CN1803609A - 超细煅烧滑石粉制备方法 - Google Patents

超细煅烧滑石粉制备方法 Download PDF

Info

Publication number
CN1803609A
CN1803609A CN 200610042268 CN200610042268A CN1803609A CN 1803609 A CN1803609 A CN 1803609A CN 200610042268 CN200610042268 CN 200610042268 CN 200610042268 A CN200610042268 A CN 200610042268A CN 1803609 A CN1803609 A CN 1803609A
Authority
CN
China
Prior art keywords
talc powder
powder
orders
broken
calcinated talc
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200610042268
Other languages
English (en)
Other versions
CN100463854C (zh
Inventor
刘兴良
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNB2006100422687A priority Critical patent/CN100463854C/zh
Publication of CN1803609A publication Critical patent/CN1803609A/zh
Application granted granted Critical
Publication of CN100463854C publication Critical patent/CN100463854C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种超细煅烧滑石粉制备方法，滑石矿经过煅烧步骤、磨剥步骤、收集烘干步骤、打散步骤，即可制成3000目－10000目的超细煅烧滑石粉，本制备方法的优点是：1.首先煅烧生滑石矿，煅烧工艺简单，便于进料出料，生产效率较高；2.采用剥片机进行磨剥，磨剥的产品粒度能达到很高的要求。

Description

超细煅烧滑石粉制备方法
技术领域
本发明涉及一种制造超细煅烧滑石粉的方法。
背景技术
滑石是一种具层状构造的含水的镁质硅酸盐矿物，化学式为Mg3[Si4O10](OH)2，以氧化物表示为3MgO·4SiO2·H2O。由于其质软，有很强的滑腻感而得名。滑石具有较高的电绝缘性、绝热性、高熔点和对油类有强烈的吸附性能，因此在工业上有广泛的用途。而且随着工业的发展，用量不断增加，应用范围日益扩大，尤其是经过煅烧的滑石粉广泛应用于陶瓷、电子元件、塑料、油漆、电瓷、橡胶、医药、食品等行业，是一种很有发展前途的多功能材料。
超细煅烧滑石粉具有更优良的特性，但至今没有一种有效的方法大批量、高效率地制造该产品。
发明内容
本发明所要解决的技术问题是提供一种大批量、高效率地生产超细煅烧滑石粉的超细煅烧滑石粉制备方法。
为实现上述目的，本发明的技术方案是：超细煅烧滑石粉制备方法，它包括以下步骤
第一步  煅烧步骤：将未经煅烧的滑石粉和滑石颗粒在900℃至1350℃之间煅烧，去掉结晶水；然后将煅烧后的滑石粉和滑石颗粒磨成200目以上的煅烧滑石粉；
第二步  磨剥步骤：将磨成200目以上的煅烧滑石粉加入水并搅拌打浆，浆液的浓度在40％-60％之间；然后用泥浆泵将浆液送剥片机超细磨剥至3000目-10000目；
第三步  收集烘干步骤：将超细磨剥至3000目-10000目的浆液过滤收集，并烘干；
第四步  打散步骤：将烘干后的超细煅烧滑石粉打散，即制成成品。
作为一种改进，所述剥片机为若干台串联使用。
作为一种改进，所述打散步骤采用气流磨打散、或叶片式打散机打散、或辊压式打散机打散。
由于采用上述技术方案，滑石矿经过煅烧步骤、磨剥步骤、收集烘干步骤、打散步骤，即可制成3000目-10000目的超细煅烧滑石粉，本制备方法的优点是：1、首先煅烧生滑石矿，煅烧工艺简单，便于进料出料，生产效率较高；2、采用剥片机进行磨剥，磨剥的产品粒度能达到很高的要求。
具体实施方式
超细煅烧滑石粉制备方法，包括以下步骤
第一步  煅烧步骤：将未经煅烧的滑石粉和滑石颗粒在900℃至1350℃之间煅烧，去掉结晶水；然后将煅烧后的滑石粉和滑石颗粒磨成200目以上的煅烧滑石粉；
第二步  磨剥步骤：将磨成200目以上的煅烧滑石粉加入水并搅拌打浆，浆液的浓度在40％-60％之间；然后用泥浆泵将浆液送剥片机超细磨剥至3000目-10000目；
第三步  收集烘干步骤：将超细磨剥至3000目-10000目的浆液过滤收集，并烘干；
第四步  打散步骤：将烘干后的超细煅烧滑石粉打散，即制成成品。
其中，所述剥片机根据产品细度要求可以采用若干台串联使用。
其中，所述打散步骤采用气流磨打散、或叶片式打散机打散、或辊压式打散机打散。

Claims (3)

1.超细煅烧滑石粉制备方法，其特征是：它包括以下步骤
第一步煅烧步骤：将未经煅烧的滑石粉和滑石颗粒在900℃至1350℃之间煅烧，去掉结晶水；然后将煅烧后的滑石粉和滑石颗粒磨成200目以上的煅烧滑石粉；
第二步磨剥步骤：将磨成200目以上的煅烧滑石粉加入水并搅拌打浆，浆液的浓度在40％-60％之间；然后用泥浆泵将浆液送剥片机超细磨剥至3000目-10000目；
第三步收集烘干步骤：将超细磨剥至3000目-10000目的浆液过滤收集，并烘干；
第四步打散步骤：将烘干后的超细煅烧滑石粉打散，即制成成品。
2.如权利要求1所述的超细煅烧滑石粉制备方法，其特征是：所述剥片机为若干台串联使用。
3.如权利要求1所述的超细煅烧滑石粉制备方法，其特征是：所述打散步骤采用气流磨打散、或叶片式打散机打散、或辊压式打散机打散。
CNB2006100422687A 2006-01-20 2006-01-20 超细煅烧滑石粉制备方法 Expired - Fee Related CN100463854C (zh)