JP2009204594A - カーボン含有耐火物の耐酸化性評価方法 - Google Patents
カーボン含有耐火物の耐酸化性評価方法 Download PDFInfo
- Publication number
- JP2009204594A JP2009204594A JP2008050183A JP2008050183A JP2009204594A JP 2009204594 A JP2009204594 A JP 2009204594A JP 2008050183 A JP2008050183 A JP 2008050183A JP 2008050183 A JP2008050183 A JP 2008050183A JP 2009204594 A JP2009204594 A JP 2009204594A
- Authority
- JP
- Japan
- Prior art keywords
- carbon
- iron
- molten iron
- containing refractory
- oxidation resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】高周波誘導炉1の反応容器5の内壁側面に耐酸化性を評価するカーボン含有耐火物(評価試料11)を内張りし、評価試料11と低炭素鉄の溶鉄10とを接触させると共に、攪拌ジグ2で溶鉄10を攪拌する。また、酸素センサー3で溶鉄中の酸素濃度を測定し、酸素濃度が高い場合は、カーボンやアルミニウムなどを溶鉄10に添加し、酸素と反応させることによって、溶鉄中の酸素濃度を制御する。所定時間経過後、評価試料11の鉄浴部の脱炭層の厚みを計測する。
【選択図】 図1
Description
材質Aは、化学成分としてアルミナ75質量%、ジルコニア12質量%、シリカ3質量%に、カーボンを6質量%含有するものである。この材質Aのれんがの本発明試験での脱炭層厚さの指数、及び気相酸化試験での摩耗量指数は、上述のとおり100とした。また、この材質Aのれんがを実炉でSNプレートとして使用し試験した結果は、摺動面の損傷が軽微であり良好であった。さらに、各試験後の評価試料の深さ方向を顕微鏡で観察したところ、本発明試験後の評価試料は、実炉使用後のSNプレートとよく類似した組織を示しており、本発明試験で、実炉と同様の耐酸化性評価を行うことができることが確認された。
材質Bは、化学成分としてアルミナ80質量%、ジルコニア10質量%、シリカ3質量%にカーボンを5質量%含有するものである。この材質Aのれんがの本発明試験での脱炭層厚さの指数は95と良好で、実炉でSNプレートとして使用し試験した結果も、摺動面の損傷が軽微で有り良好であった。一方、気相酸化試験での摩耗量指数は120と各材質中で最も悪かった。
材質Cは、化学成分としてアルミナ83質量%、ジルコニア3質量%、シリカ4質量%にカーボンを6質量%含有するものである。この材質Cのれんがの気相酸化試験での摩耗量指数は90と小さく良好であったが、本発明試験での脱炭層厚さの指数は145と脱炭が大きく不良であった。そして、材質Cのれんがを実炉でSNプレートとして使用し試験した結果は、本発明試験の結果と同様、摺動面の脱炭、損傷が大きく不良であった。
材質Dは、アルミナ76質量%、ジルコニア9質量%、シリカ4質量%にカーボンを7質量%含有するものである。この材質Dのれんがの気相酸化試験での摩耗量指数は105と比較的良好であったが、本発明試験での脱炭層厚さの指数は130と脱炭が大きく不良であった。そして、材質Dのれんがを実炉でSNプレートとして使用し試験した結果は、本発明試験の結果と同様、摺動面の脱炭、損傷が大きく不良であった。
材質Eは、アルミナ75質量%、ジルコニア10質量%、シリカ4質量%にカーボンを7質量%含有するものである。この材質Eのれんがの気相酸化試験での摩耗量指数は80と小さく良好であったが、液相酸化試験での脱炭層厚さの指数は125と脱炭が大きく不良であった。そして、材質Eのれんがを実炉でSNプレートとして使用し試験した結果は、本発明試験の結果と同様、摺動面の脱炭、損傷が大きく不良であった。
Claims (4)
- カーボン含有耐火物の耐酸化性評価方法であって、
反応容器の内壁側面にカーボン含有耐火物を内張りし、
前記反応容器に鉄を入れ、前記反応容器の周囲に設置した高周波誘導炉を用いて前記鉄を溶かして溶鉄とし、当該溶鉄の温度を1550℃〜1700℃に調整すると共に、前記溶鉄中の酸素濃度を10〜500ppmに調整し、
所定時間経過後、前記カーボン含有耐火物の鉄浴部の脱炭層を評価する
ことを特徴とするカーボン含有耐火物の耐酸化性評価方法。 - 攪拌羽を10rpm〜100rpmで回転させて前記溶鉄を攪拌することを特徴とする請求項1記載のカーボン含有耐火物の耐酸化性評価方法。
- 前記反応容器に鉄を入れた後、当該反応容器の開口部を蓋で覆い、反応容器内に不活性ガスを充填して、不活性雰囲気で前記鉄を溶かして溶鉄にすることを特徴とする請求項1又は2記載のカーボン含有耐火物の耐酸化性評価方法。
- 前記カーボン含有耐火物は、スライディングノズルプレートであることを特徴とする請求項1乃至3の何れかに記載のカーボン含有耐火物の耐酸化性評価方法。