IN2014MN01980A - - Google Patents

Download PDF

Info

Publication number
IN2014MN01980A
IN2014MN01980A IN1980MUN2014A IN2014MN01980A IN 2014MN01980 A IN2014MN01980 A IN 2014MN01980A IN 1980MUN2014 A IN1980MUN2014 A IN 1980MUN2014A IN 2014MN01980 A IN2014MN01980 A IN 2014MN01980A
Authority
IN
India
Prior art keywords
electric resistance
resistance welded
steel pipe
temperature range
cooled
Prior art date
Application number
Other languages
English (en)
Inventor
Shunsuke Toyoda
Sota Goto
Takatoshi Okabe
Tomohiro Inoue
Motoharu Egi
Atsushi Yonemoto
Original Assignee
Jfe Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jfe Steel Corp filed Critical Jfe Steel Corp
Publication of IN2014MN01980A publication Critical patent/IN2014MN01980A/en

Links

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21C—MANUFACTURE OF METAL SHEETS, WIRE, RODS, TUBES, PROFILES OR LIKE SEMI-MANUFACTURED PRODUCTS OTHERWISE THAN BY ROLLING; AUXILIARY OPERATIONS USED IN CONNECTION WITH METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL
    • B21C37/00—Manufacture of metal sheets, rods, wire, tubes, profiles or like semi-manufactured products, not otherwise provided for; Manufacture of tubes of special shape
    • B21C37/06—Manufacture of metal sheets, rods, wire, tubes, profiles or like semi-manufactured products, not otherwise provided for; Manufacture of tubes of special shape of tubes or metal hoses; Combined procedures for making tubes, e.g. for making multi-wall tubes
    • B21C37/08—Making tubes with welded or soldered seams
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21B—ROLLING OF METAL
    • B21B27/00—Rolls, roll alloys or roll fabrication; Lubricating, cooling or heating rolls while in use
    • B21B27/06—Lubricating, cooling or heating rolls
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F16—ENGINEERING ELEMENTS AND UNITS; GENERAL MEASURES FOR PRODUCING AND MAINTAINING EFFECTIVE FUNCTIONING OF MACHINES OR INSTALLATIONS; THERMAL INSULATION IN GENERAL
    • F16L—PIPES; JOINTS OR FITTINGS FOR PIPES; SUPPORTS FOR PIPES, CABLES OR PROTECTIVE TUBING; MEANS FOR THERMAL INSULATION IN GENERAL
    • F16L9/00—Rigid pipes
    • F16L9/02—Rigid pipes of metal
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21B—ROLLING OF METAL
    • B21B27/00—Rolls, roll alloys or roll fabrication; Lubricating, cooling or heating rolls while in use
    • B21B27/06—Lubricating, cooling or heating rolls
    • B21B27/08—Lubricating, cooling or heating rolls internally
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21B—ROLLING OF METAL
    • B21B3/00—Rolling materials of special alloys so far as the composition of the alloy requires or permits special rolling methods or sequences ; Rolling of aluminium, copper, zinc or other non-ferrous metals
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K11/00—Resistance welding; Severing by resistance heating
    • B23K11/002—Resistance welding; Severing by resistance heating specially adapted for particular articles or work
    • B23K11/0073—Butt welding of long articles advanced axially
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K11/00—Resistance welding; Severing by resistance heating
    • B23K11/08—Seam welding not restricted to one of the preceding subgroups
    • B23K11/087—Seam welding not restricted to one of the preceding subgroups for rectilinear seams
    • B23K11/0873—Seam welding not restricted to one of the preceding subgroups for rectilinear seams of the longitudinal seam of tubes
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B1/00—Layered products having a non-planar shape
    • B32B1/08—Tubular products
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0226—Hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0263—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment following hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/10—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of tubular bodies
    • C21D8/105—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of tubular bodies of ferrous alloys
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/08—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for tubular bodies or pipes
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/08—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for tubular bodies or pipes
    • C21D9/085—Cooling or quenching
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/08—Ferrous alloys, e.g. steel alloys containing nickel
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/16—Ferrous alloys, e.g. steel alloys containing copper
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/58—Ferrous alloys, e.g. steel alloys containing chromium with nickel with more than 1.5% by weight of manganese
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F16—ENGINEERING ELEMENTS AND UNITS; GENERAL MEASURES FOR PRODUCING AND MAINTAINING EFFECTIVE FUNCTIONING OF MACHINES OR INSTALLATIONS; THERMAL INSULATION IN GENERAL
    • F16L—PIPES; JOINTS OR FITTINGS FOR PIPES; SUPPORTS FOR PIPES, CABLES OR PROTECTIVE TUBING; MEANS FOR THERMAL INSULATION IN GENERAL
    • F16L9/00—Rigid pipes
    • F16L9/17—Rigid pipes obtained by bending a sheet longitudinally and connecting the edges
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/005—Ferrite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/50—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for welded joints
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12861—Group VIII or IB metal-base component
    • Y10T428/12951—Fe-base component
    • Y10T428/12958—Next to Fe-base component
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12861—Group VIII or IB metal-base component
    • Y10T428/12951—Fe-base component
    • Y10T428/12958—Next to Fe-base component
    • Y10T428/12965—Both containing 0.01-1.7% carbon [i.e., steel]
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12861—Group VIII or IB metal-base component
    • Y10T428/12951—Fe-base component
    • Y10T428/12972—Containing 0.01-1.7% carbon [i.e., steel]
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12861—Group VIII or IB metal-base component
    • Y10T428/12951—Fe-base component
    • Y10T428/12972—Containing 0.01-1.7% carbon [i.e., steel]
    • Y10T428/12979—Containing more than 10% nonferrous elements [e.g., high alloy, stainless]
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/13—Hollow or container type article [e.g., tube, vase, etc.]

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • General Engineering & Computer Science (AREA)
  • Manufacturing & Machinery (AREA)
  • Heat Treatment Of Articles (AREA)
  • Heat Treatment Of Steel (AREA)
IN1980MUN2014 2012-04-13 2013-04-11 IN2014MN01980A (enEXAMPLES)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2012092045 2012-04-13
PCT/JP2013/002488 WO2013153819A1 (ja) 2012-04-13 2013-04-11 優れた低温靭性を有する高強度厚肉電縫鋼管及びその製造方法

Publications (1)

Publication Number Publication Date
IN2014MN01980A true IN2014MN01980A (enEXAMPLES) 2015-07-10

Family

ID=49327403

Family Applications (1)

Application Number Title Priority Date Filing Date
IN1980MUN2014 IN2014MN01980A (enEXAMPLES) 2012-04-13 2013-04-11

Country Status (9)

Country Link
US (1) US9841124B2 (enEXAMPLES)
EP (1) EP2837708B1 (enEXAMPLES)
JP (1) JP5534111B2 (enEXAMPLES)
KR (1) KR101641450B1 (enEXAMPLES)
CN (1) CN104220622B (enEXAMPLES)
CA (1) CA2869879C (enEXAMPLES)
IN (1) IN2014MN01980A (enEXAMPLES)
RU (1) RU2613824C2 (enEXAMPLES)
WO (1) WO2013153819A1 (enEXAMPLES)

Families Citing this family (33)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5849846B2 (ja) * 2012-04-20 2016-02-03 新日鐵住金株式会社 耐火鋼材及びその製造方法
JP5516659B2 (ja) * 2012-06-28 2014-06-11 Ｊｆｅスチール株式会社 中温域の長期耐軟化性に優れた高強度電縫鋼管及びその製造方法
JP5516680B2 (ja) * 2012-09-24 2014-06-11 Ｊｆｅスチール株式会社 電縫溶接部の耐ｈｉｃ性および低温靭性に優れた電縫鋼管およびその製造方法
JP6303628B2 (ja) * 2014-03-07 2018-04-04 新日鐵住金株式会社 板厚１５ｍｍ以上の電縫鋼管用熱延鋼板
CN106715744A (zh) * 2014-09-25 2017-05-24 杰富意钢铁株式会社 电阻焊钢管用钢带和电阻焊钢管以及电阻焊钢管用钢带的制造方法
JP6394261B2 (ja) * 2014-10-14 2018-09-26 新日鐵住金株式会社 油井用電縫鋼管及びその製造方法
WO2016084335A1 (ja) * 2014-11-27 2016-06-02 Ｊｆｅスチール株式会社 電縫鋼管およびその製造方法
WO2016143270A1 (ja) * 2015-03-06 2016-09-15 Ｊｆｅスチール株式会社 高強度電縫鋼管およびその製造方法
WO2016143271A1 (ja) * 2015-03-12 2016-09-15 Ｊｆｅスチール株式会社 電縫溶接ステンレスクラッド鋼管およびその製造方法
JP6048621B1 (ja) * 2015-05-20 2016-12-21 新日鐵住金株式会社 高強度電縫鋼管、高強度電縫鋼管用の鋼板の製造方法、及び高強度電縫鋼管の製造方法
CN105643050A (zh) * 2016-02-29 2016-06-08 广船国际有限公司 一种低温高韧性钢的单面多丝埋弧焊焊接方法
CN105908088A (zh) * 2016-04-25 2016-08-31 江苏金源腾峰换热设备有限公司 一种煤气焚烧余热回收管道用合金材料的处理工艺
CN105955220B (zh) * 2016-06-17 2019-11-26 首钢集团有限公司 一种控制带钢卷取张力的方法及装置
CA3030455C (en) 2016-07-14 2021-01-26 Tata Steel Nederland Tubes Bv Method for the in-line manufacturing of steel tube
US20190292637A1 (en) * 2016-08-30 2019-09-26 Nippon Steel & Sumitomo Metal Corporation Oil well pipe for expandable tubular
US11268164B2 (en) 2016-09-28 2022-03-08 Jfe Steel Corporation Steel sheet and method for producing the same
CN110088317A (zh) * 2017-03-29 2019-08-02 日本制铁株式会社 线管用轧制状态电焊钢管
RU2652281C1 (ru) * 2017-05-31 2018-04-25 Публичное акционерное общество "Северсталь" Способ производства горячекатаных листов из высокопрочной стали
CN110546289A (zh) * 2017-06-22 2019-12-06 日本制铁株式会社 管线管用轧态电阻焊钢管及热轧钢板
CN107502836B (zh) * 2017-08-07 2019-03-01 南京钢铁股份有限公司 一种提高低温韧性的厚壁大口径高钢级管线钢及其制造方法
US10633726B2 (en) * 2017-08-16 2020-04-28 The United States Of America As Represented By The Secretary Of The Army Methods, compositions and structures for advanced design low alloy nitrogen steels
CN109423569B (zh) * 2017-08-23 2021-12-17 宝山钢铁股份有限公司 一种低温压力容器用钢及其制造方法
KR102010081B1 (ko) * 2017-12-26 2019-08-12 주식회사 포스코 고강도 고인성 열연강판 및 그 제조방법
JP7460533B2 (ja) * 2018-03-19 2024-04-02 タタ スチール リミテッド 耐水素誘起割れ（ｈｉｃ）性が強化されたｘ－６５グレードのａｐｉ ５ｌ ｐｓｌ－２仕様に適合する鋼組成物及びその鋼の製造方法
CN109234618B (zh) * 2018-09-18 2020-11-10 江阴兴澄特种钢铁有限公司 一种经济型抗hic管线钢板x70ms及其制造方法
DK3666911T3 (da) 2018-12-11 2021-11-15 Ssab Technology Ab Højstyrke-stålprodukt og fremgangsmåde til fremstilling af samme
DE102019205724A1 (de) * 2019-04-18 2020-10-22 Sms Group Gmbh Kühlvorrichtung für nahtlose Stahlrohre
JP7448804B2 (ja) * 2020-04-23 2024-03-13 日本製鉄株式会社 ラインパイプ用電縫鋼管、及びラインパイプ用熱延鋼板
KR102443927B1 (ko) * 2020-08-26 2022-09-19 주식회사 포스코 용접부 충격 인성이 우수한 열연강판 및 이의 제조방법
KR102413840B1 (ko) * 2020-09-16 2022-06-28 현대제철 주식회사 저항복비 및 고변형능 라인파이프용 강재 및 그 제조방법
CA3190830A1 (en) * 2020-10-05 2022-04-14 Akihide MATSUMOTO Electric resistance welded steel pipe and method for manufacturing the same
CN112941285A (zh) * 2021-01-25 2021-06-11 山西太钢不锈钢股份有限公司 一种q390级低屈强比厚规格黑皮钢热轧板卷及其制造方法
KR102845294B1 (ko) * 2022-12-29 2025-08-13 현대제철 주식회사 라인파이프용 강재 및 그 제조방법

Family Cites Families (16)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
SU893281A1 (ru) * 1979-12-21 1981-12-30 Московский Ордена Трудового Красного Знамени Институт Стали И Сплавов Способ изготовлени электросварных пр мошовных труб
JPS5935629A (ja) * 1982-08-24 1984-02-27 Nippon Steel Corp 低温靭性のすぐれた高張力電縫鋼管の製造方法
JPS59153839A (ja) 1983-02-23 1984-09-01 Nippon Steel Corp 低温靭性のすぐれた高張力電縫鋼管の製造方法
JPH0158253U (enEXAMPLES) 1987-10-06 1989-04-12
JPH0360888A (ja) 1989-07-31 1991-03-15 Mitsubishi Heavy Ind Ltd レーザ光を利用した穴明け加工方法
JPH0742509B2 (ja) 1990-06-07 1995-05-10 新日本製鐵株式会社 低温靭性に優れた電縫鋼管の製造方法
SU1799650A1 (ru) * 1990-10-15 1993-03-07 Mo I Stali I Splavov Способ изготовления электросварных прямошовных труб
JPH0742509A (ja) 1993-07-29 1995-02-10 Mitsubishi Heavy Ind Ltd 循環水ポンプの可動翼制御装置
RU2135622C1 (ru) * 1996-12-16 1999-08-27 Ниппон Стил Корпорейшн Сталь, имеющая высокую ударную вязкость в зоне термического воздействия при сварке
JP4268462B2 (ja) * 2002-06-26 2009-05-27 新日本製鐵株式会社 高温強度に優れた非調質低降伏比高張力鋼板の製造方法
CN100439546C (zh) * 2005-09-28 2008-12-03 株式会社神户制钢所 焊接性优异的490MPa级低屈服比冷成形钢管及其制造方法
JP5069863B2 (ja) * 2005-09-28 2012-11-07 株式会社神戸製鋼所 溶接性に優れた４９０ＭＰａ級低降伏比冷間成形鋼管およびその製造方法
JP5223375B2 (ja) 2007-03-01 2013-06-26 新日鐵住金株式会社 低温靭性に優れるラインパイプ用高強度熱延鋼板およびその製造方法
CN102046829B (zh) * 2008-05-26 2013-03-13 新日铁住金株式会社 低温韧性和延展性破坏停止性能优异的管线管用高强度热轧钢板及其制造方法
JP5660285B2 (ja) * 2010-05-31 2015-01-28 Ｊｆｅスチール株式会社 拡管性と低温靭性に優れた油井用溶接鋼管の製造方法および溶接鋼管
JP5516659B2 (ja) 2012-06-28 2014-06-11 Ｊｆｅスチール株式会社 中温域の長期耐軟化性に優れた高強度電縫鋼管及びその製造方法

Also Published As

Publication number Publication date
JPWO2013153819A1 (ja) 2015-12-17
RU2613824C2 (ru) 2017-03-21
JP5534111B2 (ja) 2014-06-25
KR20140138942A (ko) 2014-12-04
RU2014145519A (ru) 2016-06-10
CA2869879A1 (en) 2013-10-17
CA2869879C (en) 2017-08-29
US20150083266A1 (en) 2015-03-26
KR101641450B1 (ko) 2016-07-20
EP2837708A4 (en) 2015-08-12
CN104220622A (zh) 2014-12-17
EP2837708A1 (en) 2015-02-18
WO2013153819A1 (ja) 2013-10-17
US9841124B2 (en) 2017-12-12
CN104220622B (zh) 2016-11-02
EP2837708B1 (en) 2019-03-06

Similar Documents

Publication Publication Date Title
IN2014MN01980A (enEXAMPLES)
EP4254440A3 (en) Method of production of tin containing non grain-oriented silicon steel sheet
IN2014KN01251A (enEXAMPLES)
MX368208B (es) Placa de acero laminada en frío de alta maleabilidad y superresistente, y método de fabricación de la misma.
IN2014KN02799A (enEXAMPLES)
IN2014KN01291A (enEXAMPLES)
JP2011195882A5 (enEXAMPLES)
MX2012008841A (es) Metodo para fabricar tubos de acero sin costuras para tuberias y tubos de acero sin costuras para tuberias.
RU2013137456A (ru) Способ производства горячекатаного плоского стального проката
MX2018006621A (es) Metodo para producir lamina de acero electrico de grano orientado.
WO2013113304A3 (de) Höchstfester mehrphasenstahl mit verbesserten eigenschaften bei herstellung und verarbeitung
JP2011140686A5 (enEXAMPLES)
MX2013013218A (es) Metodo para la fabricacion de acero martensitico con limite de elasticidad muy alto y placa o pieza obtenida por tal metodo.
GB2548049A (en) Hot rolled light-gauge martensitic steel sheet and method for making the same
TWI456075B (zh) 深擠壓性及鋼卷內材質均勻性優異之高強度冷軋鋼板及其製造方法
MX2019011941A (es) Elemento de acero, laminas de acero laminadas en caliente para elementos de acero y metodo de produccion de los mismos.
MY180218A (en) Method for manufacturing high strenght coll rolled steel sheet having excellent workability
IN2015KN00599A (enEXAMPLES)
JP2011140688A5 (enEXAMPLES)
MX2019011940A (es) Elementos de acero, laminas de acero laminadas en caliente y metodo de produccion de los mismos.
MY161948A (en) Cold rolled steel sheet having excellent formability,shape fixability after aging,and method for manufacturing the same
RU2013126473A (ru) Заготовка для проволоки и стальная проволока, имеющие превосходные магнитные характеристики, и способ их изготовления
UA101439C2 (ru) СПОСОБ ПРОИЗВОДСТВА толстолистового прокат из стали Категории ПРОЧНОСТИ Х80 ДЛЯ ИЗГОТОВЛЕНИЯ ТРУБ ДЛЯ МАГИСТРАЛЬНЫХ ТРУБОПРОВОДОВ
JP2012177175A5 (enEXAMPLES)
MX2012007913A (es) Placa de acero laminado en frio y metodo para su elaboracion.