CS829886A2 - Electroresistive material - Google Patents
Electroresistive material Download PDFInfo
- Publication number
- CS829886A2 CS829886A2 CS868298A CS829886A CS829886A2 CS 829886 A2 CS829886 A2 CS 829886A2 CS 868298 A CS868298 A CS 868298A CS 829886 A CS829886 A CS 829886A CS 829886 A2 CS829886 A2 CS 829886A2
- Authority
- CS
- Czechoslovakia
- Prior art keywords
- parts
- electro
- black
- coresiline
- graphite
- Prior art date
Description
Vynález se týká elektroodporového materiálu pro sálavé topení.
Je znám nekovový elektroodporový materiál pro elek - trické sálavé topení, který má následující složení i grafit šedý nebo černý - 100 hmot. dílů, neutrální plnivo 0 až 50 hmot. dílů, černý lak pro vypalování - 75 až 100 hmot. dílů a koresilin - 60 až 120 hmot. dílů. Nevýhody spočívají v tom, že se zde šedý nebo černý grafit, stejně jako černý lak pro vypalování používají jako pojivo. Top né prvky, zhotovené z šedého nebo černého grafitu a čer - ného laku pro vypalování potřebují mechanické opracování, aby se dosáhlo potřebných elektrických jmenovitých hodnot Černý lak pro vypalování má relativně nízkou mechanic - kou pevnost, rychle praská a rozrušuje se a stává se neupotřebitelným. Přitom se může tento materiál používat2 jen do teploty 8d C a specifického výkonu do 700 W/m . Úkolem vynálezu je vytvořit elektroodporový mate -riál, který má dlouhou životnost, nemá potřebné přidav -né mechanické opracování, muže být použit při teplotách až do 10C| C a specifického výkonu až 1000 W/m a v praxi je lehce aplikovatelný.
Tento úkol se řeší elektroodp ořovým materiálem prosálavé topení, který má následující složení: amorfní grafit 100 hmot. dílů polyvinylasetát 10 až 18 hmot. dílů denaturováný alkohol 20 až 36 hmot. dílů koresilin 1 až 150 hmot. dílů Přednosti vynálezu .jsou následující i Tento mate -riál se může nanášet jak na malé, tak také na velké plochy, je použitelný pro teploty až do 10C^ C, přičemžo se současně dosahuje specifický výkon 1000 W/m . Mate -riál je nehořlavý a při jeho použití se dosáhne rovnoměrnéhh a příjemného topení.
Tento materiál se může nanášet na různé elektro -izolační základy, jako betonové desky, mramorové desky,atd., na stěny stropy, podlahy. Nátěr se provádí štět -cem, pistolí, nebo strojově. Při použití elektroodporového materiálu pro sálavé topení se spotřebuje až o 3θ až40 % elektrické energie méně, což je způsobeno tím,že teplo sálá z velké plochy.
Vynález bude v dalším textu blíže objasněn nanásledujících příkladech provedení. Příklad 1 K amorfnímu grafitu v množství 440 g se přidá 54 Spolyvinylacetátu. Této směsi se přidá 110 g děna -turovaného alkoholu a 615 g koresilinu. Tato směsse 5 min. promíchá. Příklad se vztahuje na topný prvek o rozměrech 600 x 1200 mm a výkonu 630 W a při specifickémvýkonu 875 W/m2 a teplot© ?c)° C. Příklad 2
Množství jednotlivých složek jsou následující:amorfní grafit 600 g, polyvinylacetat 70 S, denaturovanýalkohol 147, koresilin 822 g.
Technologie výroby materiálu je tatáž jako u pří -kladu 1. Rozměry topných prvků v tomto případě jsou800 x 1200 mm, výkon 800 W a specifický výkon 835 W/M2při teplotě 65j 0. Příklad 3
Množství jednotlivých složek jsou následující:amorfní grafit 750 g, polyvinylacetet 50 g, denaturovanýalkohol 187 g, koresilin 1032 g. Příklad vztahuje sena topný prvek o rozměrech 1000 x 1200 mm a výkonu 1000 Wpři specifickém výkonu 835 W/m^ a teplotě 65>' 0. Techno -logie výroby materiálu je stejná jako u příkladu.
Elektroodporový materiál podle vynálezu se nanášíve formě nátěrové hmoty nebo pasty na izolační podkladnebo stěny vytápěného prostoru. Tento materiál sloužípřevážně pro sálavé topení.
Claims (1)
- Předmět vynálezu Elektroodporový materiál pro sálavé topení, vy -značující se tím, že obsahuje 100 hmot. dílu amorfníhografitu, 10 až ,18 hmot. dílů polyvinylacetátu, 20 ažJ6 hmot. dílů denaturovaného alkoholu a 1 až 150 hmot.dílů koresilinu.<o C\