DE3805550A1

DE3805550A1 - Process and apparatus for producing concrete parts

Info

Publication number: DE3805550A1
Application number: DE19883805550
Authority: DE
Inventors: Richard Kraiss
Original assignee: Prinzing Georg Co KG GmbH
Current assignee: Prinzing Georg Co KG GmbH
Priority date: 1988-02-23
Filing date: 1988-02-23
Publication date: 1989-08-31
Anticipated expiration: 2008-02-24
Also published as: DE3805550C2

Abstract

An apparatus for producing concrete parts in a mould is proposed, which has a mould core, a lower bottom ring, which can be supported on a supporting device, and a mould mantel, it being possible for the bottom ring to be set infinitely variably in relation to the mould core to a height adapted to the height of the concrete part respectively to be produced, and for it to be fixed on the mould core by means of the supporting device. The supporting device can be set in relation to the mould core to the desired height mechanically by means of external force acting on the said device and can then be securely clamped, in particular hydraulically, on the mould core and conversely can be released. These operations are automated, remote-controllable and integrated in the automatic working cycle of the apparatus.

Description

Die Erfindung bezieht sich auf ein Verfahren zum Herstellen von Betonteilen der im Oberbegriff des Anspruchs 1 genannten Art.The invention relates to a method for producing Concrete parts of the type mentioned in the preamble of claim 1.

Man ist bestrebt, bei der Herstellung von Betonteilen in einer einzigen Formeinrichtung Betonteile unterschiedlich großer Bau höhen zu produzieren. Dies erreicht man dadurch, daß der untere Bodenring in der Form höhenverstellbar angeordnet wird. Hierzu bedient man sich meist unterschiedlicher Distanzringe, Unter gestelle od. dgl., die jeweils zur Auflage des unteren Boden ringes benutzt werden und jeweils die erforderliche Höhe haben, so daß sich für den darauf aufliegenden unteren Bodenring die gewünschte Höhenposition ergibt. Derartige Distanzteile, Unter gestelle od. dgl. sind nachteilig. Zum einen ist die Anordnung aufwendig. Sie stört einen automatischen Fertigungsablauf und benötigt sehr viel Zeit. Nachteilig ist ferner, daß Beton, vor allem Zementleim, nach unten auslaufen kann, wodurch die Dis tanzringe, Untergestelle od. dgl. festkleben. Das Entfernen ist somit außerordentlich zeitaufwendig und beschwerlich. One strives to manufacture concrete parts in one single molding concrete parts of different sizes construction to produce heights. This is achieved by the lower one Bottom ring in the shape is arranged adjustable in height. For this you usually use different spacer rings, sub frames or the like, each for supporting the lower floor ringes are used and each have the required height, so that for the lower bottom ring lying on it desired height position results. Such spacers, sub frames or the like are disadvantageous. Firstly, there is the arrangement complex. It interferes with an automatic production process and takes a lot of time. Another disadvantage is that concrete, before all cement paste, can leak down, causing the dis Glue dance rings, bases or the like. The removal is therefore extremely time consuming and cumbersome.

Man hat auch schon versucht, Abstützvorrichtungen in Gestalt von Anschlagringen als Auflage für den unteren Bodenring in der Höhe stufenlos einstellbar zu gestalten, und zwar mittels eines mechanischen Spindelantriebes, dessen Spin deln über Ketten miteinander gekoppelt sind, um einen Gleich lauf zu erzielen. Einrichtungen dieser Art haben sich nicht bewährt, u. a. deswegen nicht, weil die Spindeln verschmut zungsempfindlich sind, nicht rüttelsicher sind und außerdem ein Gleichlauf der Spindelantriebe auf Dauer nicht gewähr leistet ist. Zudem ist die gesamte Einrichtung kompliziert und auf Dauer nicht betriebssicher.Attempts have also been made to design supports of stop rings as a support for the lower floor ring infinitely adjustable in height, namely by means of a mechanical spindle drive, the spin chains are linked together to create an equal to achieve a run. Facilities of this type have not been found proven, u. a. not because the spindles get dirty are sensitive to tongue, are not vibration-proof and also permanent synchronization of the spindle drives is not guaranteed is accomplished. In addition, the entire setup is complicated and not reliable in the long run.

Der Erfindung liegt die Aufgabe zugrunde, ein Verfahren der im Oberbegriff des Anspruchs 1 genannten Art zu schaffen, bei dem eine stufenlose Höheneinstellung für die Abstützvorrich tung des unteren Bodenringes ermöglicht und ein fernsteuer barer automatischer Betrieb gewährleistet ist.The invention has for its object a method of in the preamble of claim 1 to create at which a stepless height adjustment for the support device enables the lower floor ring and a remote control barer automatic operation is guaranteed.

Die Aufgabe ist bei einem Verfahren der eingangs genannten Art gemäß der Erfindung durch die Merkmale im Kennzeichnungs teil des Anspruchs 1 gelöst. Weitere vorteilhafte Verfahrens merkmale dazu ergeben sich aus den Ansprüchen 2-20.The task is in a method of the aforementioned Kind according to the invention by the features in the labeling solved part of claim 1. Another advantageous method Characteristics of this result from claims 2-20.

Das erfindungsgemäße Verfahren ermöglicht eine stufenlose Höheneinstellung und macht es dabei möglich, bei jedem Ar beitstakt vom Steuerpult einer Maschine aus jeweils die ge wünschte Höhe für das zu fertigende Betonteil vorzugeben und einzustellen.Vorteilhaft ist dieses z. B. insbesondere bei sogenannten Schachtrohren, bei denen in Abhängigkeit von der jeweiligen Höhe auch noch die richtige Anzahl von Steig eisen eingebracht werden muß. Durch die Erfindung ist es hierbei möglicht, nicht nur die jeweils gewünschte Steig eisenanzahl automatisch vorzugeben, sondern dies mit der Vorgabe der jeweils gewünschten Höhe des zu fertigenden Be tonteiles zu verquicken, so daß z. B. die Vorteile der auto matischen Steigeiseneinbringung gemäß DE-GM 85 01 471.0 in vollem Maße erhalten bleiben. Da beim erfindungsgemäßen Ver fahren die Abstützvorrichtung, insbesondere deren Anschlag ring, mittels der Schnellspannvorrichtung vorzugsweise hy draulisch verspannt wird, läßt sich das Spannen und gegen sinnig dazu das Lösen steuerungstechnisch in den automati schen Fertigungsablauf integrieren. Zudem sind nur geringe Stellwege zu durchlaufen. Das Verspannen bzw. Lösen geht also sehr schnell vonstatten. Durch die insbesondere hydraulische Verspannung z. B. am Formkern können mittels des erzielten Reibschlusses außerordentlich große und somit auf jeden Fall die nötigen Abstützkräfte erzielt werden, die für die Ab stützung des unteren Bodenringes und des darauf lastenden Betonteils bei der Fertigung nötig sind. Auch bei kleinem Spann- bzw. Lösehub ergibt sich im entspannten Zustand des Anschlagringes zwischen diesem und dem Formkern ein so aus reichend großes Spiel, daß beide Teile relativ zueinander freibeweglich sind und sich nicht behindern. Im gespannten Zustand des Anschlagringes am Formkern läßt sich eine gleich mäßige Spannung und außerdem eine dichte Verbindung in diesem Bereich erzielen. Auch wenn mit Formeinrichtungen gearbeitet wird, bei denen der Formkern zur sogenannten Direkteinrütt lung mit einem Kernsegment versehen ist, ist das erfindungs gemäße Verfahren ohne Behinderung des Kernsegmentes anwend bar.The method according to the invention enables continuous Height adjustment and makes it possible for every ar the cycle from the control panel of a machine desired height for the concrete part to be manufactured and Advantageously, this is e.g. B. in particular so-called shaft pipes, in which depending on the correct number of steps at the respective height iron must be introduced. By the invention it is possible, not just the desired climb the iron number automatically, but with the Specification of the desired height of the Be to be manufactured to quicken part of the sound, so that z. B. the benefits of auto matical crampon insertion according to DE-GM 85 01 471.0 in remain fully intact. Since the ver drive the support device, in particular its stop ring, by means of the quick release device, preferably hy is drastically tensioned, the tensioning and against it makes sense to solve this in terms of control technology in the automati integrating the production process. In addition, there are only a few To travel through travel ranges. The bracing or loosening is therefore possible very quickly. Due to the particular hydraulic Bracing z. B. on the mandrel can be achieved by means of the Frictionally extraordinarily large and therefore definitely the necessary support forces can be achieved for the Ab support of the lower floor ring and the load on it Concrete part are necessary during production. Even with small ones Tension or release stroke results in the relaxed state of the Stop ring between this and the mandrel from sufficiently large game that both parts are relative to each other are free to move and do not interfere. I'm excited Condition of the stop ring on the mandrel can be the same moderate tension and also a tight connection in this Area. Even when working with molding equipment becomes, in which the mandrel to the so-called direct insertion is provided with a core segment, that is fiction apply appropriate procedures without obstructing the core segment bar.

Erfolgt die Höhenverstellung der Stützvorrichtung mittels einer maschinenseitig vorhandenen Ausstoßvorrichtung, insbesondere deren Ausstoßplatte, ist dies besonders einfach; denn die Ausstoßvorrichtung ist ja bereits vorhanden, so daß für die stufenlose Höhenverstellung der Abstützvorrichtung keine zusätzliche Einrichtung notwendig ist. Der Anschlagring selbst mit hydraulischer Verspannung ist ein sehr einfaches, robustes Teil, das im übrigen rüttelsicher arbeitet, ver schmutzungsunempfindlich ist und auf Dauer betriebssicher ist. Selbst wenn der Anschlagring für längere Zeit - ohne Höhen verstellung - an derselben Stelle verbleibt, ist aufgrund der hydraulischen Einrichtung ein einwandfreies Lösen des An schlagringes jederzeit sichergestellt. Durch die Merkmale in den Ansprüchen 13 und 14 ist es möglich, daß der Anschlag ring bei der Herstellung von Betonteilen jeweils gleicher Bauhöhe immer in der gespannten und eingestellten Höhenlage verbleibt und der übrige Betrieb, insbesondere das Ausstoßen, mittels der Ausstoßvorrichtung dadurch nicht behindert ist. Es versteht sich, daß z. B. bei ganz einfachen Formen, bei denen die Entschalung vom Formkern und der Weitertransport gefertigter Betonteile zum Abbindeplatz mittels äußerer Hebe zeuge erfolgt, auch die Abstützvorrichtung mittels dieser äußeren Hebezeuge auf die jeweils gewünschte Höhe eingestellt werden kann. Gemäß den Verfahrensmerkmalen in den Ansprüchen 10 und 11 geht man dann vor, wenn die Ausstoßvorrichtung stationär und statt dessen der Formkern auf und ab beweglich ist. Somit läßt sich das erfindungsgemäße Verfahren auch für diese Version in gleicher Weise einsetzen.If the height of the support device is adjusted by means of an ejection device provided on the machine, in particular its ejection plate, this is particularly simple; because the ejection device is already present, so that no additional device is necessary for the stepless height adjustment of the support device. The stop ring itself with hydraulic bracing is a very simple, robust part that works shake-proof in the rest, is insensitive to dirt and is reliable in the long run. Even if the stop ring remains in the same place for a long time - without height adjustment - the hydraulic device ensures that the stop ring is released properly at all times. Due to the features in claims 13 and 14, it is possible that the stop ring in the manufacture of concrete parts of the same overall height always remains in the tensioned and adjusted height and the rest of the operation, in particular the ejection, is not hindered by the ejection device. It is understood that, for. B. in very simple forms, in which the formwork from the mold core and the further transport of manufactured concrete parts to the setting site is done by means of external lifting, the support device can also be adjusted to the desired height by means of these external lifting devices. According to the process features in claims 10 and 11, one proceeds when the ejection device is stationary and instead the mold core is movable up and down. The method according to the invention can thus also be used in the same way for this version.

Durch die Merkmale in den Ansprüchen 15-20 ist erreicht, daß trotz vorhandenen Spiels zwischen unterem Bodenring, Formkern und Formmantel je nach Höhe des herzustellenden Be tonteiles eine zuverlässige Abdichtung des Formraumes nach unten gewährleistet ist. Außerdem ist der untere Bodenring an der Abstützvorrichtung, insbesondere am Anschlagring, in der Ringebene zentrierbar, so daß reproduzierbar immer die gleiche Stellung eingenommen wird. Unter Einwirkung der Rüttel kräfte beim Rütteln ist ein Verlagern des unteren Bodenringes zumindest im wesentlichen verhindert. Auch einem Anschlagen des Bodenringes am Formkern und/oder Formmantel ist entgegen gewirkt. Damit sind Beschädigungen, Verschleiß oder Zerstö rungen zwischen dem Bodenring, dem Formkern und dem Formmantel im wesentlichen vermieden. Die Erfindung schafft ferner die Voraussetzungen dafür, über den Anschlagring den Formkern und den Formmantel zumindest kraftschlüssig gegeneinander abzu stützen, so daß diese eine Einheit bilden. Dadurch ist die Lage des Formkerns zum Formmantel bei jedem Arbeitstakt die gleiche, wobei diese im Betrieb gesichert bleibt, so daß auch die Wandstärke des herzustellenden Betonteils reproduzierbar die gleiche ist und nicht variiert. Von Vorteil ist ferner, daß über den Anschlagring beim Rütteln die Schwingungen gut auf den unteren Bodenring und den Formmantel übertragen werden. Die Abstützvorrichtung, insbesondere der Anschlagring, läßt sich als eigenständiges Teil schnell ausbauen und austau schen, was Reinigung, Wartung, Reparatur und dgl. wesentlich vereinfacht.The features in claims 15-20 achieve that despite the existing clearance between the lower ring of the floor, Mold core and mold jacket depending on the height of the Be to be manufactured a reliable sealing of the mold space is guaranteed below. In addition, the lower floor ring on the support device, in particular on the stop ring, in the ring plane can be centered, so that the same position is taken. Under the influence of the vibrators Forces when shaking is a shifting of the lower floor ring at least essentially prevented. Even a striking the bottom ring on the mold core and / or mold jacket is opposed worked. This means damage, wear or destruction between the bottom ring, the mold core and the mold jacket essentially avoided. The invention also provides Preconditions for this, the mold core and the stop ring at least non-positively against the molded jacket support so that they form a unit. This is the Location of the mandrel to the form jacket with each work cycle same, which remains secured during operation, so that too the wall thickness of the concrete part to be produced is reproducible is the same and does not vary. It is also an advantage that over the stop ring when vibrating the vibrations well be transferred to the lower base ring and the molded jacket. The support device, in particular the stop ring, can quickly expand and replace as an independent part what cleaning, maintenance, repair and the like. Essential simplified.

Die Erfindung bezieht sich ferner auf eine Einrichtung zum Herstellen von Betonteilen, insbesondere zur Durchführung des Verfahrens, gemäß Oberbegriff des Anspruchs 21. Eine Ein richtung dieser Art ist erfindungsgemäß durch die Merkmale im Kennzeichnungsteil des Anspruchs 21 gekennzeichnet. Vor teilhafte Ausgestaltungen dieser Einrichtung ergeben sich aus den Ansprüchen 22-52. Die dadurch erzielten Vorteile sind der Einfachheit halber schon eingangs teilweise herausgestellt.The invention further relates to a device for Manufacture of concrete parts, in particular for implementation of the method, according to the preamble of claim 21. A one Direction of this type is according to the invention by the features characterized in the characterizing part of claim 21. Before partial configurations of this device result from claims 22-52. The benefits are: For the sake of simplicity, it was already partially highlighted at the beginning.

Im übrigen ergeben sich weitere Einzelheiten und Vorteile der Erfindung aus der nachfolgenden Beschreibung. Der vollstän dige Wortlaut der Ansprüche ist vorstehend allein zur Ver meidung unnötiger Wiederholungen nicht wiedergegeben, sondern statt dessen lediglich durch Nennung der Anspruchsnummern darauf Bezug genommen, wodurch jedoch alle diese Anspruchs merkmale als an dieser Stelle ausdrücklich und erfindungs wesentlich offenbart zu gelten haben. Dabei sind alle in der vorstehenden und folgenden Beschreibung erwähnten Merkmale sowie auch die allein aus der Zeichnung entnehmbaren Merkmale weitere Bestandteile der Erfindung, auch wenn sie nicht be sonders hervorgehoben und insbesondere nicht in den An sprüchen erwähnt sind.For the rest, there are further details and advantages of the Invention from the following description. The complete The wording of the claims above is solely for ver avoiding unnecessary repetitions, but not reproduced instead only by mentioning the claim numbers referred to, however, all of these claims Features as express and inventive at this point have to be essentially disclosed. All are in the Features mentioned above and following description as well as the features that can only be taken from the drawing further components of the invention, even if they are not be especially highlighted and especially not in the An sayings are mentioned.

Die Erfindung ist nachfolgend anhand von in den Zeich nungen gezeigten Ausführungsbeispielen näher erläutert. Es zeigen:The invention is based on in the drawing Solutions shown embodiments explained in more detail. Show it:

Fig. 1-3 jeweils einen schematischen Schnitt einer Formeinrichtung zum Herstellen von Betonteilen, gemäß einem ersten Aus führungsbeispiel und während verschiedener Stadien beim Herstellungsprozeß, Fig. 1-3 respectively a schematic sectional view of a mold device for producing concrete parts, lead, for example according to a first stop and during various stages in the manufacturing process,

Fig. 4 eine schematische Draufsicht eines An schlagringes der Formeinrichtung gemäß dem ersten Ausführungsbeispiel, Fig. 4 is a schematic plan view of an impact ring to the mold device according to the first embodiment,

Fig. 5 einen schematischen Schnitt etwa ent sprechend demjenigen in Fig. 2 einer Formeinrichtung gemäß einem zweiten Aus führungsbeispiel, Fig. 5 is a schematic section approximately accordingly to that in Fig. 2 of a molding device according to a second guidance from, for example,

Fig. 6-9 jeweils einen schematischen Schnitt von Teilen einer Formeinrichtung gemäß einem dritten bzw. vierten bzw. fünften bzw. sechsten Ausführungsbeispiel, Fig. 6-9 respectively a schematic section of parts of a molding device according to a third, fourth and fifth and sixth embodiment,

Fig. 10-12 jeweils einen schematischen Schnitt eines Anschlagringes mit enthaltenem Preßring gemäß einem siebten bzw. achten bzw. neunten Ausführungsbeispiel. Fig. 10-12 each show a schematic section of a stop ring with a press ring according to a seventh or eighth or ninth embodiment.

Bei der Formeinrichtung 10 gemäß dem ersten Ausführungs beispiel in Fig. 1-4 sind zur Vereinfachung nur die hierfür und für die nachfolgende Beschreibung wichtigen Grundelemente gezeigt und beschrieben. Diese bestehen aus einem zentralen Formkern 11, der an die jeweils herzu stellenden Betonteile 12 angepaßt ist, also z.B. Zylinder form hat oder vieleckig oder konisch oder in sonstiger Weise gestaltet ist. Der Formkern 11 ist beim gezeigten Ausführungsbeispiel mit einer Einrichtung 13 zum direkten Einbetonieren von Steigeisen 14 während des Formgebungs vorganges versehen. Diese Einrichtung 13 weist u.a. ein Kernsegment 15 auf, das zum Einsetzen der Steigeisen 14 und zum Entformen des hergestellten Betonteiles 12 in eine in Fig. 1 und 2 gezeigte Position in das Innere des Formkernes 11 einfahrbar ist bzw. für die Herstellung des Betonteiles 12 gegensinnig ausfahrbar ist in die Fig. 3 gezeigte Position, wo das Kernsegment 15 den Form kern 11 komplettiert. Eine Einrichtung 13 besagter Art ist in DE-PS 31 10 185 näher beschrieben.In the molding device 10 according to the first embodiment, for example in FIGS. 1-4, only the basic elements important for this and for the following description are shown and described for the sake of simplicity. These consist of a central mold core 11 , which is adapted to the concrete parts 12 to be produced , for example, has a cylindrical shape or is polygonal or conical or in some other way. The mandrel 11 is provided in the embodiment shown with a device 13 for the direct concreting of crampons 14 during the molding process. This device 13 has, inter alia, a core segment 15 which, for inserting the crampons 14 and for demolding the manufactured concrete part 12 into a position shown in FIGS . 1 and 2, can be moved into the interior of the mold core 11 or in opposite directions for the production of the concrete part 12 Extendable is shown in Fig. 3 position, where the core segment 15 completes the mold core 11 . A device 13 of said type is described in more detail in DE-PS 31 10 185.

Der Formkern 11 ist hier auf einen vorzugsweise zentralen Rüttler 16 aufgesetzt, an dem der Formkern 11 auswechsel bar aufgenommen und befestigt ist. Hierzu dient eine nur schematisch angedeutete Aufnahme- und Spannvorrichtung 17.The mandrel 11 is here placed on a preferably central vibrator 16 , on which the mandrel 11 is exchangeably received and fastened. A receiving and tensioning device 17 , which is only indicated schematically, serves this purpose.

Die Formeinrichtung 10 weist ferner einen zum Formkern 11 koaxialen und dazu passenden Formmantel 18 auf, der in der Formgebungsstellung (Fig. 3) den Formkern 11 mit Ab stand unter Bildung eines Formraumes 19 dazwischen umgibt. Beim ersten Ausführungsbeispiel ist der Formkern 11 statio när gehalten, während der Formmantel 18 mit Hilfe eines nicht weiter gezeigten, vertikal auf und ab bewegbaren Wagens in Achsrichtung 20 bewegbar ist.The molding device 10 also has a coaxial to the mold core 11 and matching mold shell 18 , which in the shaping position ( FIG. 3) the mold core 11 was from with surrounding a mold space 19 therebetween. In the first embodiment, the mold core 11 is held statio narily, while the mold jacket 18 is movable in the axial direction 20 with the aid of a not shown, vertically up and down movable carriage.

Die Formeinrichtung 10 weist außerdem einen unteren Boden ring 21 (Untermuffe) auf, der mit unterseitigen Stützen 22 versehen ist und so in Abstand von einer bodenseitigen Stützfläche gehalten ist, daß durch Untergreifen des Boden ringes 21 z.B. mittels eines Staplers der Abtransport des Bodenringes 21 mit darauf ruhendem, zuvor geformten Beton teil 12 möglich ist. Der Bodenring 21 ist mit Hilfe einer Abstützvorrichtung 23 vertikal abstützbar, wie noch weiter erläutert wird. Die Abstützvorrichtung 23 weist hier einen Anschlagring 24 auf, auf dem der Bodenring 21 von oben her aufliegen kann, so daß der Bodenring 21 auf diese Weise relativ zum Formkern 11 stufenlos auf eine der Höhe des jeweils herzustellenden Betonteiles 12 angepaßte Höhe eingestellt und am Formkern 11 fixiert werden kann. Da durch ist es möglich, mittels der Formeinrichtung 10 Beton teile 12 mit unterschiedlich großen Bauhöhen zu produ zieren, wobei die Höhe des Formkernes 11 sowie des Form mantels 18 so dimensioniert sind, daß diese den größt möglichen Bauhöhen gerecht werden.The shaping device 10 also has a lower bottom ring 21 (sleeve), which is provided with supports 22 on the underside and is held at a distance from a bottom-side support surface, that by reaching under the bottom ring 21, for example by means of a stacker, the removal of the bottom ring 21 with resting on it, previously formed concrete part 12 is possible. The bottom ring 21 can be supported vertically with the aid of a support device 23 , as will be explained further. The support device 23 here has a stop ring 24 , on which the base ring 21 can rest from above, so that the base ring 21 is in this way continuously adjusted relative to the mold core 11 to a height adapted to the height of the concrete part 12 to be manufactured and on the mold core 11 can be fixed. Since it is possible by means of the molding device 10 to produce concrete parts 12 with different heights, the height of the mandrel 11 and the shape jacket 18 are dimensioned so that they meet the greatest possible heights.

Der Anschlagring 24 der Abstützvorrichtung 23 ist an die Umfangskontur und Umfangsgröße des Formkernes 11 angepaßt und somit kreisförmig oder vieleckig. Er ist mittels einer Schnellspannvorrichtung 25, die vorzugsweise druck mittelbetrieben und hierbei insbesondere hydraulisch ist, am Formkern 11 radial festspannbar, und zwar so, daß der Anschlagring 24 gleichmäßig an der Außenfläche des ge samten Formkernes 11 anliegt. Ferner ist der Anschlagring 24 gegensinnig dazu entspannbar, und somit vom Formkern 11 gelöst, wobei ein ausreichendes Spiel zwischen dem Form kern 11 und dem Anschlagring 24 entsteht und dadurch eine freie Relativbewegung zwischen dem Formkern 11 und dem Anschlagring 24 möglich ist. Die insbesondere hydraulisch arbeitende Schnellspannvorrichtung 25 ist in nicht weiter gezeigter Weise fernbetätigbar, so daß das Spannen bzw. Entspannen automatisch und durch Steuerung von einem Steuerpult aus gesteuert werden können. Daher kann von einem Steuerpult aus jeweils die Einstellung auf die ge wünschte Höhe des zu fertigenden Betonteiles 12 vorge nommen werden. Durch Aktivieren der Schnellspannvorrichtung 25 ist der Anschlagring 24 selbsttätig mechanisch auf der Außenfläche des Formkernes 11 festspannbar bzw. in bezug auf den Formkern 11 entspannbar. Der Anschlagring 24 ist z.B. aus einem Metallteil gebildet und gemäß Fig. 4 zu mindest einmal geteilt. Die Schnellspannvorrichtung 25 weist einen druckmittelbetriebenen Spannantrieb 26, z.B. einen Hydraulikzylinder, auf, der im Bereich der Trenn stelle sitzt und zwischen den beiden Enden 27, 28 des Anschlagringes 24 wirksam ist. Der Spannantrieb 26 ist z.B. doppeltwirkend. Bei einem anderen, nicht gezeigten Ausführungsbeispiel ist der Spannantrieb 26 einfachwirkend ausgebildet, wobei das Festspannen kraftbetätigt gegen Federkraft,z.B.die Eigenspannung des Anschlagringes 24 oder zusätzliche Federn, Gummipuffer od.dgl., erfolgt, während das Entspannen dann aufgrund dieser Federkraft erfolgt.The stop ring 24 of the support device 23 is adapted to the circumferential contour and circumferential size of the mandrel 11 and is thus circular or polygonal. It is by means of a quick clamping device 25, which is preferably operated by pressure medium, and hereby in particular hydraulically, radially clamped on the mandrel 11, in such a way that the stop ring 24 uniformly abuts the outer surface of the entire mold core ge. 11 Further, the stop ring 24 in opposite directions detensioned, and thus released to the mold core 11, wherein a sufficient clearance between the mold core 11 and the stop ring 24 is formed and thereby a free relative movement between the mold core 11 and the stop ring 24 is possible. The particularly hydraulic quick release device 25 can be operated remotely in a manner not shown, so that the tensioning or relaxing can be controlled automatically and by control from a control panel. Therefore, the setting to the desired height of the concrete part 12 to be manufactured can be taken from a control panel. By activating the quick-clamping device 25 , the stop ring 24 can automatically be mechanically clamped onto the outer surface of the mold core 11 or can be relaxed with respect to the mold core 11 . The stop ring 24 is formed, for example, from a metal part and divided at least once according to FIG. 4. The quick release device 25 has a pressure medium-operated tensioning drive 26 , for example a hydraulic cylinder, which sits in the area of the separation point and is effective between the two ends 27 , 28 of the stop ring 24 . The tensioning drive 26 is double-acting, for example. In another embodiment, not shown, the tensioning drive 26 is designed to be single-acting, the clamping being force-actuated against spring force, for example the internal tension of the stop ring 24 or additional springs, rubber buffers or the like, while the relaxation then takes place on account of this spring force.

Der Anschlagring 24 weist einen z.B. ringförmigen oberen Auflageteil 29 auf, auf dem der untere Bodenring 21 mit seinem inneren Ringteil 30 aufliegen kann (Fig. 3). Ferner ist der Anschlagring 24 mit einem quer abstehenden Zen triervorsprung 31 versehen, der hier aus einem einzigen umlaufenden Zentrierring gebildet ist. Statt dessen können auch mehrere quer abstehende Zentriervorsprünge vorge sehen sein. Der Zentriervorsprung 31 kann so beschaffen sein, daß daran der Bodenring 21 mit einem Mittelringteil 32 unter koaxialer Zentrierung anliegen kann, wobei dieser Mittelringteil 32 etwa vertikal verläuft und sich dabei zwischen dem inneren Ringteil 30 und einem äußeren Ring teil 33 erstreckt. Durch den Zentriervorsprung 31 ist somit eine reproduzierbare zentrierte Lage des Bodenringes 21 gewährleistet.The stop ring 24 has, for example, an annular upper support part 29 on which the lower base ring 21 can rest with its inner ring part 30 ( FIG. 3). Furthermore, the stop ring 24 is provided with a transversely protruding Zen trier projection 31 , which is formed here from a single circumferential centering ring. Instead, several transversely projecting centering projections can be seen easily. The centering projection 31 can be such that the base ring 21 can rest against it with a central ring part 32 with coaxial centering, this central ring part 32 extending approximately vertically and thereby extending between the inner ring part 30 and an outer ring part 33 . The centering projection 31 thus ensures a reproducible, centered position of the base ring 21 .

Der Anschlagring 24 ist stufenlos in bezug auf den Form kern 11 höhenverstellbar, und somit ein darauf aufliegender Bodenring 21. Bei einfachen Formeinrichtungen, bei denen die Entschalung des gefertigten Betonteiles 12 vom Formkern 11 sowie der Weitertransport des gefertigten Betonteiles 12 zum Abbindeplatz jeweils mit äußeren Hebezeugen geschieht, z.B. mittels eines Kranes od.dgl., kann das äußere Hebezeug zugleich auch zur Höhenverstellung des hydraulisch verspannbaren Anschlagringes 24 dienen. Auf diese Weise kann der Anschlagring 24 mittels Kran, Stapler od.dgl. Hebezeugen relativ zum Formkern 11 jeweils in die gewünschte Höhenposition gebracht und dann mittels der Schnellspannvorrichtung 25 am Formkern 11 fest gespannt werden.The stop ring 24 is infinitely height-adjustable with respect to the mold core 11 , and thus a base ring 21 resting thereon. In the case of simple molding devices in which the formwork removal of the finished concrete part 12 from the mandrel 11 and the further transport of the finished concrete part 12 to the setting place is done in each case with external hoists, for example by means of a crane or the like, the outer hoist can also be used to adjust the height of the hydraulically tensioned Stop ring 24 serve. In this way, the stop ring 24 by means of a crane, forklift or the like. Hoists relative to the mold core 11 are each brought into the desired height position and then firmly clamped to the mold core 11 by means of the quick-clamping device 25 .

Beim ersten Ausführungsbeispiel gemäß Fig. 1-4 ist die Formeinrichtung 10 ohnehin mit einer Ausstoßvorrichtung 34 versehen, von der lediglich eine Ausstoßplatte 35 gezeigt ist, die eine vom Formkern 11 durchsetzbare Öffnung 36 aufweist. Die Ausstoßplatte 35 wird mittels eines nicht gezeigten vertikal verfahrbaren Wagens relativ zum Form kern 11 auf und ab bewegt. Der Anschlagring 24 weist nach außen abstehende Vorsprünge, insbesondere einen ringsum laufenden Flansch auf, der hier durch den Zentriervor sprung 31 gebildet ist. Dieser ist von nach innen ge richteten Stützteilen an der Ausstoßplatte 35, die hier aus einem umlaufenden Flansch 37 gebildet sind, untergreif bar. Somit kann der Anschlagring 24 mittels der Ausstoß platte 35 relativ zum Formkern 11 auf und ab bewegt und auf die jeweils gewünschte Höhe vor dem Festspannen ein gestellt werden.In the first exemplary embodiment according to FIGS . 1-4, the molding device 10 is in any case provided with an ejection device 34 , of which only one ejection plate 35 is shown, which has an opening 36 which can be penetrated by the molding core 11 . The ejection plate 35 is moved up and down relative to the mold core 11 by means of a vertically movable carriage, not shown. The stop ring 24 has outwardly protruding projections, in particular an all-round flange, which is formed here by the centering 31 jump. This is from inwardly directed support parts on the ejection plate 35 , which are formed here from a circumferential flange 37 , under gripping bar. Thus, the stop ring 24 can be moved by means of the ejection plate 35 relative to the mandrel 11 up and down and set to the desired height before tightening.

Der Fertigungsablauf mittels der Formeinrichtung 10 gemäß Fig. 1-4 ist folgendermaßen.The manufacturing process using the molding device 10 according to FIGS . 1-4 is as follows.

In Fig. 1 ist die Ausgangsstellung gezeigt, bei der zu letzt das Betonteil 12 gefertigt und z.B. überflur in die gezeigte Position nach außen ausgestoßen worden ist. Nach Abtransport, ruhend auf dem Bodenring 21, wird ein neuer Bodenring 21 z.B. maschinell auf die Ausstoßplatte 35 aufgelegt. Diese befindet sich in ihrer obersten Stellung (Fig. 1), in der sie zugleich von unten mittels des Flansches 37 den Zentriervorsprung 31 des Anschlag ringes 24 formschlüssig untergreift, wodurch dieser eben falls in dieser oberen Stellung gehalten ist. Das Kern segment 15 ist in die in Fig. 1 gezeigte Position einge fahren, so daß z.B. mit Hilfe einer Magazineinrichtung (DE-GM 85 01 471) in dieser Position die gewünschte An zahl von Steigeisen 14 in das Kernsegment 15 eingesetzt werden kann. Beim nächsten Arbeitstakt der Formein richtung 10 wird die Ausstoßplatte 35 mit darauf auf sitzendem Bodenring 21 und daran gehaltenem Anschlagring 24 relativ zum Formkern 11 soweit nach unten bewegt, bis der Anschlagring 24 die für den Bodenring 21 gewünschte Höhenposition erreicht hat. In dieser Position wird die Bewegung der Ausstoßplatte 35 gestoppt. Diese Position zeigt Fig. 2. Sodann wird das Kernsegment 15, in das einzelne Steigeisen 14 eingelegt worden sind, in die Schließstellung verfahren, in der der Formkern 11 seine komplette Formgebungskontur hat. Hiernach wird die Schnell spannvorrichtung 25 aktiviert und darüber in kürzester Zeit der Anschlagring 24 hydraulisch an der Außenfläche des Formkernes 11 festgespannt, wobei der Anschlagring 24 gleichmäßig am Formkern 11 anliegt. Hiernach wird die Ausstoßplatte 35 weiter abwärts bewegt, wobei sich der Flansch 37 vom Zentriervorsprung 31 des nun festgespannten Anschlagringes 24 abhebt. Der untere Bodenring 21 wird dabei mit dem inneren Ringteil 30 auf dem oberen Auflage teil 29 abgesetzt, wobei eine Zentrierung zwischen dem Mittelringteil 32 und dem Zentriervorsprung 31 geschieht. Zusammen mit der Abwärtsbewegung der Ausstoßvorrichtung 34 wird auch der Formmantel 18 über den Bodenring 21 mit An schlagring 24 koaxial hinweg in die unterste Stellung gemäß Fig. 3 bewegt. Der Formmantel 18 befindet sich nun in Formgebungsstellung, während die Ausstoßplatte 35 ganz unten sitzt. Die inneren Abmessungen des Formmantels 18 sind so gewählt, daß dieser mit seiner Innenfläche den Bodenring 21 umgibt, wobei hier zwar ein nötiges Bewegungs spiel vorhanden ist, jedoch dennoch ein einigermaßen dichter Abschluß geschieht.In Fig. 1 the starting position is shown, in which the concrete part 12 was last made and, for example, has been pushed out into the position shown to the outside. After removal, resting on the base ring 21 , a new base ring 21 is, for example, placed mechanically on the ejection plate 35 . This is in its uppermost position ( Fig. 1), in which it at the same time engages the centering projection 31 of the stop ring 24 from below by means of the flange 37 , whereby this is just held in this upper position. The core segment 15 is in the position shown in Fig. 1 drive so that, for example, with the help of a magazine device (DE-GM 85 01 471) in this position, the desired number of crampons 14 can be used in the core segment 15 . At the next stroke of the Formein device 10 , the ejection plate 35 with the seated bottom ring 21 and stop ring 24 held thereon is moved relative to the mandrel 11 until the stop ring 24 has reached the desired height position for the bottom ring 21 . In this position, the movement of the ejection plate 35 is stopped. This position is shown in FIG. 2. The core segment 15 , into which individual crampons 14 have been inserted, is then moved into the closed position, in which the mold core 11 has its complete shaping contour. Thereafter, the quick clamping device is activated and about 25 hydraulically clamped in a very short time, the stop ring 24 on the outer surface of the mold core 11, with the stop ring 24 is applied evenly around the mandrel. 11 Thereafter, the ejection plate 35 is moved further downward, the flange 37 lifting off from the centering projection 31 of the stop ring 24 which is now firmly clamped. The lower base ring 21 is placed with the inner ring part 30 on the upper support part 29 , centering between the middle ring part 32 and the centering projection 31 . Together with the downward movement of the ejection device 34 , the shaped jacket 18 is moved coaxially over the base ring 21 with the impact ring 24 into the lowest position according to FIG. 3. The shaped jacket 18 is now in the shaping position, while the ejection plate 35 sits at the very bottom. The inner dimensions of the shaped jacket 18 are chosen so that it surrounds the bottom ring 21 with its inner surface, although there is a necessary movement play here, but a reasonably tight closure still occurs.

In der für die Formgebung bereiten Position gemäß Fig. 3 wird dann in üblicher Weise in den Formraum 19 Betonmaterial eingefüllt und verdichtet und somit das Betonteil 12 ge formt. Anschließend an diesen Prozeß wird zunächst der Formmantel 18 hochgefahren. Die Ausstoßplatte 35 wird so weit hochbewegt, bis sie von unten her mit dem Flansch 37 am Zentriervorsprung 31 des Anschlagringes 24 anliegt. In dieser Position wird die Ausstoßplatte 35 gestoppt und der Spannantrieb 26 betätigt, wodurch der Anschlagring 24 entspannt wird und somit zwischen diesem und dem Formkern 11 ausreichend Spiel geschaffen wird. Hiernach wird die Ausstoßplatte 35 weiter nach oben bewegt, mitsamt dem daran formschlüssig gehaltenen Anschlagring 24 sowie darauf aufsitzenden Bodenring 21, auf dem das fertige Betonteil 12 ruht. Hat die Ausstoßplatte 35 die oberste Stellung gemäß Fig. 1 erreicht, wird diese stillgesetzt, so daß das Betonteil 12 abtransportiert werden und der nächste Arbeitstakt beginnen kann.In the position ready for shaping according to FIG. 3, concrete material is then filled and compacted in the mold space 19 in the usual way and thus the concrete part 12 is formed . Following this process, the mold jacket 18 is first run up. The ejection plate 35 is so far moved up until they forth of the stop ring 24 is applied from below to the flange 37 on the centering 31st In this position, the ejection plate 35 is stopped and the tensioning drive 26 is actuated, whereby the stop ring 24 is relaxed and thus sufficient play is created between the latter and the mandrel 11 . Thereafter, the ejection plate 35 is moved further upward, together with the stop ring 24 held thereon in a form-fitting manner and the base ring 21 seated thereon, on which the finished concrete part 12 rests. 35 has reached the uppermost position according to FIG. 1, the ejection plate, it will be stopped, so that the concrete part 12 be removed and the next working cycle can begin.

Die mittels der Ausstoßvorrichtung 34 durchzuführende Höhenverstellung des Anschlagringes 24 ist außerordentlich einfach. Es ist für diese Höhenverstellung kein zusätz liches Element der Formeinrichtung 10 notwendig, da die Ausstoßvorrichtung 34 mit Ausstoßplatte 35 ja ohnehin vorhanden ist, um bei dieser Ausgestaltung der Formein richtung 10 das Abwärtsbewegen des Bodenringes 21 sowie das gegensinnige Ausstoßen dieses mit darauf ruhendem Betonteil zu ermöglichen. Der Anschlagring 24 für sich ist ein sehr einfaches und robustes Teil mitsamt der Schnellspannvorrichtung 25, die eine schnelle hydraulische Verspannung ermöglicht. Diese gesamte Abstützvorrichtung 23 ist somit einfach, robust und unempfindlich, auch gegen etwaige Verschmutzung. Sie ist außerdem rüttelsicher, was insbesondere in Verbindung mit einer Formeinrichtung 10 von Vorteil ist, die für das sogenannte Rüttelpreß verfahren, wie beschrieben, geeignet ist. Selbst das Ar beiten mit Kernsegment 15 und automatischem Direkteinbau von Steigeisen 14 während des Formgebungsprozesses ist dadurch nicht behindert. Die benötigten Steigeisen 14 können ohne etwaige Behinderung durch die Abstützvorrich tung 23 eingeschoben werden. Durch die ermöglichte stufenlose Höheneinstellung kann von einem fernen Steuer pult aus die jeweils gewünschte Höhe für die zu fertigenden Betonteile eingestellt werden. Dies ist besonders vorteil haft auch für die Herstellung solcher Betonteile, die größere Längen haben und neuerdings als "Schachtrohre" bezeichnet werden, bei denen zusätzlich bei der Herstellung je nach Höhe die richtige Anzahl von Steigeisen 14 einge bracht werden muß. Die Formeinrichtung 10 erlaubt es, die gewünschte Höhe des Betonteiles 12 vorzuwählen und dies zugleich mit der automatischen Einstellung der dazu nötigen und gewünschten Steigeisenanzahl zu verquicken.The height adjustment of the stop ring 24 to be carried out by means of the ejection device 34 is extremely simple. There is no additional Lich element of the molding device 10 necessary for this height adjustment, since the ejection device 34 with ejection plate 35 is already present to enable the downward movement of the bottom ring 21 and the opposite ejection of this with the concrete part resting on it in this embodiment of the Formein device 10 . The stop ring 24 in itself is a very simple and robust part together with the quick release device 25 , which enables rapid hydraulic tensioning. This entire support device 23 is thus simple, robust and insensitive, even against any contamination. It is also vibration-proof, which is particularly advantageous in connection with a shaping device 10 which is suitable for the so-called vibratory press, as described. Even the Ar work with core segment 15 and automatic direct installation of crampons 14 during the shaping process is not hindered by this. The required crampons 14 can be inserted without any hindrance by the device 23 Ab Stützvorrich. Thanks to the stepless height adjustment, the desired height for the concrete parts to be manufactured can be set from a remote control panel. This is particularly advantageous also for the production of such concrete parts that have greater lengths and are recently referred to as "shaft pipes", in which, depending on the height, the correct number of crampons 14 must also be introduced during manufacture. The shaping device 10 makes it possible to preselect the desired height of the concrete part 12 and at the same time to combine this with the automatic setting of the necessary and desired number of crampons.

Bei einem anderen, nicht gezeigten Ausführungsbeispiel kann mit Hilfe der gleichen Formeinrichtung 10 praktisch in kinematischer Umkehr und etwa wie folgt verfahren werden. Abweichend vom ersten Ausführungsbeispiel ist hier bei die Ausstoßvorrichtung 34 mit Ausstoßplatte 35 stationär angeordnet. Zu Beginn des Formgebungszyklus legt man den Anschlagring 24 mit aufliegendem Bodenring 21 auf der stationären Ausstoßplatte 35 auf. Sodann bewegt man den Formkern 11 relativ dazu nach oben auf die gewünschte Höhe, wobei der Formkern 11 die Öffnung 36 der Ausstoßplatte 35 und ferner den Anschlagring 24 und den Bodenring 21 durch setzt. Hat der Formkern 11 bei dieser Bewegung nach oben die gewünschte, eingestellte Höhe erreicht, so wird die Schnellspannvorrichtung 25 der Abstützvorrichtung 23 be tätigt und darüber der Anschlagring 24 am Formkern 11 fest gespannt. Anschließend wird der Formkern 11 mit daran festem Anschlagring 24 und aufliegendem Bodenring 21 nach oben in die obere Endstellung bewegt. Der Formmantel 18 wird nach unten in seine untere Endstellung bewegt. Nun beginnt der normale Füll- und Verdichtungsvorgang mit Her stellung des Betonteiles 12. Nach dem Formgebungsprozeß wird zum Entformen der Formmantel 18 nach oben und der Formkern 11 mit daran festgespanntem Anschlagring 24 und aufliegendem Bodenring 21 und Betonteil 12 nach unten bis hin zur stationären Ausstoßplatte 35 bewegt. Sitzen diese Teile auf der Ausstoßplatte 35 auf, wird der Spannantrieb 26 betätigt und somit der Anschlagring 24 in bezug auf den Formkern 11 entspannt.In another exemplary embodiment, not shown, the same shaping device 10 can be used practically in kinematic reversal and approximately as follows. In a departure from the first exemplary embodiment, the ejection device 34 with the ejection plate 35 is arranged stationary here. At the beginning of the molding cycle, the stop ring 24 is placed on the stationary ejection plate 35 with the base ring 21 resting thereon. Then you move the mandrel 11 relative to it up to the desired height, the mandrel 11 through the opening 36 of the ejection plate 35 and also the stop ring 24 and the bottom ring 21 through. If the mandrel 11 has reached the desired, set height during this upward movement, the quick-release device 25 of the support device 23 is actuated and the stop ring 24 is firmly clamped to the mandrel 11 . Subsequently, the mandrel 11 with the stop ring 24 fixed thereon and the base ring 21 resting thereon is moved upward into the upper end position. The shaped jacket 18 is moved down to its lower end position. Now the normal filling and compaction process begins with the position of the concrete part 12 . After the shaping process, the mold jacket 18 is moved upwards and the mold core 11 with the stop ring 24 clamped thereon and the base ring 21 and the concrete part 12 resting thereon is moved downwards to the stationary ejection plate 35 . If these parts are seated on the ejection plate 35 , the tensioning drive 26 is actuated and the stop ring 24 is relaxed with respect to the mold core 11 .

Bei dem in Fig. 5 gezeigten zweiten Ausführungsbeispiel sind für die Teile, die dem ersten Ausführungsbeispiel entsprechen, um 100 größere Bezugszeichen verwendet, so daß dadurch zur Vermeidung von Wiederholungen auf die Beschreibung des ersten Ausführungsbeispieles Bezug ge nommen ist.In the second exemplary embodiment shown in FIG. 5, 100 larger reference numerals are used for the parts which correspond to the first exemplary embodiment, so that reference is made to the description of the first exemplary embodiment in order to avoid repetition.

In Fig. 5 ist die Ausstoßvorrichtung 134 mit solchen nach innen gerichteten Stützteilen 138 versehen, die radial wahlweise entweder in die in Fig. 5 gezeigte Unter greifungsstellung oder zurück in ihre Freigabestellung bewegbar sind. Die Mitnehmer 138 sind in der Untergreifungs stellung soweit nach innen ausgefahren, daß sie in dieser Stellung den Anschlagring 124 im Bereich des ringförmigen Zentriervorsprunges 131 formschlüssig von unten unter greifen können, wie dies beim ersten Ausführungsbeispiel durch den Flansch 37 der Ausstoßplatte 35 geschieht. In der zurückgezogenen Freigabestellung dagegen ragen die Mitnehmer 138 nicht in den Bereich des Anschlagringes 124 hinein, so daß dieser damit von der Ausstoßvorrichtung 134 freigegeben ist. Die Mitnehmer 138 weisen einen druckmittelbetriebenen Antrieb 139, insbesondere einen Hydraulikzylinder, auf, mittels dessen sie in die Unter greifungsstellung (Fig. 5) ausschiebbar bzw. gegensinnig bewegbar sind. Beim gezeigten Ausführungsbeispiel sind die Antriebe 139 fest an der Unterseite der Ausstoßplatte 135 angebracht, wobei die Mitnehmer 138 unmittelbar durch das freie Ende der ausfahrbaren Kolbenstange jedes Antriebs 139 gebildet sind. Dies ist besonders einfach. Bei einem anderen, nicht gezeigten Ausführungsbeispiel arbeiten die Antriebe 139 statt dessen auf entsprechende Mitnehmer 138, die translatorisch bewegbar oder statt dessen schwenk bar sind. In Fig. 5, the ejection device 134 is provided with such inwardly directed support members 138 which can be moved radially either in the gripping position shown in Fig. 5 under or back to its release position. The drivers 138 are in the under-gripping position so far extended that in this position they can engage the stop ring 124 in the area of the annular centering projection 131 positively from below, as happens in the first embodiment through the flange 37 of the ejection plate 35 . In the retracted release position, however, the drivers 138 do not protrude into the area of the stop ring 124 , so that it is thus released by the ejection device 134 . The drivers 138 have a pressure medium-operated drive 139 , in particular a hydraulic cylinder, by means of which they can be pushed out or moved in opposite directions in the lower engagement position ( FIG. 5). In the exemplary embodiment shown, the drives 139 are fixedly attached to the underside of the ejection plate 135 , the drivers 138 being formed directly by the free end of the extendable piston rod of each drive 139 . This is particularly easy. In another embodiment, not shown, the drives 139 instead work on corresponding drivers 138 which can be moved in translation or can be swiveled instead.

Beim zweiten Ausführungsbeispiel gemäß Fig. 5 kann somit die Abstützvorrichtung 123 von den radial in ihre Unter greifungsstellung bewegbaren Mitnehmern 138 der Ausstoß vorrichtung 134 untergriffen und formschlüssig erfaßt werden, wobei die Mitnehmer 138 nach Wunsch mechanisch zwischen der Untergreifungsstellung und Freigabestellung bewegbar sind, so daß diese Betätigung ebenfalls fern steuerbar ist und in den automatischen Fertigungsprozeß integrierbar ist. Dies ist vor allem dann vorteilhaft, wenn mittels der Formeinrichtung 110 eine Vielzahl von Betonteilen mit jeweils gleicher Bauhöhe gefertigt werden soll und dazu der Anschlagring 124 in der einmal einge stellten Höhenlage verbleiben kann. Die Mitnehmer 138 werden mittels ihrer Antriebe 139 somit nur dann in die nach innen ausgefahrene Untergreifungsstellung gemäß Fig. 5 bewegt, wenn eine Änderung der Höhenposition des Anschlagringes 124 notwendig ist, was in gleicher Weise dann durch Höhenverstellung der Ausstoßplatte 135 ge schieht. Ist die Sollhöhe des Anschlagringes 124 dagegen eingestellt und kann diese so verbleiben, werden die Mit nehmer 138 nach außen in die Freigabestellung bewegt, so daß sie nicht mehr in den Bereich des Anschlagringes 124 gelangen, wenn beim automatischen Formgebungsprozeß die Ausstoßvorrichtung 134 in üblicher Weise zum Absenken des eingelegten Bodenringes 121 und gegensinnig zum Aus stoßen betätigt wird.In the second embodiment shown in FIG. 5, the support device 123 can thus engage under radially into their greifungsstellung movable pushers 138 of the ejector 134 from the and be detected positively locking, wherein the drivers 138 are such that as desired mechanically between the Untergreifungsstellung and release position is movable, this Operation is also remotely controllable and can be integrated into the automatic manufacturing process. This is particularly advantageous if a large number of concrete parts with the same overall height are to be produced by means of the shaping device 110 and for this purpose the stop ring 124 can remain in the height position once set. The drivers 138 are only moved by means of their drives 139 into the inwardly extended grip position according to FIG. 5 when a change in the height position of the stop ring 124 is necessary, which happens in the same way by adjusting the height of the ejection plate 135 . On the other hand, if the target height of the stop ring 124 is set and this can remain so, the participants 138 are moved outward into the release position so that they no longer reach the area of the stop ring 124 when the ejection device 134 is used in the usual manner for the automatic shaping process Lowering the inserted floor ring 121 and pushing in opposite directions is pushed.

Beim dritten Ausführungsbeispiel gemäß Fig. 6 ist die Formeinrichtung 210 nicht mit einer Ausstoßvorrichtung ver sehen, über die die Höhenverstellung der Abstützvorrichtung 223 erfolgten könnte. Statt dessen erfolgt hier die Höhen verstellung der Abstützvorrichtung 223 durch den Form mantel 218, über den die Entformung des gefertigten Beton teiles 212 vorgenommen wird. Der Formmantel 218 hat hier zu am z.B. unteren Endbereich nach innen ausfahrbare bzw. gegensinnig zurückfahrbare Riegel 240, die zum Entformen weit genug ausgefahren werden, damit sie beim Hochfahren des Formmantels 218 dann unter den äußeren Ringteil 233 des unteren Bodenrings 221 fassen und diesen mitsamt darauf lastendem Betonteil 212 beim weiteren Hochfahren des Form mentels 218 vom Anschlagring 224 abheben und nach oben be wegen können.In the third embodiment according to FIG. 6, the shaping device 210 is not seen with an ejection device via which the height adjustment of the support device 223 could take place. Instead of this, the height adjustment of the support device 223 takes place through the shaped jacket 218 , via which the demolding of the finished concrete part 212 is carried out. The shaped jacket 218 here has latches 240 which are extendable inwards or in opposite directions at the lower end region, for example, and which are extended far enough for removal from the mold so that when the shaped jacket 218 is raised, they then grip under the outer ring part 233 of the lower bottom ring 221 and this together with it the load-bearing concrete part 212 when the form element 218 is raised further off the stop ring 224 and be able to move upwards.

Soll gemäß Fig. 6 der Anschlagring 224 in Höhenrichtung in Anpassung an die jeweils gewünschte Höhe des zu fertigenden Betonteiles 212 verstellt werden, so wird der Anschlagring 224 dazu in Bezug auf den Formkern 211 entspannt und statt dessen am Formmantel 218 festgespannt. Dies wird nachfolgend näher erläutert.Target of FIG. 6, the stop ring will be adjusted to be manufactured concrete part 212 224 in the height direction in adaptation to the desired height, the stop ring 224 is relaxed to with respect to the mandrel 211 and clamped instead in the mold shell 218th This is explained in more detail below.

Der Anschlagring 224 ist hier in Querrichtung des Formraumes 219 gesehen so bemessen, daß er dessen Breite zumindest im wesentlichen ausfüllt. Der Anschlagring 224 als ringsum ge schlossener und vorzugsweise metallischer Ring ausgebildet. Sowohl auf der Seite, die dem Formkern 211 zugewandt ist, als auch auf der Seite, die dem Formmantel 218 zugewandt ist, ist der Anschlagring 224 mit einer z. B. etwa U-förmigen, zur Seite hin offenen Aufnahme 241 bzw. 242 versehen, in der je weils ein Preßring 243 bzw. 244 gehalten ist. Ist der Form kern 211 analog dem ersten Ausführungsbeispiel mit einem Kernsegment für die Direkteinrüttlung von Steigeisen vorgesehen, erstreckt sich der Preßring 243 nicht über den gesamten Umfang des Formkernes 211 sondern nur über einen Umfangsteil, wobei der Bereich, auf dem sich das Kernsegment befindet, mit einem mit dem Anschlagring 224 fest verbundenen Metallring statt des Preßringes 243 versehen ist. Jeder Preß ring 243, 244 ist elastisch verformbar. Er besteht z. B. aus Gummi, Kunstgummi, Kunststoff od. dgl. Beim gezeigten Aus führungsbeispiel enthält der Preßring 243 zumindest eine innere Hohlkammer 245, die mittels eines Druckmittels über eine Zuleitung 246 aufblähbar ist. In gleicher Weise enthält auch der andere Preßring 244 zumindest eine innere Hohlkammer 247 mit Zuleitung 248 zum Aufblähen mit Hilfe eines Druck mittels. Das Druckmittel besteht vorzugsweise aus Druckflüs sigkeit, z. B. Hydrauliköl. Im einfachsten Fall ist jeder Preßring 243, 244 als aufblähbarer Schlauch, der die jewei lige Hohlkammer 245 bzw. 247 enthält, ausgebildet.The stop ring 224 is seen here in the transverse direction of the molding space 219 so that it at least substantially fills its width. The stop ring 224 is formed as a closed ge and preferably metallic ring. Both on the side that faces the mold core 211 and on the side that faces the mold shell 218 , the stop ring 224 is provided with a z. B. approximately U-shaped, open to the side receptacle 241 or 242 , in each Weil a press ring 243 or 244 is held. If the mold core 211 is provided analogously to the first exemplary embodiment with a core segment for the direct vibration of crampons, the press ring 243 does not extend over the entire circumference of the mold core 211 but only over a circumferential part, the area on which the core segment is located a metal ring fixed to the stop ring 224 is provided instead of the press ring 243 . Each press ring 243 , 244 is elastically deformable. It consists z. B. from rubber, synthetic rubber, plastic or the like. In the exemplary embodiment shown, the pressing ring 243 contains at least one inner hollow chamber 245 which can be inflated by means of a pressure medium via a supply line 246 . In the same way, the other press ring 244 also contains at least one inner hollow chamber 247 with supply line 248 for inflation by means of a pressure. The pressure medium preferably consists of Druckflüs liquid, for. B. hydraulic oil. In the simplest case, each press ring 243 , 244 is designed as an inflatable tube that contains the respective hollow chamber 245 or 247 .

Der Preßring 243 ist bei darauf von innen her wirkendem Druck des Druckmittels so verformbar, daß er gegen die Außen fläche des Formkerns 211 ringsum gleichmäßig angepreßt wird, wodurch ein ausreichend großer Reibschluß zwischen Preßring 243 und Formkern 211 erzeugt ist, über den der gesamte An schlagring 244 in der jeweils eingestellten Höhenposition fest am Formkern 211 gehalten ist. Ferner bewirkt der auf geblähte Preßring 243 eine Abdichtung im Bereich 249, der aufgrund von Toleranzen und des Spiels zwischen dem Bodenring 221 und der Außenfläche des Formkerns 211 vorhanden ist. Da durch ist vermieden, daß durch den Bereich 249 hindurch nach unten Beton, insbesondere Zementleim, auslaufen kann. Von Vorteil ist außerdem, daß dadurch eine exakte und reproduzier bare Zentrierung des Anschlagringes 224 in Bezug auf den Form kern 211 gewährleistet ist, sowie eine feste und großflächige Verbindung, die eine gute Übertragung von Schwingungen vom Formkern 211 auf den Anschlagring 224 und den darauf auf liegenden Bodenring 221 ermöglicht. Dieser liegt mit dem inneren Ringteil 230 flächig auf dem oberen Auflageteil 229 auf. Außerdem ist der Bodenring 221 im Bereich des Mittel ringteiles 232 über den ringförmigen Zentriervorsprung 231 zentriert, so daß der Bodenring 221 im Formraum 219 repro duzierbar die gleiche Stellung einnimmt und im übrigen sich nicht hin und herbewegen kann. Durch diese Festlegung des Bodenringes 221 im Formraum 219 ist trotz des vorhandenen Spiels zwischen dem Bodenring 221, dem Formmantel 218 und dem Formkern 211 vermieden, daß der Bodenring 221 insbeson dere beim Rüttelvorgang hin und herbewegt wird und am einen oder anderen Teil scheuern kann, was zu Beschädigungen, Ver schleiß oder Zerstörung der einzelnen Teile führen könnte. Der Zentriervorsprung 231 kann noch mit einem Preßring, z.B. analog den Preßringen 243, 244, versehen sein, der ein Span nen von innen nach außen und somit ein kraft- und formschlüs siges Festlegen des Bodenringes 221 ermöglicht. The press ring 243 is deformable with the pressure of the pressure medium acting on it from the inside so that it is pressed uniformly against the outer surface of the mandrel 211 all around, whereby a sufficiently large frictional connection between the press ring 243 and the mandrel 211 is produced, via which the entire impact ring is formed 244 is held firmly on the mold core 211 in the respectively set height position. Furthermore, the inflated press ring 243 effects a seal in the area 249 , which is present due to tolerances and the play between the bottom ring 221 and the outer surface of the mold core 211 . This avoids that concrete, in particular cement glue, can leak down through area 249 . It is also advantageous that this ensures an exact and reproducible centering of the stop ring 224 with respect to the mold core 211 , and a firm and large-area connection, which ensures good transmission of vibrations from the mold core 211 to the stop ring 224 and on it allows lying bottom ring 221 . This lies flat with the inner ring part 230 on the upper support part 229 . In addition, the bottom ring 221 is centered in the area of the middle ring part 232 via the annular centering projection 231 , so that the bottom ring 221 in the mold space 219 reproducibly assumes the same position and cannot otherwise move back and forth. By this determination of the bottom ring 221 in the mold space 219 is avoided despite the existing play between the bottom ring 221 , the mold jacket 218 and the mandrel 211 that the bottom ring 221 is moved back and forth in particular during the shaking process and can chafe on one or the other part of what could lead to damage, wear or destruction of the individual parts. The centering projection 231 can also be provided with a press ring, for example analogous to the press rings 243 , 244 , which allows clamping from the inside out and thus enables a force-locking and positive locking of the base ring 221 .

Der Anschlagring 224 und der aufliegende Bodenring 221 ist während des Rüttel- und Füllvorganges sicher und fest ge halten. Es ist eine gute Übertragung der Schwingungen er reicht. Der Verschleiß ist gering, so daß dadurch die Lebens dauer wesentlich erhöht wird.The stop ring 224 and the overlying base ring 221 is held securely and firmly during the shaking and filling process. It is a good transmission of vibrations. The wear is low, so that the life is significantly increased.

Auch der äußere Preßring 244 ist in gleicher Weise wie der Preßring 243 mittels eines Druckmittels aufblähbar, unter Überbrückung des Zwischenraumes bis hin zur zugewandten Fläche des Formmantels 218, so daß der Preßring 244 fest und zugleich dichtend gegen die zugewandte Fläche des Form mantels 218 anpreßbar ist. Dadurch erfolgt auch im Bereich 250, wo ein Spiel zwischen dem Bodenring 221 und dem Form mantel 218 vorhanden ist, eine Abdichtung. Auf diese Weise liegt der Anschlagring 224 fest zwischen dem Formkern 211 und dem Formmantel 218, so daß Schwingungen darüber gut bis zum Formmantel 218 übertragen werden können. Zugleich ist da durch erreicht, daß der Formmantel 218 in Bezug auf den Form kern 211 jeweils die gleiche Position behält, und zwar bei jedem Arbeitstakt, so daß die Wandstärke des hergestellten Betonteiles 212 reproduzierbar immer die gleiche ist und so mit immer exakt eingehalten werden kann. Die Abstützvorrich tung 223 läßt sich im übrigen sehr schnell ausbauen, reinigen, warten und erforderlichenfalls gegen eine andere ersetzen.The outer press ring 244 can be inflated in the same way as the press ring 243 by means of a pressure medium, by bridging the gap up to the facing surface of the molded jacket 218 , so that the press ring 244 can be pressed firmly and at the same time sealingly against the facing surface of the molded jacket 218 . As a result, there is also a seal in the region 250 , where there is play between the base ring 221 and the shaped casing 218 . In this way, the stop ring 224 is fixed between the mold core 211 and the mold jacket 218 , so that vibrations can be transmitted well to the mold jacket 218 . At the same time it is achieved by the fact that the shaped jacket 218 with respect to the mold core 211 always retains the same position, namely with every working cycle, so that the wall thickness of the concrete part 212 produced is reproducibly always the same and can thus always be exactly maintained . The Ab Stützvorrich device 223 can be very quickly removed, cleaned, maintained and, if necessary, replaced by another.

Am Anschlagring 224 befinden sich zumindest auf der Seite, die dem Formkern 211 zugewandt ist, einzelne vertikale Füh rungsleisten 251, über die der Anschlagring 224 an der zu gewandten Fläche des Formkerns 211 abgestützt ist, so daß dadurch z. B. bei der Höheneinstellung durch Verschieben des Anschlagringes 224 ein etwaiges Schrägstellen dieses verhin dert ist. Die Abstützvorrichtung 223 ist so beschaffen, daß der Preßring 243 an der zugewandten Fläche des Formkernes 211 und der Preßring 244 an der zugewandten Fläche des Formmantels 218 bei jeweils in der Hohlkammer 245 bzw. 247 wirkendem Druck mit Reibschluß und zugleich dichtend anliegen kann, wobei bei Entspannen des Druckes der jeweilige Preßring 243, 244 den Formkern 211 bzw. Formmantel 218 freigibt. Dies er schließt zugleich die Möglichkeit, wahlweise ein hydrau lisches Festspannen entweder nur am Formkern 211 oder nur an dem Formmantel 218 vorzusehen. Durch diese jeweils un abhängige Spannmöglichkeit kann durch die Relativbewegung zwischen Formkern 211 und Formmantel 218 der Anschlagring 224 in Höhenrichtung innerhalb des Formraumes 219 in jede Position gebracht werden. Dies geschieht z. B. folgender maßen. Zunächst stehen beide Preßringe 243, 244 unter Druck und bewirken ein Verspannen des Anschlagringes 224 sowohl am Formkern 211 als auch am Formmantel 218. Sodann wird die Verspannung zwischen dem Formkern 211 und dem Anschlagring 224 gelöst, und zwar durch Druckabbau im Preßring 243. Da mit ist zwischen Formkern 211 und Anschlagring 224 in diesem Bereich ausreichend Bewegungsspiel geschaffen. Der Anschlag ring 224 ist dagegen über den anderen Preßring 244 nach wie vor mit dem Formmantel 218 verspannt. Der Formmantel 218 kann nun nach oben oder nach unten in die jeweils gewünschte Stellung, die der Anschlagring 224 einnehmen soll, mitsamt dem daran verspannten Anschlagring 224 bewegt werden. Ist diese Stellung erreicht, so wird der Preßring 243 wieder mit Druckmittel beaufschlagt und darüber der Anschlagring 224 am Formkern 211 wieder hydraulisch verspannt. Anschließend kann durch Druckabbau im anderen Preßring 244 die dortige Verspannung mit dem Formmantel 218 gelöst werden. Die Beauf schlagung der Preßringe 243, 244 über die jeweilige Zulei tung 246 bzw. 248 ist vom Steuerpult fernsteuerbar, so daß auch diese Funktionen in den automatischen Ablauf integrier bar sind.On the stop ring 224 are at least on the side facing the mandrel 211 , individual vertical Füh approximately strips 251 , via which the stop ring 224 is supported on the facing surface of the mandrel 211 , so that z. B. at the height adjustment by moving the stop ring 224 , any inclination of this is prevented. The support device 223 is designed so that the press ring 243 on the facing surface of the mandrel 211 and the press ring 244 on the facing surface of the mold shell 218 can act in the hollow chamber 245 or 247 with friction and at the same time sealing, whereby at Relaxing the pressure of the respective press ring 243 , 244 releases the mold core 211 or mold shell 218 . This also includes the option of providing a hydraulic clamping either only on the mandrel 211 or only on the form jacket 218 . Through this un-dependent clamping possibility, the stop ring 224 can be brought into any position in the height direction within the molding space 219 by the relative movement between the mold core 211 and the mold jacket 218 . This happens e.g. B. following dimensions. First, both press rings 243 , 244 are under pressure and cause the stop ring 224 to be braced both on the mold core 211 and on the mold jacket 218 . The tension between the mandrel 211 and the stop ring 224 is then released , specifically by reducing the pressure in the press ring 243 . Sufficient movement is created in this area with between the mold core 211 and the stop ring 224 . The stop ring 224 , however, is still clamped over the other press ring 244 with the molded jacket 218 . The outer mold 218 can now upwardly or downwardly into the desired position which is to occupy the stop ring 224 are moved together with the clamped thereto stop ring 224th Once this position has been reached, the pressure ring 243 is again pressurized and the stop ring 224 on the mandrel 211 is hydraulically clamped again. Then, by reducing the pressure in the other press ring 244, the bracing there with the molded jacket 218 can be released. The application of the press rings 243 , 244 via the respective supply line 246 or 248 can be remotely controlled from the control panel, so that these functions can also be integrated into the automatic process.

Bei einem anderen, nicht gezeigten Ausführungsbeispiel sind die Preßringe nicht mit Hohlkammern versehen, sondern aus Vollmaterial gebildet, wobei diese dann mit einer äußeren mechanisch aufgebrachten Preßkraft belastbar sind, die den jeweiligen Preßring verformt und an die jeweilige Fläche anpressen kann. Die äußere Preßkraft kann z. B. über einen hydraulisch betätigten Klappring od. dgl. aufgebracht werden. Auch bei diesem Ausführungsbeispiel bleibt somit zusätzlich zum herstellbaren Reibschluß die Dichtfunktion der Preßringe erhalten.In another, not shown embodiment the press rings are not provided with hollow chambers, but from Solid material formed, which then with an outer mechanically applied pressing force are resilient, the each press ring deformed and to the respective surface can press. The external pressing force can, for. B. over a hydraulically operated folding ring or the like can be applied. This embodiment also remains in this embodiment the sealing function of the press rings for the producible frictional connection receive.

Bei dem in Fig. 7 gezeigten vierten Ausführungsbeispiel ist der Anschlagring 324 auf der dem Formkern 311 zugewandten Seite mit einer metallischen Spannfläche und auf der dem Formmantel 318 zugewandten Seite mit einem elastisch verform baren Preßring 344 versehen. Der Anschlagring 324 ist z.B. so wie beim ersten Ausführungsbeispiel (Fig. 4) zumindest einmal getrennt, wobei im Bereich der Trennstelle zwischen den beiden Enden des Spannringes 324 eine hydraulische Schnellspannvorrichtung analog dem ersten Ausführungsbei spiel wirksam ist, die hydraulisch das Zusammenziehen des Spannringes 324 bzw. Entspannen ermöglicht. In Fig. 7 ist die entspannte Stellung gezeigt, bei der ausreichend Spiel zwi schen Formkern 311 und Anschlagring 324 besteht. Sowohl vor her im am Formkern 311 festgespannten Zustand als auch im gezeigten Zustand gemäß Fig. 7 kann der Anschlagring 324 mit dem äußeren Preßring 344 an der zugewandten Fläche des Form mantels 318 unter Reibschluß und zugleich dichtend anliegen. Im vom Formkern 311 entspannten Zustand gemäß Fig. 7 kann der Anschlagring 324 mit dem äußeren Preßring am Formmantel 318 gespannt gehalten sein. Somit kann auch hierbei der An schlagring 324 durch Höhenverstellung des Formmantels 318 relativ zum Formkern 311 auf die jeweils gewünschte Höhe eingestellt werden. Der besondere Vorteil des vierten Aus führungsbeispiels liegt darin, daß z. B. beim Entspannen des Anschlagringes 324 vom Formkern 311 ein gleichzeitiges Festspannen des Anschlagringes 324 am Formmantel 318 er folgen kann, so daß praktisch nur die Funktion Lösen vom Formkern 311 bzw. Spannen am Formkern 311 zu steuern ist. Der äußere Preßring 344 muß hier nicht unbedingt als mit Hohlkammer versehener und somit von innen her hydraulisch aufblähbarer Spannring ausgebildet sein. Es reicht aus, daß der äußere Preßring 344 für die Phase, bei der das Ent spannen in Bezug auf den Formkern 311 geschieht, einen Reib schluß mit dem Formmantel 318 sichert, um ein Herunter rutschen des Anschlagringes 324 zu verhindern. Die Abstütz vorrichtung 323 macht es also möglich, diese am Formkern 311 festzuspannen und durch Entspannen in Bezug auf den Form kern 311 am Formmantel 318 festzuspannen, so daß darüber die Höhenverstellung erfolgen kann.In the fourth exemplary embodiment shown in FIG. 7, the stop ring 324 is provided on the side facing the mold core 311 with a metallic clamping surface and on the side facing the mold shell 318 with an elastically deformable press ring 344 . The stop ring 324 is, for example, as in the first embodiment (Fig. 4) at least once separated, wherein in the region of the separating point between the two ends of the clamping ring 324 analogously to a hydraulic quick clamping device the first Ausführungsbei game is effective, the hydraulically contraction of the clamping ring 324 or Relaxation allows. In Fig. 7 the relaxed position is shown, in which there is sufficient clearance between the mandrel 311 and stop ring 324 . Both before forth in clamped on the mandrel 311 state and in the state shown in FIG. 7, the stop ring 324 can be connected to the outer press ring 344 against the facing surface of the mold jacket 318 frictionally and sealingly at the same time. In the relaxed state according to FIG. 7 from the mandrel 311 , the stop ring 324 can be held tensioned on the shaping jacket 318 with the outer press ring. Thus, the stop ring 324 can also be adjusted to the desired height by adjusting the height of the mold shell 318 relative to the mold core 311 . The particular advantage of the fourth exemplary embodiment is that z. B. when relaxing the stop ring 324 from the mandrel 311 a simultaneous tightening of the stop ring 324 on the mold jacket 318 he can follow, so that practically only the function of loosening the mandrel 311 or clamping on the mandrel 311 is to be controlled. The outer press ring 344 need not necessarily be designed here as a clamping ring provided with a hollow chamber and thus hydraulically inflatable from the inside. It is sufficient that the outer press ring 344 for the phase in which the Ent tension with respect to the mandrel 311 occurs, a friction circuit with the mold jacket 318 ensures to prevent the stop ring 324 from sliding down. The jacking device 323 thus makes it possible for this to be tightened on the mold core 311 and by expansion with respect to the shape of core 311 on the outer mold 318 to be tightened, so that about the height adjustment can be made.

Beim fünften Ausführungsbeispiel in Fig. 8 weist der An schlagring 424 auf einer Axialseite, und zwar auf der in Fig. 8 nach unten weisenden Seite, Höhenverstellantriebe 452 auf, die einerseits am Anschlagring 224 und andererseits am Formkern 411 abstützbar sind. Alle Höhenverstellantriebe 452 sind gemeinsam an einem unteren Hilfsring 453 abgestützt, der in gleicher Weise wie der darüber befindliche Anschlag ring 324 ausgebildet ist. Er besteht aus einem geschlossenen Metallring 454 mit einem daran gehaltenen, elastisch verform baren Preßring 455 zumindest auf der Seite, die dem Formkern 411 zugewandt ist. Die Höhenverstellantriebe 452 sind als druckmittelbetriebene Arbeitszylinder, insbesondere Hydraulik zylinder, ausgebildet, die zwischen dem Hilfsring 453 und dem darüber befindlichen Anschlagring 424 wirksam sind. Dadurch ist es möglich, die Abstützvorrichtung 423 in Bezug auf den Formkern 411 auf die jeweils gewünschte Höhe einzustellen, ohne daß man hierzu eine vorhandene Ausstoßvorrichtung braucht oder den Formmantel 418 zu Hilfe nehmen muß. Viel mehr kann der Anschlagring 424 am Formkern 411 auf und ab bewegt werden mit gleichzeitiger Spannwirkung. Dies ge schieht folgendermaßen. Zunächst wird der Anschlagring 424 mittels des Preßringes 443 so, wie im Zusammenhang mit Fig. 6 beschrieben wurde, am Formkern 411 festgespannt. Sodann wird der Druck beim unteren Preßring 455 entlastet und somit dieser vom Formkern 411 gelöst. Hiernach werden die einzelnen Höhenverstellantriebe 452 gleichmäßig und gleichzeitig so betätigt, daß darüber der untere Hilfsring 453 in vertikaler Richtung nach oben bewegt wird. Sodann wird der untere Hilfsring 453 am Formkern 411 festgespannt und der Anschlagring 424 vom Formkern 411 gelöst, wie Fig. 8 zeigt. Sodann kann durch Betätigen der Höhenverstellantriebe 452 der Spannring 424 in vertikaler Richtung weiter nach oben verfahren und auf gewünschter Höhe am Formkern 411 festgespannt werden. Ist die Sollhöhe erreicht, so wird zu sätzlich zum Anschlagring 424 auch der untere Hilfsring 453 am Formkern 411 in beschriebener Weise festgespannt, so daß für das Abstützen des darauf lastenden Bodenringes möglichst große Haltekräfte erreicht werden.In the fifth exemplary embodiment in FIG. 8, the stop ring 424 on an axial side, specifically on the side pointing downward in FIG. 8, has height adjustment drives 452 which can be supported on the one hand on the stop ring 224 and on the other hand on the mold core 411 . All height adjustment drives 452 are jointly supported on a lower auxiliary ring 453 , which is formed in the same way as the stop ring 324 above it. It consists of a closed metal ring 454 with an elastically deformable press ring 455 held thereon at least on the side facing the mandrel 411 . The height adjustment drives 452 are designed as pressure-operated working cylinders, in particular hydraulic cylinders, which are effective between the auxiliary ring 453 and the stop ring 424 located above it. This makes it possible to adjust the support device 423 with respect to the mold core 411 to the desired height in each case, without the need for an existing ejection device or without having to use the mold jacket 418 . Rather, the stop ring 424 on the mandrel 411 can be moved up and down with a simultaneous tensioning effect. This happens as follows. First, the stop ring 424 is clamped to the mold core 411 by means of the press ring 443 , as was described in connection with FIG. 6. The pressure on the lower press ring 455 is then relieved and the latter is thus released from the mandrel 411 . Thereafter, the individual height adjustment drives 452 are actuated uniformly and simultaneously so that the lower auxiliary ring 453 is moved upwards in the vertical direction. The lower auxiliary ring 453 is then clamped to the mold core 411 and the stop ring 424 is detached from the mold core 411 , as shown in FIG. 8. Then, by actuating the height adjustment drives 452, the clamping ring 424 can move further upwards in the vertical direction and can be clamped to the mold core 411 at the desired height. If the desired height is reached, in addition to the stop ring 424 , the lower auxiliary ring 453 is also clamped to the mandrel 411 in the manner described, so that the greatest possible holding forces are achieved for supporting the base ring resting thereon.

Das in Fig. 9 gezeigte sechste Ausführungsbeispiel ähnelt demjenigen in Fig. 7. Zusätzlich dazu ist der Anschlagring 524 auf einer Axialseite, und zwar der Unterseite, mit z. B. mehreren Höhenverstellantrieben 552 in Gestalt einzelner vertikal ausgerichteter druckmittelbetriebener Arbeitszylin der 556, insbsondere Hydraulikzylinder, versehen. Die Ar beitszylinder 556 tragen jweils für sich am freien Ende, z. B. am freien Ende der Kolbenstange 557, federnde Druckstücke 558, mit denen diese an der Außenseite des Formkernes 511 mit Reibschluß abstützbar sind. Die Druckstücke 558 können aus Federn und/oder Gummi, Kunststoff, Kunstgummi od. dgl. be stehen. Sie sind entsprechend fest am Kolbenstangenende an gebracht.The sixth exemplary embodiment shown in FIG. 9 is similar to that in FIG. 7. In addition, the stop ring 524 is on one axial side, namely the underside, with e.g. B. several height adjustment drives 552 in the form of individual vertically oriented pressure medium-powered Arbeitszylin the 556 , especially hydraulic cylinders. The Ar beits cylinder 556 wear for themselves at the free end, for . B. at the free end of the piston rod 557 , resilient pressure pieces 558 , with which these can be supported on the outside of the mandrel 511 with friction. The pressure pieces 558 can be made of springs and / or rubber, plastic, synthetic rubber or the like. You are accordingly firmly attached to the end of the piston rod.

Der Anschlagring 524 ist in gleicher Weise wie derjenige nach Fig. 7 metallisch und z. B. einmal getrennt analog Fig. 4 und hierbei mittels einer hydraulischen Schnellspannvorrich tung mechanisch durch Zusammenziehen am Formkern 511 fest spannbar. Auch hier besteht die Möglichkeit der Höhenver stellung über die Arbeitszylinder 556 mit Druckstücken 558, die als Klemmbacken wirksam sind. Der Anpreßdruck der Druck stücke 558 ist so groß, daß das Eigengewicht des Anschlag ringes 524 im gelösten Zustand voll gehalten wird. In dieser Position kann dann der Anschlagring 524 durch Ausfahren der Arbeitszylinder 556 nach oben oder durch Einfahren dieser nach unten bewegt werden, woraufhin der Anschlagring 524 mittels der beschriebenen Schnellspannvorrichtung wieder am Formkern 511 festspannbar ist. Danach können die Arbeits zylinder 556 betätigt und die Druckstücke 558 hydraulisch längs des Kernes 511 verschoben werden, woraufhin ein er neuter Höhenverstellvorgang erfolgen kann. Auch hier ist eine automatische Betriebsweise mit Fernsteuerung vom Steuer pult aus möglich. Der äußere Preßring 544 ist entbehrlich, kann aber eine zusätzliche Abstützung durch Reibschluß am Formmantel 518 bewirken, wobei im übrigen auch ein gestri chelt eingezeichneter Haftring, analog Fig. 7, eine gewisse Haftreibung im entspannten Zustand zwischen dem Anschlagring 524 und der Außenfläche des Formkernes 511 bewirken kann.The stop ring 524 is metallic in the same manner as that in FIGS. 7 and z. B. once separately analog . Fig. 4 and mechanically by means of a hydraulic Schnellspannvorrich device by contracting the mandrel 511 firmly clamped. There is also the possibility of height adjustment via the working cylinder 556 with pressure pieces 558 , which are effective as clamping jaws. The contact pressure of the pressure pieces 558 is so large that the dead weight of the stop ring 524 is kept fully in the released state. In this position, the stop ring 524 can then be moved upwards by extending the working cylinders 556 or downwards by retracting them, whereupon the stop ring 524 can be clamped again on the mold core 511 by means of the described quick clamping device. Then the working cylinder 556 can be operated and the pressure pieces 558 hydraulically moved along the core 511 , whereupon a new height adjustment process can take place. Automatic operation with remote control from the control panel is also possible here. The outer press ring 544 is dispensable, but can cause additional support by frictional engagement on the molded jacket 518 , with the rest also a dashed-line adhesive ring, analogous to FIG. 7, a certain static friction in the relaxed state between the stop ring 524 and the outer surface of the mandrel 511 can effect.

Den Ausführungsbeispielen in Fig. 10-12 ist jeweils ge meinsam, daß der Anschlagring 624 ähnlich Fig. 6 in einer Aufnahme 641 einen Preßring 643 enthält. Der Preßring 643 enthält jedoch keinerlei Hohlkammer, sondern besteht aus Vollmaterial. Dabei versteht es sich, daß der Preßring 643 sich nur auf dem Umfangsbereich des Anschlagringes 624 be findet, der bezüglich des Formkernes nicht einem dortigen ausfahrbaren Teil, insbesondere Kernsegment analog dem ersten Ausführungsbeispiel, zugeordnet ist. Dort, wo beim Formkern das Kernsegment sitzt, ist kein Preßringteil vor handen, sondern statt dessen der Anschlagring 624 metal lisch, so daß eine Beschädigung des Preßringes in diesem Bereich nicht geschehen kann. Der Preßring 643 ist in Fig. 10 an den oben und unten befindlichen Flächen 659, 660 des An schlagringes 624 befestigt, z. B. angeklebt, anvulkanisiert od. dgl. Zwischen der seitlichen Fläche 661 des Anschlag ringes 624 und dem Preßring 643 dagegen besteht keine feste Verbindung. Der Preßring 643 kann zwar an dieser Fläche 661 anliegen oder auch, wie zur Verdeutlichung in Fig. 10 ge zeigt ist, unter Bildung einer Kammer 662 in zumindest ge ringem Abstand davon verlaufen. An den Anschlagring 624 kann über eine schematisch angedeutete, dort eingeschraubte An schlußmuffe 663 und eine Druckmittelleitung Druckmittel in die Kammer 662 oder zumindest zwischen die Fläche 661 und zugewandte Fläche des Preßringes 643 eingeleitet werden, wo durch der Preßring 643 in Fig. 10 nach rechts hin beauf schlagt wird, so daß er sich in dieser Richtung verformen und an dem hier nicht gezeigten Formkern anpressen kann. Es versteht sich, daß in analoger Weise auch beim Ausfüh rungsbeispiel in Fig. 6 der dortige äußere Preßring beschaf fen und gegen den Formmantel in dieser Weise angepreßt wer den kann. Die Ausbildung gemäß Fig. 10 hat den Vorteil, daß die Druckmittelleitung am metallischen Teil des Anschlag ringes 624 und somit zuverlässig, druckdicht und dauerhaft fest angebracht werden kann, der hierzu mit einer Gewinde bohrung versehen ist.The exemplary embodiments in FIGS . 10-12 are each common that the stop ring 624 similar to FIG. 6 contains a press ring 643 in a receptacle 641 . However, the press ring 643 does not contain any hollow chamber, but consists of solid material. It is understood that the press ring 643 is only on the peripheral region of the stop ring 624 be, which is not related to the mold core of an extendable part there, in particular core segment analogous to the first embodiment. Where the core segment sits at the mandrel, there is no press ring part before, but instead the stop ring 624 is metallic, so that damage to the press ring cannot happen in this area. The press ring 643 is fixed in Fig. 10 on the top and bottom surfaces 659 , 660 of the impact ring 624 , z. B. glued, vulcanized or the like. Between the side surface 661 of the stop ring 624 and the press ring 643, however, there is no fixed connection. The press ring 643 can rest against this surface 661 or, as is shown in FIG. 10 for ge clarification, run to form a chamber 662 at least a small distance therefrom. At the stop ring 624 via a schematically indicated, there screwed in connection sleeve 663 and a pressure medium line, pressure medium can be introduced into the chamber 662 or at least between the surface 661 and the facing surface of the press ring 643 , where through the press ring 643 in Fig. 10 to the right Beats beat so that it can deform in this direction and press against the mandrel, not shown here. It goes without saying that in an analogous manner also in the example of the embodiment in FIG. 6, the outer press ring there is obtained and pressed against the molded jacket in this way who can. In the formation of FIG. 10 has the advantage that the pressure medium line to the metallic part of the stop ring 624 and thus reliable pressure-tight manner and can be permanently fixedly mounted, which is provided for this purpose with a threaded hole.

Bei dem achten Ausführungsbeispiel in Fig. 11 ist zusätzlich zum siebten Ausführungsbeispiel gemäß Fig. 10 der Preßring 743 auf der in Fig. 11 rechten Seite oben und unten über Stützringe 764, 765 abgestützt, die die Befestigung im Be reich der Flächen 759, 760 bei Druckbeaufschlagung und Ver formung des Preßringes 743 entlasten. Die Stützringe 764,765 können mit dem Anschlagring 724 auch einstückig sein.In the eighth exemplary embodiment in FIG. 11, in addition to the seventh exemplary embodiment according to FIG. 10, the press ring 743 is supported on the right side in FIG. 11 above and below by means of support rings 764 , 765 which support the fastening in the areas 759 , 760 Relieve pressure and deformation of press ring 743 . The support rings 764 , 765 can also be in one piece with the stop ring 724 .

Beim neunten Ausführungsbeispiel in Fig. 12 hat der Anschlag ring 824 im Querschnitt etwa Schwalbenschwanzprofil, wobei die beiden Ringschenkel 866, 867 durch die zusammen gebildete, zumindest schwache Keilform eine formschlüssige Abstützung des Preßringes 843 und somit Entlastung der Befestigungsstel len bewirken.In the ninth embodiment in Fig. 12, the stop ring 824 in cross-section approximately dovetail profile, the two ring legs 866 , 867 by the together formed, at least weak wedge shape cause a positive support of the press ring 843 and thus relieve the fastening Stel len.

Claims

1. A method for producing concrete parts in a mold which has a mold core ( 11 ), a lower base ring ( 21 ) which can be supported on a support device ( 23 ) and a mold shell ( 10 ), the base ring ( 21 ) relative to the mold core ( 11 ) is continuously adjusted to a height adapted to the height of the concrete part ( 12 ) to be manufactured and is fixed to the mold core ( 11 ) by means of the support device ( 23 ), characterized in that the support device ( 23 ; 123 ; 223 ; 323 ; 423 ; 523 ) mechanically adjusts to the desired height relative to the mandrel by means of external force.

2. The method according to claim 1, characterized in that the support device ( 23 ) by means of a quick release device ( 25 ) in the respectively set height on the mandrel ( 11 ) clamped and solved for adjustment against sensible.

3. The method according to claim 1 or 2, characterized in that the supporting device ( 23 ; 123 ; 223 ; 323 ; 423 ; 523 ; 623 ) is hydraulically clamped to the mold core.

4. The method according to any one of claims 1-3, wherein the support device has a stop ring, characterized in that the stop ring ( 24 ; 124 ; 224 ; 324 ; 424 ; 524 ; 624 ) is substantially uniform, for. B. by means of at least one hydraulic cylinder acting thereon, clamped radially on the mandrel.

5. The method according to any one of claims 1-4, characterized in that the Abstützvorrich device ( 23 ) by means of external hoists, for. B. by means of a crane, a stacker or the like. Moved up and down relative to the mandrel and adjusted to the desired height before tightening.

6. The method according to any one of claims 1-4, with a pushing device ( 34 ) for the base ring ( 21 ), characterized in that the support device ( 23 ) by means of the pushing device ( 34 ) relative to the mold core ( 11 ) and moves and adjusts to the desired height before tightening.

7. The method according to claim 6, characterized in that one engages under the support device ( 23 ) with at least one support part ( 37 ) of the ejection device ( 34 ) and height-adjusted relative to the mandrel ( 11 ).

8. The method according to claim 7, characterized in that the support device ( 23 ) by means of the ejection device ( 34 ) on the preferably stationary Ren mold core ( 11 ) is moved relative to it in the desired height position downward, then the support device ( 23 ) on Mold core ( 11 ) is clamped and then the ejection device ( 34 ) and the mold jacket ( 18 ) are lowered into the lowest position relative to the mold core ( 11 ).

9. The method according to claim 8, characterized in that after the shaping process in the form of the mold jacket ( 18 ) and the ejector ( 34 ) are raised until the ejector ( 34 ) with the bottom ring ( 21 ) and concrete part ( 12th ) the support device ( 23 ) engages under that the support device ( 23 ) is then relaxed in relation to the mandrel ( 11 ) and that the ejection device ( 34 ) together with the support device ( 23 ) and the overlying base ring ( 21 ) and loading clay part ( 12 ) continue to be raised to the top demolding position.

10. The method according to claim 6 or 7, characterized in that the support device ( 23 ) with the overlying base ring ( 21 ) on the stationary Ausoßvor direction ( 34 ), that then the mold core ( 11 ) re relatively to the desired Height moves upward, which passes through the ejection device ( 34 ) with support device ( 23 ) and base ring ( 21 ), that then the support device ( 23 ) is clamped on the mold core ( 11 ), that afterwards the mold core ( 11 ) with support device ( 23 ) and the overlying base ring ( 21 ) are moved upwards into the upper end position and the molded casing ( 18 ) and the lower end position.

11. The method according to claim 10, characterized in that after the shaping process in the form of the mold shell ( 18 ) upwards and the mandrel ( 11 ) with support device ( 23 ), overlying base ring ( 21 ) and Be clay part ( 12 ) after down to the stationary Ausoßvorrich device ( 34 ) are moved and then the support device ( 23 ) in relation to the mold core ( 11 ) is relaxed.

12. The method according to any one of claims 6-11, characterized in that one engages under the support device ( 23 ) with a flange ( 37 ) of the ejection device ( 34 ) in a form-fitting manner.

13. The method according to any one of claims 6-11, characterized in that for supporting the height adjustment, the support device ( 123 ) engages with drivers ( 138 ) which can be moved radially into their gripping position as support parts on the ejection device ( 134 ), the drivers ( 138 ) can optionally be moved from this under-gripping position into a release position which does not engage under the support device ( 123 ) and back into the under-gripping position.

14. The method according to claim 13, characterized in that the movable driver ( 138 ) mechanically, in particular by means of pressure medium-operated translation drives ( 139 ), operated.

15. The method according to any one of claims 1-4, characterized in that the support device ( 223 ; 323 ; 523 ) on the mandrel ( 211 ; 311 ; 511 ) and at the same time from the inside to the outside of the mold jacket ( 218 ; 318 ; 518 ) or either on the mold core ( 211 ; 311 ; 511 ) or mold jacket ( 218 ; 318 ; 518 ).

16. The method according to claim 15, characterized in that with the support device ( 223 ; 323 ; 523 ) the mold space on the underside of the overlying base ring ( 221 ) at least essentially completely closes and against the mold core ( 211 , 311 ; 511 ) and / or form jacket ( 218 ; 318 ; 518 ) seals.

17. The method according to claim 15 or 16, characterized in that the support device ( 223 ) along vertical surface lines of the mold jacket ( 218 ) and / or mold core ( 211 ) and supports against tilting.

18. The method according to any one of claims 15-17, characterized in that the support device ( 323 ) on the mandrel ( 311 ) is clamped and by Ent clamp with respect to the mandrel ( 311 ) on the mold jacket ( 318 ) and vice versa.

19. The method according to any one of claims 15-18, characterized in that the support device ( 223 ; 323 ) ent in relation to the mold core ( 211 ; 311 ) and clamped on the mold jacket ( 218 ; 318 ) and by adjusting the height of the mold jacket ( 218 ; 318 ) relative to the mold core ( 211 ; 311 ) at the desired height and the support device ( 223 ; 323 ) on the mold core ( 211 ; 311 ) again tightened and relaxed in relation to the mold jacket ( 218 ; 318 ).

20. The method according to any one of claims 15-18, characterized in that the Abstützvorrich device ( 423 ; 523 ) with respect to the mandrel ( 411 ; 511 ) by means of at least one integrated height adjustment drive ( 452 ; 552 ) height, which on the one hand on the mold core ( 411 ; 511 ) and on the other hand on the support device ( 423 ; 523 ).

21. Device for the production of concrete parts, in particular for carrying out the method according to claim 1 or fol lowing, in particular of concrete pipes, yard or street runs, manhole rings, manhole necks or the like., In a form that a mold core ( 11 ), one on a support device supportable lower base ring ( 21 ) and a molded casing ( 18 ), the base ring ( 21 ) relative to the mold core ( 11 ) steplessly adjustable to a height of the respective concrete part ( 12 ) to be adjusted height and on the mold core ( 11 ) can be fixed by means of the support device ( 23 ), characterized in that the support device ( 23 ; 123 ; 223 ; 323 ; 423 ; 523 ) conforms to the circumferential contour and size of the mandrel ( 11 ; 111 ; 211 ; 311 ; 411 ; 511 ) adapted, radially clampable, circular or polygonal stop ring ( 24 ; 124 ; 224 ; 324 ; 424 ; 524 ; 624 ; 724 ; 824 ) with a pressure medium-operated, especially hydraulic, quick clamping device seal ( 25 ), by means of which the stop ring ( 24 ; 124 ; 224 ; 324 ; 424 ; 524 ; 624 ; 724 ; 824 ) can be mechanically clamped on the outer surface of the mandrel ( 11 ; 111 ; 211 ; 311 ; 411 ; 511 ) or can be relaxed in relation to the mandrel.

22. The device according to claim 21, characterized in that the stop ring ( 24 ) to the outside from protruding projections ( 31 ), in particular a flange, has, of the inwardly directed support parts ( 37 ) of an ejection device ( 34 ), in particular ejection plate ( 35 ), are accessible.

23. The device according to claim 22, characterized in that the inward support parts of the ejection device ( 34 ), in particular ejection plate ( 35 ), are formed from individual segments or a flange ( 37 ) GE.

24. The device according to claim 22, characterized in that the inwardly directed support parts of the ejection device ( 134 ) as a radially selectively in their under-gripping position or back in their stop ring ( 124 ) releasing release position movable driver ( 138 ) are formed which the ejection device ( 134 ) are held.

25. Device according to claim 24, characterized in that the drivers ( 138 ) have a pressure-operated drive ( 139 ), in particular a hydraulic cylinder, by means of which they can be moved into the lower position or in the opposite direction into the release position.

26. Device according to one of claims 21-25, characterized in that the stop ring ( 24 ; 124 ; 224 ) has an upper support part ( 29 ; 229 ) on which the lower base ring ( 21 ; 221 ) with its inner ring part ( 30 ; 230 ) rests.

27. Device according to one of claims 21-26, characterized in that the stop ring ( 24 ; 124 ; 224 ) has one or more transversely projecting centering projections ( 31 ; 131 ; 231 ) on which the lower base ring ( 21 ; 121 ; 221 ) with its vertical, between the inner ring part ( 30 ; 230 ) and the outer ring part ( 33 ; 233 ) duri fenden middle ring part ( 32 ; 232 ) under coaxial centering tion.

28. The device according to claim 27, characterized by a single circumferential centering ring ( 31 ; 131 ; 231 ), which preferably has a press ring which is elastically deformable at least on peripheral regions.

29. Device according to one of claims 21-28, characterized in that the stop ring ( 24 ; 124 ; 224 ; 324 ; 424 ; 524 ; 624 ; 724 ; 824 ) is formed from a metal ring, in particular a steel ring.

30. Device according to one of claims 21-29, characterized in that the stop ring ( 24 ; 124 ; 324 ; 524 ) is divided at least at one point and at the two ends ( 27 , 28 ) of this separation point a pressure medium operated tensioning drive ( 26th ), in particular hydraulic cylinder, acts as a quick release device ( 25 ).

31. The device according to claim 30, characterized in that the hydraulic cylinder ( 26 ) is double-acting.

32. Device according to claim 30, characterized in that the hydraulic cylinder is single-acting and the clamping force-actuated against spring force, for. B. causes the internal stress of the stop ring ( 24 ; 124 ; 324 ; 524 ) or additional springs, while the relaxation takes place due to the spring force.

33. Device according to one of claims 21-32, characterized in that the stop ring ( 224 ; 324 ; 524 ) extends at least over a substantial part of the mold space width between the mold core ( 211 ; 311 ; 511 ) and the mold jacket ( 218 ; 318 ; 518 ) extends.

34. Device according to one of claims 21-29, characterized in that the stop ring ( 224 ; 424 ; 624 ; 724 ; 824 ) is closed all around.

35. Device according to one of claims 21-34, characterized in that the stop ring ( 224 ; 324 ; 424 ; 524 ; 624 ; 724 ; 824 ) on its the shaped jacket ( 218 ; 318 ; 418 ; 518 ) and / or the mold core ( 211 ; 311 ; 411 ; 511 ) facing at least on the circumference areas that are assigned to non-retractable parts, such as core segments ( 15 ) or the like, of the mold core, at least one elastically deformable press ring ( 243 , 244 ; 344 ; 443 ; 544 ; 643 ; 743 ; 843 ).

36. Device according to one of claims 28-35, characterized in that the respective press ring ( 243 , 244 ; 344 ; 443 , 455 ; 544 ; 643 ; 743 ; 843 ) consists of rubber, synthetic rubber, plastic or the like .

37. Device according to claim 35 or 36, characterized in that the press ring ( 243 ; 244 ; 344 ; 443 , 455 ; 544 ; 643 ; 743 ; 843 ) with pressure acting thereon with friction and at the same time sealing on the facing surface of the Sheath ( 218 ; 318 ; 418 ; 518 ) or the mold core ( 211 ; 311 ; 411 ; 511 ) is present and releases the mold shell or mold core when the pressure is released.

38. Device according to one of claims 35-37, characterized characterized in that the press ring with a outer, e.g. B. mechanically applied, pressing force bar that can deform and press the press ring.

39. Device according to one of claims 35-38, characterized in that the press ring ( 243 , 244 ; 344 ; 443 , 455 ; 544 ; 643 ; 743 ; 843 ) with the pressure of a pressure medium, for. B. a hydraulic fluid, is resilient, which can deform and press the press ring.

40. Device according to claim 39, characterized in that the elastically deformable press ring ( 543 ; 743 ; 843 ) on a support ring ( 624 ; 724 ; 824 ) is ge, z. B. with two surfaces ( 659 , 660 ; 759 , 760 ), and with a third surface and adjoin the surface ( 661 ) of the carrier ring ( 624 ; 724 ; 824 ) limits a pressure camera ( 662 ) which can be fed with pressure medium.

41. Device according to one of claims 35-39, characterized in that the press ring ( 243 , 244 ; 344 ; 443 , 455 ; 544 ) contains at least one inner hollow chamber ( 245 ; 247 ) which is inflatable by means of pressure medium.

42. Device according to claim 41, characterized in that the respective press ring ( 243 , 244 ; 344 ; 443 , 455 ; 544 ) is designed as an inflatable tube with preferably all around leading hollow chamber ( 245 , 247 ).

43. Device according to one of claims 21-42, characterized in that the stop ring ( 224 ) on the mold core ( 211 ) and / or mold shell ( 218 ) side facing individual vertical guide strips ( 251 ) by means of which the stop ring ( 224 ) is supported on the surface of the mold core ( 211 ) or mold shell ( 218 ) that faces towards, against tilting, inclined position or the like.

44. Device according to one of claims 21-43, characterized in that the stop ring ( 324 ; 524 ) on the mold core ( 311 ; 511 ) side facing a metallic clamping surface and on the mold jacket ( 318 ; 518 ) side facing an elastic deformable press ring ( 344 ; 544 ).

45. Device according to claim 44, characterized in that the stop ring ( 324 ; 524 ) in the clamped state on the mold core ( 311 ; 511 ) with its outer press ring ( 344 ; 544 ) at the same time on the molded jacket ( 318 ; 518 ) under frictional engagement and preferably fits tightly.

46. Device according to claim 45, characterized in that the stop ring ( 324 ; 524 ) in the relaxed state of the mold core ( 311 ; 511 ) with its outer press ring ( 344 ; 544 ) on the mold jacket ( 318 ; 518 ) is held taut .

47. Device according to one of claims 21-46, characterized in that the stop ring ( 224 ; 524 ) on one axial side, in particular on its underside, has one or more height adjustment drives ( 452 ; 552 ), which on the one hand on the stop ring ( 424 ; 524 ) and on the other hand on the mandrel ( 411 ; 511 ) can be supported.

48. Device according to claim 47, characterized in that the or the height adjustment drives ( 452 ; 552 ) from pressure medium-operated working cylinders ( 556 ), in particular hydraulic cylinders, are formed.

49. Device according to claim 47 or 48, characterized in that the height adjustment drives ( 452 ) are all supported on a common lower auxiliary ring ( 453 ).

50. A device according to claim 49, characterized in that the lower auxiliary ring (453) is formed in having equivalent manner as the stopper ring (424), in particular as the stop ring (424) has a closed-end metal ring (454) and supported thereon, Elas table deformable press ring ( 455 ) at least on the side facing the mandrel ( 411 ).

51. Device according to claim 47 or 48, characterized in that the height adjustment drives ( 552 ) each carry at their free ends ( 557 ), in particular the free ends of the piston rods, resilient pressure pieces ( 558 ) with which these on the outside side of the mandrel ( 511 ) can be supported with friction.

52. Device according to claim 51, characterized in that the resilient pressure pieces ( 558 ) consist of rubber, plastic, synthetic rubber, springs or the like.