IN2014MN00819A - - Google Patents

Info

Publication number
IN2014MN00819A
IN2014MN00819A IN819MUN2014A IN2014MN00819A IN 2014MN00819 A IN2014MN00819 A IN 2014MN00819A IN 819MUN2014 A IN819MUN2014 A IN 819MUN2014A IN 2014MN00819 A IN2014MN00819 A IN 2014MN00819A
Authority
IN
India
Prior art keywords
mass
steel sheet
internal oxides
base iron
grain boundaries
Prior art date
Application number
Other languages
English (en)
Inventor
Mai Miyata
Yoshitsugu Suzuki
Yasunobu Nagataki
Yoshiyasu Kawasaki
Hirokazu Sugihara
Original Assignee
Jfe Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jfe Steel Corp filed Critical Jfe Steel Corp
Publication of IN2014MN00819A publication Critical patent/IN2014MN00819A/en

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21B—ROLLING OF METAL
    • B21B3/00—Rolling materials of special alloys so far as the composition of the alloy requires or permits special rolling methods or sequences ; Rolling of aluminium, copper, zinc or other non-ferrous metals
    • B21B3/02—Rolling special iron alloys, e.g. stainless steel
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21B—ROLLING OF METAL
    • B21B45/00—Devices for surface or other treatment of work, specially combined with or arranged in, or specially adapted for use in connection with, metal-rolling mills
    • B21B45/04—Devices for surface or other treatment of work, specially combined with or arranged in, or specially adapted for use in connection with, metal-rolling mills for de-scaling, e.g. by brushing
    • B21B45/08—Devices for surface or other treatment of work, specially combined with or arranged in, or specially adapted for use in connection with, metal-rolling mills for de-scaling, e.g. by brushing hydraulically
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/013—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of a metal other than iron or aluminium
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0226—Hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0236—Cold rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0273—Final recrystallisation annealing
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/005—Ferrous alloys, e.g. steel alloys containing rare earths, i.e. Sc, Y, Lanthanides
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/08—Ferrous alloys, e.g. steel alloys containing nickel
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/16—Ferrous alloys, e.g. steel alloys containing copper
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/44—Ferrous alloys, e.g. steel alloys containing chromium with nickel with molybdenum or tungsten
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/46—Ferrous alloys, e.g. steel alloys containing chromium with nickel with vanadium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/54—Ferrous alloys, e.g. steel alloys containing chromium with nickel with boron
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/024—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by cleaning or etching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Organic Chemistry (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Metal Rolling (AREA)
  • Coating With Molten Metal (AREA)
IN819MUN2014 2011-11-17 2012-11-02 IN2014MN00819A (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2011251960A JP5267638B2 (ja) 2011-11-17 2011-11-17 高強度溶融亜鉛めっき鋼板または高強度合金化溶融亜鉛めっき鋼板用熱延鋼板およびその製造方法
PCT/JP2012/007031 WO2013073124A1 (ja) 2011-11-17 2012-11-02 高強度溶融亜鉛めっき鋼板または高強度合金化溶融亜鉛めっき鋼板用熱延鋼板およびその製造方法

Publications (1)

Publication Number Publication Date
IN2014MN00819A true IN2014MN00819A (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html) 2015-06-12

Family

ID=48429225

Family Applications (1)

Application Number Title Priority Date Filing Date
IN819MUN2014 IN2014MN00819A (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html) 2011-11-17 2012-11-02

Country Status (8)

Country Link
US (1) US9758847B2 (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html)
EP (1) EP2781614A4 (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html)
JP (1) JP5267638B2 (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html)
KR (1) KR101552452B1 (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html)
CN (1) CN103946409A (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html)
IN (1) IN2014MN00819A (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html)
TW (1) TWI612151B (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html)
WO (1) WO2013073124A1 (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html)

Families Citing this family (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP6158630B2 (ja) * 2013-07-31 2017-07-05 Ｊｆｅスチール株式会社 溶融亜鉛めっき鋼板用の熱延鋼板の製造方法および該熱延鋼板
JP6505480B2 (ja) * 2014-08-29 2019-04-24 株式会社神戸製鋼所 溶融亜鉛めっき用または合金化溶融亜鉛めっき用原板、および溶融亜鉛めっき鋼板または合金化溶融亜鉛めっき鋼板
CN107429343B (zh) 2015-03-23 2019-05-28 新日铁住金株式会社 热轧钢板、其制造方法以及冷轧钢板的制造方法
KR101767773B1 (ko) 2015-12-23 2017-08-14 주식회사 포스코 연성이 우수한 초고강도 열연강판 및 그 제조방법
EP3505651B1 (en) * 2016-10-18 2023-09-20 Jiangyin Xing Cheng Special Steel Works Co., Ltd Toothed rack steel plate having thickness of 177.8 mm and manufactured by continuous casting billet and manufacturing method therefor
EP3578679B1 (en) 2017-01-31 2024-05-29 JFE Steel Corporation High-strength molten zinc plating hot-rolled steel sheet, and production method therefor
WO2019116531A1 (ja) * 2017-12-15 2019-06-20 日本製鉄株式会社 鋼板、溶融亜鉛めっき鋼板および合金化溶融亜鉛めっき鋼板
TWI670378B (zh) * 2017-12-15 2019-09-01 日商日本製鐵股份有限公司 鋼板、熱浸鍍鋅鋼板及合金化熱浸鍍鋅鋼板
TWI690604B (zh) * 2018-04-26 2020-04-11 日商日本製鐵股份有限公司 熔融Sn-Zn系合金鍍敷鋼板及其製造方法
JP7506350B2 (ja) * 2021-04-27 2024-06-26 日本製鉄株式会社 鋼溶接部材

Family Cites Families (21)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3241886B2 (ja) * 1993-09-02 2001-12-25 川崎製鉄株式会社 伸びフランジ性、延性及び表面性状に優れた熱延鋼板の製造方法
JP3195509B2 (ja) * 1995-02-01 2001-08-06 株式会社神戸製鋼所 表面性状に優れた熱延鋼板の製造方法
JP2000192190A (ja) * 1998-12-22 2000-07-11 Nippon Steel Corp 表面性状に優れた高強度熱延鋼板およびその製造方法
JP3956550B2 (ja) 1999-02-02 2007-08-08 Ｊｆｅスチール株式会社 強度延性バランスに優れた高強度溶融亜鉛メッキ鋼板の製造方法
JP4306068B2 (ja) * 2000-01-24 2009-07-29 Ｊｆｅスチール株式会社 加工性に優れた熱延下地の溶融亜鉛めっき高張力鋼板の製造方法
CA2521710C (en) * 2003-04-10 2009-09-29 Nippon Steel Corporation High strength molten zinc plated steel sheet and process of production of same
JP4580157B2 (ja) * 2003-09-05 2010-11-10 新日本製鐵株式会社 Ｂｈ性と伸びフランジ性を兼ね備えた熱延鋼板およびその製造方法
JP4035117B2 (ja) 2004-04-13 2008-01-16 新日本製鐵株式会社 表面性状の良好な高Ｓｉ含有鋼板の熱間圧延方法
JP4502947B2 (ja) * 2005-12-27 2010-07-14 株式会社神戸製鋼所 溶接性に優れた鋼板
EP1980638B2 (en) * 2006-01-30 2022-05-11 Nippon Steel Corporation High-strength hot-dip zinced steel sheet excellent in moldability and suitability for plating, high-strength alloyed hot-dip zinced steel sheet, and processes for producing these
JP4781836B2 (ja) * 2006-02-08 2011-09-28 新日本製鐵株式会社 耐水素脆性に優れた超高強度鋼板とその製造方法及び超高強度溶融亜鉛めっき鋼板の製造方法並びに超高強度合金化溶融亜鉛めっき鋼板の製造方法
JP4837426B2 (ja) * 2006-04-10 2011-12-14 新日本製鐵株式会社 バーリング加工性に優れた高ヤング率薄鋼板及びその製造方法
JP5103988B2 (ja) * 2007-03-30 2012-12-19 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板
JP2010126757A (ja) * 2008-11-27 2010-06-10 Jfe Steel Corp 高強度溶融亜鉛めっき鋼板およびその製造方法
JP5663833B2 (ja) * 2008-11-27 2015-02-04 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板の製造方法
JP5206705B2 (ja) 2009-03-31 2013-06-12 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板およびその製造方法
JP4924730B2 (ja) * 2009-04-28 2012-04-25 Ｊｆｅスチール株式会社 加工性、溶接性および疲労特性に優れる高強度溶融亜鉛めっき鋼板およびその製造方法
JP4883216B2 (ja) * 2010-01-22 2012-02-22 Ｊｆｅスチール株式会社 加工性とスポット溶接性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5786317B2 (ja) * 2010-01-22 2015-09-30 Ｊｆｅスチール株式会社 材質安定性と加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5786316B2 (ja) * 2010-01-22 2015-09-30 Ｊｆｅスチール株式会社 加工性および耐衝撃特性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP4893844B2 (ja) * 2010-04-16 2012-03-07 Ｊｆｅスチール株式会社 成形性および耐衝撃性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法

Also Published As

Publication number Publication date
KR20140088201A (ko) 2014-07-09
EP2781614A1 (en) 2014-09-24
KR101552452B1 (ko) 2015-09-10
EP2781614A4 (en) 2015-07-15
JP2013108107A (ja) 2013-06-06
US9758847B2 (en) 2017-09-12
CN103946409A (zh) 2014-07-23
JP5267638B2 (ja) 2013-08-21
TW201326420A (zh) 2013-07-01
WO2013073124A1 (ja) 2013-05-23
TWI612151B (zh) 2018-01-21
US20140314616A1 (en) 2014-10-23
WO2013073124A9 (ja) 2013-09-06

Similar Documents

Publication Publication Date Title
IN2014MN00819A (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html)
MX2016003144A (es) Laminas de acero galvanizadas por inmersion en caliente y laminas de acero recocidas despues de galvanizadas que tienen buen aspecto y buena adherencia al recubrimiento y metodos para la produccion de las mismas.
MX2016003143A (es) Laminas de acero galvanizadas por inmersion en caliente y laminas de acero recocidas despues de galvanizadas que tienen buen aspecto y buena adherencia al recubrimiento y metodos para la produccion de las mismas.
MX340869B (es) Lamina de acero laminada en caliente para lamina de acero laminada en frio, lamina de acero laminada en caliente para lamina de acero galvanizada, y metodo para la fabricacion de las mismas.
MX2013004337A (es) Placa de acero laminada en caliente o en frio, su proceso de fabricacion y su uso en la industria automotriz.
MX2013011750A (es) Laminas de acero laminadas en frio, de alta resistencia, que tienen deformabilidad local excelente y metodo de fabricacion de las mismas.
MX351086B (es) Lámina de acero para miembro de estampado en caliente y método para producir la misma.
MX357255B (es) Lamina de acero laminada en frio de alta resistencia que tiene excelente capacidad de conformacion en formas complejas y capacidad de perforacion de precision y metodo de fabricacion de la misma.
IN2014CN04330A (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html)
IN2014KN01170A (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html)
MX2019004000A (es) Lamina de acero recubierta de metal, metodo de fabricacion de lamina de acero galvanizada por inmersion en caliente, y metodo de fabricacion de lamina de acero galvanizada-recocida aleada.
MX2016005086A (es) Lamina de acero laminada en caliente que tiene excelente dureza de superficie despues de tratamiento termico carburizante y excelente capacidad de estiramiento.
MX2014001856A (es) Lamina de acero galvanizada por inmersion en caliente de alta resistencia que tiene excelente capacidad de embuticion profunda y metodo para la fabricacion de la misma.
MY153967A (en) High-strength hot rolled steel sheet having good formability and method for manufacturing the same
MY177135A (en) High strength cold-rolled steel sheet having excellent deep drawability and method for manufacturing the same
IN2014KN01613A (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html)
EP3431624A3 (en) Soft magnetic component steel material having excellent pickling properties, soft magnetic component having excellent corrosion resistance and magnetic properties, and production method therefor
MY177836A (en) Low yield ratio high-strength hot-dip galvanized steel sheet, low yield ratio high-strength hot-dip galvannealed steel sheet, method for manufacturing low yield ratio highstrength hot-dip galvanized steel sheet, and method for manufacturing low yield ratio high-strength hot-dip galvannealed steel sheet
IN2014KN00762A (GUID-C5D7CC26-194C-43D0-91A1-9AE8C70A9BFF.html)
MX2016002690A (es) Hoja de acero laminada en caliente que tiene excelente procesabilidad en frio y excelentes propiedades superficiales y dureza despues del procesamiento.
MX348493B (es) Hoja de acero laminada en frio teniendo una excelente conformabilidad y capacidad de fijacion de forma y metodo para la fabricacion de la misma.
MY167035A (en) Cold-rolled steel sheet having excellent formability and method for manufacturing the same
MY163017A (en) High strength cold rolled steel sheet having excellent formability, and method for manufacturing the same
MX2017015332A (es) Lamina de acero rolada en caliente, lamina de acero extra rigido rolada en frio, y metodo para fabricar lamina de acero rolada en caliente.
MX2017004854A (es) Lamina de acero galvanizada de alta resistencia.