CZ135296A3 - Plastic material with reduced speed of sulfur intake - Google Patents
Plastic material with reduced speed of sulfur intake Download PDFInfo
- Publication number
- CZ135296A3 CZ135296A3 CZ961352A CZ135296A CZ135296A3 CZ 135296 A3 CZ135296 A3 CZ 135296A3 CZ 961352 A CZ961352 A CZ 961352A CZ 135296 A CZ135296 A CZ 135296A CZ 135296 A3 CZ135296 A3 CZ 135296A3
- Authority
- CZ
- Czechia
- Prior art keywords
- bis
- tert
- butyl
- tetramethyl
- triazine
- Prior art date
Description
Plastická hmota se sníženou rychlostí přijímání síry
Oblast techniky
Vynález se týká plastických hmot se sníženou rychlostí přijímání síry, obsahujících vysokomolekulární stericky bráněný amin.
Dosavadní stav techniky
Podíl plastických hmot, používaných ve volné přírodě, například v zemědělství nebo v zahradnictví, stoupá v posledních letech kontinuálně. Jedná se při tom například o folie pro skleníky, folie pro siláže, folie nebo rohože pro vykládání pro urychlení sklizně a mnoho dalších použití. Jako materiály pro takovéto artikly mohou přicházet v úvahu všechny polymery, které odpovídají určitým požadavkům. Pro tato použití jsouvhodné obzvláště polyolefiny. Polyvinylchlorid (PVC) je vhodný specielně pro folie, prosazuje se však stále více polyethylen (PE) , homopolymery a kopolymery, například s EVA . PE-folie a PP-vlákna, zpracovaná na netkané textilie, se často používají v zemědělství k pokrývání kultur, aby se dosáhlo urychlení sklizně.
Polyolefiny na basi PE- nebo PP-homo- nebo kopolymerů se musí při použití v přírodě stabilisovat přísadami additiv, což se dlouhou dobu provádělo použitím niklových látek potlačujících hoření a UV-adsorbérů. Od počátku osmdesátých let se niklové sloučeniny stále více nahra-. vysokomolekulárními stericky bráněnými aminy (HALS) , ne2 boť pomocí HALS vybavené folie pro zemědělství nebo pro skleníky mají vyšší stabilitu vůči světlu a teplu. Stabilisace plastických hmot pomocí stericky bráněných aminů je popsána v EP 28 318 a EP 402 889 . Jako stav techniky je možno pokládat stabilisaci plastických hmot pomocí stericky bráněných aminů vzorce IV (F. Henninger, E. Pedrazetti, Plasticulture, 80, 1988/4, 5-23) .
Doba životnosti folie (Handbook of Polymer Degradation, Ed. 1, Marcel Dekkar lne., New York, 1992, kapitola 14 ; Aspects of Greenhouse Film Stabilization) závisí jednak na folii samotné (materiál, stabilisace, tloušťka, pigment, plnidlo) a jednak na vnějších vlivech, jako je konstrukce skleníku, klima, jakož i kontakt s chemikáliemi, obzvláště agrochemikáliemi (F. J. Barahona, J. M. G. Vasquez, Plasticulture, 65 /1985/, 3-10) . Chemikálie mohou značně přispívat k urychlení odbourávání takovýchto folii, přičemž se u těchto chemikálií jedná většinou o sloučeniny obsahující síru nebo halogeny. Obzvláště negativní efekt vyplývá ze síru obsahujících sloučenin, jako je například natrium-N-methyldithiokarbamát. Při tom je přímá souvislost mezi množstvím síry, zjištěným ve folii a kvalitou folie, neboť čím vyšší je obsah síry, tím horší je zbývající kvalita folie. Zničené folie se vyznačují extremně vysokým obsahem síry.
Dalšími zdroji síry, které působí na obsah síry v plastické hmotě, je sirovodík, který vzniká z agrochemikálií nebo hnilobných plynů, nebo oxid siřičitý, který vzniká při spalování elementární síry, nebo může pocházet ze vzduchu (kyselé deště) Pokud se týká působení oxidu siřičitého, nejedná se pouze o plastické hmoty specielně v oblasti mědělství, ale zcela obecně výrobků z plastických hmot (fo3 lie, desky, vytlačované výrobky, vlákna) , jakož i z nich vyrobených výrobků, jako jsou pásy, netkané textilie a tkaniny .
Podstata vynálezu
Cílem předloženého vynálezu je nalezení možnosti snížit citlivost plastických hmot vůči působení sloučenin síry (jako jsou například agrochemikálie, sirovodík a oxid siřičitý) . Nyní bylo překvapivě zjištěno, že plastická hmota, která obsahuje specielní HALS-sloučeniny, vykazuje sníženou rychlost přijímání síru obsahujících sloučenin.
Předmětem předloženého vynálezu tedy je plastická hmota, obsahující vysokomolekulární stericky bráněný amin, která jako tento amin obsahuje alespoň jeden amin ze skupiny zahrnuj ící
I. oligomerisovaný 2,2,4,4-tetramethyl-20-(oxiranylmethyl)-7-oxa-3,20-diazadispiro[5.1.11.2]heneikosan-21-on ,
II. kondensační produkt ze 2-chlor-4,6-di-(4-n-butylamíno-1,2,2,6,6-pentamethylpiperidyl) -1,3,5-triazinu a
1,2-bis-(3-aminopropylamio)-ethanu nebo
III. kondensační produkt z 1-hydroxyethyl-2,2,6,6-tetramethyl-4-hydroxypiperidinu a kyseliny jantarové.
Obzvláště vhodná je plastická hmota, která obsahuje alespoň jeden stericky bráněný amin vzorce I , vzorce nebo vzorce III , jakož i aLespoň jeden amin, zvolený ze skupiny zahrnující
IV. kondensační produkt N,N’-bis-(2,2,6,6-tetramethyl-4-piperidyl)-hexamethylendiaminu a 4-terč.-oktylamino-2,6-dichlor-l,3,5-triazinu,
V. kondensační produkt z N,N’-bis-(2,2,6,6-tetramethyl-4-piperidyl)-hexamethylendiaminu a 4-morfolino-2,6-dichlor-1,3,5-triazinu nebo
VI. kondensační produkt 2,4-dichlor-6-(4-n-butylamino-2,2,6,6-tetramethyl-piperidyl)-1,3,5-triazinu a l,2-bis-[3-(4’,6’-di-(4’’-n-butylamino-2’’,2’’,6 ’ ’ ,
6’’-tetramethylpiperidyl)-1’,3’,5’-triayinyl)aminopropylaraino]-ethanu.
Dalším předmětem předloženého vynálezu jsou tvarová tělesa, například folie, desky, extrudované výrobky a vlákna, jakož i z nich vyrobené produkty, jako jsou pásky, tkaniny nebo netkané textilie, vyrobené z plastických hmot podle předloženého vynálezu, specielně z polyolefinů (homopolymera a kopolymery) , obzvláště HDPE , výhodně LDPE (homopolymery a kopolymery) nebo PP , obzvláště výhodně homopolymery a kopolymery s EVA) , LLDPE nebo PP .
Sloučeniny vzorců I., II. nebo III. , jakož i jejich libovolné směsi, také se sloučeninami vzorců IV., V. a/nebo VI. se používají v koncentracích 0,001 až 5 % hmotnostních, obzvláště 0,02 až 1 % hmotnostní, vztaženo na organický materiál a přidávají se před, během nebo po jeho přípravě.
K plastickým hmotám, které se mohou stabilisovat způ5 sobem podle předloženého vynálezu, patří například následuji ící látky :
1. Polymery monoolefinů a diolefinů, například polyethylen vysoké, střední nebo nízké hustoty (který může být popřípadě zesítěný), polypropylen, polyisobutylen, polybuten-1, polymethylpenten-1, polyisopren nebo polybutadien, jakož i polymery cykloolefinů, jako je například cyklopenten nebo norbornen,
2. směsi polymerů, uvedených v odstavci 1. , například směsi polypropylenu s polyethylenem nebo s polyisobutylenem,
3. kopolymery monoolefinů a diolefinů navzájem nebo s jinými vinylmonomery, jako jsou například kopolymery ethylenu a propylenu, propylenu a butenu-1, propylenu a isobutylenu, ethylenu a butenu-l, ethylenu a hexenu, ethylenu a oktenu, propylenu a butadienu, ethylenu a alkylmethakrylátu, ethylenu a vinylacetátu nebo ethylenu a kyseliny akrylové, jakož i terpolymery ethylenu s propylenem a dienem, jako je hexadien, dicyklopentadien nebo ethylidennorbornen.
Organický materiál, stabilisovaný sloučeninami podle předloženého vynálezu může obsahovat popřípadě ještě další additiva, například stabilisátory pro zpracování, antioxidanty, stabilisační prostředky vůči působení světla, akceptory kyselin, desaktivátory kovů, prostředky proti rosení, nukleační činidla, antistatická činidla, prostředky pro zhášení plamene, pigmenty a plnidla.
Antioxidanty a stabilisační prostředky vůči působení světla, které se mohou přidávat vedle sloučenin podle předloženého vynálezu, jsou například sloučeniny na basi stericky bráněných aminů nebo stericky bráněných fenolů nebo deriváty 2-hydroxybenzofenonu nebo 2-(2’-hydroxyfenyl)-benzotriazolu nebo kostabilisátory, obsahující síru nebo dusík nebo fosfor.
Jako takovéto sloučeniny přicházejí například v úvahu. :
1. Antioxidanty
1.1 Alkylované monofenoly, například 2,6 di-terc.-butyl-4-methylfenol, 2-butyl-4,6-dimethylfenol, 2,6-di-terc.-butyl-4-n-butylfenol, 2,6-di-terc-butyl-4-n-butylfenol,
2.6- di-terc.-butyl-4-iso-butylfenol, 2,6-di-cyklopentyl-4-methylfenol, 2-(β-methylcyklohexyl)-4,6-dimethylfenol,
2.6- di-oktadecyl-4-methylfenol, 2,4,6-tricyklohexylfenol,
2.6- di-terc-butyl-4-methoxymethylfenol, 2,6-di-nonyl-4-methylfenol, 2,4-di-methyl-6-(1’-methyl-tridec-1’-yl)-fenol a jejich směsi.
1.2 Alkylthiomethylfenoly, například 2,4-di-oktylthiomethyl-6-terč-butylfenol, 2,4-dioktylthiomethyl-6-methylfenol, 2,4-di-oktylthomethyl-6-ethylfenol, 2,6-di-dodeclythioraethyl-4-nonylfenol.
1.3 Hydrochinony a alkylované hydrochonony, například
2.6- di-terč-butyl-4-methoxyfenol, 2,5-di-terc-butyl-hydrochinon, 2,5-di-terc.-amyl-hydrochinon,
2.6- difenyl-4-oktadecyloxyfenol, 2,6-di-terc.-butyl-hydrochinon, 2,5-di-terc.-butyl-4-hydroxyanisol,
2,5-di-terc.-butyl-4-hydroxyfenyl-stearát, bis-(4,57
-di-terč-butyl-4-hydroxyfenyl)adipát.
1.4 Hydroxylované thiodifenylthery, například 2,2’-thio-bis-(6-terc-butyl-4-methyl-fenol), 2,2’-thio-bis-(4-oktylfenol), 4,4’-thio-bis-(6-terc.-butyl-3-methyl- fenol), 4,4’-thio-bis-(6-terc.-butyl-2-methyl-fenol),
4,4’-thio-bis-(3,6-di-sek.-amyl-fenol),
4,4’-bis-(3,6-dimethyl-4-hydroxyfenyl)-disulfid.
1.5 Alkyliden-bisfenoly, například 2,2’-methylen-bis-(6-terc.-butyl-4-methylfenol), 2,2’-methylen-bis-(6-terc.-butyl-4-ethylfenol), 2,2’-methylen-bis-[4-methyl-6-(β-methylcyklohexyl)-fenol], 2,2’-methylen-bis-(4-methyl-6-cyklohexylfenol),
2,2’-methylen-bis-(6-nonyl-4-methylfenol),
2,2’-methylen-bis-(4,6-di-terc.-butylfenol),
2,2’-ethyliden-bis-(4,6-di-terc.-butylfenol),
2,2’-ethyliden-bis-(6-terc.-butyl-4-isobutylfenol),
2,2’-methylen-bis-[6-(β-methylbenzyl)-4-nonylfenol],
2,2’ -methylen-bis- [6- (β , β-dimethylbenzyl) -4-nonylfenol] ..
4,4’-methylen-bis-(2,6-di-terc.-butylfenol),
4,4’-methylen-bis-(6-terc.-butyl-2-methylfenol),
1,1’-bis-(5-terc.-butyl-4-hydroxy-2-methylfenol)-butan,
2,6-bis-(3-terč.-butyl-5-methyl-2-hydroxybenzyl)-4-methylfenol 1,1,3-tris-(5-terc.-butyl-4-hydroxy-2-methyl-fenyl)-butan,
1.1- bis-(5-terc.-butyl-4-hydroxy-2-methylfenyl)-3-n-dodecyl-merkaptobutan, bis-(3-terč.-butyl-4-hydroxy-5-methyl-fenyl)-dicyklopentadien, bis-[2-(3’-terč.-butyl-2’-hydroxy-5’-methyl-benzyl)6-terc.-butyl-4-methyl-fenyl]-tereftalát,
1.1- bis-(3,5-dimethy1-2-hydroxyfenyl)-butan,
2.2- bis-(3,5-di-terc.-butyl-4-hydroxyfeny1)-propan,
2.2- bls-(5-terc.-butyl-4-hydroxy-2-methylfenol)-4-n8
-dodecylmerkaptobutan,
1,1,5,5-tetra-(5-terč.-buty1-4-hydroxy-2-methylfenol)-pentan.
1.6 0-, N- und S-benzylové sloučeniny, například 3,5,3’,
5’-tetra-terc.-buty1-4,4’-dihydroxydibenzylether, oktadecyl-4-hydroxy-4,5,-dimethylbenzyl-mercaptoacetát, trus-(3,5-di-terc.-butyl-4-hydroxybenzyl)-amin, bis-(3,5-di-terc.-butyl-4-hydroxybenzyl)-sulfid, isooktyl-3,5-di-terc.-butyl-4-hydoxybenzyl-merkaptoacetát.
1.7 Hydroxybenzylované malonáty, například dioktadecyl-2,2-bis-(3,5-di-terc.-butyl-2-hydroxybenzyl)-malonát, di-oktadecyl-2-(3-terc.-butyl-4-hydroxy-5-methylbenzyl)-malonát, didodecylmerkaptoethyl-2,2-bis(3,5-di-terc.-butyl-4-hydroxybenzyl)-malonát.
1.8 Hydroxybenzyl-aromáty, například 1,3,5-tris-(3,5-di-terc.-butyl-4-hydroxybenzyl)-2,4,6-trimethylbenzen, l,4-bis-(3,5-di-terc.-butyl-4-hydroxybenzyl)-2,3,5,6-tetramethy1benzen, 2,4,6-tris-(3,5-di-terc.-buty1-4-hydroxybenzyl)-fenol.
1.9. Triazinové sloučeniny, například 2,4-bís-oktylmerkapto-6-(3,5-di-terc.-butyl-4-hydroxyanilino)-1,3,5-triazin,
2-octylmerkapto-4,6-bis-(3,5-di-terc.-butyl-4-hydroxyanilino) -1,3,5-triazin,
2-octylmerkapto-4,6-bis-(3,5-di-terc.-buty1-4-hydroxyfenoxy)-1,3,5-triazin,
2,4,6-tris-(3,5-di-terc.-buty1-4-hydroxyfenoxy)-1,2,3-triazin,
1.3.5- tris- (3,5-terč . -butyl-4-hydroxybenzy 1) - isoky*'.,·.· ·.; i
1.3.5- tris-(4-terc.-butyl-3-hydroxy-2,6-dimethylbenzyl)9
-isokyanurát, 2,4,6-tris-(3,5-di-terč.-butyl-4-hydroxyfenylethyl)-1,3,5-triazin,
1.3.5- tris-(3,5-di-terč.-butyl-4-hydroxy-fenyl-propionyl)hexahydro-1,3,5-triazin,
1.3.5- tris-(3,5-dicyklohexyl-4-hydroxybenzyl)-isokyanurát.
1.10 Benzylfosfonáty, například dimethyl-2,5-di-terč-bufy1 4-h.ydroxy-benzyl-f osf onát, diethyl-3,5-di-terc . -butyl4-hydroxybenzylfosfonát, dioktadecyl-3,5-di-terc.-butyl4-hydroxybenzylfosfonát, dioktadecyl-5-terc.-butyl4-hydroxy-3-methylbenzylfosfonát, vápenatá sůl monoethylesteru kyseliny 3,5-di-terc.-butyl-4-hydroxybenzylfosfonové.
1.11 Acylaminofenoly, například anilid kyseliny
4-hydroxy-laurové, anilid kyseliny 4-hydroxy-stearové, oktylester kyseliny N-(3,5-di-terc.-butyl-4-hydroxyfenyl)-karbaminové
1.12 Estery kyseliny β-(3,5-di-terc-butyl-4-hydroxyfenyl)-propionové s jednomocnými nebo vícemocnými alkoholy jako s methanolem, ethanolem, oktadekanolem, 1,6-hexandiolem, 1,9-nonandiolem, ethylenglykolem, 1,2-propandiolem, neopentylglykolem, thiodiethylenglykolem, deichylenglykolem triethylenglykolem, pentaerythritolem, tris-(hydroxyethyl)-iso-kyanurátem, diamidem kyseliny N,N’- bis-(hydroxyethyl)-oxalové, 3-thiaunekanolem, 3-thiapenta-dekanolem, trimethylhexandiolem, trimethylolpropanem,
4-hydroxymethyl-l-fosfa-2,6,7-trioxabicyklo-[2,2,2]-oktanem
1.13 Estery kyseliny β-(5-terc-butyl-4-hydroxy-3-methylfenyl)-proionové s jednomocnými nebo vícemocnými alkoh jako například s methanolem, ethanolem, oktadekanolem.
1,6-hexandiolem, 1,9-nonandiolem, ethylenglykolem,
1,2-propandiolem, neopentylglykolem, thiodietyhlenglykolem, diethylenglykolem, triethylenglykolem, pentaerythritolera, tris-(hydroxy)-ethyl-isokyanurátem, triamidem kyseliny N, N’-bis-(hydroxyethyl)-oxalové, 3-thiaundekanolem,
3- thiapentadekanolem, trimethylgexandiolem, trimethylolpropanem, 4-hydroxymethyl-l-fosfa-2,6,7-trioxabicyklo-[2,2,2]-oktanem.
1.14 Estery kyseliny β-(3,5-dicyklohexyl-4-hydroxyfenyl)-propionové s jednomocnými nebo vícemocnými alkoholy, jako například s methanolem, ethanolem, oktadekanolem,
1,6-hexandiolem, thiodiethylenglykolem, diethylenglykolem, triethylenglykolem, pentaerythritolem, tris-(hydroxy)-ethyl-isokyanurátem, diamidem kyseliny N,N’-bis-(hydroxyethyl)-oxylové, 3-thiaundekanolem, 3-thiapenta-dekanolem, trimethylhexandiolem, trimethylolpropanem, 4-hydroxymethyl- 1-fosfa-2,6,7-trioxabicyklo-(2,2,2)-oktanem.
1.15 Estery kyseliny 3,5-di-terc-butyl-4-hydroxyfenyloctové s jednomocnými nebo vícemocnými alkoholy, jako například s methanolem, ethanolem, oktadekanolem,
1,6-hexandiolem, 1,9-nonandiolem, ethylenglykolem,
1,2-propandiolem, neopentylgykolem, thiodiethylen-glykolem, diethylenglykolem, triethylenglykolem, pentaerythriolem, tris-(hydroxy)-ethyl-isokyanurátem, diamidem kyseliny N,N’-bis-(hydroxyethyl)-oxalové, 3-thiaundekanolem, 3-thiapentadekanolem, trimethylhexandiolem, trimethylolopropanem,
4- hydroxymethyl-1-fosfa-2,6,7-trioxabicyklo-[2,2,2]-oktanem
1.16 Estery kyseliny 3,3-bis-(3’-terč.-butyl-4’-hydroxyfeny1)-máselné s jednomocným nebo vícemocnými alkoholy ! například methanolem, ethanolem oktadekanlem, 1,6-hexandio11 lem, 1,9-nonadiolem, ethylenglykolem, 1,2-propandiolem, neopentylhlykolem, thiodiethylenglykolem, diethylenglykolem xriethylenglykolem, pentaerythritolem, tris-(hydroxy)-ethyl- isokyanárátem , diamidem kyseliny N,N’-bis-(hydroxyethyl)-oxalové, 3-thiaundekanolem, 3-thiapentadekanolem, trimethylhexandiolem, trimethylopranem, 4-hydroxyraethyl-l-fosfa-2,6,7-trioxabicyklo-(2,2,2]-oktanem.
1; 17 Amidy kyseliny β-(3,5-di-terc.-butyl-4-hydroxyfenyl)-propionové jako je například N,N’-bis-(3,5-di-terc.-butyj_4_hydroxyfenylpropionyl)-hexamethylendiamin, N,N’-bis-(3,5-di-terc.-buxyl-4-hydroxyfenyl-propionyl)-trimethylendiamin, N,N’-bis-(3,5-di-terc.-buty1-4-hydroxyfenylpropionyl) -hydrazin.
1.18 Hydroxylaminy, jako například dialkylhydroxylaminy, jako je N,N-dibenzylhydroxylamin, N,N-diexhylhydroxylamín,
N,N-dioktyIhydroxylamin, N,N-dilauryl-hydroxylamin,
N,N-ditetradecylhydroxylamin, N,N-dihexadecyIhydroxylamin, N,N-dioktadecylhydroxylamin, N-hexadecyl-N-oktadecylhydroxylamin, N.N-dialkyl-hydroxylamin odvozené od hydrogenovaného talgaminu.
2.0 UV-absorbéry a prostředky pro ochranu vůči působení světla
2.1 2-(2’-hydroxyfenyl)-benztriazoly, jako je například
2-(2’-hydroxy-5’-methylfenyl)-benztriazol,
2-(3’,5’-di-terc.-butyl-2’hydroxyfenyl)-benztriazol,
2-(5’-terč.-butyl-2’hydroxyfenyl)-benztriazol,
2-[2’-hydroxy-5'-(1,1,3,3-tetramethylbutyl)-fenyl]-benztriazol, 2-(3’,5’-di-terc.-butyl-2’hydroxyfenyl)12
-5-chlor-benztriazol,2-(3’-terč. -butyl-2’hydroxy-5’-methylfenyl)-5-chlor-benztriazol,
2-(3’-sek.-butyl-5’-terč.-butyl-2’-hydroxyfenyl)-benztriazol, 2-(2’-hydroxy-4’-oktoxyfenyl)-benztriazol,
2-(3’ ,5’-bis-(β,β-dimethylbenzyl)-2'hydroxyfenyl)-5-chlor-benztriazol, směsi z 2-(3’-terč.-butyl-2’-hydroxy-5’-(2-oktyloxykarbonylethyl)-fenyl)-5-chlor-benztriazolu, 2-(3’-terč-butyl-5’-[2-(2-ethylhexyloxy)-karbonylethyl]-2’-hydroxyfenyl)-5-chlor-benztriazolu,
2-(3 ’ -terč.-butyl-2’-hydroxy-5’-(2-oktyloxykarbonylethyl)fenyl)-benztriazolu, 2-(3’-dodecyl-2’-hydroxy-5’-methylfenyl)-benztriazolu a 2-(-3’-terč.-butyl-2’-hydroxy-5’- (2-isooktylocykarbonylethyl)-fenyl-benzriazolu,
2,2’-methylen-bis-[4-(1,1,3,3-tet ráme thy 1 blity 1) - 6-benztriazol-2-yl-fenol]; reakční produkt z 2-[3’-terč.-butyl-5’-methoxykarbonylethyl)-2’-hydroxy-fenyl]-benztriazolu s polyethylenglykolem 300; [R-Cř^Cl^-COOÍCl·^) 3 ] 2 s R = 3’-terc-butyl-4’-hydroxy-5'-2H-benz-triazol-2-yl-fenyl; [R-G^CF^-COOÍCi^Cí^O) n/2] 2 s n = 1 bis Sas R = 3’-terc-butyl-4’-hydroxy-5’-2H-benztriazol-2-yl-fenyl.
2.2 2-hydroxybenzofenony, jako jsou například 4-hydroxy, 4-methoxy-, 4-oktoxy, 4-decyloxy, 4-dodecyloxy-,
4-benzyloxy-, 4,2’,4’-trihydroxy-, 2’-hydroxy-4,4’-dimethoxy-deriváty.
2.3 Estery popřípadě substituovaných benzoových kyselin, jako je například 4-terc-butylfenylsalicylát, fenylsalicylát, oktylfenyl-salicylát, dibenzoylresorcin, bis-(4-terč.-butylbenzoyl)-resorcin, benzoy1resorcin,
2,4-di-terč.-butylfenylester kyseliny 3,5-di-terč.-butyl-4-hydroxy-benzoové, hexadecylester kyseliny 3,5-di -terč.-butyl-4-hydroxybenzoové, oktadecylester kyseliny
3,5-di-terc.-butyl-4-hydroxybenzoové a 2-methyl-4,6-di-terc.-butylfenylester kyseliny 3,5-di-terc.-butyl-4-hydroxybenzoové.
2.4 Akryláty, jako je například ethylester, popřípadě isooktylester kyseliny 3-kyan-P,β-difenylakrylové, methylester kyseliny β-karbomethoxy-skořicové, methylester, popřípadě butylester kyseliny β-kyano-β-meΐhyl-p-methoxy-skořicové, methylester kyseliny β-karbomethoxy.p-methoxy-skoři cové a N-^-karbomethoxy^-kyanovinyl)-2-methyl-indolin.
2.5 Sloučeniny niklu, jako jsou například komplexy niklu a 2,2’-thio-bis-[4-(1,1,3,3--tetramethylbutyl)-fenolu] , jakož i 1 : 1 nebo 1 : 2 kompex , popřípadě s přídavnými ligandy, jako je n-butylamin, triethanolamin nebo N-cyklohexyl-diethanolamin, nikldibutyldithiokarbamát, soli niklu s monoalkylestery kyseliny 4-hydroxy-3,5-di-terc.-butyl-benzylfosfonové, jako je methylester nebo ethylester, komplexy niklu s ketoximy, jako je 2-hydroxy-4-methyl-fenyl-undecylketoxim a komplexy niklu s l-fenyl-4-lauroyl-5-hydroxy--pyrazolem, popřípadě s přídavnými ligandami.
2.6. Stéricky bráněné aminy, jako je například bis-(2,2,6,6-tetrámethylpiperidyl)-sebakát, bis-(2,2,6,6-tetramethylpiperidyl)-glutarát, bis-(2,2,6,6-tetramethylpiperidyl)-sukcinát, bis-(1,2,2,6,6-pentamethylpiperidyl)-sebakát, bis-(1,2,2,6,6-pentamethylpiperidyl)-glutarát, bis-(1,2,2,6,6-pentamethylpiperidyl)-sebekát, bis-(1,2,2,6,6-pentamethylpiperidyl)-ester kyseliny n-buty1-3,5-di-terc.-butyl-4-hydroxybenzy1-malonové,
2.2.6.6- tetramethylpiperidylbehenát,
1.2.2.6.6- pentamethylpiperidylbehenát, tris-(2,2,6,6-tetramethyl-4-piperidyl)-nitrilotriacetát, tetrakis-(2,2,6,6-tetramethy1-4-p iperidyl)-1,2,3,4-butantetraoát, tetrakis-(1,2,2,6,6-pentamethyl-4-piperidyl)-1,2,3,4-butantetraoát, 1,1’-(1,2-ethandiyl)-bis-(3,5,5,5-tertamethylpiperazinon), 4-benzoyl-2,2,6,6-tetramethyl-piperidin,
4-stearyloxy-l,2,2,6,6-pentamethylpiperidin, 4-stearoyloxy-1,2,2,6,6-pentamethylpiperidin, bis-(1,2,2,6,6-pentamethylpiperidyl)-2-n-butyl-2-(2-hydroxy-3,5-di-terc.-butyl-benzyl) -malonát, bis-(1,2,2,6,6-pentamethylpiperidyl)-2-n-butyl-2-n-butyl-2-(4-hydroxy-3,5-di-terc.-butylbenzyl)-malonát,
3-n-oktyl-7,7,9,9-tetramethyl-l,3,8-triazaspiro [4,5]dekan-2,4-dion, bis-(l-oktyloxy-2,2,6,6-tetramethylpiperidyl-sebakát, bis-(l-oktyloxy-2,2,6,6-tetramethylpiperidyl)-sukcinát, kondensační produkt ze 2-chlor-4,6-di-(4-n-butylamino-2,2,6,6-tetramethylpiperidyl)-1,3,5-triazinu a 1,2-bis-(3-amino-propylamino)-ethanu, kondensační produkt ze 2-chlor-4,6-di-(4-methoxy-propylamino-1,2,2,6,6-pentamethylpiperidyl)--1,3,5-triazinu a 1,2-bis-(3-amino-propylamino)-ethanu, kondensační produkt ze 2-chlor-4,6-di-(4-n-butylamino-1,2,2,6,6-pentamethylpiperidyl)-1,3,5-triazinu a 1,2-bis-(3-aminopropylamino)-ethanu, reakční produkty 2-chlor-4,6-di-(4-n-butylamino-2,2,6,6-tetra-methylpiperidyl)-1,3,5-triazinu s jedno nebo vícemocnými aminy, přičemž na aminu je nahrazen jeden až všechny aktivní vodíkové atomy, jako s ethylen-diaminem, di-ethylentriaminem, triethylentetraminem, hexamethylendiaminem, 1,2-bis-(4-aminopropylamino)-ethanem, reakční produkty 2-chlor-4,6-di-(4-n-butyl-amino-l,2,2,6,6-pentamethylpiperidyl)-1,3,5-triazinu s jedno nebo vícemocnými aminy, přičemž na aminu je nahrazen jeden všechny aktivní atomy, jako s ethylendiaminem, diethylentriaminem, triethylentetraminem, hexa-methylendiaminem, 1,2-bis-(3-aminopropylamino)ethanem, reakční produkty 2-chlor-4,6-di-(4-n-butylamino-2,2,6,6-tetramethylpiperidyl)-1,3,5-triazinu a 4-terc-oktylamino-2,6-dichlor-1,3,5-s-triazinu s jedno nebo vícemocnými aminy, přičemž na aminu je nahrazen jeden až všechny aktivní atomy, jako s ethylendiaminem, diethylentriaminem, triethylentetraminem, hexamethylendiaminem, 1,2-bis-(3-aminopropyl-amino)ethanem, reakční produkty 2-chlor-4,6-di-(4-n-butyl-amino-l, 2,2,6 ,, 6 -pentamethylpiperidyl)-1,3,5-triazinu a 4-terc-oktylamino-2,6-dichlor-l,3,5-s-triazinu s jedno nebo vícemocnými aminy, přičemž na aminu je nahrazen jeden až všechny aktivní atomy, jako s ethylendiaminem, diethylentriaminem, triethylentetraminem, hexamethylendiaminem, 1,2-bis-(3-amino-propylamino)ethanem, reakční produkty 2-chlor-4,6-di-(4-n-butylamino-2,2,6,6 -tetramethylpiperidyl)-1,3,5-triazinu a 4-(4-n-butylamino-2,2,6,6-tetra-methylpiperidyl)-2,6-dichlor-1,3,5-s-triazinu s jedno nebo vícemocnými aminy, přičemž na aminu je nahrazen jeden až všechny aktivní atomy, jako s ethylendiaminem, diethylentriaminem, triethylentetraminem, hexamethylendiaminem,
1.2- bis-(3-aminopropyl-amino)ethanem, reakční produkty 2-chlor-4,6-di-(4-n-butylamino-1,2,2,6,6-pentamethylpiperidyl)-1,3,5-triazinu a 4-(4-n-butylamino-2,2,6,6-tetramethyl-piperidyl)-2,6-dichlor-1,3,5-s-triazinu s jedno nebo vícemocnými aminy, přičemž na aminu je nahrazen jeden až všechny aktivní atomy, jako s ethylendiaminem, diethylentriaminem, triethylentetraminem, hexamethylendiaminem,
1.2- bis-(3-aminopropylamino)ethanem, 3-dodecyl-7,7,9,9 -tetra-methy1-1,3,8-triaza-spiro[4,5]děkan-2,4-dion oligomerisovaný 2,2,4,4-tetra-methyl-20-(oxiranyl-methyl)7-oxa-3,20-diazadispiro[5.1.11.2]heneikosan-21-on, oligomerisovaný 1,2,2,4,4-pentamethyl-20-(ox iranylmethyl)-7-oxa-3,20-diaza-dispiro[5.1.11.2]heneikosan-21-on, oligomerisovaný l-acetyl-2,2,4,4-tetramethyl-20-(oxiranylmethyl) -7-oxa-3,20-diazadispiro[5.1.11.2]heneikosan-21-on, dodecyl-1-(2,2,4,4-tetramethyl-4-piperidyl)-pyrrolidin-2,5-dion, 3-dodecyl-1-(1,2,2,6,6-pentamethyl-4-piperidyl)pyrrolidin-2,5-dion, 2,2,4,4-tetramethyl-7-oxa-3,20-diaza-dispiro-[5.1.11.2]-heneikosan-21-on, dodecylester kyseliny 2,2,4,4-tetramethyl-7-oxa-21-oxo3,20-diaza-dispiro-[5.1.11.2]-heneikosan-3-propanové, tetradecylester kyseliny 2,2,4,4-tetramethyl-7-oxa-21-oxo3,20-diaza-dispiro-[5.1.11.2]-heneikosan-3-propanové,
2.2.3.4.4- pentamethyl-7-oxa-3,20-diaza-dispiro-[5.1.11.2]-heneikosan-21-on, dodecylester kyseliny
2.2.3.4.4- pentamethyl-7-oxa-21-oxo-3,20-diaza-dispiro-[5.1.11.2]-heneikosan-3-propanové, tetradecylester kyseliny
2,2,3,4,4-pentamethyl-7-oxa-21-oxo-3,20-diaza-dispiro-[5.1.11.2]-heneikosan-3-propanové,
3-acetyl-2,2,4,4-pentamethyl-7-oxa-3,20-diaza-dispiro-[5.1.11.2]-heneikosan-21-on, dodecylester kyseliny 3-acetyl-2,2,4,4-pentamethyl-7-oxa-21-oxo-3,20-diazadispiro- [5.1.11.2]-heneikosan-3-propanové, tetradecylester kyseliny 3-acetyl-2,2,4,4-tetramethyl-7-oxa-21-oxo3,20-diaza-dispiro-[5.1.11.2]-heneikosan-3-propanové,
1,1’,3,3’,5,5’-hexahydro-2,2’,4,4’,6,6’-hexaaza-2,2’,6,6’-bismethano-7,8-dioxo-4,4’-bis-(1,2,2,6,6-pentamethyl-4-piperidyl)-bifenyl, poly-Ν,Ν’-bis-(2,2,6,6-tetramethyl-4-piperidyl)-1,8-diazadecklen, addiční sloučenina
2,2,6,6-tetramethyl-4-allyloxy-piperidinu a polyme
-hydrogensiloxanu (molekulová hmotnost až 4000), addíční sloučenina 1,2,2,6,6-pentamethyl-4-allyloxy-piperidinu a polymethyl-hydrogensiloxanu (molekulová hmotnost až 4000), N,N’-di-formyl-N,N’-bis-(2,2,6,6-tetramethyl-4-piperidyl)-hexamethylendiamin,
N,N’-di-formyl-N,N’-bis-(1,2,2,6,6-pentamethyl-4-piperidyl)-hexa-methylendiamin,
5.11- bis-(2,2,6,6-tetramethyl-4-piperidyl)-3,5,7,9,11,13-hexaaza-tetracyklo-[7.4.0.0^’^.l^’^^]-tetradekan-8,14-dion,
5.11- bis-(l,2,2,6,6-pentamethyl-4-piperidyl)-3,5,7,9,11,13-hexaaza-tetracyklo-[7.4.0.O2’?.1^’]-tetradekan-8,14-dion, 7,7,9,9-tetramethyl-8-acetyl-3-dodecyl-l,3,8-triaza-spiro[4.5]-děkan-2,4-dion, bis-(2,2,6,6-tetramethyl-4-piperidinyl)-ester kyseliny [(4-methoxyfenyl)-methylen]-propanové, bis-(1,2,2,6,6-pentamethyl-4-piperidinyl)-ester kyseliny [(4-methoxyfenyl)-methylen]-propanové,
2,4,6-tris-(N-cyklohexyl-N-[2-(3,3,4,5,5-pentamethyl-piperazinon-l-yl)-ethyl]-amino)-1,3,5-triazin, kopolymer ze styrenu s β-methylstyenem a anhydridem kyseliny zreagovaný se 4-amino-1,2,2,6,6-pentamethylpiperidinem a oktadecylaminem, polykarobnát ze 2,2’-[(2,2,6,6-tetramethyl-4-methyl-piperidinyl)-imino]-bis-[ethanolu] jako diolovou komponentou, polykarbonát ze
2,2’-[(1,2,2,6,6-pentamethyl-4-piperidinyl)-imino]-bis-[ethanolu] jako diolovou komponentou, kopolymer z anhydridu kyseliny maleinové a β-olefinu až C30 zreagovaný se
4-amino-2,2,6,6-tetra-methylpiperidinem, kopolymer z anhydridu kyseliny maleinové a β-olefinu až C30 , zreagovaný s 1-acetyl-4-amino-2,2,6,6-tetramethylpiperidinem, kopolymer z anhydridu kyseliny maleinové a β-olefinu až C30, zreagovaný se 4-amino-l,2,2,6,6-pentamethylpiperidinem, 20,20’-(2-hydroxy-1,3-propandiy1)-bis-[2,2,4,4-tetramethy1-7-oxa-3,20-diazadispiro[5.1.11.2]heneikosan-2 L-on],
20,20’-(2-acetyloxy-1,3 -propand iyl)-bis-[2,2,4,4-tetrámethy1
-7-oxa-3,20-diazadispiro[5.1.11.2]heneikosan-21-on],
20,20’-(2-methyloxy-l,3-propandiyl)-bis-[2,2,4,4-tetramethyl -7-oxa-3,20-diazadispiro[5.1.11.2]heneikosan-21-on],
20,20’-(2-hydroxy-l,3-propandiyl)-bis-[1,2,2,4,4-pentamethyl-7-oxa-3,20-diazadispiro[5.1.11.2]heneikosan-21-on], 20,20’-(2-methyloxy-l,3-propandiyl)-bis-[1,2,2,4,4-pentamethyl-7-oxa-3,20-diazadispiro[5.1.11.2]heneikosan-21-on], 20,20’-(2-trimethylsilyloxy-1,3-propandiyl)-bis-[2,2,4,4tetramethyl-7-oxa-3,20-diazadispiro[5.1.11.2]heneikosan-21-on],
20,20’-(2-fenylaminokarbonyloxy-l,3-propandiyl)-bis-[2,2,4,4 tetramethyl-7-oxa-3,20-diazadispiro[5.1.11.2]heneikosan-21-on], jakož i N-alkylderiváty a N-arylderiváty výše uvedených sloučenin s volnými NH-skupinami na piperidinu, specielně β-methylbenzyloxy- a alkyloxy Cl až C18 .
2.7 Diamidy kyseliny oxalové, jako je například 4,4’-diokztyloxy-oxanilid, 2,2’-di-oktyloxy-5-5’-di-terč.-butyloxanilid, 2,2’-di-dodecyloxy-5-5’-di-terc.-butyl-oxanilid, 2-ethoxy-2’-ethyl-oxanilid, N,N’-bis-(3-dimethylaminopropyl)-oxalamid, 2-ethoxy-5-terc.-butyl-2’-ethoxyanilid a jeho směs s 2-ethoxy-2’-ethyl-5,4’-di-terčbuty1-oxanilidem, směsi o-methoxy- a p-methoxy-, jakož i o-ethoxy- a p-ethoxy-disubstituované oxanilidy.
2.8 2-(2-hydroxyfenyl)-1,3,5-triaziny, jako je například
2,4,6-tris-(2-hydroxy-4-oktyloxy-fenyl)-1,3,5-triazin,
2-(2-hydroxy-4-oktyloxyfenyl)-4,6-bis-(2,4-dimethyl-fenyl)-1,3,5-triazin , 2-(2,4-dihydroxyfeny1)-4,6-bis-(2,4-dimethylfenyl) -1 , 3 , 5-triazin , 2-(2,4-dihydroxyfenyl)-4,6 -bis-(2,4-dimethylfenyl)-1,3,5-triazin , 2,4-bis-(2-hydroxy-4-propyloxyfenyl)-6-(2,4-dimethylfenyl)-1,3,4 -triazin ,
2-(2-hydroxy-4-okxyloxyfenyl)-4,6-bis-(4-mexhylfenyl)-1,3,5-Xriazin , 2-(2-hydroxy-4-dodecyloxyfenyl)-4,6-bis-(2,4-dimexhylfenyl)-1,3,5-xriazin , 2-(2-hydroxy-4-(2-hydroxy-3-buXyloxy-propyloxy)-fenyl]-4,6-bis-(2,4-dimeXhylfenyl)-1,3,5-xriazin , 2-[2-hydroxy-4-(2-hydroxy-3-okxyloxy-propyloxy)-fenyl]-4,6-bis-(2,4-dimexhyl-fenyl)-1,3,5-Xriazin.
3. Kovové desakxiváxory, jako je například diamid kyseliny N,N’-difenyloxalové , N-salicylal-N’-salicyloylhydrazin, N,N’-bis-(salicyloyl)-hydrazin , N,N’-bis-(3,5-di-xerc.-buXyl-4-hydroxyfenylpropionyl)-hydrazin , 3-salicyloylamino-1,2,4-Xriazol , hydrazid kyseliny bis-(benzyliden)-oxalové , oxanilid , dihydrazid kyseliny isofxalové, bis-fenylhydrazid kyseliny sebakové , dihydrazid kyseliny N,N’-diaceXyl-adipové , dihydrazid kyseliny N,N’-bis-salicyloyl-oxalové , dihydrazid kyseliny N,N’-bis-salicyloyr Xhiopropionové , 2,2’-oxamido-bis-(exhyl)-3-(3,3-di-xerc.-buXyl-4-hydroxyfenyl)-propionáx , oligomery z chloridu fosforixého a 4,4’-di-(5-xerc.-buxyl-4-hydroxy-2-mexhyl)xhioexher.
4. Fosfixy a fosfonixy, jako je například xrifenylfosfix, difenylalkylfosfixy, fenyldialkylfosfixy, Xris-(nonylfenyl) fosfix , Xrilaurylfosfix , Xriokxadecylfosfix , disxearylpenxaeryxhrixdifosfix , Xris-(2,4-di-xerc.-buxylfenyl)-fosfix , diisodecylpenxaeryxhrix-difosfix , bis-(2,4-di-Xerc.-buXyl-fenyl)-penxaeryxhrixdifosfix , bis-sxearyl-penxaeryxhrixdifosfix , bis-(2,6-di-xerc.-buty1-4-mexhylfenyl)-penxaeryxhrixdifosfix , bis-isodecyloxy-penxaeryxhrixdifosfix , bis-(2,4-di-xerc.-buxyl-6-merhylfenyl)-penxaeryxhrixdifosfix , bis-(2,4,6 - xri - xerc . - butylf enj·' > -penxaeryxhrixdifosfix , Xristearyl-sorbit-trifosfix , tetrakis-(2,4-di-terc.-butylfenyl)-4,4’-bifenylen-difosfonit , 6-isooktyloxy-2,4,8,10-tetra-terč.-butyl-12H-dibenzo[d,g]-1,3,2-dioxafosfocin , 6-fluor-2,4,8,10-tetra-terc.-butyl-12H-dibenzo[d,g]-1,3,2-dioxafosfocin , bis-(2,4-di-terc.-butyl-6-methylfenyl)-methylfosf it , bis-(2,4-di-terc.-butyl-6-methylfenyl)-ethylfosfit , tris-(2-terč.-butyl-4-thio-(2’-methenyl-4’-hydroxy-5’-terč.-butyl)-fenyl-5-methenyl)-fenylfosfit , 2,2’,2’’-nitrilo-ethanol-tris-(3,3’,5,5’-tetra-terč.-butyl-1,1’-bifenyl-2,2’-diyl)-fosfit , bis-(2,4-dikumyl-fenyl)-pentaerythritol-difosfit.
5. Sloučeniny rozkládající peroxidy, jako jsou například estery kyseliny thio-dipropionové, například laurylester, stearylester, myristylester nebo tridecylester, merkaptobenzimidazol, zimečnatá sůl merkaptobenzimidazolu, zinek-alkyl-dithiokarbamáty , zinek-butyl-dithiokarbamát, dioktadecylmonosulfid, dioktadecyldisulfid, pentaerythrit-tetrakis-(β-dodecylmerkapto)-propionát.
6. Polyamidové stabilisátory, jako jsou například soli měďi v kombinaci s jodidy a/nebo sloučeninami fosforu a solemi dvojmocného manganu.
7. Basické kostabilisátory, jako je například melamin, polyvinylpyrrolidon, dikyandiamid, triallylkyanurát, deriváty močoviny, deriváty hydrazinu, aminy, polyamidy, polyurethany, soli alkalických kovů a kovů alkalických zemin s vyššími mastnými kyselinami, například stearát vápenatý, stearát zinečnatý, benenát hořečnatý, stearát hořečnatý, ricinoleát sodný, palmitát draselný, pyrokatechinát antimonitý nebo pyrokatechinát cínatý, oxidy · , například oxid hořečnatý a oxid zinečnatý, jakož i akcep21 tory kyselin na basi iontoměničů nebo molekulových sít, například hydrokalcity nebo zeolity.
8. Nukleační činidla, jako je například kyselina
4-terč.-butylbenzoová, kyselina adipová, kyselina difenyloctová, benzoát sodný, mastek, monobenzylidensorbitoly nebo dibenzylidensorbitoly, které jsou popřípadě substituované.
9. Plnidla a ztužovadla, jako je například uhličitan vápenatý, silikáty, skleněná vlákna, asbest, mastek, kaolin, slída, síran barnatý, oxidy kovů, hydroxidy kovů, saze, grafit, zeolity, IR-aktivní substance a IR-reflektory, jako například zeolity nebo silikáty.
10. Benzofuranony.
11. Prostředky proti rosení, jako jsou například estery sorbitolu nebo glycerolu.
12. Antistatika, jako jsou například ethoxylované aminy, alkansulfonáty, estery mastných kyselin, kvartérní amoniové sloučeniny.
13. Pigmenty, jako je například oxid titaničitý, saze, anorganické a organické barevné pigmenty.
14. Ostatní přísady, jako jsou například změkčovadla, maziva, emulgátory, optické zjasňovače, ochranné prostředky proti hoření, antistatika, nadouvadla.
Additiva se zapracovávaj í do organických polymerí· pomocí všeobecně obvyklých metod. Zapracovávání se může například provádět vmíšením nebo nanesením sloučenin a popřípadě dalších additiv do nebo na polymery bezprostředně po polymeraci, nebo do taveniny před nebo během procesu tvarování. Zapracovávání se může provádět také nanesením rozpuštěných nebo dispergovaných sloučenin na polymery nebo přimíšením do roztoku, suspense nebo emulse polymerů, popřípadě za dodatečného odpaření rozpouštědla. Sloučeniny jsou také účinné, když se dodatečně zapracují do již granulovaného polymeru ve zvláštním pracovním kroku.
Sloučeniny používané podle předloženého vynálezu se mohou přidávat do stabilisovaných polymerů také ve formě předsměsi (masterbatch) , která obsahuje tyto sloučeniny například v koncentraci 1 až 75 % hmotnostních, výhodně
2,5 až 30 % hmotnostních.
Z polymerů, stabilisovaných podle předloženého vynálezu, se dají vyrobit všechny předměty, které jsou z těchto polymerů obvyklé. Toto mohou být například tenká vlákna 1 dtex až silné monofilamenty s průměrem 5 mm , jakož i z nich vyrobené předměty, jako jsou například rohože pro urychlení sklizně nebo vyfukované nebo extrudované folie o tloušťce 0,01 mm až 3 mm , dloužené nebo nedloužené, které se přímo používají, nebo se například dále zpracovávají na pásky, nebo také desky s tloušťkou až 5 mm, které se například mohou použít při stavbě skleníků.
Příklady provedení vynálezu
Následující příklady provedení slouží k bližšímu objasnění vynálezu. Jako příklady pro zdroje síry se po. sirovodík, oxid siřičitý/kyselina siřičitá a natrium-N-met23 hyldithiokarbamát.
Přiklad 1
Výroba folie
2000 g LDPE 3 g HALS
Stericky bráněný amin se rozpustí ve 300 ml acetonu, přidá se k práškovitému LDPE a rozpouštědlo se v rotační odparce při teplotě 60 °C znovu odpaří, ke konci za vakua vodní vývěvy. Prášek se dvakrát extruduje a granuluje (teplotní profil 130 °C / 150 °C / 170 °C , 125 otáček za minutu). Granulát se v Góttfertově laboratorním extruderu s vyfukovací foliovou hlavou zpracuje na folii o tloušťce 200 μ (teplotní profil 160 °C / 170 °C / 1870 °C / 200 °C, 50 ot/min) .
Příklad2
Vliv sirovodíku
Vliv sirovodíku na dobu životnosti folií se zjišťuje pomocí následujícího testovacího cyklu (s přihlédnutím k DIN 53 387) . Po vždy 125 hodinách osvětlování ve xenotestu 450 (relativní vlhkost vzduchu 20 % , teplota černé desky 50 °C) následuje dvouhodinové zpracování sirovodíkem. K tomu se zkušební tělesa skladují po dobu 2 hodin za tmy v atmosféře čistého sirovodíku. Potom začíná cyklus znovu od začátku. Po vždy 250 hodinách (250 h , 500 h , 750 h ... až 1750 h) se zjišťuje obsah síry vc zkušebních tělesech. V tabulce 1 je uvedeno průměrné přijetí síry pro zpracování sirovodíkem.
Tabulka 1
Průměrné přijetí síry pro zpracování sirovodíkem.
HALS | ppm síry |
14 | |
IV | 20 |
II | 14 |
III/IV (1:1) | 15 |
III/V (1:1) | 14 |
III/VI (1:1) | 16 |
I | 12 |
Příklad 3
Vliv oxidu siřičitého/kyseliny siřičité
Testovací cyklus probíhá stejně jako je popsáno v příkladě 1 . Folie se však máčí po dobu dvou hodin v 0,1 N kyselině siřičité. Po usušení přilnuté kyseliny siřičité se zkušební tělesa znovu osvětluj í. Před stanovováním obsahu síry se zkušební tělesa důkladně omyjí demineralisovanou vodou, aby se vyloučila možnost chyby vlivem přilnutých sloučenin síry. V tabulce 2 je uvedeno průměrné přijetí síry pro zpracování kyselinou siřičitou.
Tabulka 2
Průměrné přijetí síry pro zpracování kyselinou siřičitou
HALS | ppm síry |
- | 17 |
IV | 30 |
I | 24 |
Příklad 4
Vliv natrium-N-methyIdithiokarbamátu
Testovací cyklus probíhá stejně jako je popsáno v příkladě 2 . Folie se však máčí po dobu dvou hodin ve 3% roztoku natrium-N-methyldithiokarbamátu. Po usušení přilnutého roztoku se zkušební tělesa znovu osvětlují. Před stanovováním obsahu síry se zkušební tělesa důkladně omyjí demineralisovanou vodou, aby se vyloučila možnost chyby vlivem přilnutých sloučenin síry. V tabulce 3 je uvedeno průměrné přijetí síry pro zpracování natrium-N-methylkarbamátem.
Tabulka 2
Průměrné přijetí síry pro zpracování natrium-N-methylkarbamátem
HALS | ppm síry |
- | 62 |
IV | 62 |
II | 53 |
III/IV (1:1) | 54 |
III/V (1:1) | 53 |
III/VI (1:1) | 55 |
V | 63 |
VI | 62 |
I | 49 |
JUOr. ΜΠοδ všrrrčKA advoká.
ISO CG Ρ«>·ΗΑ '1 Ί ?/ mi-K
Claims (7)
- PATENTOVÉ1. Plastická hmota, obsahující vysokomolekulární stericky bráněný amin, vyznačující se tím, že jako stericky bráněný amin obsahuje alespoň jeden amin ze skupiny zahrnuj ící1. oligomerisovaný 2,2,4,4-tetramethyl-20-(oxiranylmethyl)-7-oxa-3,20-diazadispiro[5.1.11.2]heneikosan-21-on ,II. kondensační produkt ze 2-chlor-4,6-di-(4-n-butylamino-1,2,2,6,6-pentamethylpiperidyl)-1,3,5-triazinu a 1,2-bis-(3-aminopropylamio)-ethanu neboIII. kondensační produkt z l-hydroxyethyl-2,2,6,6-tetramethyl-4-hydroxypiperidinu a kyseliny jantarové.
- 2. Plastická hmota podle nároku 1 , vyznačující se tím, že obsahuje alespoň jeden stericky bráněný amin vzorce I , vzorce II nebo vzorce III , jakož i alespoň jeden amin, zvolený ze skupiny zahrnuj ícíIV. kondensační produkt N,N’-bis-(2,2,6,6-tetramethyl 4-piperidyl)-hexamethylendiaminu a 4-terč.-oktylamino-2,6-dichlor-1,3,5-triazinu,V.kondensační produkt z Ν,N’-bis-(2,2,6,6-tetramethy128-4-piperidyl)-hexaraethylendiaminu a 4-morfolino-2,6-dichlor-1,3,5-triazinu neboVI. kondensační produkt 2,4-dichlor-6-(4-n-butylamino-2,2,6,6-tetramethyl-piperidyl)-1,3,5-triazinu a l,2-bis-[3-(4’,6’-di-(4’’-n-butylamino-2’’,2’’,6’’,6’’-tetraraethylpiperidyl)-1’,3’,5’-triayinyl)aminopropylamino]-ethanu.
- 3. Plastická hmota podle nároku 1 nebo 2 , vyznačující se tím, že podíl jednotlivého aminu činí 0,1 až 99,9 % hmotnostních, výhodně 1 až 99 % hmotnostních, obzvláště výhodně 10 až 90 % hmotnostních, vztaženo na použitý amin.
- 4. Plastická hmota podle některého z nároků 1 až 3 , vyznačující se tím, že obsahuje 0,001 až 5 % hmotnostních, výhodně 0,02 až 1 % hmotnostní, vysokomolekulárniho, stericky bráněného aminu, vztaženo na hmotnost plastické hmoty.
- 5. Plastická hmota podle některého z nároků 1 až 4 , vyznačující se tím, že plastickou hmotou je homopolymer nebo kopoiymer monoolefinu nebo diolefinu.
- 6. Plastická hmota podle některého z nároků 1 až 4 , vyznačující se tím, že plastickou hmotou je směs polymerů podle nároku 5
- 7. Plastická hmota podle některého z nároků 1 až 4 , vyznačující se tím, že plastickou hmotou je kopoiymer monoolefinů nebo diolefinů navzájem jinými vinylpolymery.