ES2644357T3 - Lámina de acero de fase dual y procedimiento para la producción de la misma - Google Patents

Lámina de acero de fase dual y procedimiento para la producción de la misma Download PDF

Info

Publication number
ES2644357T3
ES2644357T3 ES13842321.5T ES13842321T ES2644357T3 ES 2644357 T3 ES2644357 T3 ES 2644357T3 ES 13842321 T ES13842321 T ES 13842321T ES 2644357 T3 ES2644357 T3 ES 2644357T3
Authority
ES
Spain
Prior art keywords
less
steel sheet
temperature
steel
cooling
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
ES13842321.5T
Other languages
English (en)
Spanish (es)
Inventor
Tatsuo Yokoi
Hiroshi Shuto
Eisaku Sakurada
Hiroyuki Okada
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nippon Steel Corp
Original Assignee
Nippon Steel and Sumitomo Metal Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel and Sumitomo Metal Corp filed Critical Nippon Steel and Sumitomo Metal Corp
Application granted granted Critical
Publication of ES2644357T3 publication Critical patent/ES2644357T3/es
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/013—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of a metal other than iron or aluminium
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/001—Heat treatment of ferrous alloys containing Ni
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/002—Heat treatment of ferrous alloys containing Cr
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/005—Heat treatment of ferrous alloys containing Mn
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/007—Heat treatment of ferrous alloys containing Co
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/008—Heat treatment of ferrous alloys containing Si
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0226—Hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0263—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment following hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/005—Ferrous alloys, e.g. steel alloys containing rare earths, i.e. Sc, Y, Lanthanides
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/008—Ferrous alloys, e.g. steel alloys containing tin
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/08—Ferrous alloys, e.g. steel alloys containing nickel
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/10—Ferrous alloys, e.g. steel alloys containing cobalt
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/16—Ferrous alloys, e.g. steel alloys containing copper
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/28—Ferrous alloys, e.g. steel alloys containing chromium with titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/32—Ferrous alloys, e.g. steel alloys containing chromium with boron
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/58—Ferrous alloys, e.g. steel alloys containing chromium with nickel with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0224—Two or more thermal pretreatments
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/004—Dispersions; Precipitations
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12785—Group IIB metal-base component
    • Y10T428/12792—Zn-base component
    • Y10T428/12799—Next to Fe-base component [e.g., galvanized]

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Coating With Molten Metal (AREA)
  • Heat Treatment Of Steel (AREA)
  • Soft Magnetic Materials (AREA)
ES13842321.5T 2012-09-26 2013-09-26 Lámina de acero de fase dual y procedimiento para la producción de la misma Active ES2644357T3 (es)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2012212783 2012-09-26
JP2012212783 2012-09-26
PCT/JP2013/076149 WO2014051005A1 (ja) 2012-09-26 2013-09-26 複合組織鋼板およびその製造方法

Publications (1)

Publication Number Publication Date
ES2644357T3 true ES2644357T3 (es) 2017-11-28

Family

ID=50388400

Family Applications (1)

Application Number Title Priority Date Filing Date
ES13842321.5T Active ES2644357T3 (es) 2012-09-26 2013-09-26 Lámina de acero de fase dual y procedimiento para la producción de la misma

Country Status (14)

Country Link
US (1) US9863026B2 (enExample)
EP (1) EP2896715B9 (enExample)
JP (1) JP5610103B2 (enExample)
KR (1) KR101658744B1 (enExample)
CN (1) CN104685087B (enExample)
BR (1) BR112015006077B1 (enExample)
CA (1) CA2882333C (enExample)
ES (1) ES2644357T3 (enExample)
IN (1) IN2015DN01476A (enExample)
MX (1) MX353772B (enExample)
PL (1) PL2896715T3 (enExample)
RU (1) RU2605014C2 (enExample)
TW (1) TWI480389B (enExample)
WO (1) WO2014051005A1 (enExample)

Families Citing this family (52)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE102013004905A1 (de) * 2012-03-23 2013-09-26 Salzgitter Flachstahl Gmbh Zunderarmer Vergütungsstahl und Verfahren zur Herstellung eines zunderarmen Bauteils aus diesem Stahl
MX2016013898A (es) * 2014-04-23 2017-02-02 Nippon Steel & Sumitomo Metal Corp Placa de acero laminada en caliente para una pieza en blanco laminada a la medida, pieza en blanco laminada a la medida y metodos para producirlas.
JP6303782B2 (ja) * 2014-05-08 2018-04-04 新日鐵住金株式会社 熱延鋼板およびその製造方法
ES2734741T3 (es) * 2014-07-14 2019-12-11 Nippon Steel Corp Chapa de acero laminada en caliente
JP6304381B2 (ja) 2014-07-14 2018-04-04 新日鐵住金株式会社 熱延鋼板
MX390392B (es) 2014-09-17 2025-03-20 Nippon Steel Corp Hoja de acero laminada en caliente.
WO2016132549A1 (ja) * 2015-02-20 2016-08-25 新日鐵住金株式会社 熱延鋼板
EP3260566B1 (en) * 2015-02-20 2019-11-27 Nippon Steel Corporation Hot-rolled steel sheet
ES2743814T3 (es) 2015-02-20 2020-02-20 Nippon Steel Corp Chapa de acero laminada en caliente
MX2017010532A (es) 2015-02-25 2017-12-14 Nippon Steel & Sumitomo Metal Corp Lamina o placa de acero laminada en caliente.
WO2016135898A1 (ja) 2015-02-25 2016-09-01 新日鐵住金株式会社 熱延鋼板
CN104878301B (zh) * 2015-05-15 2017-05-03 河冶科技股份有限公司 喷射成形高速钢
MX2018001082A (es) 2015-07-27 2018-06-06 Jfe Steel Corp Lamina de acero laminada en caliente de alta resistencia y metodo para la fabricacion de la misma.
EP3330394B1 (en) * 2015-07-31 2020-08-26 Nippon Steel Corporation High_strength_ hot_rolled steel sheet
CN107849652B (zh) * 2015-07-31 2020-04-03 日本制铁株式会社 加工诱发相变型复合组织钢板及其制造方法
JP6536328B2 (ja) * 2015-10-02 2019-07-03 日本製鉄株式会社 疲労特性と成形性に優れた高強度鋼板およびその製造方法
CN108350536B (zh) * 2015-11-19 2020-06-16 日本制铁株式会社 高强度热轧钢板及其制造方法
JP6676973B2 (ja) * 2016-01-13 2020-04-08 日本製鉄株式会社 熱延鋼板およびその製造方法
TWI629369B (zh) 2016-08-05 2018-07-11 Nippon Steel & Sumitomo Metal Corporation 鋼板及鍍敷鋼板
EP3495529B1 (en) 2016-08-05 2021-03-03 Nippon Steel Corporation Steel sheet and plated steel sheet
WO2018026016A1 (ja) 2016-08-05 2018-02-08 新日鐵住金株式会社 鋼板及びめっき鋼板
TWI602932B (zh) * 2016-08-16 2017-10-21 新日鐵住金股份有限公司 熱壓製成形構件
EP3502291B1 (en) 2016-08-16 2023-10-18 Nippon Steel Corporation Hot press-formed part
TWI607096B (zh) * 2016-08-18 2017-12-01 新日鐵住金股份有限公司 熱軋鋼板
BR112019002593A2 (pt) * 2016-08-18 2019-05-21 Nippon Steel & Sumitomo Metal Corporation chapa de aço laminado a quente
CA3049859A1 (en) * 2017-01-24 2018-08-02 Nippon Steel Corporation Steel material and method for producing steel material
RU2635122C1 (ru) * 2017-01-25 2017-11-09 Акционерное общество "Выксунский металлургический завод" (АО "ВМЗ") Способ производства толстолистового проката классов прочности K80, X100, L690 для изготовления электросварных труб магистральных трубопроводов
US10633726B2 (en) * 2017-08-16 2020-04-28 The United States Of America As Represented By The Secretary Of The Army Methods, compositions and structures for advanced design low alloy nitrogen steels
CN107675090B (zh) * 2017-09-15 2019-11-15 山东钢铁股份有限公司 一种布氏硬度650hbw级别高耐磨性钢板及其制备方法
DE102017131247A1 (de) 2017-12-22 2019-06-27 Voestalpine Stahl Gmbh Verfahren zum Erzeugen metallischer Bauteile mit angepassten Bauteileigenschaften
DE102017131253A1 (de) 2017-12-22 2019-06-27 Voestalpine Stahl Gmbh Verfahren zum Erzeugen metallischer Bauteile mit angepassten Bauteileigenschaften
KR102020415B1 (ko) 2017-12-24 2019-09-10 주식회사 포스코 저항복비 특성이 우수한 고강도 강재 및 그 제조방법
KR102119975B1 (ko) * 2018-11-29 2020-06-08 주식회사 포스코 저온인성과 연신율이 우수하며, 항복비가 작은 후물 고강도 라인파이프용 강재 및 그 제조방법
KR102662624B1 (ko) * 2019-01-09 2024-05-07 닛폰세이테츠 가부시키가이샤 열간 압연 강판 및 용접 이음매, 그리고 그들의 제조 방법
MX2022008076A (es) 2020-02-06 2022-08-02 Nippon Steel Corp Lamina de acero laminada en caliente y metodo para fabricar la misma.
US20230140358A1 (en) * 2020-03-19 2023-05-04 Nippon Steel Corporation Steel sheet
JP7440804B2 (ja) 2020-10-28 2024-02-29 日本製鉄株式会社 熱間圧延鋼板
CN115121616B (zh) * 2021-03-24 2025-09-09 宝山钢铁股份有限公司 一种基于产品合同信息辅助轧制控制系统的方法
US20240254584A1 (en) * 2021-05-17 2024-08-01 Jfe Steel Corporation High-strength hot-rolled steel sheet and method for manufacturing high-strength hot-rolled steel sheet
US20240247332A1 (en) * 2021-05-17 2024-07-25 Jfe Steel Corporation High-strength hot-rolled steel sheet and method for manufacturing high-strength hot-rolled steel sheet
JP7688287B2 (ja) * 2021-06-22 2025-06-04 日本製鉄株式会社 熱延鋼板およびその製造方法
CN114855091A (zh) * 2022-05-30 2022-08-05 江苏沃盾耐磨新材料有限公司 一种高韧性耐磨复合板及其制备方法
CN115466903A (zh) * 2022-07-13 2022-12-13 海峡(晋江)伞业科技创新中心有限公司 一种高强度特种钢及其生产工艺
KR20250067186A (ko) * 2022-11-02 2025-05-14 닛폰세이테츠 가부시키가이샤 열간 압연 강판
EP4613893A4 (en) * 2022-11-02 2026-01-07 Nippon Steel Corp HOT-ROLL-ON STEEL SHEET
CN115584428B (zh) * 2022-11-07 2023-08-18 鞍钢股份有限公司 一种短流程低成本冷轧dh590钢及其生产方法
KR20250087710A (ko) * 2022-11-22 2025-06-16 제이에프이 스틸 가부시키가이샤 고강도 열연 강판 및 그의 제조 방법
CN116043115B (zh) * 2023-01-31 2024-05-14 马鞍山钢铁股份有限公司 一种高铁制动盘用抗冷热疲劳锻钢及其热处理方法和生产方法
CN116837285B (zh) * 2023-06-09 2026-01-30 河北河钢材料技术研究院有限公司 一种490MPa级双相钢外板及其生产方法
JPWO2025164310A1 (enExample) * 2024-01-29 2025-08-07
JPWO2025164309A1 (enExample) * 2024-01-29 2025-08-07
WO2025234230A1 (ja) * 2024-05-08 2025-11-13 日本製鉄株式会社 鋼板、それを含む部品及び鋼板の製造方法

Family Cites Families (24)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5545270A (en) * 1994-12-06 1996-08-13 Exxon Research And Engineering Company Method of producing high strength dual phase steel plate with superior toughness and weldability
FR2735147B1 (fr) 1995-06-08 1997-07-11 Lorraine Laminage Tole d'acier laminee a chaud a haute resistance et haute emboutissabilite renfermant du titane, et ses procedes de fabrication.
DZ2531A1 (fr) * 1997-12-19 2003-02-08 Exxon Production Research Co Procédé de préparation d'une tôle d'acier double phase cette tôle et procédé pour renforcer la résistance à la propagation des fissures.
US6589369B2 (en) 2000-04-21 2003-07-08 Nippon Steel Corporation High fatigue strength steel sheet excellent in burring workability and method for producing the same
JP2001303187A (ja) * 2000-04-21 2001-10-31 Nippon Steel Corp バーリング加工性に優れる複合組織鋼板およびその製造方法
JP3637885B2 (ja) 2001-09-18 2005-04-13 Ｊｆｅスチール株式会社 加工性に優れた超高張力鋼板ならびにその製造方法および加工方法
JP3888128B2 (ja) 2000-10-31 2007-02-28 Ｊｆｅスチール株式会社 材質均一性に優れた高成形性高張力熱延鋼板ならびにその製造方法および加工方法
JP3882577B2 (ja) 2000-10-31 2007-02-21 Ｊｆｅスチール株式会社 伸びおよび伸びフランジ性に優れた高張力熱延鋼板ならびにその製造方法および加工方法
JP3704306B2 (ja) 2001-12-28 2005-10-12 新日本製鐵株式会社 溶接性、穴拡げ性および耐食性に優れた溶融亜鉛めっき高強度鋼板およびその製造方法
JP3775340B2 (ja) 2002-04-30 2006-05-17 Ｊｆｅスチール株式会社 加工性に優れた高張力熱延鋼板および加工方法
JP3775339B2 (ja) 2002-04-30 2006-05-17 Ｊｆｅスチール株式会社 加工性に優れた高張力熱延鋼板ならびにその製造方法および加工方法
JP3775341B2 (ja) 2002-04-30 2006-05-17 Ｊｆｅスチール株式会社 加工性に優れた高張力熱延鋼板ならびにその製造方法および加工方法
JP4304421B2 (ja) 2002-10-23 2009-07-29 住友金属工業株式会社 熱延鋼板
JP4180909B2 (ja) 2002-12-26 2008-11-12 新日本製鐵株式会社 穴拡げ性、延性及び化成処理性に優れた高強度熱延鋼板及びその製造方法
JP5076394B2 (ja) 2005-08-05 2012-11-21 Ｊｆｅスチール株式会社 高張力鋼板ならびにその製造方法
JP5025931B2 (ja) 2005-09-16 2012-09-12 ダイコク電機株式会社 スロットマシン
RU2418094C2 (ru) * 2006-01-30 2011-05-10 Ниппон Стил Корпорейшн Высокопрочный горячеоцинкованный погружением стальной лист и высокопрочный отожженный после цинкования стальной лист с превосходными формуемостью и способностью к нанесению гальванопокрытия и способы изготовления и устройства для изготовления таких листов
JP4964494B2 (ja) 2006-05-09 2012-06-27 新日本製鐵株式会社 穴拡げ性と成形性に優れた高強度鋼板及びその製造方法
JP5195399B2 (ja) 2008-12-24 2013-05-08 新日鐵住金株式会社 低サイクル疲労特性と塗装後耐食性に優れた高強度熱延鋼板およびその製造方法
JP4623233B2 (ja) * 2009-02-02 2011-02-02 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板およびその製造方法
JP5338525B2 (ja) * 2009-07-02 2013-11-13 新日鐵住金株式会社 バーリング性に優れた高降伏比型熱延鋼板及びその製造方法
JP2011184788A (ja) * 2010-03-11 2011-09-22 Nippon Steel Corp 伸びと穴拡げ性のバランスに優れた鋼板及びその製造方法
JP5510023B2 (ja) * 2010-04-20 2014-06-04 新日鐵住金株式会社 疲労特性と局部延性に優れた高強度薄鋼板およびその製造方法
JP5527051B2 (ja) 2010-06-30 2014-06-18 新日鐵住金株式会社 バーリング性に優れた焼付け硬化型熱延鋼板及びその製造方法

Also Published As

Publication number Publication date
PL2896715T3 (pl) 2017-12-29
MX353772B (es) 2018-01-29
US9863026B2 (en) 2018-01-09
EP2896715B1 (en) 2017-08-02
MX2015002803A (es) 2015-05-15
EP2896715A1 (en) 2015-07-22
RU2015112969A (ru) 2016-11-20
EP2896715B9 (en) 2022-09-21
JP5610103B2 (ja) 2014-10-22
TWI480389B (zh) 2015-04-11
BR112015006077A2 (pt) 2017-07-04
RU2605014C2 (ru) 2016-12-20
IN2015DN01476A (enExample) 2015-07-03
TW201425599A (zh) 2014-07-01
BR112015006077B1 (pt) 2020-01-28
CA2882333C (en) 2018-03-20
KR101658744B1 (ko) 2016-09-21
CN104685087B (zh) 2017-03-15
KR20150038727A (ko) 2015-04-08
JPWO2014051005A1 (ja) 2016-08-22
CA2882333A1 (en) 2014-04-03
US20150203949A1 (en) 2015-07-23
EP2896715A4 (en) 2016-06-15
CN104685087A (zh) 2015-06-03
WO2014051005A1 (ja) 2014-04-03

Similar Documents

Publication Publication Date Title
ES2644357T3 (es) Lámina de acero de fase dual y procedimiento para la producción de la misma
US10590506B2 (en) Hot-rolled steel sheet for tailored rolled blank and tailored rolled blank
JP6455599B2 (ja) 加工誘起変態型複合組織鋼板およびその製造方法
CN105814227B (zh) 高强度热浸镀锌钢板及其制造方法
ES2712177T3 (es) Un método de producción de una lámina de acero de calibre fino de alta resistencia excelente en elongación y capacidad de expansión de agujeros
WO2021019947A1 (ja) 高強度鋼板およびその製造方法
ES2689230T3 (es) Chapa de acero laminado en caliente y método de producción de la misma
JP5095958B2 (ja) 高強度鋼板およびその製造方法
WO2020184154A1 (ja) 高強度鋼板およびその製造方法
US10960487B2 (en) Weldability improvements in advanced high strength steel
EP2787098B1 (en) Steel material with excellent crashworthiness and manufacturing process therefor
TWI575084B (zh) 應變誘發相變態型複合組織鋼板及其製造方法
TW202022137A (zh) 成形性、韌性及熔接性優異的高強度鋼板、以及其製造方法
JP2002069584A (ja) 成形性の優れた高強度鋼管およびその製造方法