JP2006521411A - 構造的に変性されたシリカ - Google Patents
構造的に変性されたシリカ Download PDFInfo
- Publication number
- JP2006521411A JP2006521411A JP2004559676A JP2004559676A JP2006521411A JP 2006521411 A JP2006521411 A JP 2006521411A JP 2004559676 A JP2004559676 A JP 2004559676A JP 2004559676 A JP2004559676 A JP 2004559676A JP 2006521411 A JP2006521411 A JP 2006521411A
- Authority
- JP
- Japan
- Prior art keywords
- silica
- water
- coating
- wax
- coated silica
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
ポリエチレンホモポリマー及びコポリマーワックス;数平均分子量700〜10000g/mol、80〜140℃の滴点を有する。
チーグラー金属触媒を用いて製造したC2〜C18−α−オレフィンのホモポリマー又はコポリマー及び次のグループから選択される、助剤としての1種又は数種の他のワックス
− PEワックス、
− PTFEワックス、
− PPワックス、
− アミドワックス、
− FTパラフィン、
− モンタンワックス、
− 天然ワックス
− マクロ結晶及び微結晶パラフィン、
− 極性ポリオレフィンワックス又は
− ソルビタンワックス
チーグラーメタロセン触媒を用いて製造したC2〜C18−α−オレフィンのホモポリマー又はコポリマーは有利に次の特性を有している:
滴点(Dp):80〜165℃ 90〜155℃
酸価(AV):0〜50mgKOH/g
密度:0.87〜1.03g/cm3
170℃での溶融物の粘度:10〜100000mPas
適当なポリオレフィンワックスはエチレン又はプロピレンのホモポリマーであるか又はエチレン及びプロピレンのそれぞれの又は1種又は複数の1−オレフィンとのコポリマーである。
次の水中油型エマルション
有機変性されたポリシロキサン(有機変性:C2〜C8−アルコール及びEO/POポリエーテル)
近似的平均Mw:1000〜5000g/mol
(疎水性シリカで充填)エマルションの活性物質含有量:約20%
水及び被覆剤の混入の際にシリカの容積は極めてわずかに減少するだけであるため、エアーディスペンサー処理された熱分解シリカ中に当初存在する一次粒子の会合は実質的に保持されると想定される。水及び被覆剤の負荷の結果として、シリカの表面の部分的溶解が生じるため、溶解したシリカが存在する。これは、引き続く乾燥の間に一次粒子を一緒に全ての接触点で結合させる。
沈殿しない、又は再分散が容易、
艶消し効果は損なわれない、
触感の改善、
透明ラッカーのより高い透明性が可能、
低い水分含有量、従って、水分硬化性PU系(ポリウレタン系)中で使用できる、
チキソトロピーが低いために、良好な流動性。
本発明により構造的に被覆されたシリカの製造
次の物理学的特性を有する親水性熱分解シリカ(Aerosil 300)を使用した:
BETによる比表面積[m2/g]:290.0
pH:4.2
圧密化された密度[g/l]:35
乾燥による減量[%]:0.8
DBP値[%]:305.0
炭素含有量[%]:0
鋤羽ミキサーを混合容器として使用する。この被覆剤は室温で2つの流動ノズルを用いて吹き付ける。
被覆剤A
被覆剤AはEP 0 341 383 A2から公知であり、かつこれはワックスエマルションであり、かつ次のように製造される:
このワックスエマルションは、スチームで加熱することがでるオートクレーブ中で製造され、かつ分散装置を用いて準備される。この中で、アルキルポリグリコールエーテル(Marlowet(R) GFW)4.8質量部を100℃でまず、約100℃の水81.0質量部中に溶解させる。次いで、低圧ポリエチレンワックス14.2質量部を添加し、この混合物を130℃に加熱する。130℃に達する際に、この分散装置をスイッチオンし、かつこの混合物を30分間分散させる。この温度を、この期間、130〜140℃に維持する。分散装置をスイッチオフし、かつ約110℃に冷却した後、最終エマルションを排出させた。
平均分子量 1000
凝固点 100〜104℃
滴点 110〜117℃
密度(g/cm3) 0.93
このエマルションは次いで必要なpHに調節される。
被覆剤BはEP 0 341 383 A2から公知である。これはワックスエマルションであり、次のように製造される:
このワックスエマルションは、スチームで加熱することがでるオートクレーブ中で製造され、かつ分散装置を用いて準備される。この中で、アルキルポリグリコールエーテル(Marlowet(R) GFW)4.8質量部を100℃でまず、約100℃の水81.0質量部中に溶解させる。次いで、低圧ポリエチレンワックス14.2質量部を添加し、この混合物を130℃に加熱する。130℃に達する際に、この分散装置をスイッチオンし、かつこの混合物を30分間分散させる。この温度を、この期間の間、130〜140℃に維持する。分散装置をスイッチオフし、かつ約110℃に冷却した後、最終エマルションを排出させた。
平均分子量 2700
凝固点 92〜96℃
滴点 102〜110℃
密度(g/cm3) 0.92
このエマルションは次いで必要なpHに調節される。
被覆剤Cは、水210gに溶解された水性ポリシロキサンエマルション656.4gからなり、これは必要なpHに調節される。
被覆剤Dは、水116gで希釈された水性アルキルエステル/ポリジメチルシロキサンエマルション503.0gからなり、これは必要なpHに調節される。
被覆剤Eはエステルワックス及びカルナウバワックスと水346gの水性エマルション365.6gからなる。この混合物は、10.6のpHに調節される。
比較のために、被覆剤の代わりに水(アルカリで調節)だけを実施例8に使用した。
湿った材料の製造
湿った材料の粉砕及び乾燥
物理化学的データ
BET比表面積
BET表面積はDIN66131に従って窒素を用いて測定される。
この圧密化された密度DIN ISO 787/XIに基づく方法を用いて測定
圧密化された密度の測定のための基本
圧密化された密度(以前には圧密化された容積)は、一定の条件下での圧密化容積計中で圧密化した後の粉末の質量及び容積の商に等しい。DIN ISO 787/XIによると、圧密化された密度はg/cm3で示される。この酸化物の極めて低い圧密化された密度のため、この値をg/lで示す。更に、乾燥及びスクリーニング操作を行わず、圧密化プロセスも繰り返さない。
圧密化容積計
メスシリンダー
実験室用はかり(0.01gを計測できる)
圧密化された密度の測定方法
空隙なくかつ表面が水平となるように、酸化物200±10mlを圧密化容積計のメスシリンダー中に入れる。
このpHは4%の濃度の水性分散液中で測定し、疎水性酸化物の場合には水:メタノール1:1中で測定する。
蒸留水又は脱イオン水、pH>5.5
メタノール、AR
緩衝溶液pH7.00pH4.66
pHの測定のための装置
実験室用はかり(0.1gを計測できる)
ビーカー、250ml
磁気攪拌機
磁気ロッド、長さ4cm
pH複合電極
pH器具
ディスペンセット(Dispensette)、100ml
pHの測定のための器具
pHの測定のためのこの方法はDIN/ISO 787/IXに基づく:校正:pHの測定の前に前記器機を緩衝溶液で校正する。数回の測定を連続して行う場合には、1回の校正手順で十分である。
DIN ISO 787IIに記載された10gの量を最初に秤量するのとは異なり、1gの量を乾燥による減量の測定のために使用した。ふたを置き、冷却する。第2の乾燥は実施しない。
強熱減量を測定するための装置
るつぼふた付き磁製るつぼ
マッフル炉
分析用はかり(0.1mgを計測できる)
デシケーター
強熱減量の測定のために使用する方法
DIN55921とは異なり、予め乾燥していない基材を0.1mgの精度で、予め強熱したふた付きの磁製るつぼ中に量り取り、1000℃で2時間マッフル炉中で強熱する。粉塵の生成を回避する努力を行わなければならないマッフル炉が詰めたい間に、秤量した試料を前記マッフル炉に入れることが有利であることが明らかとなった。前記炉をゆっくりと加熱することにより、磁製るつぼ中の著しい空気乱流は回避される。
強熱減量は105℃で2時間乾燥した試料に関して、次の式にを計算のために使用する:
LOD=乾燥による減量(%)
m1=強熱された試料の質量(g)
この結果は小数点1桁まで記録される。
DBP値の決定のための装置
上皿はかり
プラスチックビーカー(250ml)
計量ユニットを備えたブラベンダープラストグラフ
試薬
ジブチルフタレート(工業的)
方法
1. カットオフポイントをチェックする。
2. 校正
− 計量ポンプなしでプラストグラフをスイッチオンする。
− 試料12.5gをプラスチックビーカー中に量り取り、配合チャンバに入れる。指示があれば、この重量はこの値とは異なることができる(例えば8又は20g)。DBP測定ユニットをスイッチオンする。充填手順(ディスプレーF)が完了した後すぐに、プラストグラフは使用のために準備される。
本発明による実施例1〜7によるシリカを、多様なラッカー系中で試験した。この試験の結果を次の表5〜8に記載した。
表中の値から、被覆及び低いグラインドメータ値(粒子サイズ)の存在にもかかわらず、高い艶消し効果の傷害が示されないことが観察された。
ほとんど全ての被覆された試料は、著しく改善された懸濁した粒子挙動を示す。いくつかは、全く沈殿が観察されなかった(実施例3及び4)。
全ての試料は低いチキソトロピーを有し、かつこのラッカー系に関してわずかな又はゼロの流動学的効果を示すだけである。これはラッカー加工特性に関して有利な効果である。
秤量された溶剤の量:エトキシプロピルアセテート35g、秤量された艶消し剤の量:1g
手動で混合
乾燥庫中で50℃で一晩中貯蔵
Claims (8)
- 構造的に被覆されたシリカ。
- 10〜30質量%の炭素含有量を有する、請求項1記載の構造的に被覆されたシリカ。
- 80〜450m2/gのBET表面積を有する、請求項1記載の構造的に被覆されたシリカ。
- 10〜60g/lの嵩密度を有する、請求項1又は2記載の構造的に被覆されたシリカ。
- 2.4〜3.8のDBP値を有する、請求項1から3までのいずれか1項記載の構造的に被覆されたシリカ。
- 適当な混合容器中で熱分解シリカに水及び被覆剤を吹き付けかつ混合し、次いで粉砕しかつ引き続き乾燥させる、請求項1から4までのいずれか1項記載の構造的に被覆されたシリカの製造方法。
- ラッカー中での艶消し剤としての、請求項1から4までのいずれか1項記載の構造的に被覆されたシリカの使用。
- 請求項1から4までのいずれか1項記載の構造的に被覆されたシリカを含有する、ラッカー及び/又はラッカー系。