CN101912187A - 一种海水珍珠的漂白方法 - Google Patents
一种海水珍珠的漂白方法 Download PDFInfo
- Publication number
- CN101912187A CN101912187A CN2010102468056A CN201010246805A CN101912187A CN 101912187 A CN101912187 A CN 101912187A CN 2010102468056 A CN2010102468056 A CN 2010102468056A CN 201010246805 A CN201010246805 A CN 201010246805A CN 101912187 A CN101912187 A CN 101912187A
- Authority
- CN
- China
- Prior art keywords
- bleaching
- pearl
- liquid
- water
- solvent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种海水珍珠的漂白方法,该方法分为两步,第一步是甲醇溶液漂白,第二步是水溶液漂白,(1)甲醇溶液漂白:在漂白条件下,将珍珠浸泡在装有以甲醇为溶剂的漂白液的烧瓶中,5天后用清水漂洗,直至无泡沫为止,将珍珠烘干,重复5~6次;(2)水溶液漂白:在漂白条件下,将珍珠浸泡在装有以水为溶剂的漂白液的烧瓶中,3天后用清水漂洗,直至无泡沫为止,将珍珠烘干,重复3~4次,直至珍珠白透为止。该方法具有漂白速度快,成本低,漂白过的珍珠光泽强、不易返黄、“长麻”率低等优点,而且该工艺操作方便,容易控制,可以有效提高海水珍珠的质量,促进我国海水珍珠产业的持续发展。
Description
技术领域
本发明涉及一种珍珠漂白方法,特别涉及一种海水珍珠的漂白方法,属于珍珠加工技术领域。
背景技术
海水珍珠是海水珍珠母贝生命活动的分泌物,是由许多文石结晶薄片与有机质薄片重迭粘结而成。由于育珠母贝特征性状不同,养殖海区水质条件、养殖插核技术等的影响,通常海水珍珠只有极少数呈白色,绝大部分呈灰白色、灰黑色等各种不良颜色。从解剖海水珍珠观察可知,不良颜色物质主要分布在珠核与珍珠层之间。
海水珍珠漂白的目的,主要是去除珍珠内的不良颜色物质,使珍珠改色变白。在漂白过程中珍珠结构不可受破坏,珍珠表面不得受腐蚀,更要想方设法地提高珍珠的光泽。根据化学反应的原理,提高漂液的浓度、温度可以加快化学反应速度,可以缩短漂白时间。但是漂液浓度过高,温度超过一定范围,化学反应过激,会产生过大的内应力使珍珠层破裂或使海水珍珠表面受腐蚀,出现“长麻”现象,甚至脱层现象,从而降低珍珠的光泽。而在表面活性剂的帮助下,漂白液充分湿润色素物质,部分色素物质溶解于漂液,在清洗更换漂液时被漂液带出而被清除掉,使珍珠得到部分脱色;某些不稳定的色素物质在光照条件下会产生光异构或光化学作用,使珍珠部分光致脱色;漂液的pH值和光照条件均对珍珠漂白影响很大,所以选择漂白配方和漂白的条件才能发挥好漂白作用。
目前,珍珠漂白的技术主要有(1)过氧化氢漂白;(2)以表面活性剂等作助剂进行漂白;(3)光促漂白技术;(4)低温漂白和固体漂白。由于存在于珍珠中有色物质种类很多,既有有机物又有无机物等,只使用单一漂白方法是难于彻底去除有色物质的,而且每一个漂白配方都不是万能的,要发挥多方法配方的优势,在保证不损坏珍珠结构和光泽的前提下,尽可能使用多种技术、配方接力的方法提高珍珠的白度。日本是研究珍珠漂白技术最早的国家,其对珍珠漂白的技术研究有悠久的历史,而且技术水平在世界上处于领先技术水平,但由于日本对珍珠漂白技术严加保密,其珍珠漂白技术一直鲜为外界知道,所以世界各国都致力于珍珠漂白的技术的研究,但由于技术及资料交流甚少,近年来珍珠漂白技术发展很不平衡,严重影响了珍珠漂白技术的发展。
发明内容
本发明的目的是提供一种海水珍珠漂白的方法,提高我国海水珍珠的质量,促进我国海水珍珠产业的可持续发展。
为了解决上述问题,本发明所采用的技术方案是:
一种海水珍珠的漂白方法,包括如下步骤:
(1)甲醇溶液漂白:在漂白条件下,将珍珠浸泡在装有以甲醇为溶剂的漂白液的烧瓶中,每天将烧瓶内的珍珠进行搅拌、上下翻动数次,5天后用清水漂洗,直至无泡沫为止,将珍珠烘干,更换成新的甲醇漂白液,重复该工序5~6次后,再进行下一步的水漂白工序;
(2)水溶液漂白:在漂白条件下,将珍珠浸泡在装有以水为溶剂的漂白液的烧瓶中,每天将烧瓶内的珍珠搅拌、上下翻动数次,3天后用清水漂洗,直至无泡沫为止,将珍珠烘干,更换成新的水漂白液,重复该工序3~4次后,直至珍珠白透为止;
所述的漂白条件为,在漂白车间或漂白柜中进行,漂白温度为16~18℃,光照强度为(20±5)×103LX,漂白溶液的pH值在8~9,漂白液面高于珍珠平面的1~2cm。
上述的以甲醇为溶剂的漂白液的配制方法如下:
(1)硅酸钠溶液的配制:将1g硅酸钠用适量蒸馏水溶解,定容至1000ml,备用;
(2)将1000ml甲醇、30-40ml的30%过氧化氢、30-40ml硅酸钠溶液和2ml吐温-80混合均匀即可得到以甲醇为溶剂的漂白液。
上述的以水为溶剂的漂白液的配制方法如下:
(1)硅酸钠溶液的配制:将1g硅酸钠用适量蒸馏水溶解,定容至1000ml,备用;
(2)将1000ml蒸馏水、30-40ml的30%过氧化氢、30-40ml硅酸钠溶液和2ml吐温-80混合均匀即可得到以水为溶剂的漂白液。
过氧化氢和硅酸钠溶液的加入量可以根据海水珍珠颜色的深浅调整其加入量。
本发明相对于现有技术的有益效果是:本发明的珍珠漂白方法可用于海水珍珠的漂白工艺,具有漂白速度快、珍珠光泽强、不易返黄、“长麻”率低、成本低的优点;漂白工艺方便操作、容易控制,有利于提高海水珍珠的质量,促进我国海水珍珠产业的可持续发展。
具体实施方式
下面通过实施例对本发明做进一步详细说明,这些实施例仅用来说明本发明,并不限制本发明的范围。
实施例1
一种白色海水珍珠的漂白方法,包括如下步骤:
(1)甲醇溶液漂白:在漂白条件下,将珍珠浸泡在装有以甲醇为溶剂的漂白液的烧瓶中,每天将烧瓶内的珍珠进行搅拌、上下翻动数次,5天后用清水漂洗,直至无泡沫为止,将珍珠烘干,更换成新的甲醇漂白液,重复该工序5~6次后,再进行下一步的水溶液漂白工序;
(2)水溶液漂白:在漂白条件下,将珍珠浸泡在装有以水为溶剂的漂白液的烧瓶中,每天将烧瓶内的珍珠搅拌、上下翻动数次,3天后用清水漂洗,直至无泡沫为止,将珍珠烘干,更换成新的水漂白液,重复该工序3~4次后,直至珍珠白透为止;
上述漂白条件为:在漂白车间或漂白柜中进行,漂白温度为16~18℃,光照强度为(20±5)×103LX,漂白溶液的pH值在8~9,漂白液面高于珍珠平面的1~2cm。
以甲醇为溶剂的漂白液的配制方法如下:
(1)硅酸钠溶液的配制:将1g硅酸钠用适量蒸馏水溶解,定容至1000ml,备用;
(2)将1000ml甲醇、30ml的30%过氧化氢、30ml硅酸钠溶液和2ml吐温-80混合均匀即可得到以甲醇为溶剂的漂白液。
以水为溶剂的漂白液的配制方法如下:
(1)硅酸钠溶液的配制:将1g硅酸钠用适量蒸馏水溶解,定容至1000ml,备用;
(2)将1000ml蒸馏水、30ml的30%过氧化氢、30ml硅酸钠溶液和2ml吐温-80混合均匀即可得到以水为溶剂的漂白液。
上述的工艺适合白色珍珠的漂白。
实施例2
一种深色海水珍珠的漂白方法,包括如下步骤:
(1)甲醇溶液漂白:在漂白条件下,将珍珠浸泡在装有以甲醇为溶剂的漂白液的烧瓶中,每天将烧瓶内的珍珠进行搅拌、上下翻动数次,5天后用清水漂洗,直至无泡沫为止,将珍珠烘干,更换成新的甲醇漂白液,重复该工序5~6次后,再进行下一步的水溶液漂白工序;
(2)水溶液漂白:在漂白条件下,将珍珠浸泡在装有以水为溶剂的漂白液的烧瓶中,每天将烧瓶内的珍珠搅拌、上下翻动数次,3天后用清水漂洗,直至无泡沫为止,将珍珠烘干,更换成新的水漂白液,重复该工序3~4次后,直至珍珠白透为止;
上述漂白条件为:在漂白车间或漂白柜中进行,漂白温度为16~18℃,光照强度为(20±5)×103LX,漂白溶液的pH值在8~9,漂白液面高于珍珠平面的1~2cm。
以甲醇为溶剂的漂白液的配制方法如下:
(1)硅酸钠溶液的配制:将1g硅酸钠用适量蒸馏水溶解,定容至1000ml,备用;
(2)将1000ml甲醇、40ml的30%过氧化氢、40ml硅酸钠溶液和2ml吐温-80混合均匀即可得到以甲醇为溶剂的漂白液。
以水为溶剂的漂白液的配制方法如下:
(1)硅酸钠溶液的配制:将1g硅酸钠用适量蒸馏水溶解,定容至1000ml,备用;
(2)将1000ml蒸馏水、40ml的30%过氧化氢、40ml硅酸钠溶液和2ml吐温-80混合均匀即可得到以水为溶剂的漂白液。
上述的工艺适合深色珍珠的漂白。
Claims (3)
1.一种海水珍珠的漂白方法,其特征在于该方法包括如下步骤:
(1)甲醇溶液漂白:在漂白条件下,将珍珠浸泡在装有以甲醇为溶剂的漂白液的烧瓶中,每天将烧瓶内的珍珠进行搅拌、上下翻动数次,5天后用清水漂洗,直至无泡沫为止,将珍珠烘干,更换成新的甲醇漂白液,重复该工序5~6次后,再进行下一步的水漂白工序;
(2)水溶液漂白:在漂白条件下,将珍珠浸泡在装有以水为溶剂的漂白液的烧瓶中,每天将烧瓶内的珍珠搅拌、上下翻动数次,3天后用清水漂洗,直至无泡沫为止,将珍珠烘干,更换成新的水漂白液,重复该工序3~4次后,直至珍珠白透为止;
所述的漂白条件为,在漂白车间或漂白柜中进行,漂白温度为16~18℃,光照强度为(20±5)×103LX,漂白溶液的pH值为8~9,漂白液面高于珍珠平面1~2cm。
2.根据权利要求1所述的一种海水珍珠的漂白方法,其特征在于:所述的以甲醇为溶剂的漂白液的配制方法如下:
(1)硅酸钠溶液的配制:将1g硅酸钠用适量蒸馏水溶解,定容至1000ml,备用;
(2)将1000ml甲醇、30-40ml的30%过氧化氢、30-40ml硅酸钠溶液和2ml吐温-80混合均匀即可得到以甲醇为溶剂的漂白液。
3.根据权利要求1所述的一种海水珍珠的漂白方法,其特征在于:所述的以水为溶剂的漂白液的配制方法如下:
(1)硅酸钠溶液的配制:将1g硅酸钠用适量蒸馏水溶解,定容至1000ml,备用;
(2)将1000ml蒸馏水、30-40ml的30%过氧化氢、30-40ml硅酸钠溶液和2ml吐温-80混合均匀即可得到以水为溶剂的漂白液。