1日間乾燥させ、ついで50℃で1日間乾燥させて塗膜を形成した。
得られた塗膜を25mm角に切断し、これを純水に1日間浸漬させた。浸漬後の塗膜の色調を目視にて観察し、以下に示す評価基準にて評価した。結果を表3に示す。
○:塗膜は透明である。
△:塗膜にやや青みがある。
×:塗膜が白化し、不透明である。
水性樹脂として表3〜5に示す種類の水性樹脂を用いた以外は、実施例1−1と同様にして白塗料Aおよびクリア塗料Aを調製し、各評価を行った。結果を表3〜5に示す。
従って、本発明の水性樹脂であれば、塗膜に優れた耐汚染性と耐水性を付与できる。
(a)成分を含有しないモノマー混合物を共重合して得た水性樹脂(N)を用いて調製した比較例1−2の白塗料Aは、塗膜の耐汚染性が低かった。
(c)成分を含有しないモノマー混合物を共重合して得た水性樹脂(O)を用いて調製した比較例1−3の白塗料Aおよびクリア塗料Aは、水性樹脂の合成中に凝集が生じたため、評価の対象とならなかった。
(b)成分を含有しないモノマー混合物を共重合して得た水性樹脂(P)を用いて調製した比較例1−4のクリア塗料Aは、塗膜の耐水性が低かった。また、比較例1−4で得られた白塗料Aは、実施例に比べて塗膜の耐汚染性が低かった。
(a)成分の含有量が3.0質量%と少ないモノマー混合物を共重合して得た水性樹脂(Q)を用いて調製した比較例1−5の白塗料Aは、塗膜の耐汚染性が低かった。
(a)成分の含有量が98.0質量%と多いモノマー混合物を共重合して得た水性樹脂(R)を用いて調製した比較例1−6の白塗料Aおよびクリア塗料Aは、水性樹脂の合成中に凝集が生じたため、評価の対象とならなかった。
<白塗料Bの調製>
白ベース塗料B100部(樹脂固形分:36部)に、水性樹脂(A)18部(樹脂固形分:3.6部)を添加し、白塗料Bを調製した。
クリアベース塗料B100部(樹脂固形分:48部)に、水性樹脂(A)24部(樹脂固形分:4.8部)を添加し、クリア塗料Bを調製した。
水性樹脂として表6〜8に示す種類の水性樹脂を用いた以外は、実施例2−1と同様にして白塗料Bおよびクリア塗料Bを調製し、各評価を行った。結果を表6〜8に示す。
従って、本発明の水性樹脂であれば、塗膜に優れた耐汚染性と耐水性を付与できる。
(a)成分を含有しないモノマー混合物を共重合して得た水性樹脂(N)を用いて調製した比較例2−2の白塗料Bは、塗膜の耐汚染性が低かった。
(c)成分を含有しないモノマー混合物を共重合して得た水性樹脂(O)を用いて調製した比較例2−3の白塗料Bおよびクリア塗料Bは、水性樹脂の合成中に凝集が生じたため、評価の対象とならなかった。
(b)成分を含有しないモノマー混合物を共重合して得た水性樹脂(P)を用いて調製した比較例2−4のクリア塗料Bは、塗膜の耐水性が低かった。また、比較例2−4で得られた白塗料Bは、実施例に比べて塗膜の耐汚染性が低かった。
(a)成分の含有量が3.0質量%と少ないモノマー混合物を共重合して得た水性樹脂(Q)を用いて調製した比較例2−5の白塗料Bは、塗膜の耐汚染性が低かった。
(a)成分の含有量が98.0質量%と多いモノマー混合物を共重合して得た水性樹脂(R)を用いて調製した比較例2−6の白塗料Bおよびクリア塗料Bは、水性樹脂の合成中に凝集が生じたため、評価の対象とならなかった。
Claims (3)
- アミノ基を有するエチレン性不飽和モノマー(a)と、アルコキシシリル基を有するエチレン性不飽和モノマー(b)と、カルボキシル基を有するエチレン性不飽和モノマー(c)を含有するモノマー混合物を共重合して得られる塗料用水性樹脂であって、
前記アミノ基を有するエチレン性不飽和モノマー(a)の含有量が、前記モノマー混合物100質量%中、5.00〜95.00質量%であることを特徴とする塗料用水性樹脂。 - 前記アルコキシシリル基を有するエチレン性不飽和モノマー(b)の含有量が、前記モノマー混合物100質量%中、0.01〜5.00質量%であることを特徴とする請求項1に記載の塗料用水性樹脂。
- 前記カルボキシル基を有するエチレン性不飽和モノマー(c)の含有量が、前記モノマー混合物100質量%中、0.50〜20.00質量%であることを特徴とする請求項1または2に記載の塗料用水性樹脂。