JP2006193696A - 離型フィルム用樹脂組成物及び離型フィルム - Google Patents
離型フィルム用樹脂組成物及び離型フィルム Download PDFInfo
- Publication number
- JP2006193696A JP2006193696A JP2005009542A JP2005009542A JP2006193696A JP 2006193696 A JP2006193696 A JP 2006193696A JP 2005009542 A JP2005009542 A JP 2005009542A JP 2005009542 A JP2005009542 A JP 2005009542A JP 2006193696 A JP2006193696 A JP 2006193696A
- Authority
- JP
- Japan
- Prior art keywords
- release film
- weight
- polydimethylsiloxane
- mol
- resin composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】オレフィン系重合体95〜99.99重量%、及びアミノ基当量が500g/mol以上50000g/mol以下であるポリジメチルシロキサン(A)0.01〜5重量%とからなる離型フィルム用樹脂組成物を製造し、用いる。
Description
本発明の離型フィルム用樹脂組成物は、通常用いられる樹脂の混合装置により製造することができる。例えば、単軸押出機、二軸押出機、バンバリ−ミキサー、加圧ニーダ−、回転ロールなどの溶融混練装置、ヘンシェルミキサー、Vブレンダー、リボンブレンダー、タンブラーなどが挙げられる。溶融混練装置を用いる場合、溶融温度はオレフィン系重合体の融点〜350℃程度が好ましい。
JIS K6922−1(1997年)に準拠して測定した。
JIS K6922−1(1997年)に準拠して測定した。
実施例により得られた積層体の離型フィルム側表面に巾50mm、長さ150mmの布粘着テープ(スリオンテック社製 商品名布粘着テープNo.3310)を貼付し、線圧5kg/cm、速度5m/分の条件でゴムロール間を通過させた後、40℃の雰囲気で7日間放置し、離型性測定用試料を得た。その後、試料を巾15mmに裁断し、布粘着テープと離型フィルムとの接着強度を引張試験機(島津製作所製 オートグラフDCS−100)にて測定した。剥離速度は300mm/分である。
上記離型性試験により離型フィルム表面から剥離した巾15mmの布粘着テープをアルミニウム板(東洋アルミニウム(株)製 商品名A1N30H−H18、厚み0.1mm)に5kg/cmの線圧で貼付した。23℃の雰囲気にて1日放置した後、布粘着テープとアルミニウム板との接着強度を引張試験機(島津製作所製 オートグラフDCS−100)にて測定した。剥離速度は300mm/分である。粘着テープの粘着剤表面が離型フィルムにより汚染された場合、粘着テープの再粘着性が低下し、粘着テープとしての性能を損なう。すなわち、再粘着強度は高い方が好ましい。
実施例により得られた積層体の紙/離型フィルム間の接着強度を引張試験機(島津製作所製 オートグラフDCS−100)にて測定した。剥離速度は300mm/分、試験片の巾は15mmである。基材である紙の材質破壊が起こる程度に接着していれば、基材との接着性が良好であると言える。
オレフィン系重合体として、MFRが8g/10分、密度が918kg/m3である低密度ポリエチレン(東ソー(株)製 商品名ペトロセン213、以下LDPEと記す場合がある)99重量%、アミノ基当量が500g/mol以上50000g/mol以下であるポリジメチルシロキサン(A)として、アミノ基当量1800g/mol、粘度1200cStであるアミノ変性ポリジメチルシロキサン(東レ・ダウ・コーニング・シリコーン(株)製 商品名SF8417、以下、A−1と記す場合がある)を1重量%になるよう配合し、単軸押出機(プラコー社製 口径50mm)にて溶融混練(混練温度150℃)し離型フィルム用樹脂組成物のペレットを得た。
オレフィン系重合体として、LDPEを99重量%、アミノ変性ポリジメチルシロキサン(A−1)を1重量部とする代わりに、LDPEを99.5重量%、アミノ変性ポリジメチルシロキサン(A−1)を0.5重量%とした以外は実施例1と同様にして離型フィルムを得た。評価結果は表1に示した。
オレフィン系重合体として、LDPEを99重量%、アミノ変性ポリジメチルシロキサン(A−1)を1重量部とする代わりに、LDPEを98重量%、アミノ変性ポリジメチルシロキサン(A−1)を2重量%とした以外は実施例1と同様にして離型フィルムを得た。評価結果は表1に示した。
オレフィン系重合体として、LDPEを99重量%、アミノ変性ポリジメチルシロキサン(A−1)を1重量部とする代わりに、LDPEを99重量%、アミノ変性ポリジメチルシロキサン(A−1)を1重量%とからなる組成物100重量部に対し、官能基当量が350g/molであるエポキシ基を有するポリジメチルシロキサン(B−1)(信越化学工業(株)製 商品名信越シリコーンKF101、以下、B−1と記す場合がある)を0.1重量部添加した以外は実施例1と同様にして離型フィルムを得た。評価結果は表1に示した。
オレフィン系重合体として、LDPEを99重量%、アミノ変性ポリジメチルシロキサン(A−1)を1重量部の代わりに、LDPEを99重量%、アミノ変性ポリジメチルシロキサン(A−1)を1重量%とからなる組成物100重量部に対し、官能基当量が750g/molであるカルボキシル基を有するポリジメチルシロキサン(B−2)(東レ・ダウ・コーニング・シリコーン(株)製 商品名BY16−750、以下、B−2と記す場合がある)を0.1重量部添加した以外は実施例1と同様にして離型フィルムを得た。評価結果は表1に示した。
オレフィン系重合体として、LDPEを99重量%、アミノ変性ポリジメチルシロキサン(A−1)を1重量部の代わりに、LDPEを99重量%、アミノ変性ポリジメチルシロキサン(A−1)を1重量%とからなる組成物100重量部に対し、官能基当量が3200g/molであるカルボキシル基を有するポリジメチルシロキサン(B−3)(東レ・ダウ・コーニング・シリコーン(株)製 商品名SF8411、以下、B−3と記す場合がある)を0.1重量部添加した以外は実施例1と同様にして離型フィルムを得た。評価結果は表1に示した。
オレフィン系重合体として、LDPEの代わりに、MFRが7.5g/10分、密度が902kg/m3であるエチレン・1−オクテン共重合体(ダウケミカル製 商品名アフィニティPT1450、以下C8LLと記す場合がある)とした以外は実施例1と同様にして離型フィルムを得た。評価結果は表1に示した。
オレフィン系重合体として、LDPEを99重量%、アミノ変性ポリジメチルシロキサン(A−1)を1重量部の代わりに、LDPEを100重量%とした以外は実施例1と同様にして離型フィルムを得た。評価結果を表2に示したが、布粘着テープと離型フィルムの接着強度が高く、離型性が劣っていた。また、粘着剤が離型フィルム面に残存し、粘着性も劣っていた。
オレフィン系重合体として、LDPEを99重量%、アミノ変性ポリジメチルシロキサンを1重量部の代わりに、LDPEを94重量%、アミノ変性ポリジメチルシロキサンを6重量%とした以外は実施例1と同様にして離型フィルムの製造を試みたが、押出不良のためフィルムを得ることができなかった。
オレフィン系重合体として、LDPEを99重量%、アミノ変性ポリジメチルシロキサン(A−1)を1重量%の代わりに、LDPEを99重量%、官能基当量が350g/molであるエポキシ基を有するポリジメチルシロキサン(B−1)を1重量%とした以外は実施例1と同様にして離型フィルムを得た。評価結果を表2に示したが、布粘着テープと離型フィルムの接着強度が高く、離型性が劣っていた。また、粘着剤が離型フィルム面に残存し、粘着性も劣っていた。
オレフィン系重合体として、LDPEを99重量%、アミノ変性ポリジメチルシロキサン(A−1)を1重量%の代わりに、LDPEを99重量%、官能基当量が750g/molであるカルボキシル基を有するポリジメチルシロキサン(B−2)を1重量%とした以外は実施例1と同様にして離型フィルムを得た。評価結果を表2に示したが、布粘着テープと離型フィルムの接着強度が高く、離型性が劣っていた。また、粘着剤が離型フィルム面に残存し、粘着性も劣っていた。
Claims (9)
- オレフィン系重合体95〜99.99重量%及びアミノ基当量が500g/mol以上50000g/mol以下であるポリジメチルシロキサン(A)0.01〜5重量%とからなる離型フィルム用樹脂組成物。
- オレフィン系重合体が、JIS K6922−1(1999年)で測定したメルトマスフローレイトが0.1〜50g/10分、JIS K6922−1(1999年)で測定した密度が880〜970kg/m3であることを特徴とする請求項1に記載の離型フィルム用樹脂組成物。
- オレフィン系重合体95〜99.99重量%及びアミノ基当量が500g/mol以上50000g/mol以下であるポリジメチルシロキサン(A)0.01〜5重量%からなる組成物100重量部に対して、エポキシ基及び/又はカルボキシル基を有するポリジメチルシロキサン(B)を0.001〜2.5重量部配合してなることを特徴とする請求項1又は請求項2に記載の離型フィルム用樹脂組成物。
- アミノ基当量が500g/mol以上50000g/mol以下であるポリジメチルシロキサン(A)とエポキシ基及び/又はカルボキシル基を有するポリジメチルシロキサン(B)の重量比[(A)/(B)]が1000:1〜2:1(重量比)の範囲であることを特徴とする請求項3に記載の離型フィルム用樹脂組成物。
- 請求項1〜請求項4のいずれかに記載の離型フィルム用樹脂組成物を用いてなることを特徴とする離型フィルム。
- 少なくとも片面が酸化されていることを特徴とする請求項5に記載の離型フィルム。
- 酸化処理が、コロナ放電処理、フレーム処理、プラズマ処理からなる群から選ばれる少なくとも1種以上の処理方法であることを特徴とする請求項6に記載の離型フィルム。
- 請求項5〜請求項7のいずれかに記載の離型フィルムを少なくとも1層以上含むことを特徴とする積層体。
- 紙、布、合成樹脂からなる織布又は不織布から選ばれる1種以上の基材と積層されてなることを特徴とする請求項8に記載の積層体。