CN1931928A - 一种油漆废渣再生方法 - Google Patents

一种油漆废渣再生方法 Download PDF

Info

Publication number
CN1931928A
CN1931928A CN 200610068764 CN200610068764A CN1931928A CN 1931928 A CN1931928 A CN 1931928A CN 200610068764 CN200610068764 CN 200610068764 CN 200610068764 A CN200610068764 A CN 200610068764A CN 1931928 A CN1931928 A CN 1931928A
Authority
CN
China
Prior art keywords
solvent
paint
underpressure distillation
controlled
30min
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200610068764
Other languages
English (en)
Other versions
CN100540614C (zh
Inventor
冯立明
郑培学
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
MATERIALS INST SHANDONG ARCHITECHTURE UNIV
Original Assignee
MATERIALS INST SHANDONG ARCHITECHTURE UNIV
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by MATERIALS INST SHANDONG ARCHITECHTURE UNIV filed Critical MATERIALS INST SHANDONG ARCHITECHTURE UNIV
Priority to CNB200610068764XA priority Critical patent/CN100540614C/zh
Publication of CN1931928A publication Critical patent/CN1931928A/zh
Application granted granted Critical
Publication of CN100540614C publication Critical patent/CN100540614C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明一种油漆废渣再生方法。涉及废渣利用领域。特点是包括以下工序：有机溶剂与油漆废渣混合、均质分散、减压蒸馏、粉碎过滤、调整黏度、产品包装。通过该方法将汽车、农用车、摩托车、家用电器等涂装过程中产生大量油漆废渣，加工为各项性能指标达到原漆质量标准的油漆，实现资源的再利用和社会的可持续发展。

Description

一种油漆废渣再生方法
技术领域
本发明涉及废渣利用领域，尤其涉及一种油漆废渣再生方法。
背景技术
溶剂型油漆通常采用高压空气喷涂、高压无空气喷涂、静电喷涂等施工方法，油漆的一次利用率一般在50％～85％之间，尤其采用高压空气喷涂时，油漆的利用率随工件形状不同有所差异，但一般不超过60％，因此施工过程中，造成大量油漆浪费，产生大量有机废渣，对环境造成污染。油漆废渣已成为汽车、农用车、摩托车、家用电器等厂家的一大负担，也是一大难题。
目前对油漆废渣的处理有采用专用设备高温分解、燃烧的报道，该技术虽然处理了废渣，但资源得不到再利用，而且有可能造成大气等二次污染；目前的回收利用方式过于简单，利用率不高，回收产品效果不理想，难以实现工业化应用。
随着我国危险固体废物处理条例的颁布实施，研究并实现油漆废渣的再生利用，是发展循环经济、减少环境污染、实现社会可持续发展的需要，必将产生巨大的经济效益和社会效益。
发明内容
根据油漆废渣的组成、树脂结构特点，本发明提出了一种既便宜、实用，操作又简单的油漆废渣再生回收方法。
本发明所述的一种油漆废渣再生方法，包括将有机溶剂与油漆废渣混合后经过均质分散、减压蒸馏、粉碎过滤、调整黏度、产品包装等工序，使油漆废渣再生为合格油漆。
其中有机溶剂可以是醇类和/或酯类和/或芳烃类和/或烷烃类。根据油漆废渣的成份可选用不同成份和比例的有机溶剂及其混合物。
其中所述醇类有机溶剂包括：乙醇和/或丁醇和/或异丙醇和/或异丁醇。
其中所述酯类有机溶剂包括：乙酸乙酯和/或乙酸丁酯。
其中所述芳烃类有机溶剂包括：甲苯和/或二甲苯。
其中所述烷烃类有机溶剂包括：200#溶剂汽油。
在生产过程中，均质分散采用机械搅拌。
回收所用的有机溶剂，可根据所处理漆的树脂结构特点进行选择，对单一溶剂依据相似相溶原理，对混合溶剂依据容度参数规则选择，使混合溶剂的容度参数与树脂容度参数之差小于0.5。醇酸树脂油漆以醇酸树脂和植物油为主要成膜物，极性较弱，因此以200#溶剂汽油为溶剂；氨基醇酸树脂漆中氨基树脂和醇酸树脂结构中含有多个羟基，因此以醇类溶剂为溶剂；丙烯酸树脂漆树脂结构为丙烯酸酯，以酯及醇的混合物为溶剂；环氧树脂漆结构中含有大量苯环，因此以二甲苯等作为溶剂。
减压蒸馏可采用循环水式真空泵或机械密封式真空泵，真空度为0.9～0.99Mpa，馏程控制在所处理漆的固化温度以下。
减压蒸馏是利用多相共沸原理，在低温下通过溶剂的蒸发，在不引入其他杂质成分的前提下，达到去除油漆中残留水分、树脂再分散溶解等目的，使油漆废渣恢复其性能。减压蒸馏的真空度控制在0.9～0.99Mpa，温度范围以低于树脂固化温度20℃为宜。
调整黏度按照常规方法加入溶剂调整至所需黏度，调整黏度的溶剂与溶解过程中的溶剂相同。
本发明所述方法可应用于处理醇酸树脂漆、环氧树脂漆、氨基醇酸树脂漆、丙烯酸树脂漆、过氯乙烯漆、硝基漆等挥发型或高温烘烤型的溶剂型油漆，在空气喷涂、高压无空气喷涂、静电喷涂等施工过程中，经干式喷漆室、水循环式喷漆室回收的废漆渣。
本发明能使废渣再生的油漆的涂层性能，如韧性、附着力、耐冲击强度、光泽度等达到合格油漆性能指标，从而变废为宝。
具体实施方式
实施例1
将醇酸树脂油漆废渣置入反应釜中，按质量比加入1∶2的溶剂，溶剂采用200#溶剂汽油，经过机械搅拌30min后，减压蒸馏30min，馏程控制在60℃以下。再用溶剂稀至施工黏度。
                   回收前后油漆性能对照表
  附着力/划圈法   韧性   光泽度/％   耐冲击强度/kg.cm
  原漆   1级   1mm   80   50kg.cm
  回收漆   1级   1mm   70   50kg.cm
实施例2
将氨基醇酸树脂油漆废渣置入反应釜中，按质量比加入1∶2的溶剂，溶剂采用体积比为4∶1的异丙醇与异丁醇混合液，搅拌30min后，减压蒸馏30min，馏程控制在90℃以下，再用溶剂稀至施工黏度。
                  回收前后油漆性能对照表
  附着力/划圈法   韧性  光泽度/％   耐冲击强度/kg.cm
  原漆   1级   1mm   90   50kg.cm
  回收漆   1级   1mm   85   50kg.cm
实施例3
将丙烯酸树脂漆废渣置入反应釜中，按质量比加入1∶2的溶剂，溶剂采用体积比为6∶2∶2的乙酸丁酯、乙醇、二甲苯混合液，搅拌30min后，减压蒸馏30min，热塑性树脂控制在60℃以下，热固性树脂控制在100℃以下，再用溶剂稀至施工黏度。
                     回收前后油漆性能对照表
  附着力/划圈法   韧性   光泽度/％   耐冲击强度/kg.cm
  原漆   1级   1mm   85   50kg.cm
  回收漆   1级   1mm   80   50kg.cm
实施例4
环氧树脂油漆废渣置入反应釜中，按质量比加入1∶2的溶剂，溶剂采用二甲苯，搅拌30min后，减压蒸馏20min，馏程控制在60℃以下，再用溶剂稀至施工黏度。
               回收前后油漆性能对照表
 附着力/划圈法   韧性  光泽度/％   耐冲击强度/kg.cm
  原漆   1级   1mm   70   50kg.cm
  回收漆   1级   1mm   70   50kg.cm
实施例5
将过氯乙烯树脂漆废渣置入反应釜中，按质量比加入1∶2的溶剂，溶剂采用体积比为3∶1的乙酸丁酯、二甲苯混合液，搅拌30min后，减压蒸馏30min，温度控制在60℃以下，再用溶剂稀至施工黏度。
                   回收前后油漆性能对照表
  附着力/划圈法   韧性   光泽度/％   耐冲击强度/kg.cm
  原漆   1级   1mm   80   50kg.cm
  回收漆   1级   1mm   75   50kg.cm
实施例6
将过硝基漆废渣置入反应釜中，按质量比加入1∶2的溶剂，溶剂采用体积比为4∶3∶3的乙酸乙酯、乙醇、二甲苯混合液，搅拌30min后，减压蒸馏30min，温度控制在60℃以下，再用溶剂稀至施工黏度。
                     回收前后油漆性能对照表
  附着力/划圈法   韧性   光泽度/％   耐冲击强度/kg.cm
  原漆   1级   1mm   80   50kg.cm
  回收漆   1级   1mm   70   50kg.cm

Claims (10)

1.一种油漆废渣再生方法，其特征在于包括以下工序：有机溶剂与油漆废渣混合、均质分散、减压蒸馏、粉碎过滤、调整黏度、产品包装。
2.如权利要求1的方法，其中所述有机溶剂是醇类和/或酯类和/或芳烃类和/或烷烃类。
3.如权利要求1或2的方法，其中所述醇类有机溶剂包括：乙醇和/或丁醇和/或异丙醇和/或异丁醇；其中所述酯类有机溶剂包括：乙酸乙酯和/或乙酸丁酯；其中所述芳烃类有机溶剂包括：甲苯和/或二甲苯；其中所述烷烃类有机溶剂包括：200#溶剂汽油。
4.如权利要求1的方法，其中所述减压蒸馏采用真空度为0.9～0.99Mpa，馏程控制在所处理漆的固化温度以下，减压蒸馏20～30min。
5.如权利要求1的方法，其特征在于应用于处理醇酸树脂漆时，将醇酸树脂油漆废渣置入反应釜中，按质量比加入1∶2的溶剂，溶剂采用200#溶剂汽油，经过机械搅拌均匀，减压蒸馏30min，馏程控制在60℃以下，再用溶剂稀至施工黏度。
6.如权利要求1的方法，其特征在于应用于处理氨基醇酸树脂油漆时，将氨基醇酸树脂油漆废渣置入反应釜中，按质量比加入1∶2溶剂，溶剂采用体积比为4∶1的异丙醇与异丁醇混合液，搅拌均匀，减压蒸馏30min，馏程控制在90℃以下，再用溶剂稀至施工黏度。
7.如权利要求1的方法，其特征在于应用于处理丙烯酸树脂漆时，将丙烯酸树脂漆废渣置入反应釜中，按质量比加入1∶2溶剂，溶剂采用体积比为6∶2∶2的乙酸丁酯、乙醇、二甲苯混合液，搅拌均匀，减压蒸馏30min，热塑性树脂控制在60℃以下，热固性树脂控制在100℃以下，再用溶剂稀至施工黏度。
8.如权利要求1的方法，其特征在于应用于处理环氧树脂油漆时，将环氧树脂油漆废渣置入反应釜中，按质量比加入1∶2溶剂，溶剂采用二甲苯，搅拌均匀，减压蒸馏20min，馏程控制在60℃以下，再用溶剂稀至施工黏度。
9.如权利要求1的方法，其特征在于应用于处理过氯乙烯树脂漆时，将过氯乙烯树脂漆废渣置入反应釜中，按质量比加入1∶2的溶剂，溶剂采用体积比为3∶1的乙酸丁酯、二甲苯混合液，搅拌30min后，减压蒸馏30min，温度控制在60℃以下，再用溶剂稀至施工黏度。
10.如权利要求1的方法，其特征在于应用于处理硝基漆时，将硝基漆废渣置入反应釜中，按质量比加入1∶2的溶剂，溶剂采用体积比为4∶3∶3的乙酸乙酯、乙醇、二甲苯混合液，搅拌均匀，减压蒸馏30min，温度控制在60℃以下，再用溶剂稀至施工黏度。
CNB200610068764XA 2006-09-05 2006-09-05 一种油漆废渣再生方法 Expired - Fee Related CN100540614C (zh)