CN1785871A - 一种含磷锂铝硅玻璃陶瓷及其制备方法 - Google Patents
一种含磷锂铝硅玻璃陶瓷及其制备方法 Download PDFInfo
- Publication number
- CN1785871A CN1785871A CN 200510061302 CN200510061302A CN1785871A CN 1785871 A CN1785871 A CN 1785871A CN 200510061302 CN200510061302 CN 200510061302 CN 200510061302 A CN200510061302 A CN 200510061302A CN 1785871 A CN1785871 A CN 1785871A
- Authority
- CN
- China
- Prior art keywords
- oxide
- glass
- ceramic
- lithium aluminium
- containing phosphorus
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (2)