HU219309B - Lubricating composition for using heat-forming of metals on work-body - Google Patents
Lubricating composition for using heat-forming of metals on work-body Download PDFInfo
- Publication number
- HU219309B HU219309B HU9601314A HUP9601314A HU219309B HU 219309 B HU219309 B HU 219309B HU 9601314 A HU9601314 A HU 9601314A HU P9601314 A HUP9601314 A HU P9601314A HU 219309 B HU219309 B HU 219309B
- Authority
- HU
- Hungary
- Prior art keywords
- weight
- sodium
- lubricant composition
- water
- polymethphosphate
- Prior art date
Abstract
A találmány tárgya kenőanyag-készítmény munkadarabokon valóalkalmazásra fémek melegalakításakor. A találmány szerinti kenőanyagösszetétele az alábbi: a) 0–80 tömeg% üvegpor és/vagy 0–50 tömeg%üvegfritt (szinterezett üveg), b) 10–25 tömeg% természetes vagyszintetikus grafit, c) 5–20 tömeg% Me2O.n SiO2 képletű alkálifém-szilikát(ok), mely képletben Me jelentése lítium, kálium vagy nátrium,és n értéke 1-től 4-ig terjedő szám, d) 1–6 tömeg% vízben oldódónátrium-polimetafoszfát, e) 0–3 tömeg% vízben oldhatatlan nátrium-polimetafoszfát, f) 0,5–3 tömeg% sűrítőszer, g) 0–1 tömeg% bórax. Akenőanyag alkalmas 800–1300 °C felületi hőmérsékletű munkadarabokközvetlen kenésére. ŕ
Description
A találmány tárgya új kenőanyag-készítmény, amely a melegalakításnak szánt munkadarabok felületén alkalmazható. Az új készítmény főleg tömbök és szelvények meleghengerlése vagy üreges tömbök úgynevezett lökőpad-berendezéseken történő előállítása esetén alkalmazható.
Tekintettel arra, hogy a feldolgozni kívánt fémek felületi hőmérséklete körülbelül 800-1300 °C, a gyakorlatban mind ez ideig inkább az olyan szerszámok kenésére volt példa, amelyek legfeljebb 400 °C felületi hőmérsékletükkel a klasszikus kenés számára nem problémásak. Bár a CH-PS 660 023 szerinti kenőanyag-diszperzióval állítólag 600 °C feletti hőmérsékletű munkadarabok is kezelhetők, a gyakorlati rekonstruáláskor a 800 °C és 1200 °C közötti hőmérséklet-tartományban hatékony, tapadó kenőanyagfilm kialakulása nem volt észlelhető. A tapadás hiánya lényegében arra vezethető vissza, hogy a szerves alkotók azonnal pirolizálódnak, így tapadó film nem alakulhat ki. A szerves alkotók pirolízisének más hátránya is van: füst keletkezik, ami a környezetben dolgozók számára igen kellemetlen. Kenőanyagfilm kialakulása a CH-PS 670 106 szerinti, por alakjában alkalmazható kenőanyag/pácanyag gyakorlati alkalmazása során sem volt észlelhető. Már a por alakú készítmény egyenletes felhordása önmagában lényeges nehézség.
Ha a munkadarab helyett a szerszámot kenik, ez is - a szerszám típusától függően - különböző nehézségekkel jár. A kenőanyag felvitele gyakran a szerszám geometriai kialakítása miatt már nehéz, vagy a szerszám alacsony hőmérséklete (100 °C körül) nem engedi a kenőfilm szabályos kialakulását. Tekintettel arra, hogy a szerszámot rendszerint nagy mennyiségű hűtővízzel hűtik, nagy mennyiségű kenőanyag megy veszendőbe a hűtővízzel együtt, ami azt jelenti, hogy a hűtővíz elszennyeződik és tisztító utókezelésre szorul. Jó kenéshez a fenti módszer esetén viszonylag sok kenőanyag kell.
A találmány feladata olyan kenőanyag-készítmény kifejlesztése volt, amely a fent említett hátrányoktól mentes és ezért alkalmas arra, hogy 800 °C és 1300 °C közötti felületi hőmérsékletű munkadarabokat egyenletes, jól tapadó, vízben oldhatatlan kenőanyagfilmmel ellásson.
A fenti feladatot az 1. igénypont szerinti kenőanyag-készítménnyel oldottuk meg, amelynek összetétele az alábbi:
a) 0-80 tömeg% üvegpor és/vagy 0-50 tömeg% üvegfritt (szinterezett üveg),
b) 10-25 tömeg% természetes vagy szintetikus grafit,
c) 5-20 tömeg% Me2O.n SiO2 képletű alkálifém-szilikát(ok), mely képletben Me jelentése lítium, kálium vagy nátrium, és n értéke 1-től 4-ig terjedő szám,
d) 1-6 tömeg% vízben oldódó nátrium-polimetafoszfát,
e) 0-3 tömeg% vízben oldhatatlan nátrium-polimetafoszfát,
f) 0,5-3 tömeg% sűrítőszer,
g) 0-1 tömeg% bórax.
A 800 °C-ot meghaladó felületi hőmérsékletű munkadarabok esetén előnyösen az alábbi összetételű kenőanyag-készítményt alkalmazzuk:
a) 0-20 tömeg% üvegpor és/vagy 30-50 tömeg% üvegfritt,
b) 20-25 tömeg% természetes vagy szintetikus grafit,
c) 7-20 tömeg% Me20.n SiO2 képletű alkálifémszilikát(ok), mely képletben Me jelentése lítium, kálium vagy nátrium, és n értéke 1-től 4-ig terjedő szám,
d) 2-6 tömeg% vízben oldódó nátrium-polimetafoszfát,
e) 0-1 tömeg% vízben oldhatatlan nátrium-polimetafoszfát,
f) 3-4 tömeg% sűrítőszer,
g) 0,2-0,7 tömeg% bórax.
Az 1000 °C-ot meghaladó felületi hőmérsékletű munkadarabok esetén előnyösen az alábbi összetételű kenőanyag-készítményt alkalmazzuk:
a) 45-70 tömeg% üvegpor és/vagy 0-20 tömeg% üvegfritt,
b) 20-25 tömeg% természetes vagy szintetikus grafit,
c) 7-20 tömeg% Me2O.n SiO2 képletű alkálifémszilikát(ok), mely képletben Me jelentése lítium, kálium vagy nátrium, és n értéke l-től 4-ig terjedő szám,
d) 1-2 tömeg% vízben oldódó nátrium-polimetafoszfát,
e) 0-1 tömeg% vízben oldhatatlan nátrium-polimetafoszfát,
f) 1,5-2 tömeg% sűrítőszer,
g) 0-0,25 tömeg% bórax.
Üvegporként célszerűen normálüveget alkalmazunk, amelynek szemcsemérete d5o<100 pm, lágyulótartománya körülbelül 700-900 °C (CAS No. 65997-17-3). Az üvegpomak lényeges szerepe van a kenőanyag kiváló filmképző tulajdonságaiban. A magas lágyulópont miatt akkor alkalmazunk növekvő mértékben üvegport, ha a munkadarab felületi hőmérséklete meghaladja az 1000 °C-ot.
Ezzel szemben az üvegfritt főleg akkor kerül alkalmazásra, ha a felhasználási hőmérséklet az alsó tartományban, 800 °C-tól van. Az üvegporhoz viszonyítva a frittnek alacsonyabb, 500-700 °C körüli lágyulópontja van, így filmképző tulajdonságai jól érvényesülnek. Az üvegfritt kémiai összetétele előnyösen alkálifém-alkáliföldfém-alumínium-bór-szilikát, átlagos szemcsemérete általában d5o<100 pm.
Az üvegport és az üvegfrittet az alkalmazási körülményektől függően, a megadott határokon belül tetszőleges keverési arányokban használhatjuk fel.
További lényeges alkotóelem a grafit. Mind szintetikus, mind természetes eredetű grafitot alkalmazhatunk. A grafit átlagos szemcsemérete célszerűen d50<100 pm. Előnyösen erősen kristályos grafitot alkalmazunk, azaz olyat, amelynek a krisztallithossza Le 100 nm-nél nagyobb.
A vízben oldódó alkálifém-szilikátok lényegében a kötőanyag szerepét látják el. Az Me20.n SiO2 általános képletű vízben oldódó alkálifém-szilikátok - e képletben Me jelentése lítium, kálium vagy nátrium, és n értéke l-től 4-ig teijedő szám - külön-külön vagy egymással alkotott keverék formájában lehetnek jelen a kenőanyagban. Előnyösen a fenti képletnek megfelelő nátrium-metaszilikátot (n= 1-1,5) vagy nátrium-szilikátot
HU 219 309 Β (n=3,3-3,5; vízüveg), vagy az említett nátrium-szilikátok és K20.n SiO2 képletű kálium-szilikát (n=2,4-3) és/vagy Li20.n SiO2 képletű lítium-szilikát (n=2,4-3) eutektikus elegyét alkalmazzuk. Különösen előnyös az említett előnyös alkálifém-szilikátoknak az alábbi tömegarányú elegye: nátrium-szilikát:káliumszilikát : lítium-szilikát=12,3%: 67,5%: 20,7%.
A kenőanyagban lévő, vízben oldódó nátrium-metapolifoszfát feladata a habzás gátlása. A polifoszfát előnyösen (NaPO3)n általános képlet, ahol n<450. Ezek a vegyületek a „hexametafoszfát” vagy „Graham- féle só” elnevezéssel is ismeretesek.
Lehetséges továbbá vízben oldhatatlan nátrium-metapolifoszfát kötőanyagként! adagolása. Különösen alkalmasak e célra a „Madrell-féle só” elnevezésű, (NaPO3)n képletű vegyületek, ahol n értéke 40-70.
A sűrítőszer, előnyösen poliszacharid vagy poliszacharidszármazék adagolása igen fontos azért, hogy a kenyőanyag-diszperzió viszkozitása és stabilitása nagyobb hőmérséklet-tartományon belül állandó legyen. A sűrítőszer további feladata, hogy a diszperzió szilárd részecskéinek a kiülepedését gátolja. Előnyösen biopoliszacharidok, így xantángumi, ramsángumi vagy alkil-cellulóz, például hidroxi-metil-cellulóz kerül alkalmazásra.
Sűrítőszerként a poliakrilsav alkálifémsói, előnyösen a nátrium-poliakrilátok is megfelelő eredményt adnak.
Baktériumok támadása elleni védekezésképpen előnyösen kereskedelmi forgalomban kapható biocidet adagolunk a kenőanyaghoz.
Végül, tapadásfokozó adalékként a kenőanyag bóraxot (nátrium-tetraborát-dekahidrátot) is tartalmazhat.
A találmány szerinti kenőanyagot előnyösen 20-50 tömeg% szilárd anyagot tartalmazó vizes diszperzió alakjában alkalmazzuk, de a szilárd anyag részaránya ennél kisebb vagy nagyobb is lehet. A diszperzió előállítása a kereskedelemben kapható, nagy nyíróerőt kifejtő diszpergálókészülékben (EP 218 989) történhet.
Az alkalmazásra kész diszperzió viszkozitása célszerűen 1000-7000 MPas (Rheomat 15, 20 °C-on, Bcella, 5. sebesség), de a viszkozitás sűrítőszer adagolásával tovább variálható. A diszperzió felvitele a diszperz rendszerek permetezésére ismert berendezésekkel történhet (EP-A 453 801).
A találmány értelmében a fent leírt kenőanyag-készítményt 800-1300 °C felületi hőmérsékletű munkadarabokon alkalmazható fémek melegalakításakor, főleg tömbök és szelvények meleghengerlése vagy üreges tömbök úgynevezett lökőpadon történő előállítása esetén. A diszperzió felvitele a munkadarabra közvetlenül az alakítás előtt történik. A reve eltávolítása előnyös, de nem feltétlenül szükséges. A víz azonnali elpárolgását követően a munkadarab felületén néhány másodpercen belül egyenletes, vízben oldhatatlan kenőfilm alakul ki, amelyet az alakítás művelete nem roncsol.
Példák
A viszkozitást Rheomat 15 típusú műszerrel, 20 °Con (B-cella, 5. sebesség) mértük.
1. készítmény (850-1200 °C felületi hőmérsékletű munkadarabokra alkalmas)
49,17 tömeg% üvegfritt (kötőfritt K2244, d7ü<100 pm, Schauer Co., Wien, Ausztria)
20,00 tömeg% grafit (szintetikus grafit T 75, d50 24 pm, LONZA G&T, Sins, Svájc)
15,67 tömeg% vízüveg (vízben oldódó nátrium-szilikát Na2O.n SiO2, n=3,3-3,5)
6,00 tömeg% vízben oldódó nátrium-polifoszfát (Alcopon, Benckiser-Knapsack, Ladenburg, Német Szövetségi Köztársaság)
3.33 tömeg% hidroxi-metil-cellulóz (Dow Chemical) 0,67 tömeg% bórax
0,16 tömeg% biocid
Vizes diszperzió, szárazanyag-tartalma 20 tömeg% Viszkozitás: 1000-2000 MPas
2. készítmény (1000-1250 °C felületi hőmérsékletű munkadarabokra alkalmas)
64,85 tömeg% üvegpor (üvegpor 300, d70<63 pm, Mineralienwerke Kuppenheim)
24,94 tömeg% grafit (szintetikus grafit T 75, D50 24 pm, LONZA G&T, Sins, Svájc)
6,98 tömeg% vízben oldódó nátrium-szilikát (Na2O.n SiO2, n=1-1,15)
1,67 tömeg% vízben oldódó nátrium-polifoszfát (Alcopon, Benckiser-Knapsack, Ladenburg, Német Szövetségi Köztársaság)
1.33 tömeg% hidroxi-metil-cellulóz (Dow Chemical) 0,22 tömeg% xantángumi
0,01 tömeg% biocid
Vizes diszperzió, szárazanyag-tartalma 40 tömeg% Viszkozitás: 1000-3000 MPas.
3. készítmény (1000-1250 °C felületi hőmérsékletű munkadarabokra alkalmas)
47,78 tömeg% üvegpor (300, d70<63 pm, Mineralienwerke Kuppenheim)
16.53 tömeg% üvegfritt (kötőfritt K2244, d70<100 pm,
Schauer Co., Wien, Ausztria)
24,84 tömeg% grafit (szintetikus grafit T 75, d50 24 pm,
LONZA G&T, Sins, Svájc)
6,74 tömeg% vízben oldódó alkálifém-szilikátok keveréke (nátrium-szilikát: kálium-szilikát: lítium-szilikát = 12,3:67,5:20,7, Me2.n SiO2, n=2,7)
1,32 tömeg% vízben oldódó nátrium-polifoszfát (Alcopon, Benckiser-Knapsack, Ladenburg, NSZK),
0,92 tömeg% vízben oldhatatlan nátrium-polifoszfát (Dentphos M, Benckiser-Knapsack, Ladenburg, NSZK)
0,25 tömeg% bórax,
0,45 tömeg% xantángumi, l,10tömeg% hidroxi-metil-cellulóz (Dow Chemical) 0,07 tömeg% biocid
Vizes diszperzió, szárazanyag-tartalma 40 tömeg% Viszkozitás: 2000-5000 MPa s
4. készítmény (850-1250 °C felületi hőmérsékletű munkadarabokra alkalmas)
49.53 tömeg% üvegfritt (kötőfritt K2244, d70<100 pm,
Schauer Co., Bécs, Ausztria)
HU 219 309 Β
24,76 tömeg% grafit (szintetikus grafit T 75, d50 24 pm, LONZA G&T, Sins, Svájc)
6,74 tömeg% vízben oldódó alkálifém-szilikátok keveréke (nátrium-szilikát: kálium-szilikát: lítium-szilikát= 12,3:67,5:20,7, Me2n SiO2, n=2,7)
2,64tömeg% vízben oldódó nátrium-polifoszfát (Alcopon, Benckiser-Knapsack, Ladenburg, NSZK),
0,66tömeg% bórax
3,30 tömeg% hidroxi-metil-cellulóz (Dow Chemical) 0,71 tömeg% nátrium-poliakrilát (Carbopol, Goodrich
Chemical)
0,14 tömeg% biocid
Vizes diszperzió, szárazanyag-tartalma 20 tömeg% Viszkozitás 2000-5000 MPa s
1. összehasonlító készítmény (CH-PS 660 023 1. példája szerint) tömeg% kristályos grafit tömeg% Maddrell-féle só tömeg% bórax tömeg% nátrium-szilikát (vízüveg
SiO2/Na2O=3,3) tömeg% polietilén tömeg% alkil-cellulóz
Vizes diszperzió, szilárdanyag-tartalma 30 tőmeg%
2. összehasonlító készítmény (CH-PS 670 106 2. példája szerint) tömeg% nátrium-tripolifoszfát (Na5P3O10) tömeg% grafit tömeg% Na2B2O4x8H2O porkeverék
Összehasonlítási teszt Kísérleti körülmények cm χ 6 cm x 3 cm méretű, 800-1050 °C felületi hőmérsékletű, 1,5 m/s sebességgel függőlegesen mozgatott acéltömbre 43 cm távolságban lévő fúvókéból 50xl05 Pa nyomással rápermetezzük az 1-4. készítményt, valamint a két összehasonlító készítményt. A 2. összehasonlító készítményt szárazon fújjuk. A kialakuló kenőanyagfilmet az alábbi skála szerint értékeljük:
nincs kenőanyagfilm törékeny kenőfilm kialakulása, rövid idejű (néhány másodperc) tapadás egyenletes, máz jellegű, jól tapadó, nagy mechanikai állóságú és nagy vízállóságú kenőfilm azonnali kialakulása
Eredmények
Készítmény | Teszteredmény |
1. | 3 (850 °C-tól) |
2. | 3 (1000 °C-tól) |
3. | 3 (1000 °C-tól) |
4. | 3 (850 °C-tól) |
1. összehasonlító | 1 |
2. összehasonlító | 2 |
Claims (12)
- SZABADALMI IGÉNYPONTOK1. Kenőanyag-készítmény munkadarabokon való alkalmazásra fémek melegalakításakor, amelynek összetétele az alábbi:ai) 0-80 tömeg% üvegpor és/vagy a2) 0-50 tömeg% üvegfritt (szinterezett üveg), azzal a megkötéssel, hogy és a2 közül legalább az egyik mennyisége zérustól különbözőb) 10-25 tömeg% természetes vagy szintetikus grafit,c) 5-20 tömeg% Me2O.n SiO2 képletű alkálifém-szilikát(ok), mely képletben Me jelentése lítum, kálium vagy nátrium, és n értéke 1-től 4-ig terjedő szám,d) 1-6 tömeg% vízben oldódó nátrium-polimetafoszfát,e) 0-3 tömeg% vízben oldhatatlan nátrium-polimetafoszfát,f) 0,5-3 tömeg% sűrítőszer,g) 0-1 tömeg% bórax.
- 2. Az 1. igénypont szerinti kenőanyag-készítmény, azzal jellemezve, hogy a benne lévő üvegpor átlagos szemcsemérete d5o<lOO pm, lágyulótartománya körülbelül 700-900 °C.
- 3. Az 1. vagy 2. igénypont szerinti kenőanyag-készítmény, azzal jellemezve, hogy a benne lévő üvegfritt átlagos szemcsemérete d50< 100 pm, lágyulótartománya körülbelül 500-700 °C.
- 4. Az 1-3. igénypontok bármelyike szerinti kenőanyag-készítmény, azzal jellemezve, hogy a benne lévő, vízben oldódó alkálifém-szilikát(ok) az Me2O.n SiO2 általános képletnek felel(nek) meg, ahol Me jelentése lítium, kálium vagy nátrium, és n értéke 1-től 4-ig terjedő szám.
- 5. Az 1-4. igénypontok bármelyike szerinti kenőanyag-készítmény, azzal jellemezve, hogy vízben oldódó nátrium-polimetafoszfátként (NaPO3)n képletű Graham-féle sót tartalmaz, ahol n<450.
- 6. Az 1-5. igénypontok bármelyike szerinti kenőanyag-készítmény, azzal jellemezve, hogy vízben oldhatatlan nátrium-polimetafoszfátként (NaPO3)n képletű Maddrell-féle sót tartalmaz, ahol n értéke 40 és 70 közötti.
- 7. Az 1-6. igénypontok bármelyike szerinti kenőanyag-készítmény, azzal jellemezve, hogy sűrítőszerként poliszacharidot, poliszacharidszármazékot vagy poliakrilát nátriumsóját tartalmazza.
- 8. Az 1-7. igénypontok bármelyike szerinti kenőanyag-készítmény, azzal jellemezve, hogy vizes diszperzió alakjában van jelen.
- 9. Az 1-8. igénypontok bármelyike szerinti kenőanyag-készítmény, azzal jellemezve, hogy 20-50 tömeg% szilárd anyagot tartalmazó vizes diszperzió alakjában van jelen.
- 10. Az 1-9. igénypontok bármelyike szerinti kenőanyag-készítmény 800 °C feletti felületi hőmérsékletű munkadarabokon való alkalmazásra, azzal jellemezve, hogy összetétele az alábbi:a) 0-20 tömeg% üvegpor és/vagy 30-50 tömeg% üvegfritt,b) 20-25 tömeg% természetes vagy szintetikus grafit,HU 219 309 Βc) 7-20 tömeg% Me2O.n SiO2 képletű alkálifém-szilikát(ok), mely képletben Me jelentése lítium, kálium vagy nátrium, és n értéke 1-től 4-ig terjedő szám,d) 2-6 tömeg% vízben oldódó nátrium-polimetafoszfát,e) 0-1 tömeg% vízben oldhatatlan nátrium-polimetafoszfát,f) 3-4 tömeg% sűrítőszer,g) 0,2-0,7 tömeg% bórax.
- 11. Az 1-9. igénypontok bármelyike szerinti kenőanyag-készítmény 1000 °C feletti felületi hőmérsékletű munkadarabokon való alkalmazásra, azzal jellemezve, hogy összetétele az alábbi:a) 45-70 tömeg% üvegpor és/vagy 0-20 tömeg% üvegfritt,b) 20-25 tömeg% természetes vagy szintetikus grafit,c) 7-20 tömeg% Me2O.n SiO2 képletű alkálifém-szilikát(ok), mely képletben Me jelentése lítium, kálium vagy nátrium, és n értéke 1-től 4-ig terjedő szám,d) 1-2 tömeg% vízben oldódó nátrium-polimetafoszfát,e) 0-1 tömeg% vízben oldhatatlan nátrium-polimetafoszfát,f) 1,5-2 tömeg% sűrítőszer,g) 0-0,25 tömeg% bórax.
- 12. Az 1 -11. igénypontok bármelyike szerinti kenőanyag-készítmény alkalmazása körülbelül 800-1300 °C felületi hőmérsékletű munkadarabok közvetlen kenésére fémek melegalakítása során.