JP2004163925A - 感光性樹脂印刷版原版、その製造方法およびこれを用いた樹脂凸版印刷版の製造方法 - Google Patents
感光性樹脂印刷版原版、その製造方法およびこれを用いた樹脂凸版印刷版の製造方法 Download PDFInfo
- Publication number
- JP2004163925A JP2004163925A JP2003363147A JP2003363147A JP2004163925A JP 2004163925 A JP2004163925 A JP 2004163925A JP 2003363147 A JP2003363147 A JP 2003363147A JP 2003363147 A JP2003363147 A JP 2003363147A JP 2004163925 A JP2004163925 A JP 2004163925A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- photosensitive resin
- heat
- printing plate
- sensitive mask
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】支持体上に、水に溶解または分散可能な樹脂および紫外光により硬化可能なモノマーを含有する感光性樹脂層(A)、および赤外線吸収物質を含有する水不溶性の感熱マスク層(C)がこの順に積層されていることを特徴とする感光性樹脂印刷版原版。感熱マスク層(C)に架橋構造または疎水性成分を導入して水不溶性とすることで、層(A)と層(C)の極性の違いから、両層間での物質移動を防ぐことができ、また感熱マスク層(C)の耐傷性が格段に向上するため原版のハンドリングが容易となる。
【選択図】なし
Description
「支持体上に、水に溶解または分散可能な樹脂および紫外光により硬化可能なモノマーを含有する感光性樹脂層(A)、および赤外線吸収物質を含有する水不溶性の感熱マスク層(C)がこの順に積層されていることを特徴とする感光性樹脂印刷版原版。」である。
「(1)基板上に感光性樹脂層(A)を積層して感光性樹脂シートを得る工程
(2) 水不溶性の感熱マスク層(C)を含む感熱マスク要素を得る工程
(3)感光性樹脂シートの感光性樹脂層(A)の表面と、感熱マスク要素をラミネートする工程、を含む感光性樹脂印刷版原版の製造方法。」である。
「(1)本発明の感光性樹脂印刷版原版を用い、
(2)赤外レーザーで感熱マスク層(C)に像様照射することによって画像マスク(C’)を形成し、
(3)形成された画像マスク(C’)側から紫外光を用いて露光し、感光性樹脂層(A)に潜像を形成し、
(4)水を主成分とする液により現像処理し、画像マスク(C’)および紫外光未露光部の感光性樹脂層(A)を除去することを特徴とする樹脂凸版印刷版の製造方法。」である。
D=log10(100/T)=log10(I0/I)
(ここで、Tは透過率(単位は%)、I0は透過率測定の際の入射光強度、Iは透過光強度である)。
数平均分子量600のポリエチレングリコールの両末端にアクリロニトリルを付加し、これを水素還元して得たα,ω−ジアミノポリオキシエチレンとアジピン酸との等モル塩 60重量部、ε−カプロラクタム 20重量部およびヘキサメチレンジアミンとアジピン酸との等モル塩 20重量部を溶融重合して、相対粘度(ポリマー1gを抱水クロラール100mlに溶解し、25℃で測定した粘度)2.50の水溶性ポリアミド樹脂1を得た。
撹拌用ヘラおよび冷却管を取り付けた3つ口フラスコ中に(a)水溶性ポリアミド樹脂1 50重量部、(b)水34重量部および(c)エタノール22重量部を入れ、撹拌しながら90℃で2時間加熱し、水溶性ポリアミド樹脂1を溶解させた。70℃に冷却した後、(d)グリシジメメタクリレート(“ブレンマー”G、日本油脂(株)製)1.5重量部を添加し、30分間撹拌した。さらに、(e)グリセリンジメタクリレート(“ブレンマー”GMR、日本油脂(株)製)8重量部、(f)2−アクロイロキシエチル−2−ヒドロキシエチルフタル酸(HOA−MPE、共栄社化学(株)製)24重量部、(g)ポリエチレングリコール(PEG#400、ライオン(株)製)5重量部、(h)N,N,N’,N’−テトラ(2−ヒドロキシ−3−メタアクロイルオキシプロピル)−m−キシレンジアミン 5重量部、(i)テトラメチロールメタントリアクリレート(“NKエステル”A−TMM−3、新中村化学(株)製)4重量部、(j)ベンジルジメチルケタール(“イルガキュア”651、チバ・ガイギー(株)製)1.3重量部および(k)ハイドロキノンモノメチルエーテル 0.01重量部を添加して30分間撹拌し、感光性樹脂層(A1)用の塗工液組成物1を得た。
上記で合成した水溶性ポリアミド樹脂1を、水/エタノール=50/50(重量比)の混合溶媒中に固形分濃度15重量%となるように80℃で溶解させ、接着調整層(B1)用の塗工液組成物2を得た。
“MA100”(カーボンブラック、三菱化学(株)製)25重量部、硝化綿“SL−1”(ニトロセルロース、旭化成工業(株)製)26重量部、可塑剤ATBC(アセチルクエン酸トリブチル、(株)ジェイ・プラス製)6重量部および“PMアセテート”(プロピレングリコールモノメチルエーテルアセテート、大阪印刷インキ製造(株)製)30重量部をあらかじめ混合させたものを、3本ロールミルを用いて混練分散させ、カーボンブラック分散液を調製した。該分散液に“アラルダイト”6071(エポキシ樹脂、旭チバ(株)製)17重量部、“ユーバン”2061(メラミン樹脂、三井化学(株)製)24重量部、(g)“ライトエステル”P−1M(リン酸モノマー、共栄社化学(株)製)1重量部および(h)メチルイソブチルケトン 600重量部を添加し、30分間撹拌した。その後、固形分濃度が16重量%になるように(d)“PMアセテート”を添加し、感熱マスク層(C1)用の塗工液組成物3を得た。
鹸化度91%〜94%のポリビニルアルコール(“ゴーセノール”AL−06、日本合成化学(株)製)100重量部を、水/エタノール=40/60(重量比)の混合溶媒に固形分濃度10重量%となるように80℃で溶解させ、剥離補助層(D1)用の塗工液組成物4を得た。
鹸化度91%〜94%のポリビニルアルコール(“ゴーセノール”AL−06、日本合成化学(株)製)100重量部および赤外線吸収剤(“PROJET”825、AVECIA(株)製)2重量部を、水/エタノール=40/60(重量比)の混合溶媒に固形分濃度10重量%となるように80℃で溶解させ、剥離補助層(D2)用の塗工液組成物5を得た。
250μmのポリエステルフィルム“ルミラー”S10(東レ(株)製)に予めポリエステル系接着剤を塗布した基板上に、感光性樹脂層(A1)用の塗工液組成物1を流延させ、60℃で2時間乾燥し、基板を含めて厚さ950μmの感光性樹脂シート1を得た。感光性樹脂シート1の膜厚は基板上に所定厚みのスペーサーを設置し、スペーサーをはみ出している部分の塗工液組成物1を、水平な金尺で掻き出すことによって行った。
厚さ100μmのポリエステルフィルム“ルミラー”S10(東レ(株)製)を層(E)として使用し、該フィルム上に、塗工液組成物4をバーコーターを用いて乾燥膜厚が0.5μmになるように塗布、120℃で30秒間乾燥し、剥離補助層(D1)/保護層(E)の積層体を得た。
厚さ100μmのポリエステルフィルム“ルミラー”S10(東レ(株)製)上に、塗工液組成物5をバーコーターを用いて乾燥膜厚が0.5μmになるように塗布、120℃で30秒間乾燥し、剥離補助層(D2)/保護層(E)の積層体を得た。
厚さ100μmのポリエステルフィルム“ルミラー”S10(東レ(株)製)上に、塗工液組成物5をバーコーターを用いて乾燥膜厚が1μmになるように塗布、120℃で30秒間乾燥し、剥離補助層(D2)/保護層(E)の積層体を得た。
(実施例1)
上記した感光性樹脂シート1の感光性樹脂層(A1)上に、水/エタノール=70/30重量%の混合溶媒をバーコーター#20を用いて塗布して感光性樹脂層(A1)を膨潤させ、感熱マスク要素1の感熱マスク層(C1)が感光性樹脂層(A1)に接するようにローラー圧着し、1週間静置して、基板/感光性樹脂層(A1)/感熱マスク層(C1)/剥離補助層(D1)/保護層(E)の順に積層された感光性樹脂印刷版原版1を得た。
(実施例2)
実施例1において、感熱マスク要素2を用いた以外は、実施例1とすべて同様にして、基板/感光性樹脂層(A1)/感熱マスク層(C1)/剥離補助層(D2)/保護層(E)の順に積層された感光性樹脂印刷版原版2を得た。実施例1と同様に描画を行ったが、出力6W、ドラム回転数500rpmで、ベタ部の感熱マスク層(C1)が実質上レーザー融除され、下層の感光性樹脂層(A1)表面へのレーザー掘削や描画パターンの歪みなどのレーザー出力過多による弊害は発生しなかった。感熱マスク層(C1)の上層の剥離補助層(D2)に赤外線吸収剤が添加されているため、剥離補助層(D2)がレーザー融除されやすくなっており、実施例1より高いドラム回転数(つまり1スポット当たりのレーザー出力が低い)での描画が可能となった。また、実施例1と同様に超高圧水銀灯による露光およびブラシ式現像機による現像を行ったところ、シャープな形状のレリーフが得られた。
(実施例3)
上記感光性樹脂シート1の感光性樹脂層(A1)上に、水/エタノール=70/30重量%の混合溶媒をバーコーター#20を用いて塗布して感光性樹脂層(A1)を膨潤させ、感熱マスク要素3の接着調整層(B1)が感光性樹脂(A1)に接するようにローラー圧着し、1週間静置して、基板/感光性樹脂層(A1)/接着調整層(B1)/感熱マスク層(C1)/剥離補助層(D2)/保護層(E)の順に積層された感光性樹脂印刷版原版3を得た。実施例2と同様、出力6W、ドラム回転数500rpmでの描画が可能であった。
(a)部分鹸化ポリビニルアルコール(“Mowiol”4−80、Hoechst社製)2重量部を(b)水 40重量部に溶解し、接着調整層(B2)用の塗工液組成物6を得た。
(a)カーボンブラック(“Printex”U、Degussa社製)2重量部、(b)部分鹸化ポリビニルアルコール(KP205、クラレ(株)製)8重量部、(c)n−プロパノール 20重量部および(d)水 80重量部を混合し、分散機“Ultra Turrax”中で2時間処理して、感熱マスク層(C2)用の塗工液組成物7を得た。
厚さ100μmのポリエステルフィルム“ルミラー”S10(東レ(株)製)を層(E)として用い、該フィルム上に、塗工液組成物7をバーコーターを用いて乾燥膜厚が6μmになるように塗布、120℃で30秒間乾燥し、感熱マスク層(C2)/保護層(E)の積層体を得た。
(比較例1)
上記した感光性樹脂シート1の感光性樹脂層(A1)上に、水/エタノール=70/30重量%の混合溶媒をバーコーター#20を用いて塗布して感光性樹脂層(A1)を膨潤させ、感熱マスク要素4の接着調整層(B2)が感光性樹脂(A1)に接するようにローラー圧着し、1週間静置して、基板/感光性樹脂層(A1)/接着調整層(B2)/感熱マスク層(C2)/保護層(E)の順に積層された感光性樹脂印刷版原版4を得た。実施例1と同様に、プレートセッターによる描画、超高圧水銀灯による露光およびブラシ式現像機による現像を行った。感熱マスク層(C2)はカーボンブラックを、水溶性樹脂である部分鹸化ポリビニルアルコールに分散させただけであるために、膜強度が弱く、版の取り扱い時に傷が入りやすかった。実施例1と同様の方法で感熱マスク層(C2)の耐傷性を評価したところ、1回往復擦りで貫通性の傷が入った。感熱マスク層(C2)に傷が入ると、その部分で紫外光を遮断する機能がなくなり、紫外光での硬化を防止したい部分が硬化されてしまう。これにより、不必要なレリーフが形成されることになり、印刷版としては好ましくなかった。また、感熱マスク層(C2)は水現像を発現するため、水溶性樹脂をバインダーとして用いており、経時により、同じく親水性を有する接着調整層(B2)や感光性樹脂層(A1)中に感熱マスク層(C2)の成分が混入している様子が見られた。感光性樹脂層(A1)に感熱マスク層(C2)の成分が混入していたため、混入部分で光硬化不良が起こりやすくなり、満足のいくレリーフが得られなかった。
ε−カプロラクタム 10重量部、N−(2−アミノエチル)ピペラジンとアジピン酸のナイロン塩 90重量部および水 100重量部をステンレス製オートクレーブに入れ、内部の空気を窒素ガスで置換した後に180℃で1時間加熱し、次いで水分を除去して水溶性ポリアミド樹脂2を得た。
<変性ポリビニルアルコール1の合成>
冷却管をつけたフラスコ中に、部分鹸化ポリビニルアルコール“ゴーセノール”KL−05(鹸化度 78.5%〜82.0%、日本合成化学工業(株)製)50重量部、無水コハク酸 2重量部およびアセトン 10重量部を入れ、60℃で6時間加熱した後、冷却管を外してアセトンを揮発させた。その後、100重量部のアセトンで未反応の無水コハク酸を溶出させる精製工程を2回行った後、60℃で減圧乾燥を5時間行い、水酸基にコハク酸がエステル結合した、変性ポリビニルアルコール1を得た。
撹拌ヘラおよび冷却管をつけた3つ口フラスコ中に、水溶性ポリアミド樹脂2を7.5重量部、変性ポリビニルアルコール1を47.5重量部、ジエチレングリコール 11重量部、水 38重量部およびエタノール 44重量部を入れ、撹拌しながら110℃で30分間、次いで70℃で90分間加熱しポリマーを溶解させた。ついで、“ブレンマー”G(グリシジルメタクリレート、日本油脂(株)製)3重量部を添加し、70℃で30分間撹拌した。さらに“ブレンマー”GMR(グリシジルメタクリレートのメタクリル酸付加物、日本油脂(株)製)12重量部、“ライトエステル”G201P(グリシジルメタクリレートのアクリル酸付加物、共栄社化学(株)製)5重量部、“エポキシエステル”70PA(プロピレングリコールジグリシジルエーテルのアクリル酸付加物、共栄社化学(株)製)6重量部、“NKエステル”A−200(平均分子量200のポリエチレングリコールのジアクリレート、新中村化学工業(株)製)5重量部、“イルガキュア”651(ベンジルジメチルケタール、チバ・ガイギー(株)製)0.1重量部、“イルガキュア”184(α−ヒドロキシケトン、チバ・ガイギー(株)製)1.5重量部、“Suminol Fast Cyanine Green G conc.”(酸性染料、カラーインデックス C. I. Acid Green 25、住友化学工業(株)製)0.01重量部、“ダイレクトスカイブルー6B”(浜本染料(株)製)0.01重量部、“フォーマスタ”(消泡剤、サンノプコ(株)製)0.05重量部、“チヌビン”327(紫外線吸収剤、チバ・ガイギー(株)製)0.015重量部、“TTP−44”(ビス−{2−(2−エトキシエトキシカルボニル)エチルチオ}オクチルチオ ホスフィン、淀化学(株)製)0.2重量部および“Q−1300”(アンモニウム N−ニトロソフェニルヒドロキシルアミン、和光純薬工業(株)製)0.005重量部を添加して30分間撹拌し、流動性のある感光性樹脂層(A2)の塗工液組成物8を得た。
“バイロン31SS”(不飽和ポリエステル樹脂のトルエン溶液、東洋紡績(株)製)260重量部および“PS−8A”(ベンゾインエチルエーテル、和光純薬工業(株)製)2重量部の混合物を70℃で2時間加熱後30℃に冷却し、エチレングリコールジグリシジルエーテルジメタクリレート 7重量部を加えて2時間混合した。さらに、“コロネート”3015E(多価イソシアネート樹脂の酢酸エチル溶液、日本ポリウレタン工業(株)製)25重量部および“EC−1368”(工業用接着剤、住友スリーエム(株)製)14重量部を添加し、接着剤組成物1を得た。
接着剤塗布基板2を接着剤塗工側から超高圧水銀灯で1000mJ/cm2露光した後、感光性樹脂層(A2)用の塗工液組成物8を接着剤塗布基板2の接着剤塗布面に流延し、60℃のオーブン中で5時間乾燥させて、基板を含めておよそ厚さ900μmの感光性樹脂シート2を得た。感光性樹脂シート2の厚さは、基板上に所定厚のスペサーを設置し、スぺーサーからはみ出ている部分の塗工液組成物8を、水平な金尺で掻き出すことによって制御した。
“ゴーセノール”AL−06(鹸化度91%〜94%のポリビニルアルコール、日本合成化学工業(株)製)4重量部を水 55重量部、メタノール 14重量部、n−プロパノール 10重量部およびn−ブタノール 10重量部に溶解させ、剥離補助層(D3)用の塗工液組成物9を得た。
“MA100”(カーボンブラック、三菱化学(株)製)23重量部、“ダイアナール”BR−95(アルコール不溶性のアクリル樹脂、三菱レーヨン(株)製)15重量部、可塑剤ATBC(アセチルクエン酸トリブチル、(株)ジェイ・プラス製)6重量部および“PMアセテート”(プロピレングリコールモノメチルエーテルアセテート、大阪印刷インキ製造(株)製)30重量部をあらかじめ混合させたものを、3本ロールミルを用いて混練分散させ、カーボンブラック分散液2を調整した。分散液2に“アラルダイト”6071(エポキシ樹脂、旭チバ(株)製)20重量部、“ユーバン”2061(メラミン樹脂、三井化学(株)製)27重量部、“ライトエステル”P−1M(リン酸モノマー、共栄社化学(株)製)0.7重量部およびメチルイソブチルケトン 140重量部を添加し、30分間撹拌した。その後、固形分濃度が33重量%になるように“PMアセテート”を添加し、感熱マスク層(C3)用の塗工液組成物10を得た。
“MA100”(カーボンブラック、三菱化学(株)製)23重量部、“ダイアナール”BR−95(アルコール不溶性のアクリル樹脂、三菱レーヨン(株)製)15重量部、可塑剤ATBC(アセチルクエン酸トリブチル、(株)ジェイ・プラス製)6重量部およびジエチレングリコールモノエチルエーテルモノアセテート 30重量部をあらかじめ混合させたものを、3本ロールミルを用いて混練分散させ、カーボンブラック分散液3を調整した。分散液3に“アラルダイト”6071(エポキシ樹脂、旭チバ(株)製)20重量部、“ユーバン”2061(メラミン樹脂、三井化学(株)製)27重量部、“ライトエステル”P−1M(リン酸モノマー、共栄社化学(株)製)0.7重量部およびメチルイソブチルケトン 140重量部を添加し、30分間撹拌した。その後、固形分濃度が33重量%になるようにジエチレングリコールモノエチルエーテルモノアセテートを添加し、感熱マスク層(C3)用の塗工液組成物11を得た。
“エピコート”1004(エポキシ樹脂、ジャパン・エポキシ・レジン(株)製)10重量部をシクロヘキサノン 90重量部に溶解させ、接着調整層(B3)用の塗工液組成物12を得た。
厚さ100μmのポリエステルフィルム“ルミラー”S10(東レ(株)製)上に、塗工液組成物9をバーコーターを用いて乾燥膜厚が0.25μmになるように塗布、100℃で25秒間乾燥し、剥離補助層(D3)/保護層(E)の積層体を得た。このようにして得られた積層体の剥離補助層(D3)側に、塗工液組成物10をバーコーターを用いて乾燥膜厚が2μmになるように塗布、140℃で90秒間乾燥し、感熱マスク層(C3)/剥離補助層(D3)/保護層(E)の積層体である感熱マスク要素5を得た。この感熱マスク要素5の光学濃度(オルソクロマチックフィルター、透過モード)は3.8であった。
<感熱マスク要素6の製造>
厚さ100μmのポリエステルフィルム“ルミラー”S10(東レ(株)製)上に、塗工液組成物9をバーコーターを用いて乾燥膜厚が0.25μmになるように塗布、100℃で25秒間乾燥し、剥離補助層(D3)/保護層(E)の積層体を得た。このようにして得られた積層体の剥離補助層(D3)側に、塗工液組成物11をバーコーターを用いて乾燥膜厚が2μmになるように塗布、140℃で90秒間乾燥し、感熱マスク層(C4)/剥離補助層(D3)/保護層(E)の積層体である感熱マスク要素6を得た。この感熱マスク要素6の光学濃度(オルソクロマチックフィルター、透過モード)は3.8であった。
厚さ100μmのポリエステルフィルム“ルミラー”S10(東レ(株)製)上に、塗工液組成物9をバーコーターを用いて乾燥膜厚が0.25μmになるように塗布、100℃で25秒間乾燥し、剥離補助層(D3)/保護層(E)の積層体を得た。このようにして得られた積層体の剥離補助層(D3)側に、塗工液組成物10をバーコーターを用いて乾燥膜厚が2μmになるように塗布、140℃で90秒間乾燥し、感熱マスク層(C3)/剥離補助層(D3)/保護層(E)の積層体を得た。このようにして得られた積層体の剥離補助層(C3)側に、塗工液組成物12をバーコーターを用いて乾燥膜厚が1μmになるように塗布、140℃で60秒間乾燥し、接着調整層(B3)/感熱マスク層(C3)/剥離補助層(D3)/保護層(E)の積層体である感熱マスク要素7を得た。この感熱マスク要素7の光学濃度(オルソクロマチックフィルター、透過モード)は3.8であった。
(実施例4)
感光性樹脂シート2の感光性樹脂層(A2)上に塗工液組成物8を展開し、その上に、感熱マスク要素5を感熱マスク層(C3)が塗工液組成物8が展開された感光性樹脂層(A2)に接するようにかぶせて、80℃に加熱したカレンダーロールでラミネートを行い、接着剤塗布基板2/感光性樹脂層(A2)/感熱マスク層(C3)/剥離補助層(D3)/保護層(E)の順に積層された感光性樹脂印刷版原版5を得た。カレンダーロールのクリアランスは、原版5から保護層(E)を剥離した後における積層体の厚みが950μmになるように調整した。展開された塗工液組成物8は、ラミネート後1週間静置させることによって、残存溶媒が自然乾燥し、追加の感光性樹脂層(A2)を形成する。
(実施例5)
感光性樹脂シート2の感光性樹脂層(A2)上に塗工液組成物8を展開し、その上に、感熱マスク要素6を感熱マスク層(C4)が塗工液組成物8が展開された感光性樹脂層(A2)に接するようにかぶせて、80℃に加熱したカレンダーロールでラミネートを行い、接着剤塗布基板2/感光性樹脂層(A2)/感熱マスク層(C4)/剥離補助層(D3)/保護層(E)の順に積層された感光性樹脂印刷版原版6を得た。カレンダーロールのクリアランスは、原版6から保護層(E)を剥離した後における積層体の厚みが950μmになるように調整した。展開された塗工液組成物8は、ラミネート後1週間静置させることによって、残存溶媒が自然乾燥し、追加の感光性樹脂層(A2)を形成する。
(実施例6)
感光性樹脂シート2の感光性樹脂層(A2)上に塗工液組成物8を展開し、その上に、感熱マスク要素7を接着調整層(B3)が塗工液組成物8が展開された感光性樹脂層(A2)に接するようにかぶせて、80℃に加熱したカレンダーロールでラミネートを行い、接着剤塗布基板2/感光性樹脂層(A2)/接着調整層(B3)/感熱マスク層(C3)/剥離補助層(D3)/保護層(E)の順に積層された感光性樹脂印刷版原版7を得た。カレンダーロールのクリアランスは、原版7から保護層(E)を剥離した後における積層体の厚みが950μmになるように調整した。展開された塗工液組成物8は、ラミネート後1週間静置させることによって、残存溶媒が自然乾燥し、追加の感光性樹脂層(A2)を形成する。
<感熱マスク要素8の製造>
厚さ100μmのポリエステルフィルム“ルミラー”S10(東レ(株)製)上に、塗工液組成物9をバーコーターを用いて乾燥膜厚が0.25μmになるように塗布、100℃で25秒間乾燥し、剥離補助層(D3)/保護層(E)の積層体を得た。このようにして得られた積層体の剥離補助層(D3)側に、真空蒸着法でアルミニウムの薄膜を形成させ、感熱マスク層(C5)/剥離補助層(D3)/保護層(E)の積層体で、光学濃度(オルソマチックフィルター、透過モード)が3.5の感熱マスク要素8を製造した。
<感熱マスク要素9の製造>
感熱マスク要素8において、層(C5)の代わりに、テルルの金属蒸着膜である層(C6)を設けた以外は同様の手順で感熱マスク要素9を製造した。要素9の光学濃度(オルソクロマチックフィルター、透過モード)は3.8であった。
(実施例7)
感光性樹脂シート2の感光性樹脂層(A2)上に塗工液組成物8を展開し、感熱マスク要素8の感熱マスク層(C5)を、塗工液組成物8が展開された感光性樹脂層(A2)に接するようにかぶせて、80℃に加熱されたカレンダーロールでラミネートを行い、接着剤塗布基板2/感光性樹脂層(A2)/感熱マスク層(C5)/剥離補助層(D3)/保護層(E)の順に積層された感光性樹脂印刷原版8を得た。カレンダーロールのクリアランスは、原版8から保護層(E)を剥離した後における積層体の厚みが950μmになるように調整した。展開された塗工液組成物8は、ラミネート後1週間静置させることにより、残存溶媒が自然乾燥し、追加の感光性樹脂層(A2)を形成する。
(実施例8)
実施例7において、感熱マスク要素8の代わりに感熱マスク要素9を用いた以外は全て同様の手順で感光性樹脂印刷版原版9を得た。
<感熱マスク要素10の製造>
実施例1に使用した感熱マスク要素1において、層(C1)用の塗工液3の代わりに層(C2)用の塗工液7を用い、層(C2)の乾燥膜厚を6μmに、層(C2)の乾燥条件を120℃で30秒にした以外は全て同様の手順で作製し、感熱マスク層(C2)/剥離補助層(D1)/保護層(E)の積層体である感熱マスク要素10を得た。この感熱マスク要素10の光学濃度(オルソクロマチックフィルター、透過モード)は3.4であった。
<感熱マスク要素11の製造>
実施例4に使用した感熱マスク要素5において、層(C3)用の塗工液10の代わりに層(C2)用の塗工液7を用い、層(C2)の乾燥膜厚を6μmに、層(C2)の乾燥条件を120℃で30秒にした以外は全て同様の手順で作製し、感熱マスク層(C2)/剥離補助層(D3)/保護層(E)の積層体である感熱マスク要素11を得た。この感熱マスク要素11の光学濃度(オルソクロマチックフィルター、透過モード)は3.4であった。
(比較例2)
実施例1において、感熱マスク要素1の代わりに感熱マスク要素10を用いた以外は同様にして原版の製造を行い、基板/感光性樹脂層(A1)/感熱マスク層(C2)/剥離補助層(D1)/保護層(E)の積層体である感光性樹脂印刷版原版10を得た。実施例1で評価した原版1との違いは、架橋構造を有する感熱マスク層(C1)の代わりに、非架橋で水溶性の感熱マスク層(C2)を用いたことのみである。
(比較例3)
実施例4において、感熱マスク要素5の代わりに感熱マスク要素11を用いた以外は同様にして原版の製造を行い、基板/感光性樹脂層(A2)/感熱マスク層(C2)/剥離補助層(D3)/保護層(E)の積層体である感光性樹脂印刷版原版11を得た。実施例4で評価した原版5との違いは、架橋構造を有する感熱マスク層(C3)の代わりに、非架橋で水溶性の感熱マスク層(C2)を用いたことのみである。
Claims (18)
- 支持体上に、水に溶解または分散可能な樹脂および紫外光により硬化可能なモノマーを含有する感光性樹脂層(A)、および赤外線吸収物質を含有する水不溶性の感熱マスク層(C)がこの順に積層されていることを特徴とする感光性樹脂印刷版原版。
- 水不溶性の感熱マスク層(C)が、硬化性の樹脂で架橋された層である請求項1に記載の感光性樹脂印刷版原版。
- 硬化性の樹脂が、多官能イソシアネートおよび多官能エポキシ化合物からなる群から選ばれる少なくとも1種の化合物と、尿素樹脂、アミン系化合物、アミド系化合物、水酸基含有化合物、カルボン酸化合物、チオール系化合物からなる群から選ばれる少なくとも1種の化合物との組み合わせである請求項2記載の感光性樹脂印刷版原版。
- 水不溶性の感熱マスク層(C)が、金属薄膜である請求項1に記載の感光性樹脂印刷版原版。
- 感光性樹脂層(A)と感熱マスク層(C)の間に、接着調整層(B)が設けられている請求項1〜4のいずれかに記載の感光性樹脂印刷版原版。
- 接着調整層(B)が水に溶解または分散可能な樹脂を含有する請求項5に記載の感光性樹脂印刷版原版。
- 感光性樹脂層(A)が、ポリアミド樹脂を含有する請求項1〜6のいずれかに記載の感光性樹脂印刷版原版。
- 感光性樹脂層(A)がポリビニルアルコールまたは部分鹸化ポリビニルアルコールまたはそれらの変性体を含有する請求項1〜7のいずれかに記載の感光性樹脂印刷版原版。
- 感熱マスク層(C)がアクリル樹脂を含有し、ニトロセルロースを含有しない請求項1〜3、5〜8のいずれかに記載の感光性樹脂印刷版原版。
- 感熱マスク層(C)の上に、保護層(E)、または剥離補助層(D)および保護層(E)が積層された請求項1〜9のいずれかに記載の感光性樹脂印刷版原版。
- 剥離補助層(D)が赤外線吸収物質および/または熱分解性化合物を含有する請求項10に記載の感光性樹脂印刷版原版。
- (1)基板上に感光性樹脂層(A)を積層して感光性樹脂シートを得る工程、
(2)水不溶性の感熱マスク層(C)を含む感熱マスク要素を得る工程、
(3)感光性樹脂シートの感光性樹脂層(A)の表面と、感熱マスク要素をラミネートする工程、を含む感光性樹脂印刷版原版の製造方法。 - 感熱マスク要素が保護層(E)と感熱マスク層(C)を含み、感光性樹脂層(A)の表面に感熱マスク要素の感熱マスク層(C)側が接するようにラミネートする工程からなる請求項12に記載の感光性樹脂印刷版原版の製造方法。
- 保護層(E)と感熱マスク層(C)の間に剥離補助層(D)を設ける請求項13に記載の感光性樹脂印刷版原版の製造方法。
- 感熱マスク要素が感熱マスク層(C)と接着調整層(B)を含み、感光性樹脂層(A)の表面に感熱マスク要素の接着調整層(B)側が接するようにラミネートする工程からなる請求項12に記載の感光性樹脂印刷版原版の製造方法。
- 感熱マスク要素を得る工程において、感熱マスク層(C)を積層する際に、加熱することによって感熱マスク層(C)に架橋構造を形成させる請求項12〜15のいずれかに記載の感光性樹脂印刷版原版の製造方法。
- (1)請求項1〜11のいずれかに記載の感光性樹脂印刷版原版を用い、
(2)赤外レーザーで感熱マスク層(C)に像様照射することによって画像マスク(C’)を形成し、
(3)形成された画像マスク(C’)側から紫外光を用いて露光し、感光性樹脂層(A)に潜像を形成し、
(4)水を主成分とする液により現像処理し、画像マスク(C’)および紫外光未露光部の感光性樹脂層(A)を除去することを特徴とする樹脂凸版印刷版の製造方法。 - (1)請求項10または11に記載の感光性樹脂印刷版原版を用い、
(2)赤外レーザーで感熱マスク層(C)に像様照射するに際して、少なくとも保護層(E)の一部を剥離する請求項17に記載の樹脂凸版印刷版の製造方法。