JP2010116490A - 塗布用アンカーコート剤 - Google Patents
塗布用アンカーコート剤 Download PDFInfo
- Publication number
- JP2010116490A JP2010116490A JP2008291060A JP2008291060A JP2010116490A JP 2010116490 A JP2010116490 A JP 2010116490A JP 2008291060 A JP2008291060 A JP 2008291060A JP 2008291060 A JP2008291060 A JP 2008291060A JP 2010116490 A JP2010116490 A JP 2010116490A
- Authority
- JP
- Japan
- Prior art keywords
- coating
- anchor
- weight
- parts
- silicone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】有機溶媒中に、(1)一般式RnSi(OR1)4−n(式中、Rは有機基を表す。OR1は加水分解可能な基を表す。nは0〜2の整数を表す。)で表されるアルコキシシランと、(2)一般式R2 mSi(OR3)4−m(式中、R2は、(メタ)アクリロイル基を表す。mは1〜2の整数を表す。)で表されるアルコキシシランと、金属キレートとを添加して得られた塗布用アンカーコート剤(ただし、前記(1)で表されるアルコキシシランは、(メタ)アクリロイル基を有することはない)。
【選択図】なし
Description
そのため、従来の機能性シリコーン組成物についてはプラスチックフィルムへの密着性を良くする目的で、ある種のシラン、シロキサンなどを配合して自己接着性を付与することも提案されている。これらはいずれも縮合反応を用いて硬化させるもので、硬化に高温が必要とされるため、プラスチックフィルム上に硬化シリコーン被膜を形成するにあっては不向きである。また、このエポキシ基を末端または側鎖に含有するシロキサンを用い、これを付加反応で硬化させるようにした組成物も知られている。しかしながら硬化皮膜の非粘着性において満足できるものではなかった。
なお、従来技術としては、下記特許文献1〜7が例示される。
請求項2に記載の発明は、前記有機溶媒が、親水性溶媒と疎水性有機溶媒の両者をともに含むことを特徴とする請求項1記載の塗布用アンカーコート剤である。
請求項3に記載の発明は、前記金属キレートが、一般式R4OH(R4は炭素1〜8のアルキル基を示す。)及び/又はR5COCH2COR6(R5は炭素1〜8のアルキル基、R6は炭素1〜8のアルキル基又はアルコキシ基を示す。)で表される化合物を配位子とし中心に金属を有する少なくとも1種類の金属キレートであることを特徴とする請求項1記載の塗布用アンカーコート剤である。
請求項4に記載の発明は、 前記(1)アルコキシシラン100重量部に対し、(2)アルコキシシランが20〜500重量部の割合で添加され、前記(1)および(2)のアルコキシシランが0.2〜3.0重量%の割合で添加され、前記金属キレートが前記(1)および(2)のアルコキシシランに対して0.5〜30.0重量%の割合で添加されることを特徴とする請求項1記載の塗布用アンカーコート剤である。
請求項5に記載の発明は、前記塗布用アンカーコート剤溶液中に含まれる水分が、全アルコキシシランを加水分解するに必要な理論水分量の0.5〜1.5倍であることを特徴とする請求項4記載の塗布用アンカーコート剤である。
請求項6に記載の発明は、前記塗布用アンカーコート剤溶液により形成されたアンカーコート層の硬化温度が100〜200℃であり、かつ硬化時間が10〜60秒であることを特徴とする請求項1記載の塗布用アンカーコート剤である。
請求項7に記載の発明は、基材上に、請求項1〜6のいずれかに記載の塗布用アンカーコート剤溶液を用いてアンカーコート層を設け、さらに該アンカーコート層上にシリコーン層を形成したことを特徴とする積層体である。
アルコキシシラン濃度が低い場合、反応は不十分であり、成膜性が悪くなることがある。一方、アルコキシシラン濃度が高い場合、反応が速い、アンカーコート剤の安定性が弱く、密着性も悪くなる。また、(1)アルコキシシラン100重量部に対し、(2)アルコキシシランが20〜500重量部の割合の範囲外であると、アンカーコート効果が十分に発揮されなくなり、密着性が弱くなる恐れがある。さらに、金属キレートの添加量が上記範囲外であると、反応促進不十分(0.5重量%未満)または成膜阻害(30.0重量%超)となる恐れがある。
さらに、アルコキシシランの濃度が0.2〜3.0重量%であるために、アルコキシシラン加水分解反応速度を調整することができる。
プラスチック基材(特に光学フィルム)は熱収縮し易いため、硬化時間が長く、又は硬化温度が高くなると熱シワが多くなる。本発明は上記の特徴を持っているために、熱シワの改善することができる。
本発明の塗布用アンカーコート剤は、例えば、室温で1時間攪拌した後、基材上に塗布し、100〜200℃で加熱乾燥、硬化させることによりアンカーコート層を形成することができる。その上に、シリコーン層を作製する。得られた積層体は優れた密着性を持っている。
ハードコート層としては、透明性が高く、反射防止材の表面硬度、機械強度を向上させるものであれば特に限定するものではなく、公知のものを用いることができる。
<アンカーコート剤(塗液)>
3−メタクリロキプロピルトリエトキシシラン(信越化学製) 2.5重量部
テトラエトキシラン(東京化成製) 2.5重量部
アルミキレートBY24−846E
(東レ・ダウェーニング社製40wt%) 2.5重量部
トルエンとメチルエチルケトン(1:1wt%) 492重量部
蒸留水(溶媒中含まれた水分と合わせて) 1.2重量部
各成分を混合して約1時間攪拌するとアンカーコート剤塗液が得られた。
<シリコーン機能性層形成材料(塗液)>
シリコリースUV POLY200(荒川化学工業(株)製) 4重量部
シリコリースUV CVATA211
(光開始剤/モメンティブ製) 0.2重量部
酢酸エチル 48重量部
n−ヘキサン 48重量部
以上により、実施例1のシリコーン機能性フィルムを作製した。
硬化直後のシリコーン機能性層及びこれを室温下で半年間保存後の硬化シリコーン機能性層の表面を人差し指で1 0 回(往復)擦った後、黒マジックインキを塗布して、表面の状態を観察し、下記の基準で評価した。
◎ : 硬化シリコーン機能性層の全面でマジックインキを弾く、
○ : 擦った部分に僅かにマジックインキが塗布される、
◇ : 擦った部分にマジックインキが塗布される、
△ : マジックインキが塗布される〜 シリコーン機能性層が部分的に脱落する、
× : シリコーン機能性層が脱落する。
得られたシリコーン機能性フィルムは自動分光光度計(日立製作所製、U−4000)を用い、C光源、2度視野の条件下で、低屈折率層形成面について入射角5°における分光透過率を測定した。
硬化後のシリコーン機能性層を40℃、90%湿度の環境下で1ヶ月保存した後、25℃、50%湿度で1日放置した。そのシリコーン機能性層の表面を人差し指で10 回(往復)擦った後、黒マジックインキを塗布して、表面の状態を観察し、上記の基準で評価した。
硬化後のシリコーン機能性層を90℃蒸留水中に浸漬5時間後、25℃、50%湿度で1日放置した。そのシリコーン機能性層の表面を人差し指で10 回(往復)擦った後、黒マジックインキを塗布して、表面の状態を観察し、上記の基準で評価した。
得られたシリコーン機能性層と半年間保存後の硬化シリコーン機能性層の表面の上で、油性黒マジックインキを塗布して、キムタオル(日本製紙クレシア社製)で10回軽く擦る。表面の状態を観察し、下記の基準で評価した。
A: マジックインキが完全に無くなる、
B: マジックインキが僅かに残る、
C: マジックインキが残る。
実施例1の評価結果は表1に示した。その結果から、アンカーコート層がある場合、得られたシリコーン機能性フィルムは防汚性、高い透明性と優れた密着性を持っていることが分かった。
<シリコーン機能性層形成材料(塗液)>
シリコーン LTC750A(東レ・ダウェーニング(株)製) 2重量部
シリコーン触媒 SRX−212(東レ・ダウェーニング(株)製)0.02重量部
トルエン 49重量部
メチルエチルケトン 49重量部
実施例2の評価結果は表1に示した。その結果から、アンカーコート層がある場合、得られたシリコーン機能性フィルムは優れた密着性、防汚性と高い透明性を持っていることが分かった。
<アンカーコート剤(塗液)>
3−アクリロキシプロピルトリエトキシシラン(信越化学製) 2.5重量部
テトラエトキシラン(東京化成製) 2.5重量部
アルミキレートBY24−846E
(東レ・ダウェーニング社製40wt%) 2.5重量部
トルエンとメチルエチルケトン(1:1wt%) 492重量部
蒸留水(溶媒中含まれた水分と合わせて) 1.2重量部
各成分を混合して約1時間攪拌するとアンカーコート剤塗液が得られた。
<シリコーン機能性層形成材料(塗液)>
シリコーン LTC750A(東レ・ダウェーニング(株)製) 2重量部
シリコーン触媒 SRX−212(東レ・ダウェーニング(株)製) 0.02重量部
トルエン 49重量部
メチルエチルケトン 49重量部
以上により、実施例3のシリコーン機能性フィルムを作製した。実施例3の評価結果から、アンカーコート層がある場合、得られたシリコーン機能性フィルムは優れた密着性、高い透明性と防汚性を持っている。
<アンカーコート剤(塗液)>
3−メタクリロキプロピルトリエトキシシラン(信越化学社製) 2.5重量部
3−グリシドキシプロピルトリエトキシシラン(信越化学社製) 2.5重量部
アルミキレートBY24−846E
(東レ・ダウェーニング社製40wt%) 2.5重量部
トルエンとメチルエチルケトン(1:1wt%) 492重量部
蒸留水(溶媒中含まれた水分と合わせて) 1.2重量部
<アンカーコート剤(塗液)>
3−メタクリロキプロピルトリエトキシシラン(信越化学社製) 4.5重量部
3−グリシドキシプロピルトリエトキシシラン(信越化学社製) 0.5重量部
アルミキレートBY24−846E
(東レ・ダウェーニング社製40wt%) 2.5重量部
トルエンとメチルエチルケトン(1:1wt%) 492重量部
蒸留水(溶媒中含まれた水分と合わせて) 1.2重量部
<アンカーコート(塗液)>
3−メタクリロキプロピルトリエトキシシラン(信越化学社製) 0.5重量部
3−グリシドキシプロピルトリエトキシシラン(信越化学社製) 4.5重量部
アルミキレートBY24−846E
(東レ・ダウェーニング社製40wt%) 2.5重量部
トルエンとメチルエチルケトン(1:1wt%) 492重量部
蒸留水(溶媒中含まれた水分と合わせて) 1.2重量部
<アンカーコート剤(塗液)>
3−メタクリロキプロピルトリエトキシシラン(信越化学社製) 2.5重量部
3−グリシドキシプロピルトリエトキシシラン(信越化学社製) 2.5重量部
アルミキレートBY24−846E
(東レ・ダウェーニング社製40wt%) 5.0重量部
トルエンとメチルエチルケトン(1:1wt%) 488重量部
蒸留水(溶媒中含まれた水分と合わせて) 1.2重量部
<アンカーコート剤(塗液)>
3−メタクリロキプロピルトリエトキシシラン(信越化学社製) 2.5重量部
3−グリシドキシプロピルトリエトキシシラン(信越化学社製) 2.5重量部
アルミキレートBY24−846E
(東レ・ダウェーニング社製40wt%) 0.05重量部
トルエンとメチルエチルケトン(1:1wt%) 495重量部
蒸留水(溶媒中含まれた水分と合わせて) 1.2重量部
<アンカーコート剤(塗液)>
3−メタクリロキプロピルトリエトキシシラン(信越化学社製) 2.5重量部
3−グリシドキシプロピルトリエトキシシラン(信越化学社製) 2.5重量部
アルミキレートBY24−846E
(東レ・ダウェーニング社製40wt%) 2.5重量部
トルエンとメチルエチルケトン(1:1wt%) 491重量部
蒸留水(溶媒中含まれた水分と合わせて) 2.0重量部
<アンカーコート剤(塗液)>
3−メタクリロキプロピルトリエトキシシラン(信越化学社製) 2.5重量部
3−グリシドキシプロピルトリエトキシシラン(信越化学社製) 2.5重量部
アルミキレートBY24−846E
(東レ・ダウェーニング社製40wt%) 2.5重量部
トルエンとメチルエチルケトン(1:1wt%) 492重量部
蒸留水(溶媒中含まれた水分と合わせて) 0.5重量部
アンカーコート剤の中で、含水量は加水分解するに必要な理論水分量の0.5〜1.5倍以外になると得られたシリコーン機能性フィルムの密着性が弱くなる。
Claims (7)
- 有機溶媒中に、(1)一般式RnSi(OR1)4−n(式中、Rは有機基を表す。OR1は加水分解可能な基を表す。nは0〜2の整数を表す。)で表されるアルコキシシランと、(2)一般式R2 mSi(OR3)4−m(式中、R2は、(メタ)アクリロイル基を表す。mは1〜2の整数を表す。)で表されるアルコキシシランと、金属キレートとを添加して得られた塗布用アンカーコート剤(ただし、前記(1)で表されるアルコキシシランは、(メタ)アクリロイル基を有することはない)。
- 前記有機溶媒が、親水性溶媒と疎水性有機溶媒の両者をともに含むことを特徴とする請求項1記載の塗布用アンカーコート剤。
- 前記金属キレートが、一般式R4OH(R4は炭素1〜8のアルキル基を示す。)及び/又はR5COCH2COR6(R5は炭素1〜8のアルキル基、R6は炭素1〜8のアルキル基又はアルコキシ基を示す。)で表される化合物を配位子とし中心に金属を有する少なくとも1種類の金属キレートであることを特徴とする請求項1記載の塗布用アンカーコート剤。
- 前記(1)アルコキシシラン100重量部に対し、(2)アルコキシシランが20〜500重量部の割合で添加され、前記(1)および(2)のアルコキシシランが0.2〜3.0重量%の割合で添加され、前記金属キレートが前記(1)および(2)のアルコキシシランに対して0.5〜30.0重量%の割合で添加されることを特徴とする請求項1記載の塗布用アンカーコート剤。
- 前記塗布用アンカーコート剤溶液中に含まれる水分が、全アルコキシシランを加水分解するに必要な理論水分量の0.5〜1.5倍であることを特徴とする請求項4記載の塗布用アンカーコート剤。
- 前記塗布用アンカーコート剤溶液により形成されたアンカーコート層の硬化温度が100〜200℃であり、かつ硬化時間が10〜60秒であることを特徴とする請求項1記載の塗布用アンカーコート剤。
- 基材上に、請求項1〜6のいずれかに記載の塗布用アンカーコート剤溶液を用いてアンカーコート層を設け、さらに該アンカーコート層上にシリコーン層を形成したことを特徴とする積層体。