JP2007243026A - セラミック粉末及びこれを用いた導電ペースト、積層セラミック電子部品、その製造方法 - Google Patents
セラミック粉末及びこれを用いた導電ペースト、積層セラミック電子部品、その製造方法 Download PDFInfo
- Publication number
- JP2007243026A JP2007243026A JP2006065946A JP2006065946A JP2007243026A JP 2007243026 A JP2007243026 A JP 2007243026A JP 2006065946 A JP2006065946 A JP 2006065946A JP 2006065946 A JP2006065946 A JP 2006065946A JP 2007243026 A JP2007243026 A JP 2007243026A
- Authority
- JP
- Japan
- Prior art keywords
- electronic component
- ceramic
- conductive paste
- internal electrode
- ceramic powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
【解決手段】 誘電体セラミック層と内部電極層とが交互に積層された積層セラミック電子部品において、内部電極層を形成するための導電ペーストに添加するセラミック粉末として、ペロブスカイト型結晶構造を有し、テトラゴナル相の含有量Wtとキュービック相の含有量Wcの重量比率Wt/Wcが2以上のセラミック粉末を用いる。テトラゴナル相とキュービック相の重量比率Wt/Wcは、リートベルト法による多相解析により求める。セラミック粉末は例えばチタン酸バリウム粉末である。
【選択図】 図3
Description
粉末X線回折(XRD)測定は、粉末X線回折装置(リガク社製、商品名Rint2000)を用いて行い、リートベルト解析用のXRDプロファイルデータを得た。このとき、ステップ幅は0.01°、最大ピークカウントが約10000カウントとなるように電流、電圧を設定して測定を行った。
得られたXRDプロファイルについて、リートベルト解析用ソフトウエアRIETAN−2000(Rev.2.4.1)(ウインドウズ用)を用いて解析を行った。各相の質量分率を求めるにあたっては、マイクロアブソープション(Microabsorption)を補正して質量分率を求めた。
ペロブスカイト型結晶構造を有するチタン酸バリウム粉末(比表面積SSA6.16m2/g、走査型電子顕微鏡SEMによる平均粒径0.16μm)について、リートベルト法による解析を試みた。リートベルト解析としては、テトラゴナル相(正方晶)単相としての解析、キュービック相(立方晶)単相としての解析、テトラゴナル相(正方晶)+キュービック相(立方晶)の2相としての解析の3種類である。各解析における信頼度因子を表1に示す。
各種セラミック粉末(チタン酸バリウム粉末)を用い、前述した製造方法に準じて積層セラミックコンデンサを作製した(実施例1〜4、比較例1、2)。作製した積層セラミックコンデンサの寸法は、1.0mm×0.5mm×0.5mmであり、誘電体セラミック層の積層数は160、誘電体セラミック層1層あたりの厚みは1.6μm、内部電極層の厚みは1.0μmとした。内部電極層の形成に使用した導電ペーストに含まれるセラミック粉末(共材)の比表面積SSA、走査電子顕微鏡により計測した平均粒径(SEM粒径)、テトラゴナル相の含有量Wt、キュービック相の含有量Wc、これらの重量比率Wt/Wc(=X)、焼結体の粒径、粒径のバラツキ(標準偏差)σ、作製した積層セラミックコンデンサのIR不良率、IR寿命を表2に示す。
Claims (10)
- 誘電体セラミック層と内部電極層とが交互に積層された積層セラミック電子部品の前記内部電極層を形成するための導電ペーストに添加されるセラミック粉末であって、
ペロブスカイト型結晶構造を有し、テトラゴナル相の含有量Wtとキュービック相の含有量Wcの重量比率Wt/WcをXとしたときに、X≧2であることを特徴とするセラミック粉末。 - 前記テトラゴナル相の含有量Wtとキュービック相の含有量Wcは、リートベルト法による多相解析により求められた値であることを特徴とする請求項1記載のセラミック粉末。
- 比表面積が10m2/g以上であることを特徴とする請求項1または2記載のセラミック粉末。
- チタン酸バリウム粉末を主成分とすることを特徴とする請求項1から3のいずれか1項記載のセラミック粉末。
- 誘電体セラミック層と内部電極層とが交互に積層された積層セラミック電子部品の前記内部電極層を形成するための導電ペーストであって、
導電材料とセラミック粉末を含有し、前記セラミック粉末として請求項1から4のいずれか1項記載のセラミック粉末を含むことを特徴とする導電ペースト。 - 前記導電材料は、卑金属を主成分とすることを特徴とする請求項5記載の導電ペースト。
- 前記卑金属がNiであることを特徴とする請求項6記載の導電ペースト。
- 誘電体セラミック層と内部電極層とが交互に積層された積層セラミック電子部品であって、
前記内部電極層は、請求項5から7のいずれか1項記載の導電ペーストにより電極前駆体層を形成し、これを焼成することにより形成されることを特徴とする積層セラミック電子部品。 - 積層セラミックコンデンサであることを特徴とする請求項8記載の積層セラミック電子部品。
- 誘電体ペーストと導電ペーストにより誘電体グリーンシートと電極前駆体層とを交互に積層形成した後、これを焼成して積層セラミック電子部品とするに際し、
前記導電ペーストとして請求項5から7のいずれか1項記載の導電ペーストを用いることを特徴とする積層セラミック電子部品の製造方法。