DE1089934B - Optisches Kronglas - Google Patents

Optisches Kronglas

Info

Publication number
DE1089934B
DE1089934B DEJ16910A DEJ0016910A DE1089934B DE 1089934 B DE1089934 B DE 1089934B DE J16910 A DEJ16910 A DE J16910A DE J0016910 A DEJ0016910 A DE J0016910A DE 1089934 B DE1089934 B DE 1089934B
Authority
DE
Germany
Prior art keywords
percent
oxides
weight
crown glass
barium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
DEJ16910A
Other languages
English (en)
Inventor
Dr Walter Jahn
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Schott AG
Original Assignee
Jenaer Glaswerk Schott and Gen
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jenaer Glaswerk Schott and Gen filed Critical Jenaer Glaswerk Schott and Gen
Priority to DEJ16910A priority Critical patent/DE1089934B/de
Priority to FR835413A priority patent/FR1264864A/fr
Priority to GB27851/60A priority patent/GB955816A/en
Priority to US50564A priority patent/US3216836A/en
Publication of DE1089934B publication Critical patent/DE1089934B/de
Pending legal-status Critical Current

Description

Die Erfindung bezieht sich auf Kronigläser. extremer optischer Lage, die bei Brechungsindizes zwischen etwa 1,53 und 1,68 eine relativ kleine Dispersion haben. Die Gläser bestehen aus Bororthophosphat (Borphosphc<rsäure), den Porophosphaten des Strontiums!, bzw. Bariums sowie ein· oder mehreren Metalloxy^den. Alle diese Glaskomponenten sind für sich allein keine Glasbildner, sondern erstarren kristallin. Gläsef werden erst durch das Zusammenschmelzen der einzelnen Phosphate und Oxyde in geeigneten Gewichtsverhältnissen erhalten.
Als Phosphatkomponenten lassen sich die Pyrophosphate des Bariums bzw. Strontiums weiterhin durch die betreffenden Meta- "oder Orthophosphate ersetzen. Die resultierenden Gläser zeigen ebenfalls gute optische Eigenschaften.
Die Gläser gemäß vorliegender Erfindung bestehen aus bis zu 78 Gewichtsprozent Bororthophosphat und aus bis zu 48 Gewichtsprozent der Alkalioxyde, Erdalkalioxyde, der Oxyde des Aluminiums, Zinks, Cadmiums, Lanthans, Arsens, Antimons, Bleis und Wismuts, einzeln oder gemeinsam.
Die Gläser gemäß einer weiteren Ausbildung der Erfindung bestehen aus 14 bis 78 Gewichtsprozent Bororthophosphat, 0 bis 84 Gewichtsprozent Barium- und/oder Strontiumpyrophosphat sowie aus 2 bis 48 Gewichtsprozent der Alkalioxyde, Erdalkalioxyde, der Oxyde des Aluminiums, Zinks, Cadmiums, Lan>thans, Arsens, Antimons, Bleis und Wismuts, einzeln oder gemeinsam.
Gemäß der weiterenAusbildung der Erfindung kann der Anteil an Barium- und/oder Strontiumpyrophosphat 'ganz oder teilweise durch Barium- und/oder Strontiumphosphat in Form der Meta- oder Orthoverbindungen ersetzt sein.
Prinzipiell ist zwar die Möglichkeit der Verwendung oxydischer Rohstoffe als Einzelkomponenten zum Herstellen der optischen Gläser möglich, wenn ein ausreichender Überschuß der leicht sublimier- oder verdampfbaren Komponenten zum Gemenge gegeben wird. Die Wahl oxydischer Ausgangsstoffe ist jedoch mit verschiedenen schwerwiegenden Nachteilen be-Optiscb.es Kronglas
Anmelder:
JENAer Glaswerk Schott & Gen.,
Mainz, Hattenbergstr. 10
Dr. Walter Jahn, Mainz-Mombach,
ist als Erfinder genannt worden
züglich der optischen Qualität und der Reproduzierbarkeit der optischen Werte verbunden, da starke Schlierenbildunig auftritt und durch die Neigung des
so Phosphorpentoxyds zur Sublimation und Verdampfung immer Verluste an Substanz eintreten.
Zum Erschmelzen der optischen Gläser gemäß der Erfindung werden wie üblich Rohstoffe eines außerordentlichen Reinheitsgrades innig gemischt und das Gemenge in einen Tiegel gegeben, der seinerseits in einen üblichen Ofen gestellt wind. Als Material für den Schmelztiegel ist Platin geeignet, jedoch können auch andere Materialien Verwendung finden. Zum Erschmelzen der optischen Gläser auf Phosphatbasis gemäß der Erfindung sind Temperaturen von 1200 bis 1300° C nötig. Zur Homogenisierung muß die Schmelze gerührt werden, wobei man während des Rührens die Schmelze zweckmäßig auf etwa 1200 bis 1100° C abkühlen läßt. Nach der Entnahme der Tiegel aus dem Schmelzofen wird das Glas nach Erreichen gewünschter Zähigkeitsgrade in vorgewärmte Formen gegossen, die in übliche Kühlofen übergeführt werden. Das Transformationsgebiet der Gläser liegt zwischen etwa 500 und 600° C.
In den folgenden Tabellen sind Beispiele von Zusammensetzungen von Krongläsern gemäß der Erfindung in Gewichtsprozent angegeben.
Tabelle 1
3968 I 3984 21,37
74,15
4,48
1,6114
64,54		 Nr.
4013 I 4022 | 4032		 19,88
68,99
11,13
1,6236
62,55		 18,84
65,36
15,80
1,6291
61,19		 4141
BPO4
Ba2P2O7
ZnO ,
n,, .' 		29,40
67,12
3,48
1,6024 '■
66,04		 20,46
70,97
8,57
1,6184
63,55		 14,86
71,42
13,72
1,6339
60,65
ν
009 609/189
Tabelle 2
4177 4003 N
4176		 r.
4008		 4020 4023
BPO4
Ba2P2O7
MgO
CaO 		72,41
27,59
1,5314
76,97		 29,16
66,57
4,27
1,6046
66,07		 39,39
50,10
10,51
1,5793
67,55		 33,26
60,44
6,30
1,6019
66,53		 27,71
63,26
9,03
1,6098
65,67		 20,60
71,46
7,94
1,6167
64,42
ν
Tabelle 3
Nr.
4153
4156
4154
4155
4075
4242
BPO4 ..
Ba2P2O7
BaO ....
nd
ν
54,93 16,64 28,43
1,5840 68,56
56,17
43,83
1,5932
67,40
50,13 16,35 33,52
1,5936 67,24
45,48 16,07 38,45
1,6021 66,38
32,52 39,03 28,45
1,6130 65,17
45,64
6,79 47,57
1,6114 64,95
Tabelle 4
Nr.
4158
4039
4066
4048
4068
3938
BPO4 ..
Ba2P2O7
SrO ....
PbO ....
nd
ν
59,51 40,49
1,5826 68,29
33,82
61,45
4,73
1,5995
67,25
35,83 42,99 21,18
1,6033 66,80
29,61 53,82 16,57
1,6093 65,46
17,06
79,06
3,88
1,6129 64,68
21,46 74,43
4,11 1,6160 61,64
Tabelle 5
4228 N
4236 i 4229		 35,48
30,09
34,43
1,6476
57,79		 r.
3971		 3975 3925
BPO4
Ba2P2O7
CdO 		18,29
67,85
13,86
1,6379
60,54		 16,07
76,63
7,30
1,6274
62,31		 29,14
66,54
4,32
1,6003
66,72		 21,53
74,70
3,77
1,6080
65,17		 29,64
67,68
Al2O3
Na2O 		2,68
1,5916
66,26
ν
Tabelle 6
4104 4100 Nr.
4108 I 4111		 20,51
71,15
2,86
5,48
1,6154
64,80		 4278 4285
BPO4
Ba3(PO4),
Ba2P2O7
ZnO 		32,87
44,02
2,22
20,89
1,6146
64,49		 26,41
47,98
17,41
8,20
1,6273
61,42		 34,45
46,11
4,64
14,80
1,6077
66,27		 42,11
40,98
16.91
1,5951
67,06		 41,25
40,36
BaO 18,39
SrO 1,5985
66,51
ν
1 UO3
Tabelle
DM 3706 DM 3722 N
DM 3723		 r.
4279		 4291 4288
BPO4
Ba3(POJ2
Sr(PO3),
Sr3(POJ2
MgO
CaO
ZnO
BaO
CdO 		35
35
30
1,6025
65,67		 18
31
36
15
1,6274
61,49		 50
8
7
35
1,6119
60,04		 41,32
42,04
16,64
1,6045
65,44		 20,47
71,02
8,51
1,5975
65,88		 30,71
55,88
13,49
1,6150
62,55
ν
Tabelle
Nr.
4316
4297
4275 A 4304
4317
4307
BPO4 ... Ba3 (P O4) 2
SrO
Ba(PO3),
CdO
Ba2P2O7 . As2O3 ... Sb2O3 ... Bi2O3 ....
ν
33,00 57,76
9,24
1,6149 64,68
20,98
71,17 7,85
1,6144 63,16
42,11
16,91 40,98
1,5948 67,64 26,43
59,00
14,57
1,6224
53,03
27,72
38,66
33,62
1,6406 58,67
18,97
64,33
16,70
1,6766 46,49

Claims (3)

Patentansprüche:
1. Optisches Kronglas, dadurch gekennzeichnet,
daß es aus bis zu 78 Gewichtsprozent Bororthophosphat und bis zu 48 Gewichtsprozent der Alkalioxyde, Erdalkalioxyde, der Oxyde des Aluminiums, Zinks, Cadmiums, Lanthans, Arsens, Antimons, Bleis und Wismuts, einzeln oder gemeinsam, besteht.
2. Optisches Kronglas nach Anspruch 1, dadurch gekennzeichnet, daß es aus 14 bis 78 Gewichtsprozent Bororthopfaosphat, 0 bis 84 Gewichtsprozent Barium- und/oder Strontiumpyrophosphat sowie 2 bis 48 Gewichtsprozent der Alkalioxyde, Erdalkalioxyde, der Oxyde des Aluminiums, Zinks, Cadmiums, Lanthans, Arsens, Antimons, Bleis und Wismuts, einzeln oder gemeinsam, besteht.
3. Optisches Kronglas nach Anspruch 1 und 2, dadurch gekennzeichnet, daß der Anteil an Barium- und/oder Strontiumpyrophosphat ganz oder teilweise durch Barium- und/oder Strontiumphosphat in Form der Meta- oder Orthoverbindungen ersetzt ist.
© 009 609/189 9.60
DEJ16910A 1959-08-29 1959-08-29 Optisches Kronglas Pending DE1089934B (de)