JP2006070688A - 壁面化粧構造体 - Google Patents
壁面化粧構造体 Download PDFInfo
- Publication number
- JP2006070688A JP2006070688A JP2005062064A JP2005062064A JP2006070688A JP 2006070688 A JP2006070688 A JP 2006070688A JP 2005062064 A JP2005062064 A JP 2005062064A JP 2005062064 A JP2005062064 A JP 2005062064A JP 2006070688 A JP2006070688 A JP 2006070688A
- Authority
- JP
- Japan
- Prior art keywords
- coating material
- weight
- finish coating
- parts
- finish
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】隣接した乾式ボード間の目地部にパテ材Cが充填され、乾式ボード及び目地部を含む全面に仕上塗材層Eが形成されてなる壁面化粧構造体において、前記仕上塗材層が、抗張積5N/mm以上であるベース塗材に粒子径0.05〜5mmの骨材が混合されてなり、前記ベース塗材の固形分100重量部に対する骨材比率が10〜2000重量部である仕上塗材によって形成されたものであり、前記パテ材の抗張積が、前記ベース塗材の抗張積の1.2〜100倍である壁面化粧構造体。
【選択図】図1
Description
一例として、実公昭55−594号公報(特許文献1)には、2枚のパネルを接合し、接合部に形成された目地部に弾性パテを充填した後、化粧塗装を行うことが記載されている。特開昭61−200256号公報(特許文献2)には、外装材同士の目地部にシーラントを充填した後、弾性パテを塗布し、その表面に硬性塗料を塗布することが記載されている。実開平2−39036号公報(特許文献3)には、端部に加工を施した外壁材どうしを重ね合わせて目地部を形成し、その目地部に弾性クロスを介在した弾性パテ層と、弾性塗料層を設けることが記載されている。実開平4−110839号公報(特許文献4)には、サイディングボード間のV字状目地部に、弾性パテを埋めた後、その上に塗料を塗布することが記載されている。
1.隣接した乾式ボード間の目地部にパテ材が充填され、乾式ボード及び目地部を含む全面に仕上塗材層が形成されてなる壁面化粧構造体において、
前記仕上塗材層が、抗張積5N/mm以上であるベース塗材に粒子径0.05〜5mmの骨材が混合されてなり、前記ベース塗材の固形分100重量部に対する骨材比率が10〜2000重量部である仕上塗材によって形成されたものであり、
前記パテ材の抗張積が、前記ベース塗材の抗張積の1.2〜100倍であることを特徴とする壁面化粧構造体。
2.隣接した乾式ボード間の目地部にパテ材が充填され、乾式ボード及び目地部を含む全面に仕上塗材層が形成されてなる壁面化粧構造体において、
前記仕上塗材層が少なくとも2種の仕上塗材の積層によって形成されたものであり、
乾式ボードに近接する第1の仕上塗材層が、抗張積5N/mm以上であるベース塗材に粒子径0.05〜5mmの骨材が混合されてなり、前記ベース塗材の固形分100重量部に対する骨材比率が0〜1500重量部である仕上塗材によって形成されたものであり、
前記第1の仕上塗材層上に積層される第2の仕上塗材層が、抗張積5N/mm以上であるベース塗材に粒子径0.05〜5mmの骨材が混合されてなり、前記ベース塗材の固形分100重量部に対する骨材比率が10〜2000重量部である仕上塗材によって形成されたものであり、
前記第1の仕上塗材層の骨材比率が、前記第2の仕上塗材層の骨材比率よりも小さく、
前記パテ材の抗張積が、前記ベース塗材の抗張積の1.2〜100倍であることを特徴とする壁面化粧構造体。
3.前記パテ材の伸びが100〜600%であることを特徴とする1.または2.記載の壁面化粧構造体。
本発明では、乾式ボード間の目地部における経時的なひび割れ、段差の発生等を抑制することができるため、初期の仕上外観を長期にわたり維持することができる。
本発明は、各種の乾式ボードAによって構成された建築物の壁面に適用するものである。このような壁面は通常、幅3〜50mm程度の目地部を設けて複数枚の乾式ボードAを突き合わせることによって形成される。乾式ボードAとしては、例えば、セメントボード、押出成形板、スレート板、PC板、ALC板、繊維強化セメント板、金属系サイディングボード、窯業系サイディングボード、セラミック板、珪酸カルシウム板、石膏ボード、プラスチックボード、硬質木片セメント板、塩ビ押出サイディングボード、合板等が挙げられる。
また、シーリング材Bの充填前には、予めバックアップ材充填やプライマー塗付等の処理を行っておいてもよい。バックアップ材としては、例えば、発泡ポリエチレン系バックアップ材等を使用することができる。プライマーとしては、例えば、合成ゴム系プライマー、アクリル系プライマー、ウレタン系プライマー、エポキシ系プライマー、シリコーンレジン系プライマー、シラン系プライマー等を使用することができる。
パテ材の抗張積は、上記条件を満たす範囲内であればよいが、通常は25N/mm以上(好ましくは100N/mm以上、より好ましくは200N/mm以上)程度である。パテ材の抗張積の上限は特に限定されないが、通常は1000N/mm以下(好ましくは800N/mm以下、より好ましくは500N/mm以下)程度である。
パテ材Cの抗張積が小さすぎる場合は、目地部において仕上塗材層Eにひび割れ、段差等が発生しやすくなる。パテ材Cの抗張積が大きすぎる場合は、パテ材Cあるいは乾式ボードAに亀裂が発生したり、仕上塗材層Eにひび割れが生じるおそれがある。
伸び(%)={(L−20)/20}×100
ここに、L:破断時の標線間距離(mm)
抗張積(N/mm)=T×(L−20)
ここに、T:引張り強さ(N/mm2)
網状体としては、各種の天然繊維、合成繊維等からなる繊維質網状体が好適である。このような繊維質網状体において、使用する繊維の材質、径、強度等は要求性能等に応じて適宜設定することができ、2種以上の繊維を組み合せることもできる。また、繊維によって網状体を形成する際の編み方、接合方法等は種々の方法を採用することができる。繊維質網状体における開口部分の大きさや数については、パテ材Cが食い込み可能な程度であればよく、網状体の幅は、通常、目地幅より大きく、かつパテ材Cの塗付幅より小さくなるように設定すればよい。網状体の厚みは、概ね5〜500μm程度である。
ベース塗材の抗張積は5N/mm以上であるが、好ましくは20N/mm以上、より好ましくは30N/mm以上、さらに好ましくは40N/mm以上である。ベース塗材の抗張積の上限は特に限定されないが、通常は250N/mm以下、好ましくは200N/mm以下、より好ましくは150N/mm以下である。ベース塗材の抗張積がこのような範囲内であれば、目地部におけるひび割れ発生を十分に抑制することができる。また、乾式ボードAに反りが生じるのを抑制することもできる。
ベース塗材の伸びは、通常50〜600%、好ましくは100〜500%、より好ましくは150〜400%である。
合成樹脂エマルションのガラス転移温度は適宜設定することができ、通常は−50〜50℃、好ましくは−40〜40℃、より好ましくは−30〜30℃である。
体質顔料の混合比率は、合成樹脂エマルションの固形分100重量部に対し、固形分換算で通常10〜1000重量部、好ましくは20〜500重量部、より好ましくは30〜300重量部である。
着色顔料の混合比率は、合成樹脂エマルションの固形分100重量部に対し、固形分換算で通常1〜300重量部、好ましくは2〜200重量部、より好ましくは3〜150重量部である。
骨材としては、自然石、自然石の粉砕物等の天然骨材、及び着色骨材等の人工骨材から選ばれる少なくとも1種以上を好適に使用することができる。具体的には、例えば、大理石、御影石、蛇紋岩、花崗岩、蛍石、寒水石、長石、石灰石、珪石、珪砂、砕石、雲母、珪質頁岩、及びこれらの粉砕物、陶磁器粉砕物、セラミック粉砕物、ガラス粉砕物、ガラスビーズ、ガラスフレーク、樹脂粉砕物、樹脂ビーズ、ゴム粒、プラスチック片、金属粒等が挙げられる。また、貝殻、珊瑚、木材、炭、活性炭等の粉砕物を使用することもできる。
骨材の粒子径は0.05〜5mm(好ましくは0.1〜3mm)であるが、骨材の粒子径が小さすぎる場合は、乾式ボードA間の継目を目立たなくすることが難しくなる。骨材の粒子径が大きすぎる場合は、骨材が塗膜から脱落しやすくなる。なお、本発明における粒子径は、JIS Z8801−1:2000に規定される金属製網ふるいを用いて測定される値である。
第1の仕上塗材と第2の仕上塗材におけるベース塗材が異なる場合、第1の仕上塗材におけるベース塗材の抗張積を高く設定することもできる。
第1の仕上塗材層E1の厚みは0.1〜3mm程度であり、第2の仕上塗材層E2の厚み(凸部の厚み)は0.5〜10mm程度である。
アクリルシリコン樹脂エマルション(ガラス転移温度0℃、固形分50重量%)200重量部、重質炭酸カルシウム(粒子径4〜5μm)100重量部、酸化チタン20重量部、パルプ繊維2重量部、増粘剤2重量部、造膜助剤18重量部、消泡剤1重量部を均一に攪拌混合してベース塗材1を得た。このベース塗材1の抗張積は75N/mm、伸びは260%であった。
アクリルシリコン樹脂エマルション(ガラス転移温度5℃、固形分50重量%)200重量部、ビニロン繊維1重量部、増粘剤1重量部、造膜助剤10重量部、消泡剤2重量部を均一に攪拌混合してベース塗材2を得た。このベース塗材2の抗張積は70N/mm、伸びは180%であった。
アクリル樹脂エマルション(ガラス転移温度40℃、固形分50重量%)200重量部、重質炭酸カルシウム(粒子径4〜5μm)1080重量部、酸化チタン10重量部、パルプ繊維1重量部、増粘剤2重量部、造膜助剤24重量部、消泡剤2重量部を均一に攪拌混合してベース塗材3を得た。このベース塗材3の抗張積は4N/mm、伸びは5%であった。
窯業系サイディングボード(900×2400×12mm)を2枚用意し、板間に10mm幅の目地部を設け、そこに変性シリコーン系シーリング材を打設したものを下地とした。
この下地の目地部に、パテ材1(湿気硬化型ウレタン樹脂パテ材、固形分95重量%、樹脂:充填剤=100:90(固形分比)、抗張積260N/mm、伸び450%)を目地近傍のサイディングボード表面にわたって目地幅の15倍の幅で充填塗付し、直ちにクロスを貼り付けた。室温で4時間乾燥させた後、再度、パテ材1を塗付し平滑にならし、室温で16時間乾燥させた。
その後、目地部を含むサイディングボード全体に水性エポキシ樹脂系下塗材を塗装(乾燥厚み約0.03mm)して下塗材層を形成させた。室温で2時間乾燥後、仕上塗材1を凹凸状(乾燥厚み約2〜3mm)に塗装して化粧仕上を施した。その結果、目地部の目立ちもなく、均一な仕上りが得られた。
なお、仕上塗材1としては、上記ベース塗材1の固形分100重量部にゴム粉(粒子径0.5〜1mm)10重量部、珪砂(粒子径0.2〜1mm)100重量部を均一に混合して得られたものを使用した。
仕上塗材層の塗装において、仕上塗材2を平坦に塗装し(乾燥厚み約0.8mm)、次いで仕上塗材3をスタッコ状(乾燥厚み約1〜3mm)に塗装して化粧仕上を施した以外は、実施例1と同様にして試験を行った。実施例2では、変位量=H(サイディングボードの高さ(mm))/100においても仕上塗材層に亀裂は認められなかった。
なお、仕上塗材2としては、上記ベース塗材1の固形分100重量部に、寒水石(粒子径0.2〜0.4mm)40重量部を均一に混合して得られたものを使用した。
仕上塗材3としては、上記ベース塗材1の固形分100重量部に、寒水石(粒子径0.2〜0.4mm)40重量部、及び珪砂(粒子径0.5〜2mm)150重量部を均一に混合して得られたものを使用した。
仕上塗材層の塗装において、仕上塗材2を平坦に塗装し(乾燥厚み約0.8mm)、次いで仕上塗材4をスタッコ状(乾燥厚み約1〜3mm)に塗装して化粧仕上を施した以外は、実施例1と同様にして試験を行った。実施例3では、変位量=H(サイディングボードの高さ(mm))/100においても仕上塗材層に亀裂は認められなかった。
なお、仕上塗材2としては、上記ベース塗材1の固形分100重量部に、寒水石(粒子径0.2〜0.4mm)40重量部を均一に混合して得られたものを使用した。
仕上塗材4としては、上記ベース塗材2の固形分100重量部に、寒水石(粒子径0.2〜0.4mm)50重量部、及び着色骨材(粒子径0.5〜2mm)400重量部を均一に混合して得られたものを使用した。
仕上塗材層の塗装において、ベース塗材1を平坦に塗装し(乾燥厚み約0.6mm)、次いで仕上塗材4をスタッコ状(乾燥厚み約1〜3mm)に塗装して化粧仕上を施した以外は、実施例1と同様にして試験を行った。実施例4では、変位量=H(サイディングボードの高さ(mm))/100においても仕上塗材層に亀裂は認められなかった。
なお、仕上塗材4としては、上記ベース塗材2の固形分100重量部に、寒水石(粒子径0.2〜0.4mm)50重量部、及び着色骨材(粒子径0.5〜2mm)400重量部を均一に混合して得られたものを使用した。
パテ材1をパテ材2(変性シリコーン系パテ材、固形分95重量%、抗張積80N/mm、伸び280%)に替えた他は、実施例1と同様にして試験を行った。その結果、面内せん断試験において仕上塗材層に亀裂が認められた。また、目地部において段差(盛上がり)が発生した。
パテ材1をパテ材3(エポキシ系パテ材、固形分95重量%、抗張積6N/mm、伸び2%)に替えた他は、実施例1と同様にして試験を行った。その結果、面内せん断試験において、早期にパテ材が破断し、仕上塗材層に亀裂が生じてしまった。
仕上塗材層の塗装において、仕上塗材1に代えて仕上塗材5を使用した以外は、実施例1と同様にして試験を行った。比較例3では、面内せん断試験において仕上塗材層に亀裂が生じてしまった。
なお、仕上塗材5としては、上記ベース塗材3の固形分100重量部に、ゴム粉(粒子径0.5〜1mm)10重量部、珪砂(粒子径0.2〜1mm)100重量部を均一に混合して得られたものを使用した。
B:シーリング材
C:パテ材
D:下塗材層
E:仕上塗材層
E1:第1の仕上塗材層
E2:第2の仕上塗材層
Claims (3)
- 隣接した乾式ボード間の目地部にパテ材が充填され、乾式ボード及び目地部を含む全面に仕上塗材層が形成されてなる壁面化粧構造体において、
前記仕上塗材層が、抗張積5N/mm以上であるベース塗材に粒子径0.05〜5mmの骨材が混合されてなり、前記ベース塗材の固形分100重量部に対する骨材比率が10〜2000重量部である仕上塗材によって形成されたものであり、
前記パテ材の抗張積が、前記ベース塗材の抗張積の1.2〜100倍であることを特徴とする壁面化粧構造体。 - 隣接した乾式ボード間の目地部にパテ材が充填され、乾式ボード及び目地部を含む全面に仕上塗材層が形成されてなる壁面化粧構造体において、
前記仕上塗材層が少なくとも2種の仕上塗材の積層によって形成されたものであり、
乾式ボードに近接する第1の仕上塗材層が、抗張積5N/mm以上であるベース塗材に粒子径0.05〜5mmの骨材が混合されてなり、前記ベース塗材の固形分100重量部に対する骨材比率が0〜1500重量部である仕上塗材によって形成されたものであり、
前記第1の仕上塗材層上に積層される第2の仕上塗材層が、抗張積5N/mm以上であるベース塗材に粒子径0.05〜5mmの骨材が混合されてなり、前記ベース塗材の固形分100重量部に対する骨材比率が10〜2000重量部である仕上塗材によって形成されたものであり、
前記第1の仕上塗材層の骨材比率が、前記第2の仕上塗材層の骨材比率よりも小さく、
前記パテ材の抗張積が、前記ベース塗材の抗張積の1.2〜100倍であることを特徴とする壁面化粧構造体。 - 前記パテ材の伸びが100〜600%であることを特徴とする請求項1または請求項2記載の壁面化粧構造体。