CN1853524A - 一种珍珠漂白方法 - Google Patents

一种珍珠漂白方法 Download PDF

Info

Publication number
CN1853524A
CN1853524A CN 200510049716 CN200510049716A CN1853524A CN 1853524 A CN1853524 A CN 1853524A CN 200510049716 CN200510049716 CN 200510049716 CN 200510049716 A CN200510049716 A CN 200510049716A CN 1853524 A CN1853524 A CN 1853524A
Authority
CN
China
Prior art keywords
pearl
bleaching
bleaching method
bleeding agent
illumination
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 200510049716
Other languages
English (en)
Inventor
陈海军
杨天擎
翁学庆
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZHEJIANG SHANXIAHU PEAL GROUP CO Ltd
Original Assignee
ZHEJIANG SHANXIAHU PEAL GROUP CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHEJIANG SHANXIAHU PEAL GROUP CO Ltd filed Critical ZHEJIANG SHANXIAHU PEAL GROUP CO Ltd
Priority to CN 200510049716 priority Critical patent/CN1853524A/zh
Publication of CN1853524A publication Critical patent/CN1853524A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种珍珠的漂白方法，包括如下步骤：(1)珍珠在70－90℃去离子水中蒸煮10min－2h；(2)将过氧化氢溶液调节pH至7－8，在渗透剂作用下，将珍珠在上述溶液中进行漂白处理。本发明所述漂白方法漂白稳定性高、速度快，漂白的珍珠品质好。

Description

一种珍珠漂白方法
(一)技术领域
本发明涉及一种珍珠的漂白方法。
(二)背景技术
现有的珍珠漂白通常是用双氧水(过氧化氢)配上其它溶剂、助剂来对珍珠进行漂白处理的。由于加工厂的设备比较落后，漂白配方及工艺仅凭操作人员的经验来控制，以至于漂白出来的珍珠质量不够稳定，还经常有珍珠表皮脱皮的现象的产生，造成珍珠的成品率不高。本发明可提高漂白的稳定性及成品率，提升珍珠的价值。
(三)发明内容
为克服现有技术中漂白质量不稳定、效果差的缺点，本发明提供了一种珍珠漂白方法。
所述的漂白方法包括如下步骤：
(1)珍珠在70-90℃去离子水中蒸煮10min-2h；
(2)将过氧化氢溶液调节pH至7-8，在渗透剂作用下，将珍珠在上述溶液中进行漂白处理。
步骤(2)中所述的pH可以采用三乙醇胺和Britton-Robinson缓冲剂进行调节。调节pH值至7-8是为了减少珍珠表面受腐蚀破坏，同时还增加了珍珠的光洁度。
所述的渗透剂优选为烷基硫酸钠，如十二烷基硫酸钠。渗透剂有利于漂白液渗入珍珠内外层，以加快漂白的速度。
所述的漂白处理温度优选为30-35℃，处理时间优选为4-20天。
漂白处理在充分光照下进行可以提高漂白的效果。
本发明所得的珍珠产品在漂白中受到漂白剂过氧化氢(H2O2)的氧化作用，导致某些化学键和基团被破坏，从而使其中杂质或有色物质发生解离失去颜色，达到漂白的目的。
另外，珍珠在漂白前先作热处理，不但可以使珍珠中某些色素热分解脱色，还使得珍珠的结构疏松，以利于漂白液的渗透。
影响珍珠漂白的因素还有漂白液的浓度、溶剂、反应温度和反应时间等。
本发明所述漂白方法推荐的步骤如下：
适量的过氧化氢加甲醇溶剂中，加入少量渗透剂剂起到渗透分散作用，再用三乙醇胺及Britton-Robison缓冲液调节PH值为7-8，然后在30-35℃和充分光照下，将珍珠浸泡在漂白液中1-2.5周时间进行漂白处理(以四天为一周期，要更换一次漂白液，检查漂白达到要求的珍珠并及时取出水洗)。另外，珍珠在漂白前要在70-90℃去离子水中蒸煮作热处理，方可进行漂白处理。
本发明所述漂白方法漂白稳定性高、速度快，漂白的珍珠品质好。
(四)具体实施方式
下面结合实施例对本发明作进一步说明，但本发明的保护范围并不限于此。
                           实施例1
1、珍珠试样分选、打孔，并在80℃去离子水中蒸煮1h；
2、先在玻璃瓶中分别加入50mlH2O2和1000ml甲醇，搅拌均匀；
3、再分别加入10mlBritton-Robinson缓冲液(PH＝7.5)和2ml三乙醇胺，调节漂白液pH值为7.5；
4、添加30wt％十二烷基硫酸钠溶液10ml作为渗透剂；
5、然后在30℃充分光照下，将150g珍珠浸泡在漂白液中16天进行漂白处理(四天更换一次上述制得的漂白溶液)；
6、水洗、干燥、抛光，即得已漂白的优质珍珠。
                            实施例2
1、珍珠试样分选、打孔，并在70℃去离子水中蒸煮2h；
2、先在玻璃瓶中分别加入100mlH2O2和1000ml甲醇，搅拌均匀；
3、再分别加入10mlBritton-Robinson缓冲液(pH＝7.5)和2ml三乙醇胺，调节漂白液PH值为7.2；
4、添加30wt％十二烷基硫酸钠溶液10ml作为渗透剂；
5、然后在35℃充分光照下，将200g珍珠浸泡在漂白液中8天进行漂白处理(四天更换一次上述制得的漂白溶液)；
6、水洗、干燥、抛光，即得已漂白的优质珍珠。
                           实施例3
1、珍珠试样分选、打孔，并在90℃去离子水中蒸煮0.5h；
2、先在玻璃瓶中分别加入70mlH2O2和1000ml甲醇，搅拌均匀；
3、再分别加入10mlBritton-Robinson缓冲液(pH＝7.5)和2ml三乙醇胺，调节漂白液PH值为7.8；
4、添加30wt％十二烷基硫酸钠溶液10ml作为渗透剂；
5、然后在33℃充分光照下，将200g珍珠浸泡在漂白液中8天进行漂白处理(四天更换一次上述制得的漂白溶液)；
6、水洗、干燥、抛光，即得已漂白的优质珍珠。

Claims (7)

1、一种珍珠漂白方法，包括如下步骤：
(1)珍珠在70-90℃去离子水中蒸煮10min-2h；
(2)将过氧化氢溶液调节pH至7-8，在渗透剂作用下，将珍珠在上述溶液中进行漂白处理。
2、如权利要求1所述的珍珠漂白方法，其特征在于所述的步骤(2)中过氧化氢溶液采用三乙醇胺和Britton-Robinson缓冲剂调节pH。
3、如权利要求1所述的珍珠漂白方法，其特征在于所述的渗透剂为烷基硫酸钠。
4、如权利要求3所述的珍珠漂白方法，其特征在于所述的渗透剂为十二烷基硫酸钠。
5、如权利要求1～4之一所述的珍珠漂白方法，其特征在于所述的漂白温度为30-35℃，漂白时间为4-20天。
6、如权利要求1所述的珍珠漂白方法，其特征在于所述的漂白在充分光照下进行。
7、如权利要求5所述的珍珠漂白方法，其特征在于所述的漂白在充分光照下进行。
CN 200510049716 2005-04-29 2005-04-29 一种珍珠漂白方法 Pending CN1853524A (zh)