CN101497535B - 电解法漂白珍珠方法 - Google Patents
电解法漂白珍珠方法 Download PDFInfo
- Publication number
- CN101497535B CN101497535B CN2008100260925A CN200810026092A CN101497535B CN 101497535 B CN101497535 B CN 101497535B CN 2008100260925 A CN2008100260925 A CN 2008100260925A CN 200810026092 A CN200810026092 A CN 200810026092A CN 101497535 B CN101497535 B CN 101497535B
- Authority
- CN
- China
- Prior art keywords
- pearl
- bleaching
- electrolysis
- anode
- electrolyte solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明属电化学技术领域。为了避免漂白时H 2O 2的酸性对珍珠的腐蚀作用,本发明用电解法漂白珍珠。由于电解时在阳极(珍珠置于阳极)未生成对珍珠起腐蚀作用的酸,故避免对珍珠的腐蚀作用。于阳极生成的起漂白作用的HO 2 -的浓度随电解电压或电流的增大而增大,因此,可通过调节电解电压或电流的大小来调节漂白速率的快慢。漂白时,将事先已经预处理并已钻孔的珍珠置于电解池的阳极,以电解质和表面活性剂混合溶液为电解液,电解液的温度控制于0~60℃,电解电压为1~100伏的直流电,每次1~120分钟。电解后珍珠继续浸泡于电解液中,每次电解前更换电解液。一般经8~35天,可漂白全部珍珠。
Description
技术领域:
本发明属电化学技术领域。
背景技术:
人工插核生产的珍珠绝大多数用作装饰品,这就要求珍珠呈白色或其它美丽的颜色。但在珍珠核与珍珠层间及珍珠层与珍珠层间往往夹杂一些污物,使得多数珍珠带有棕黑色、棕黄色等不良颜色,需要漂白。
传统的漂白珍珠的方法是将钻孔后的珍珠浸泡于含低浓度H2O2的漂白液中进行漂白。其中H2O2的酸性对珍珠有严重的腐蚀作用,而使漂白出的珍珠受损。为了减轻H2O2的酸性对珍珠的腐蚀作用,只好降低H2O2的浓度,这又减慢了漂白速率。因此,我国现行的用H2O2漂白珍珠的方法,需要30~50天才能完全漂白珍珠。
发明内容:
为了避免漂白时H2O2的酸性对珍珠的腐蚀作用,本发明用电解法漂白珍珠。由于电解时在阳极(珍珠置于阳极)未生成对珍珠起腐蚀作用的酸,故避免对珍珠的腐蚀作用。于阳极生成的起漂白作用的HO2 -的浓度随电解电压或电流的增大而增大,因此,可通过调节电解电压或电流的大小来调节漂白速率的快慢。
本发明的具体技术方案是:漂白时,将事先已经预处理并已钻孔的珍珠置于电解池的阳极,以电解质和表面活性剂混合溶液为电解液,电解液的温度控制于0~60℃,电解电压为1~100伏的直流电,每次1~120分钟。电解后珍珠继续浸泡于电解液中,每次电解前更换电解液。一般经8~35天,可漂白全部珍珠。
具体实施方式:
实施例一
将1公斤已经预处理并已钻孔的淡棕黑色的有核海水珍珠置于电解池的阳极,以5%NaHCO3溶液为电解液,电解液的温度控制于16℃,电解电压为16伏的直流电,每天电解漂白15分钟,电解后珍珠继续浸泡于电解液中,每次电解前更换电解液、挑出已漂白的珍珠。经15天,可漂白全部珍珠。
实施例二
将1公斤已经预处理并已钻孔的深黑色的有核海水珍珠置于电解池的阳极,以8%NaHCO3溶液为电解液,电解液的温度控制于20℃,电解电压为12伏的直流电,每天电解漂白25分钟,电解后珍珠继续浸泡于电解液中,每次电解前更换电解液、挑出已漂白的珍珠。经25天,可漂白全部珍珠。
Claims (1)
1.电解法漂白珍珠方法,其特征在于:漂白时,将事先已经预处理并已钻孔的珍珠置于电解池的阳极,以电解质和表面活性剂混合溶液为电解液,电解液的温度控制于0~60℃,电解电压为1~100伏的直流电,每次1~120分钟,电解后珍珠继续浸泡于电解液中,每次电解前更换电解液。