ES2033473T3 - Acido silicico de precipitacion finamente dividido con elevada estructura, procedimiento para su preparacion y empleo. - Google Patents

Acido silicico de precipitacion finamente dividido con elevada estructura, procedimiento para su preparacion y empleo.

Info

Publication number
ES2033473T3
ES2033473T3 ES198989103046T ES89103046T ES2033473T3 ES 2033473 T3 ES2033473 T3 ES 2033473T3 ES 198989103046 T ES198989103046 T ES 198989103046T ES 89103046 T ES89103046 T ES 89103046T ES 2033473 T3 ES2033473 T3 ES 2033473T3
Authority
ES
Spain
Prior art keywords
silica
suspension
water
mixture
din
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
ES198989103046T
Other languages
English (en)
Other versions
ES2033473T5 (es
Inventor
Dieter Dr. Kerner
Adolf Wagner
Felix Dr. Schmidt
Dietrich Dr. Bauer
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Evonik Operations GmbH
Original Assignee
Degussa GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=6353905&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=ES2033473(T3) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by Degussa GmbH filed Critical Degussa GmbH
Publication of ES2033473T3 publication Critical patent/ES2033473T3/es
Application granted granted Critical
Publication of ES2033473T5 publication Critical patent/ES2033473T5/es
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

EL ACIDO SILICICO DE PRECIPITACION DE PARTICULAS FINAS CON: SUPERFICIE BET (DIN60132) ENTRE 150 Y 350 M (AL CUADRADO) /G; DENSIDAD DE APISONADO (DIN 53194) ENTRE 60 Y 120 G/L; NUMERO DBP ENTRE 3.0 Y 4.0 ML/G; DISTRIBUCION DE GROSOR DE MINIMO 70% DE 1 A 6 (MU)M PARTICULAS ESTE ACIDO SILICICO SE PUEDE PRODUCIR CALENTANDO UNA MEZCLA DE AGUA Y SILICATO SODICO EN AGITACION A UNA TEMPERATURA DE 70 A 80 (GRADOS) C, A/ADIENDO A ESTE PRINCIPIO ACIDO SULFURICO CONCENTRADO HASTA QUE ESTE NEUTRALIZADA LA MITAD DEL ALCALI PRESENTE. A CONTINUACION SE TRATA LA MEZCLA DE REACCION POR MEDIO DE UNA CIZALLA, ELEVANDO EN SU CASO LA TEMPERATURA A 86 (MAS MENOS) 5 (GRADOS) C. TRAS UN TIEMPO DE 30 A 120 MINUTOS, SE AÑADE ACIDO SULFURICO CONCENTRADO A MAYOR VELOCIDAD, HASTA QUE EL PH DE LA SUSPENSION DE ACIDO SILICICO SEA DE 3,0 A 3,5. EN SU CASO SE DILUYE LA SUSPENSION DE ACIDO SILICICO CON AGUA, A SU VEZ, SI ES NECESARIO SE SEPARA LA PARTE GRUESA POR MEDIO DE UNA BOMBA CENTRIFUGA Y DE UN HIDROCICLON; A CONTINUACION SE FILTRA EL ACIDO SILICICO CON FILTROS YA CONOCIDOS Y SE LAVA LA TORTA DE ACIDO SILICICO PARA RETIRAR EL SULFATO. SE REDISPERSA ENTONCES LA TORTA DE ACIDO SILICICO, AÑADIENDO AGUA, POR MEDIO DE UN DISPOSITIVO DE REMOVIDO PARA FORMAR UNA SUSPENSION CON UN CONTENIDO SOLIDO DE 80 (MAS MENOS) 10 G/L. A ESTA DISPERSION SE AÑADE EN SU CASO ALQUILDIMETILBENZIL- AMONIOCLORURO. LA SUSPENSION SE SECA POR PULVERIZADO Y, EN SU CASO, SE MUELE EL PRODUCTO SECO. EL ACIDO SILICICO DE PRECIPITACION SE PUEDE USAR TANTO REVESTIDO COMO SIN REVESTIR COMO MATEADOR EN LACAS.
ES89103046T 1988-05-07 1989-02-22 Acido silicico de precipitacion finamente dividido con elevada estructura, procedimiento para su preparacion y empleo. Expired - Lifetime ES2033473T5 (es)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
DE3815670A DE3815670A1 (de) 1988-05-07 1988-05-07 Feinteilige faellungskieselsaeure mit hoher struktur, verfahren zu seiner herstellung und verwendung

Publications (2)

Publication Number Publication Date
ES2033473T3 true ES2033473T3 (es) 1993-03-16
ES2033473T5 ES2033473T5 (es) 1997-03-16

Family

ID=6353905

Family Applications (1)

Application Number Title Priority Date Filing Date
ES89103046T Expired - Lifetime ES2033473T5 (es) 1988-05-07 1989-02-22 Acido silicico de precipitacion finamente dividido con elevada estructura, procedimiento para su preparacion y empleo.

Country Status (9)

Country Link
US (2) US5034207A (es)
EP (1) EP0341383B2 (es)
JP (1) JPH01320215A (es)
AT (1) ATE77353T1 (es)
CA (1) CA1340129C (es)
DE (2) DE3815670A1 (es)
DK (1) DK160289A (es)
ES (1) ES2033473T5 (es)
ZA (1) ZA892021B (es)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN110562988A (zh) * 2019-09-12 2019-12-13 青岛美高集团有限公司 一种隔热保温材料及其生产方法

Families Citing this family (73)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6143281A (en) * 1987-03-31 2000-11-07 Smithkline Beecham P.L.C. Dentifrice compositions
DE3919940A1 (de) * 1989-06-19 1990-12-20 Merck Patent Gmbh Dispersionen kugelfoermiger anorganischer partikel
US5409687A (en) * 1990-02-22 1995-04-25 Vereinigte Aluminum-Werke Aktiengesellschaft Gallosilicate catalysts and method of making same
DE4133319A1 (de) * 1991-10-08 1993-04-15 Sued Chemie Ag Verwendung von amorpher faellungskieselsaeure als fuellstoff in der waermeempfindlichen schicht eines waermeempfindlichen aufzeichnungsmaterials
CA2082035A1 (en) * 1991-11-07 1993-05-08 Derek Aldcroft Silica products
EP0541359B1 (en) * 1991-11-07 1995-07-19 Crosfield Limited Silica products
EP0588497A1 (en) * 1992-08-19 1994-03-23 JOSEPH CROSFIELD & SONS LTD. Process for preparing precipitated silicas
WO1994011302A1 (en) * 1992-11-12 1994-05-26 Crosfield Limited Silicas
DE4330342A1 (de) * 1993-09-08 1995-03-09 Basf Ag Stabile wäßrige Polyolefinwachsdispersionen
EP0670813B1 (fr) * 1993-09-29 2003-03-12 Rhodia Chimie Silice precipitee
US6001322A (en) 1993-09-29 1999-12-14 Rhone-Poulenc Chimie Precipitated silicas
FR2710630B1 (fr) * 1993-09-29 1995-12-29 Rhone Poulenc Chimie Nouvelles silices précipitées, leur procédé de préparation et leur utilisation au renforcement des élastomères.
DE4427137B4 (de) * 1993-10-07 2007-08-23 Degussa Gmbh Fällungskieselsäure
GB9409388D0 (en) * 1994-05-11 1994-06-29 Unilever Plc Silica products
FR2722185B1 (fr) * 1994-07-07 1996-09-27 Rhone Poulenc Chimie Suspension concentree de silice de precipitation, procedes pour sa preparation et utilisations de cette suspension
JP3329946B2 (ja) * 1994-07-15 2002-09-30 本田技研工業株式会社 艶消し塗膜
JP2908253B2 (ja) † 1994-09-26 1999-06-21 日本化学工業株式会社 水和珪酸とその製造方法
US5571494A (en) * 1995-01-20 1996-11-05 J. M. Huber Corporation Temperature-activated polysilicic acids
DE19516253A1 (de) * 1995-04-26 1996-10-31 Grace Gmbh Mattierungsmittel auf Basis von aggregiertem Siliciumdioxid mit verbesserter Effizienz
US5911963A (en) * 1995-05-12 1999-06-15 Ppg Industries Ohio, Inc. Amorphous precipitated silica having a low proportion of small pores
DE19526476A1 (de) * 1995-07-20 1997-01-23 Degussa Fällungskieselsäure
DE19527278A1 (de) * 1995-07-26 1997-01-30 Degussa Fällungskieselsäure
US5891421A (en) * 1996-03-22 1999-04-06 J.M. Huber Corporation Precipitated silicas having improved dentifrice performance characteristics and methods of preparation
US6395247B1 (en) 1997-12-12 2002-05-28 Degussa Ag Precipitated silica
DE19755287A1 (de) * 1997-12-12 1999-07-08 Degussa Fällungskieselsäure
DE19828364A1 (de) * 1998-06-25 1999-12-30 Degussa Hydrophobe Fällungskieselsäure
US6770128B1 (en) 1999-04-13 2004-08-03 Grace Gmbh & Co. Kg Matting agent radiation for curing coatings
US6573032B1 (en) 1999-04-22 2003-06-03 J. M. Huber Corporation Very high structure, highly absorptive hybrid silica and method for making same
DE10138491A1 (de) * 2001-08-04 2003-02-13 Degussa Verfahren zur Herstellung einer hydrophoben Fällungskieselsäure mit hohem Weißgrad und extrem niedriger Feuchtigkeitsaufnahme
GB0127220D0 (en) * 2001-11-13 2002-01-02 Ineos Silicas Ltd Silica matting agents
GB0130907D0 (en) 2001-12-22 2002-02-13 Ineos Silicas Ltd Amorphous silica
DE10209698A1 (de) * 2002-03-06 2003-09-18 Sachtleben Chemie Gmbh Verfahren zur Herstellung von gecoateten, feinteiligen, anorganischer Festkörpern und deren Verwendung
DE10241273A1 (de) * 2002-09-06 2004-03-18 Degussa Ag Effiziente Mattierungsmittel basierend auf Fällungskieselsäuren
EP1431338B1 (de) * 2002-12-17 2010-02-24 Evonik Degussa GmbH Strukturgecoatete Kieselsäure
AU2003303062A1 (en) * 2002-12-18 2004-07-09 Degussa Ag Texture-coated silica
CN100436548C (zh) * 2002-12-18 2008-11-26 德古萨公司 结构改性二氧化硅
DE60324090D1 (de) * 2003-01-29 2008-11-27 Evonik Degussa Gmbh Strukturgecoatete Kieselsäure
TWI333545B (en) * 2003-04-02 2010-11-21 Cholestech Corp Adhered membranes retaining porosity and biological activity
DE102004012090A1 (de) * 2003-05-14 2004-12-09 Degussa Ag Oberflächenmodifizierte Fällungskieselsäuren
ES2290625T3 (es) * 2003-05-14 2008-02-16 Evonik Degussa Gmbh Silices de precipitacion modificadas en la superficie.
JP2005053744A (ja) * 2003-08-05 2005-03-03 Dsl Japan Co Ltd 高吸油性非晶質シリカ粒子
DE102004029074A1 (de) * 2004-06-16 2005-12-29 Degussa Ag Lackformulierung zur Verbesserung der Oberflächeneigenschaften
US7037476B1 (en) 2004-12-27 2006-05-02 Council Of Scientific And Industrial Research Process for preparing amorphous silica from kimberlite tailing
CA2592518C (en) * 2004-12-30 2013-04-16 Council Of Scientific And Industrial Research Process for preparing amorphous silica from kimberlite tailing
US20060228632A1 (en) * 2005-04-11 2006-10-12 Boyer James L Treated filler and process for producing
WO2006110424A1 (en) * 2005-04-11 2006-10-19 Ppg Industries Ohio, Inc. Treated filler and process for producing
US20060229386A1 (en) * 2005-04-11 2006-10-12 Raman Narayan K Treated filler and process for producing
US20060225615A1 (en) * 2005-04-11 2006-10-12 Raman Narayan K Treated filler and process and producing
EP1926769A1 (en) * 2005-08-25 2008-06-04 E.I. Dupont De Nemours And Company Modified nanoparticles
WO2007054955A1 (en) * 2005-11-10 2007-05-18 Council Of Scientific & Industrial Research A process for the preparation of sodium silicate from kimberlite tailings
CN100572456C (zh) * 2006-04-24 2009-12-23 广州慧谷化学有限公司 纳米内核夹心式结构二氧化硅消光剂及其制备方法
CN101230212B (zh) * 2007-01-24 2012-08-22 沈阳化工股份有限公司 一种白碳黑表面复合改性制备方法
KR101559897B1 (ko) * 2007-05-03 2015-10-13 카운실 오브 사이언티픽 엔드 인더스트리얼 리서치 미세하게 분할된 침강 실리카의 제조방법
AU2008328191B2 (en) 2007-11-19 2015-01-15 Grace Gmbh Anti-corrosive particles
US7985292B2 (en) * 2007-11-26 2011-07-26 Evonik Degussa Corporation Precipitated silica for thickening and creating thixotropic behavior in liquid systems
DE102008000290A1 (de) 2008-02-13 2009-08-20 Evonik Degussa Gmbh Lagerstabile Produktsyteme für Prämixformulierungen
FR2928363B1 (fr) * 2008-03-10 2012-08-31 Rhodia Operations Nouveau procede de preparation de silices precipitees, silices precipitees a morphologie, granulometrie et porosite particulieres et leurs utilisations, notamment pour le renforcement de polymeres
AR074508A1 (es) * 2008-12-08 2011-01-19 Grace Gmbh & Co Kg Particulas anticorrosivas
DE102009028255A1 (de) 2009-08-05 2011-02-10 Evonik Degussa Gmbh Mikrostrukturierte multifunktionale anorganische Coating-Additive zur Vermeidung von Fouling (Biofilmbewuchs) bei aquatischen Anwendungen
DE102009036767A1 (de) 2009-08-08 2011-02-10 Evonik Degussa Gmbh Kompositpartikel für den Einsatz in der Mundhygiene
DE102009045116A1 (de) * 2009-09-29 2011-03-31 Evonik Degussa Gmbh Niederdruckvermahlungsverfahren
US20120329937A1 (en) * 2009-12-23 2012-12-27 Bluestar Silicones France Precipitated silica
CN101838479B (zh) * 2010-03-19 2013-11-20 福建师范大学 一种可分散超细二氧化硅的制备方法
ES2745113T3 (es) 2010-04-09 2020-02-27 Pacira Pharmaceuticals Inc Método para formular liposomas multivesiculares
FR2962996B1 (fr) * 2010-07-23 2012-07-27 Rhodia Operations Nouveau procede de preparation de silices precipitees
WO2013004008A1 (en) 2011-07-05 2013-01-10 Basf Se Filled elastomer comprising polyurethane
DE102012210294A1 (de) 2012-06-19 2013-12-19 Evonik Industries Ag Bewuchsmindernde-Additive, Verfahren zu deren Herstellung und deren Verwendung in Beschichtungen
WO2014030192A1 (ja) * 2012-08-24 2014-02-27 パナソニック株式会社 シリカ多孔体および光マイクロフォン
CN105350106A (zh) * 2015-12-01 2016-02-24 北京三联虹普新合纤技术服务股份有限公司 一种制备消光剂悬浮液的方法
BR112018068332B1 (pt) 2016-03-21 2022-10-04 Basf Se Poliuretano reticulado, compósito, mistura, processo para produzir um compósito e usos de poliuretano reticulado
CN109319794A (zh) * 2018-11-20 2019-02-12 福建省三明同晟化工有限公司 一种连续法制备沉淀二氧化硅的方法
CN110156033B (zh) * 2019-07-01 2022-07-29 福建正盛无机材料股份有限公司 一种高结构高比表高分散白炭黑的制备方法
CN110591416A (zh) * 2019-08-23 2019-12-20 广州凌玮科技股份有限公司 一种无定形二氧化硅防锈颜料的制备方法

Family Cites Families (16)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE1160415B (de) * 1960-10-04 1964-01-02 Chem Fab Hoesch K G Verfahren zur Herstellung hochaktiver Kieselsaeure
DE1567459B1 (de) * 1966-06-18 1970-10-29 Degussa Verfahren zur Herstellung feinteiliger,organisch modifizierter Kieselsaeuren
US4001379A (en) * 1968-04-27 1977-01-04 Deutsche Gold- Und Silber-Scheideanstalt Vormals Roessler Process of making superfine amorphous high structural silicic acid
DE1767922B2 (de) * 1968-07-02 1980-12-18 Degussa Ag, 6000 Frankfurt Mattierungsmittel für Lackfarben
US3709980A (en) * 1971-05-17 1973-01-09 Ppg Industries Inc Precipitation of siliceous pigment
DE2414478C3 (de) * 1974-03-26 1978-07-13 Deutsche Gold- Und Silber-Scheideanstalt Vormals Roessler, 6000 Frankfurt Aerogelartige strukturierte Kieselsäure und Verfahren zu ihrer Herstellung
AU505536B2 (en) * 1975-03-12 1979-11-22 J.M. Huber Corp. Methods for production and use of siliceous products
US4097302A (en) * 1976-02-17 1978-06-27 Scm Corporation Flatting agents
DE2803917A1 (de) * 1978-01-30 1979-08-02 Degussa Faellungskieselsaeuregranulate
EP0008613B2 (en) * 1978-06-12 1987-09-09 Ppg Industries, Inc. Process for treating pellets of silica and coating compositions containing the soft-settling flatting agent thus obtained
CH645410A5 (de) * 1979-01-12 1984-09-28 Akzo Nv Verfahren zur herstellung von wasserhaltigen fasern.
US4243428A (en) * 1979-01-24 1981-01-06 Donnet Jean Baptise Processes for the manufacturing of precipitated silica
DE3144299A1 (de) * 1981-11-07 1983-05-19 Degussa Ag, 6000 Frankfurt Faellungskieselsaeuren mit hoher struktur und verfahren zu ihrer herstellung
JPS5973419A (ja) * 1982-10-18 1984-04-25 Tokuyama Soda Co Ltd 超微細珪酸の製造方法
FR2562534B1 (fr) * 1984-04-06 1986-06-27 Rhone Poulenc Chim Base Nouvelle silice precipitee a caracteres morphologiques ameliores, procede pour son obtention et application, notamment comme charge
JPS62252312A (ja) * 1986-04-25 1987-11-04 Nippon Chem Ind Co Ltd:The 含水珪酸の製造方法

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN110562988A (zh) * 2019-09-12 2019-12-13 青岛美高集团有限公司 一种隔热保温材料及其生产方法
CN110562988B (zh) * 2019-09-12 2023-10-31 青岛美高集团有限公司 一种隔热保温材料及其生产方法

Also Published As

Publication number Publication date
EP0341383B1 (de) 1992-06-17
EP0341383B2 (de) 1997-01-15
DE3815670C2 (es) 1993-07-15
ES2033473T5 (es) 1997-03-16
EP0341383A2 (de) 1989-11-15
DE58901670D1 (de) 1992-07-23
DE3815670A1 (de) 1990-01-25
DK160289A (da) 1989-11-08
JPH055767B2 (es) 1993-01-25
EP0341383A3 (en) 1990-09-05
ZA892021B (en) 1989-11-29
DK160289D0 (da) 1989-04-03
US5123964A (en) 1992-06-23
JPH01320215A (ja) 1989-12-26
CA1340129C (en) 1998-11-17
US5034207A (en) 1991-07-23
ATE77353T1 (de) 1992-07-15

Similar Documents

Publication Publication Date Title
ES2033473T5 (es) Acido silicico de precipitacion finamente dividido con elevada estructura, procedimiento para su preparacion y empleo.
KR840002326A (ko) 고분자 구조를 갖는 침강 실리카의 제조방법
US4122161A (en) Amorphous precipitate silica compositions
JP5328073B2 (ja) 沈降珪酸、その製造法および該沈降珪酸の使用
KR970064702A (ko) 유기규소 화합물로 개질된 실리케이트 충전제를 기재로 하는 분산성이 우수한 저분진 과립
KR960037569A (ko) 실리카 및 알루미늄 술페이트 또는 알룸의 수성 현탁액, 상기 현탁액의 제조 및 사용 방법
EP0153827B1 (en) Porous particulate materials
JPH032914B2 (es)
PL157686B1 (en) Method of obtaining barium sulfate of chemically reactive surface
KR940005835B1 (ko) 충전입자에 대한 내산성 피막 형성방법
RU97101898A (ru) Концентрированная суспензия осажденной двуокиси кремния, способы ее приготовления и использование этой суспензии
KR0143881B1 (ko) 탄산칼슘 침전물의 제조방법
CN103936013B (zh) 一种制备白炭黑浆液的方法
CA1166404A (en) Preparation of aqueous suspensions of talc
US3228784A (en) Amorphous hydrogen alumino silicate pigments
US5151124A (en) Method for forming aggregated kaolin pigment
US5232495A (en) Method of producing aggregated kaolinite pigment using organic silicon compounds
US6068825A (en) Method for the preparation of a high-quality powder of amorphous silicic acid
US3658566A (en) Titanium oxide pigments
WO1994019413A1 (en) Method of producing aggregated kaolinite pigment using organic silicon compounds
GB1229125A (es)
CS232120B1 (cs) SpOsob přípravy disperzného hydrooxidu křemičitého
JPS57118020A (en) Manufacture of spherical particle of tricalcium aluminate hydrate
SU1193145A1 (ru) Способ получени тонкодисперсного муллитового порошка
RU2090582C1 (ru) Способ получения железосодежащего пигмента

Legal Events

Date Code Title Description
FG2A Definitive protection

Ref document number: 341383

Country of ref document: ES