DE2928484B1 - Verfahren zur Herstellung flexibler Schleifmittel - Google Patents

Verfahren zur Herstellung flexibler Schleifmittel

Info

Publication number
DE2928484B1
DE2928484B1 DE2928484A DE2928484A DE2928484B1 DE 2928484 B1 DE2928484 B1 DE 2928484B1 DE 2928484 A DE2928484 A DE 2928484A DE 2928484 A DE2928484 A DE 2928484A DE 2928484 B1 DE2928484 B1 DE 2928484B1
Authority
DE
Germany
Prior art keywords
fabric
abrasive
parts
polyester
abrasives
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
DE2928484A
Other languages
English (en)
Inventor
Guenter Dipl-Chem D Bigorajski
Harald Dipl-Chem Dr Guembel
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ver Schmirgel & Maschf
Original Assignee
Ver Schmirgel & Maschf
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ver Schmirgel & Maschf filed Critical Ver Schmirgel & Maschf
Priority to DE2928484A priority Critical patent/DE2928484B1/de
Priority to FR8010860A priority patent/FR2461553A1/fr
Priority to GB8021033A priority patent/GB2053997B/en
Priority to US06/163,951 priority patent/US4386943A/en
Publication of DE2928484B1 publication Critical patent/DE2928484B1/de
Ceased legal-status Critical Current

Description

Die Erfindung bezieht sich auf ein Verfahren zur Herstellung flexibler Schleifmittel unter Verwendung eines Polyester enthaltenden Trägergewebes.
Zur Herstellung flexibler Schleifmittel auf Gewebeunterlage ist es in der Regel erforderlich, das Trägergewebe vor dem Aufbringen der zur Verankerung der Schleifkörner bestimmten Bindemittelschicht mit einer Appretur zu versehen. Diese Appretur soll mehrere Aufgaben erfüllen: Sie soll dem Rohgewebe eine ausreichende Stabilität und Steifheit geben, der Gewebeoberfläche eine der Größe der aufzubringenden Schleifkörner angepaßte Struktur verleihen, beim fertigen Schleifmittel eine vorgegebene Flexibilität und Dehnung bewirken und eine gute Verankerung der Korn-Bindemittel-Schicht auf dem Gewebe gewährleisten.
Diese Forderungen sind bei Trägergeweben aus Polyester nicht mit den von der Ausrüstung von Baumwollgeweben her bekannten Appreturmassen zu erfüllen. Man greift daher bei der Entwicklung von Schleifmitteln auf Basis von Polyestergeweben auf Erkenntnisse zurück, die in der Gummi-Industrie gewonnen wurden, um -eine gute Haftung zwischen Polyester und Elastomeren zu bewirken.
So schreibt die DE-OS 25 31 642 eine Vorbehandlung des Polyestergewebes mit einem Resorcin-Formaldehyd-Harz vor.
Die DE-OS 26 24 029 beschreibt eine Ausrüstung auf der Basis von Phenol-Formaldehyd-Harzen.
Überraschenderweise ist erfindungsgemäß gefunden worden, daß sich ausgezeichnete Schleifmittel-Trägergewebe herstellen lassen, wenn man auf den Einsatz von Harzen auf der Basis von Phenolen, darunter auch Resorcin, völlig verzichtet und Appreturmassen verwendet, die Amin-Formaldehyd-Harze in hoher Konzentration enthalten.
Diese erfindungsgemäße Arbeitsweise bietet namentlich den Vorteil, die Härtung der Appretur bei wesentlich niedrigeren Temperaturen als bei Verwendung von Phenolharzen mit wirtschaftlich vertretbaren Geschwindigkeiten durchführen zu können.
Ferner wird die Abluft nicht durch Phenole belastet.
Das erfindungsgemäße Verfahren führt zu Schleifmitteln mit geringer Dehnung, benutzt kostengünstigere Rohstoffe; schließlich besitzen die auf dem erfindungsgemäßen Trägergewebe hergestellten Schleifmittel beim Schleifen mit hoher Beanspruchung eine Kornhaftung, die derjenigen von Schleifmitten auf mit Phenolharzen ausgerüsteten Polyestergeweben überle
gen ist.
Die folgenden Beispiele dienen zur Erläuterung der Erfindung.
Beispiel 1
Ein Gewebe aus Polyester-Stapelfasergarn, Bindung Atlas j , 290 g/m2, 37 Fäden/cm in der Kette und 15
Fäden/cm im Schuß, wird mit folgender Mischung to imprägniert:
50 Teile Harnstoff-Formaldehyd-Harz
(Molverhältnis Harnstoff: Formaldehyd = 1:1,8; Wasserverdünnbarkeit 1:4, Festkörpergehalt 80 Gew.-°/o),
J 80 Teile Styrol-Acrylat-Dispersion
(40%ig, Gläsübergangstemperatur + 25° C),
20 Teile Wasser,
0,5 Teile Entschäumer,
und bei 130° getrocknet.
Der Auftrag beträgt 100 g/m2 (trocken).
Anschließend wird ein Rückenstrich aufgebracht, bestehend aus
150 Teilen Imprägniermasse nachobiger Rezeptur
75 Teilen Kaolin,
und bei 130° C getrocknet.
Der Auftrag beträgt 90 g/m2 (trocken).
Aus dem so ausgerüsteten Gewebe wird ein Schleifmittel hergestellt, indem man in üblicher Weise eine Phenol-Harz-Grundbindung aufträgt, mit Schleifkorn, Korngröße 36, elektrostatisch bestreut und eine Deckbindung auf Phenol-Harzbasis aufbringt
Das so erhaltene Schleifmittel besitzt eine Steifigkeit, die im Bereich der als »X-Schleifmittel« bezeichneten Typen liegt. Die relative Dehnung bei einer Belastung von 900 N/5 cm beträgt 1,8%; die Kornhaftung ist so hoch, daß beim Schleifen von Stahlrohren mit einem Anpreßdruck von 35 N kein Kornausbruch eintritt, sondern die Schleif körner bis zum Verstumpfen abgenutzt werden.
Zum Vergleich wurde in gleicher Weise ein Schleifmittel auf einem Polyestergewebe hergestellt, das nach dem in der DE-OS 25 31 642, Beispiel 2, beschriebenen Verfahren unter Verwendung von Phenolharzen ausgerüstet worden war. Während des Trocknens der Ausrüstungsmassen entwichen, wie zu erwarten war, phenolhaltige Dämpfe in die Abluft Die relative Dehnung des fertiggestellten Schleifmittels bei
so 900 N/5 cm betrug 3%, und beim Schleifen von Stahlrohren unter dem obengenannten Anpreßdruck brachen zahlreiche Schleif körner aus, so daß der Schleifversuch vor dem Verstumpfen abgebrochen wurde.
'Beispiel 2
Das in Beispiel 1 genannte Gewebe wird mit folgender Mischung imprägniert:
' 0 53,3 Teile Melamin-Formaldehyd-Harz/Festkörper
gehalt 75%, Viskosität nach
DIN 35211120 Sekunden,
Dichte 1,23 f/cm3, :
80 Teile Styrol-Acrylat-Dispersion/40%ig
Glasübergangstemperatur + 25° C,
16,7 Teile Wasser,
0,5 Teile Entschäumer
und bei 130° C getrocknet.
ORIGINAL INSPECTED
Anschließend wird ein Rückenstrich aufgebracht, bestehend aus
150 Teilen Imprägniermasse nach obiger Rezeptur, 75 Teilen Kaolin
und bei 1300C getrocknet. Der Auftrag beträgt 90 g/m2 (trocken). Die weitere Verarbeitung zum fertigen Schleifmittel geschieht wie in Beispiel 1 beschrieben.
Das Schleifmittel besitzt eine X-Steifigkeit, weist eine Dehnung von 1,6% bei 900 N/5 cm auf, und beim Schleifen von Stahlrohren mit 35 N Anpreßdruck tritt kein Kornausbruch auf.

Claims (2)

Patentansprüche:
1. Verfahren zur Herstellung flexibler Schleifmittel unter Verwendung eines Polyester enthaltenden Trägergewebes, dadurch gekennzeichnet, daß Polyester-Rohgewebe mit einer Masse imprägniert wird, die in der Trockensubstanz mehr als 10 Gew.-°/o eines oder mehrerer Amin-Formaldehyd-Harze enthält, wobei die Auftragsmenge nach dem Trocknen mehr als 20 Gew.-°/o, bezogen auf das Rohgewebe, ausmacht.
2. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß als Amin-Formaldehyd-Harz ein Harnstoff-Formaldehyd-Harz verwendet wird.
DE2928484A 1979-07-14 1979-07-14 Verfahren zur Herstellung flexibler Schleifmittel Ceased DE2928484B1 (de)