CN101864199A - 一种改性复合超细滑石粉制备方法 - Google Patents

一种改性复合超细滑石粉制备方法 Download PDF

Info

Publication number
CN101864199A
CN101864199A CN 201010199123 CN201010199123A CN101864199A CN 101864199 A CN101864199 A CN 101864199A CN 201010199123 CN201010199123 CN 201010199123 CN 201010199123 A CN201010199123 A CN 201010199123A CN 101864199 A CN101864199 A CN 101864199A
Authority
CN
China
Prior art keywords
grinding
talcum powder
fine
ultra
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201010199123
Other languages
English (en)
Inventor
朱自学
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 201010199123 priority Critical patent/CN101864199A/zh
Publication of CN101864199A publication Critical patent/CN101864199A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种改性复合超细滑石粉制备方法，制备过程包括以下步骤：(1)对原料进行破碎处理，再将破碎后的物料用粉磨磨成细粉；(2)将粉磨后的物料加水和助磨药剂配置成固浓度在50％～70％的浆料并搅拌均匀；(3)将复合改性剂硅烷偶联剂和硬脂酸钠配置成表面改性溶液倒入制浆的物料中改性；(4)对改性处理后的物料进行湿式超细精磨，矿浆超细精磨的细度要求颗粒小于2μm的比例占95％以上；(5)对超细精磨后的物料进行强力干燥并收集制品。本发明采用湿法超细剥磨和强力干燥工艺，制成的改性复合超细滑石粉，其粒度较普通滑石粉更细、分布更窄，并且耐曝嗮，抗高温，且耐水性好，耐污染、耐老化性能较强。

Description

一种改性复合超细滑石粉制备方法
技术领域
本发明涉及一种改性复合超细滑石粉的制备方法。
背景技术
滑石粉是一种含水的镁硅酸盐矿物，其化学式为3MgO·4SiO2·H2O。由于滑石粉对大多数化学试剂呈现惰性，与酸接触不分解，是电的不良导体，导热性低且耐热冲击性高，加热到900℃的高温仍不分解，这些优良性能使得其成为一种很好的填充剂，可用于填充塑料或用于涂料的添加剂。目前滑石粉已经被广泛应用于涂料、造纸、塑料和化妆品等行业，而国内市场所需的滑石粉主要依靠进口。尤其是超细滑石粉，由于生产技术要求很高，目前国内市场尚较为稀缺。而现有的超细滑石粉制备方法普遍采用干法超细粉碎工艺，由于制作过程中所需的流化床气流粉碎机能耗大、成本高、生产效率低且深加工能力差，导致滑石粉产品成本高昂且细度不够和粒度分布较宽的缺陷。
发明内容
本发明所要解决的技术问题就是提供一种改性复合超细滑石粉的制备方法，制备出的滑石粉粒度更细、耐水性更好、耐酸碱腐蚀性更强、生产成本更低。
为解决上述技术问题，本发明采用如下技术方案：一种改性复合超细滑石粉制备方法，其特征在于制备过程包括以下步骤：
(1)对原料进行破碎处理，即将矿山开采出来的滑石矿经破碎机粉碎；将破碎后的物料用粉磨磨成细粉；
(2)将粉磨后的物料加水和助磨药剂配置成固浓度在50％～70％的浆料并搅拌均匀，其中加入助磨药剂的量为浆料总重的0.5～3％；
(3)将复合改性剂硅烷偶联剂和硬脂酸钠配置成表面改性溶液倒入制浆的物料中改性；
(4)对改性处理后的物料进行湿式超细精磨，矿浆超细精磨的细度要求颗粒小于2μm的比例占95％以上；
(5)对超细精磨后的物料进行强力干燥并收集制品。
作为优选，所述硅烷偶联剂与硬脂酸钠的重量比为1∶3，所述硅烷偶联剂与硬脂酸钠加入量占制浆后物料总重量的5％。
作为优选，所述滑石粉经过粉磨后细粉细度达到350目。
作为优选，所述助磨药剂为聚丙烯酸、聚丙烯酸盐、磷酸盐、磷酸盐多聚物中的一种或者两种以上的混合物。
作为优选，所述湿式超细精磨根据细度要求，或者用单台设备循环生产，或者串联2台至6台进行连续生产。
本发明采用湿法超细剥磨和强力干燥工艺，研制而成的改性复合超细滑石粉，其粒度较普通滑石粉更细、分布更窄，并且耐曝嗮，抗高温，在紫外光照射下不变色，能长期保持原有的光泽和色彩，有较好的耐酸碱腐蚀的性能，且耐水性好，耐污染、耐老化性能较强。广泛应用于农业、运输、能源、环保新材料工业，尤其适用于具有特殊功能需求的有机物高科技市场。具有广阔的市场前景。
具体实施方式
一种改性复合超细滑石粉制备方法实施例，制备过程包括以下步骤：
(1)对原料进行破碎处理，即将矿山开采出来的滑石矿经破碎机粉碎。将破碎后的物料用雷蒙磨或其他设备粉磨，使物料达到一定细度；所述滑石粉经过粉磨后细粉细度达到350目。
(2)将粉磨后的物料加水和助磨药剂配置成固浓度在50％～70％的浆料并搅拌均匀，其中加入助磨药剂的量为浆料总重的0.5～3％；所述助磨药剂为聚丙烯酸、聚丙烯酸盐、磷酸盐、磷酸盐多聚物中的一种或者两种以上的混合物。
(3)配置表面改性溶液，将复合改性剂硅烷偶联剂和硬脂酸钠倒入制浆的物料中；所述硅烷偶联剂与硬脂酸钠的重量比为1∶3，所述硅烷偶联剂与硬脂酸钠加入量占制浆后物料总重量的5％。
(4)对改性处理后的物料进行湿式超细精磨。矿浆超细精磨的细度要求颗粒小于2μm的比例占95％以上，设备的使用可根据具体细度要求串联2台至6台进行连续生产或单台设备循环生产；
(5)对超细精磨后的物料进行强力干燥并收集制品。强力干燥机的干燥可以有效获得水分小于1％的产品，其粉碎是指将干燥后的滑石粉颗粒再碎散达到原来的细度。

Claims (5)

1.一种改性复合超细滑石粉制备方法，其特征在于制备过程包括以下步骤：
(1)对原料进行破碎处理，即将矿山开采出来的滑石矿经破碎机粉碎；将破碎后的物料用粉磨磨成细粉；
(2)将粉磨后的物料加水和助磨药剂配置成固浓度在50％～70％的浆料并搅拌均匀，其中加入助磨药剂的量为浆料总重的0.5～3％；
(3)将复合改性剂硅烷偶联剂和硬脂酸钠配置成表面改性溶液倒入制浆的物料中改性；
(4)对改性处理后的物料进行湿式超细精磨，矿浆超细精磨的细度要求颗粒小于2μm的比例占95％以上；
(5)对超细精磨后的物料进行强力干燥并收集制品。
2.根据权利要求1所述的改性复合超细滑石粉制备方法，其特征在于：所述硅烷偶联剂与硬脂酸钠的重量比为1∶3，所述硅烷偶联剂与硬脂酸钠加入量占制浆后物料总重量的5％。
3.根据权利要求1所述的改性复合超细滑石粉制备方法，其特征在于：所述滑石粉经过粉磨后细粉细度达到350目。
4.根据权利要求2所述的改性复合超细滑石粉制备方法，其特征在于：所述助磨药剂为聚丙烯酸、聚丙烯酸盐、磷酸盐、磷酸盐多聚物中的一种或者两种以上的混合物。
5.根据权利要求1所述的改性复合超细滑石粉制备方法，其特征在于：所述湿式超细精磨根据细度要求，或者用单台设备循环生产，或者串联2台至6台进行连续生产。
CN 201010199123 2010-06-11 2010-06-11 一种改性复合超细滑石粉制备方法 Pending CN101864199A (zh)