JP2010015971A - 金属微粒子を含有した熱処理配位高分子金属錯体を用いた燃料電池用触媒、膜電極接合体、燃料電池、及び酸化還元触媒 - Google Patents
金属微粒子を含有した熱処理配位高分子金属錯体を用いた燃料電池用触媒、膜電極接合体、燃料電池、及び酸化還元触媒 Download PDFInfo
- Publication number
- JP2010015971A JP2010015971A JP2008332433A JP2008332433A JP2010015971A JP 2010015971 A JP2010015971 A JP 2010015971A JP 2008332433 A JP2008332433 A JP 2008332433A JP 2008332433 A JP2008332433 A JP 2008332433A JP 2010015971 A JP2010015971 A JP 2010015971A
- Authority
- JP
- Japan
- Prior art keywords
- catalyst
- fuel cell
- heat
- metal complex
- metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】分子内に−NH2、=NH、=N−から選択される化学構造を2個以上含有し、平面構造を有する配位子と、金属からなる高度に構造制御された金属−N4構造を含有し、かつ、多孔質であるために高い比表面積を有する配位高分子金属錯体を熱処理した熱処理配位高分子金属錯体に金属微粒子を担持した燃料電池用触媒、又は、前記燃料電池用触媒をさらに導電性担体へ担持した触媒担持導電体、又は、前記燃料電池用触媒、あるいは前記触媒担持導電体を熱処理した熱処理触媒担持導電体からなる、酸化還元触媒、並びに、ポリマー被覆燃料電池用触媒である。
【選択図】なし
Description
1.分子内に−NH2、=NH、=N−から選択される化学構造を2個以上含有し、平面構造を有する配位子と、金属からなる多孔質骨格構造を有する配位高分子金属錯体を熱処理した熱処理配位高分子金属錯体へ金属微粒子を担持してなることを特徴とする燃料電池用触媒。
2.ピラジン骨格、ビピリジル骨格、イミダゾール骨格、ビスベンゾチアゾール骨格、ビスベンゾオキサゾール骨格からなる群から選ばれる少なくとも1種類以上の化学構造を含む前記1.に記載の配位子からなる配位高分子金属錯体を熱処理した熱処理配位高分子金属錯体へ金属微粒子を担持してなることを特徴とする燃料電池用触媒。
3.前記配位高分子金属錯体のBET比表面積が100〜5000m2/gであることを特徴とする前記1又は2.に記載の燃料電池用触媒。
4.前記金属微粒子の粒径が10nm以下であることを特徴とする前記1〜3.のいずれかに記載の燃料電池用触媒。
5.前記金属微粒子は遷移金属であることを特徴とする前記1〜4.のいずれかに記載の燃料電池用触媒。
6.前記金属微粒子は貴金属であることを特徴とする前記1〜5.のいずれかに記載の燃料電池用触媒。
7.配位高分子金属錯体の金属が、Zn、Mn、Fe、Co、Ni、Cu、Ruからなる群から選ばれる少なくとも1種類の金属である前記1〜6.のいずれかに記載の燃料電池用触媒。
8.ヘリウム、ネオン、クリプトン、キセノン、アルゴン、窒素、アンモニア、アセトニトリルからなる群から選ばれる少なくとも1種類の雰囲気で、300〜1200℃で熱処理してなることを特徴とする前記1〜7.のいずれかに記載の燃料電池用触媒。
9.前記1〜8.のいずれかに記載の燃料電池用触媒を導電性担体に担持してなることを特徴とする触媒担持導電体。
10.前記導電性担体のBET比表面積が200〜2000m2/gであることを特徴とする前記9.に記載の触媒担持導電体。
11.前記導電性担体が炭素系担体であることを特徴とする前記9、又は、10.のいずれかに記載の触媒担持導電体。
12.前記炭素系担体が、活性炭、熱分解炭素、カーボンファイバー、カーボンブラック、カーボンナノチューブ、フラーレン、カーボンナノクラスター、及びカーボンナノホーンよりなる群から選ばれる1種又は2種以上であることを特徴とする前記11.に記載の触媒担持導電体。
13.前記1〜12.のいずれかに記載の燃料電池用触媒、又は触媒担持導電体を熱処理することを特徴とする熱処理触媒担持導電体。
14.前記燃料電池用触媒、又は触媒担持導電体、熱処理触媒担持導電体において、イオン伝導性のポリマーで被覆されることを特徴とする前記1〜13.のいずれかに記載のポリマー被覆燃料電池用触媒。
15.前記ポリマー被覆燃料電池用触媒を用いたことを特徴とする前記14.に記載の膜電極接合体。
16.前記膜電極接合体を用いたことを特徴とする前記15.に記載の燃料電池。
17.前記燃料電池用触媒を用いる前記1〜13.のいずれかに記載の酸化還元触媒。
先ず、本発明の配位高分子金属錯体について説明する。
次に、本発明の熱処理配位高分子金属錯体について説明する。
次に、本発明の燃料電池用触媒について説明する。
次に、本発明の触媒担持導電体について説明する。
次に、本発明の熱処理触媒担持導電体について説明する。
次に、本発明のポリマー被覆燃料電池用触媒について説明する。
比表面積はASAP2010(micromeritics社)を用い、BET法により算出した。液体窒素温度(77K)における窒素吸着等温線の測定結果から下式(1)、(2)により単分子層吸着量を算出し、窒素の分子占有面積(0.162nm2)より比表面積を算出するBET多点法により実施した。
金属微粒子の粒径は、透過型電子顕微鏡(TEM)写真で観察される100個の粒子の平均から算出した。
デュポン社製20%ナフィオン(登録商標)溶液に、調製した燃料電池用触媒、又は、触媒担持導電体、熱処理触媒担持導電体と少量の超純水及びイソプロパノールを加え、均一になるまで攪拌し、ポリマー被覆燃料電池用触媒ペーストを調製した。このポリマー被覆燃料電池用触媒ペーストを、別途疎水化した東レ製カーボンペーパーTGPH−060に金属付着量が0.1mg/cm2になるようにアプリケーターを用いて均一に塗布、乾燥して、カソード用の触媒層付ガス拡散層を作製した。同様の手法で、市販の40%白金触媒担持カーボンを用いて、別途疎水化した前記カーボンペーパー上に電極触媒層を形成することで、アノード用の触媒層付ガス拡散層を作製した(0.4mg−白金/cm2)。前記2種類の触媒層付ガス拡散層の間に、触媒層がプロトン交換膜に接するように膜を挟み、ホットプレス機により180℃、3分間加熱することで膜電極接合体(以下MEAと略記する場合もある)を作製した。このMEAを用い、評価用燃料電池セルに組み込んで、アノード側には水素ガスを、カソード側には酸素を供給し、セル温度80℃、常圧、水素利用率を70%、酸素利用率を40%とし、ガス加湿は水素及び酸素を85℃のバブラーを通して行い、電流−電圧特性試験を実施した。
アルゴン雰囲気下で、ピラジン0.80gと炭酸ナトリウム1.06gにメタノール5mlを加え、しばらく撹拌した後、硝酸コバルト(II)六水和物1.46gを溶解したメタノール溶液5mlを滴下して、室温で1時間撹拌した後、粉末を吸引ろ過より取り出した。当該粉末をメタノールで十分に洗浄した後、室温で真空乾燥して配位高分子金属錯体を得た。
上記配位高分子金属錯体を窒素雰囲気、5℃/分で650℃まで加熱し、650℃で2時間熱処理した。その後、室温まで放冷し、熱処理配位高分子金属錯体を得た。乳鉢で粉砕した熱処理配位高分子金属錯体0.50gに硝酸銀(I)0.08gを溶解したメタノール溶液470mlを加え、室温で6時間浸漬した後、粉末を吸引ろ過より取り出した。当該粉末をメタノールで十分に洗浄した後、室温で真空乾燥して燃料電池用触媒を得た。透過型電子顕微鏡での金属微粒子の粒径観察の結果を表1に示す。
乳鉢で粉砕した燃料電池用触媒を導電性担体として用いるカーボンブラックの水溶液に加えて15分間撹拌した後、粉末を吸引ろ過より取り出した。当該粉末を水で十分に洗浄した後、90℃で真空乾燥して、触媒担持導電体を得た。
予め乳鉢で粉砕した上記触媒担持導電体を減圧条件下で28GHzのマイクロ波を1時間照射して熱処理し、熱処理触媒担持導電体を得た。これを用い、前記手法によりMEAを作製し、発電特性を評価した。その結果を表1に示す。
アルゴン雰囲気下で、ピラジン0.80gと3,3′,4,4′−ベンゾフェノンテトラカルボン酸二無水物1.61g、炭酸ナトリウム1.06gに水10mlを加え、しばらく撹拌した後、酢酸マンガン(II)四水和物2.45gを溶解した水溶液5mlを滴下して、還流反応を96時間行った。放冷した後、粉末を吸引ろ過より取り出し、水で十分に洗浄した後、100℃で真空乾燥して配位高分子金属錯体を得た。
上記配位高分子金属錯体をアルゴン雰囲気、5℃/分で600℃まで加熱し、600℃で2時間熱処理した。その後、室温まで放冷し、熱処理配位高分子金属錯体を得た。乳鉢で粉砕した熱処理配位高分子金属錯体0.50gを水10mlに分散させ、クエン酸一水和物0.06g、塩化白金(IV)酸六水和物0.13gを溶解した水溶液1000mlを加えた後、水素化ホウ素ナトリウム0.11gを溶解した水溶液30mlを滴下して、還流反応を1時間行った。放冷した後、粉末を吸引ろ過より取り出し、水で十分に洗浄した後、100℃で真空乾燥して燃料電池用触媒を得た。透過型電子顕微鏡での金属微粒子の粒径観察の結果を表1に示す。
MEAを実施例1と同様に作製し、発電特性を評価した。その結果を表1に示す。
アルゴン雰囲気下で、ビピジジル0.80gに酢酸銅(II)一水和物1.02gを溶解したメタノール溶液10mlを加え、室温で1時間撹拌した後、粉末を吸引ろ過より取り出した。当該粉末をメタノールで十分に洗浄した後、60℃で真空乾燥して配位高分子金属錯体を得た。
上記配位高分子金属錯体をアンモニア雰囲気、5℃/分で600℃まで加熱し、600℃で2時間熱処理した。その後、室温まで放冷し、熱処理配位高分子金属錯体を得た。乳鉢で粉砕した熱処理配位高分子金属錯体0.50gにテトラクロロ金(III)酸四水和物0.11gを溶解したメタノール溶液260mlを加え、室温で6時間浸漬した後、粉末を吸引ろ過より取り出した。当該粉末をメタノールで十分に洗浄した後、室温で真空乾燥して燃料電池用触媒を得た。透過型電子顕微鏡での金属微粒子の粒径観察の結果を表1に示す。
乳鉢で粉砕した燃料電池用触媒を導電性担体として用いるカーボンナノホーン(管状部直径:約2〜3nm、管状部長さ:30nm)の水溶液に加えて15分間撹拌した後、粉末を吸引ろ過より取り出した。当該粉末を水で十分に洗浄した後、90℃で真空乾燥して、触媒担持導電体を得た。これを用い、前記手法によりMEAを作製し、発電特性を評価した。その結果を表1に示す。
アルゴン雰囲気下で、ビピジジル0.80gとトリメシン酸0.54g、炭酸カリウム0.71gにメタノール10mlを加え、しばらく撹拌した後、塩化鉄(III)六水和物1.38gを溶解したメタノール溶液5mlを滴下して、還流反応を96時間行った。放冷した後、粉末を吸引ろ過より取り出し、メタノールで十分に洗浄した後、60℃で真空乾燥して配位高分子金属錯体を得た。
上記配位高分子金属錯体を窒素雰囲気、5℃/分で550℃まで加熱し、550℃で2時間熱処理した。その後、室温まで放冷し、熱処理配位高分子金属錯体を得た。乳鉢で粉砕した熱処理配位高分子金属錯体0.50gにジニトロジアミン白金(II)0.08gを溶解したメタノール溶液260mlを加え、室温で6時間浸漬した後、粉末を吸引ろ過より取り出した。当該粉末をメタノールで十分に洗浄した後、室温で真空乾燥して燃料電池用触媒を得た。透過型電子顕微鏡での金属微粒子の粒径観察の結果を表1に示す。
乳鉢で粉砕した燃料電池用触媒を導電性担体として用いるカーボンファイバー(平均直径:100nm)の水溶液に加えて15分間撹拌した後、粉末を吸引ろ過より取り出した。当該粉末を水で十分に洗浄した後、90℃で真空乾燥して、触媒担持導電体を得た。
予め乳鉢で粉砕した上記触媒担持導電体を減圧条件下で28GHzのマイクロ波を1時間照射して熱処理し、熱処理触媒担持導電体を得た。これを用い、前記手法によりMEAを作製し、発電特性を評価した。その結果を表1に示す。
アルゴン雰囲気下で、ベンズイミダゾール0.80gと炭酸ナトリウム0.72gにN,N−ジメチルホルムアミド5mlを加え、しばらく撹拌した後、銅(II)アセチルアセトナート1.77gを溶解したN,N−ジメチルホルムアミド溶液10mlを滴下して、還流反応を36時間行った。放冷した後、粉末を吸引ろ過より取り出し、N,N−ジメチルホルムアミド、メタノールの順で十分に洗浄した後、60℃で真空乾燥して配位高分子金属錯体を得た。
上記配位高分子金属錯体をアンモニア雰囲気、5℃/分で600℃まで加熱し、600℃で2時間熱処理した。その後、室温まで放冷し、熱処理配位高分子金属錯体を得た。乳鉢で粉砕した熱処理配位高分子金属錯体0.50gを水10mlに分散させ、クエン酸一水和物0.06g、ジニトロジアミン白金(II)0.04g、硝酸ルテニウム(III)0.07gを溶解した水溶液1000mlを加えた後、水素化ホウ素ナトリウム0.11gを溶解した水溶液30mlを滴下して、還流反応を2時間行った。放冷した後、粉末を吸引ろ過より取り出し、水で十分に洗浄した後、90℃で真空乾燥して燃料電池用触媒を得た。透過型電子顕微鏡での金属微粒子の粒径観察の結果を表1に示す。
MEAを実施例1と同様に作製し、発電特性を評価した。その結果を表1に示す。
アルゴン雰囲気下で、イミダゾール0.80gと2,6−ナフタレンジカルボン酸1.27gにN,N−ジメチルホルムアミド10mlを加え、しばらく撹拌した後、水素化ナトリウム0.28gを加え銅(II)アセチルアセトナート3.08gを溶解したメタノール溶液2mlを滴下して、還流反応を72時間行った。放冷した後、粉末を吸引ろ過より取り出し、N,N−ジメチルホルムアミド、メタノールの順で十分に洗浄した後、60℃で真空乾燥して配位高分子金属錯体を得た。
上記配位高分子金属錯体を窒素雰囲気、5℃/分で600℃まで加熱し、600℃で2時間熱処理した。その後、室温まで放冷し、熱処理配位高分子金属錯体を得た。乳鉢で粉砕した熱処理配位高分子金属錯体0.50g、炭酸ナトリウム0.09gにメタノール1000mlを加えた後、硝酸コバルト(II)六水和物0.02gを溶解したメタノール溶液10mlを滴下した。その後、ジニトロジアミン白金(II)0.07gを溶解したメタノール溶液10mlを滴下して、還流反応を6時間行った。放冷した後、粉末を吸引ろ過より取り出し、メタノールで十分に洗浄した後、室温で真空乾燥して燃料電池用触媒を得た。透過型電子顕微鏡での金属微粒子の粒径観察の結果を表1に示す。
MEAを実施例1と同様に作製し、発電特性を評価した。その結果を表1に示す。
116%のポリリン酸59.30gに窒素雰囲気下、1,2,4,5−テトラアミノベンゼン四塩酸塩4.20gと安息香酸3.60gを加え、70℃で15分間撹拌した。さらに120℃まで昇温させ、21時間撹拌した後、150℃まで昇温させ3時間撹拌した。この反応液を水1L中へ再沈して、析出してきた粉末を吸引ろ過より取り出した。得られた粉末を水で十分に洗浄した後、90℃で真空乾燥し、ビスベンゾイミダゾール誘導体を得た。
アルゴン雰囲気下で、前記ビスベンゾイミダゾール誘導体0.80gと2,5−ジメチルテレフタル酸0.25g、炭酸ナトリウム0.27gにN,N−ジメチルホルムアミド15mlを加え、しばらく撹拌した後、酢酸ニッケル(II)四水和物1.28gを溶解したメタノール溶液2mlを滴下して、還流反応を96時間行った。放冷した後、粉末を吸引ろ過より取り出し、N,N−ジメチルホルムアミド、メタノールの順で十分に洗浄した後、60℃で真空乾燥して配位高分子金属錯体を得た。
上記配位高分子金属錯体を窒素雰囲気、5℃/分で700℃まで加熱し、700℃で2時間熱処理した。その後、室温まで放冷し、熱処理配位高分子金属錯体を得た。乳鉢で粉砕した熱処理配位高分子金属錯体0.50gにテトラクロロ金(III)酸四水和物0.11gを溶解した2−プロパノール溶液260mlを加え、室温で30分間浸漬した後、粉末を吸引ろ過より取り出した。当該粉末を2−プロパノールで十分に洗浄した後、室温で真空乾燥して燃料電池用触媒を得た。透過型電子顕微鏡での金属微粒子の粒径観察の結果を表1に示す。
乳鉢で粉砕した燃料電池用触媒を導電性担体として用いるカーボンブラックの水溶液に加えて15分間撹拌した後、粉末を吸引ろ過より取り出した。当該粉末を水で十分に洗浄した後、90℃で真空乾燥して、触媒担持導電体を得た。これを用い、前記手法によりMEAを作製し、発電特性を評価した。その結果を表1に示す。
116%のポリリン酸59.30gに窒素雰囲気下、2,5−ジアミノ−1,4−ベンゼンジチオール二塩酸塩4.20gと安息香酸4.20gを加え、70℃で15分間撹拌した。さらに120℃まで昇温させ、21時間撹拌した後、150℃まで昇温させ3時間撹拌した。この反応液を水1L中へ再沈して、析出してきた粉末を吸引ろ過より取り出した。得られた粉末を水で十分に洗浄した後、90℃で真空乾燥し、ビスベンゾチアゾール誘導体を得た。
アルゴン雰囲気下で、前記ビスベンゾチアゾール誘導体0.80gとピロメリット酸無水物0.25gにN,N−ジメチルホルムアミド20mlを加え、しばらく撹拌した後、水素化ナトリウム0.22gを加え、酢酸ニッケル(II)四水和物1.16gを溶解したメタノール溶液2mlを滴下して、還流反応を96時間行った。放冷した後、粉末を吸引ろ過より取り出し、N,N−ジメチルホルムアミド、メタノールの順で十分に洗浄した後、60℃で真空乾燥して配位高分子金属錯体を得た。
上記配位高分子金属錯体をアルゴン雰囲気、5℃/分で700℃まで加熱し、700℃で2時間熱処理した。その後、室温まで放冷し、熱処理配位高分子金属錯体を得た。乳鉢で粉砕した熱処理配位高分子金属錯体0.50gに硝酸銀(I)0.08gを溶解した2−プロパノール溶液1000mlを加え、還流反応を6時間行った。放冷した後、析出物を吸引ろ過より取り出し、2−プロパノールで十分に洗浄した後、70℃で真空乾燥して燃料電池用触媒を得た。透過型電子顕微鏡での金属微粒子の粒径観察の結果を表1に示す。
MEAを実施例1と同様に作製し、発電特性を評価した。その結果を表1に示す。
カーボンブラック0.50gにエタノール1000mlを加えた後、酢酸ニッケル(II)四水和物0.02gを溶解したエタノール溶液10mlを滴下した。その後、ジニトロジアミン白金(II)0.07gを溶解したエタノール溶液10mlを滴下して、還流反応を6時間行った。放冷した後、析出物を吸引ろ過より取り出し、エタノールで十分に洗浄した後、70℃で真空乾燥して金属微粒子含有錯体を得た。透過型電子顕微鏡での金属微粒子の粒径観察の結果を表1に示す。
MEAを実施例1と同様に作製し、発電特性を評価した。その結果を表1に示す。
2 配位子
3 金属
4 多孔質骨格構造
5 空孔
6 三次元格子構造
7 金属−N4構造
Claims (17)
- 分子内に−NH2、=NH、=N−から選択される化学構造を2個以上含有し、平面構造を有する配位子と、金属からなる多孔質骨格構造を有する配位高分子金属錯体を熱処理した熱処理配位高分子金属錯体へ金属微粒子を担持してなることを特徴とする燃料電池用触媒。
- ピラジン骨格、ビピリジン骨格、イミダゾール骨格、ビスベンゾチアゾール骨格、ビスベンゾオキサゾール骨格からなる群から選ばれる少なくとも1種類以上の化学構造を含む請求項1に記載の配位子からなる配位高分子金属錯体を熱処理した熱処理配位高分子金属錯体へ金属微粒子を担持してなることを特徴とする燃料電池用触媒。
- 前記配位高分子金属錯体のBET比表面積が100〜5000m2/gであることを特徴とする請求項1又は2に記載の燃料電池用触媒。
- 前記金属微粒子の粒径が10nm以下であることを特徴とする請求項1〜3のいずれかに記載の燃料電池用触媒。
- 前記金属微粒子は遷移金属であることを特徴とする請求項1〜4のいずれかに記載の燃料電池用触媒。
- 前記金属微粒子は貴金属であることを特徴とする請求項1〜5のいずれかに記載の燃料電池用触媒。
- 配位高分子金属錯体の金属が、Zn、Mn、Fe、Co、Ni、Cu、Ruからなる群から選ばれる少なくとも1種類の金属である請求項1〜6のいずれかに記載の燃料電池用触媒。
- ヘリウム、ネオン、クリプトン、キセノン、アルゴン、窒素、アンモニア、アセトニトリルからなる群から選ばれる少なくとも1種類の雰囲気で、300〜1200℃で熱処理してなることを特徴とする請求項1〜7のいずれかに記載の燃料電池用触媒。
- 請求項1〜8のいずれかに記載の燃料電池用触媒を導電性担体に担持してなることを特徴とする触媒担持導電体。
- 前記導電性担体のBET比表面積が200〜2000m2/gであることを特徴とする請求項9に記載の触媒担持導電体。
- 前記導電性担体が炭素系担体であることを特徴とする請求項9、又は、10のいずれかに記載の触媒担持導電体。
- 前記炭素系担体が、活性炭、熱分解炭素、カーボンファイバー、カーボンブラック、カーボンナノチューブ、フラーレン、カーボンナノクラスター、及びカーボンナノホーンよりなる群から選ばれる1種又は2種以上であることを特徴とする請求項11に記載の触媒担持導電体。
- 請求項1〜12のいずれかに記載の燃料電池用触媒、又は触媒担持導電体を熱処理することを特徴とする熱処理触媒担持導電体。
- 前記燃料電池用触媒、又は触媒担持導電体、熱処理触媒担持導電体において、イオン伝導性のポリマーで被覆されることを特徴とする請求項1〜13のいずれかに記載のポリマー被覆燃料電池用触媒。
- 前記ポリマー被覆燃料電池用触媒を用いたことを特徴とする請求項14に記載の膜電極接合体。
- 前記膜電極接合体を用いたことを特徴とする請求項15に記載の燃料電池。
- 前記燃料電池用触媒を用いる請求項1〜13のいずれかに記載の酸化還元触媒。