CN1778853A - 虫胶快速漂白及脱氯的方法 - Google Patents

虫胶快速漂白及脱氯的方法 Download PDF

Info

Publication number
CN1778853A
CN1778853A CN 200410079567 CN200410079567A CN1778853A CN 1778853 A CN1778853 A CN 1778853A CN 200410079567 CN200410079567 CN 200410079567 CN 200410079567 A CN200410079567 A CN 200410079567A CN 1778853 A CN1778853 A CN 1778853A
Authority
CN
China
Prior art keywords
shellac
glue
bleaching
chlorine
dechlorination
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200410079567
Other languages
English (en)
Other versions
CN100345926C (zh
Inventor
李琳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNB2004100795679A priority Critical patent/CN100345926C/zh
Publication of CN1778853A publication Critical patent/CN1778853A/zh
Application granted granted Critical
Publication of CN100345926C publication Critical patent/CN100345926C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供一种虫胶快速漂白及脱氯的方法，它将虫胶、纯碱及水混合加热至75～95℃，溶解成浓度小于25％的虫胶碱溶液，过滤并恒温在75～95℃；按50－90r/min的速度对所得虫胶碱溶液搅拌，同时加入含氯漂白剂，使有效氯含量为15～22％，搅拌30－40min，得漂白胶液；再升温至85～95℃，并按50－90r/min的速度搅拌3～8min，得脱氯胶液。它缩短了50％的漂白时间，并使产品氯含量在1％以下，有效延长了储存期，省去了次氯酸钠的稀释过程及设备，而且产品质量稳定，保质期长，在使用时不会改变或影响使用对象的颜色，从而有效增加了漂白虫胶在各行业中的应用范围。

Description

虫胶快速漂白及脱氯的方法
技术领域
本发明涉及一种漂白及脱氯的方法，尤其是一种对虫胶进行快速漂白及脱氯的方法，属于化工产品加工与处理技术领域。
背景技术
虫胶是一种粘合力较强的树脂。虫胶树脂是由分子量为300-3000的羟基酸衍生而成的聚酯树脂，主要由罂子桐酸和壳脑酸组成，此外还含有蜡质和色素等物质。除粘合力外，虫胶树脂还具有较好的电绝缘性能、防水性能、防潮和防锈性能、防紫外线性能以及耐油、耐酸性能，并对人体无毒性和刺激性，而且可塑性强，固色性能好等等，因此被广泛应用于农业、轻工业、重工业生产中以及人们的吃、穿、用等生活用品中，所涉及的用途达200多种以上。就工业用途来说，主要用在涂料、木器、制模、制帽、服装、医药和食品工业、绝缘、造纸、油墨、国防工业等，特别是近年来由于人们对食品安全的要求越来越高，因此，在医药、食品工业及其相关领域，人们更加关注或需求纯天然的绿色环保产品。而作为纯天然树脂的虫胶必将替代化工合成树脂，使之成为药膜包衣、果蔬涂膜保鲜、食品防潮的首选原料。为满足上述工业需求，所用的虫胶必须具有不影响使用对象的颜色，且绝缘性能优越，粘度和水溶性较强等特点。这就要求虫胶颜色尽量浅，蜡质含量低。但目前已有的漂白虫胶或精制漂白虫胶(脱蜡漂白胶)由于受现有工艺中漂白方法的制约，使漂白后的胶液中残留有大量的游离氯，而残留的游离氯在虫胶储存过程中易使之变质，从而影响虫胶产品质量。此外，现有的加工工艺还存在着漂白时间长，连续性差，生产设备多，成本高，生产效率低等不足。因此，有必要对现有技术加以改进。
发明内容
本发明的目的在于克服现有技术之不足，提供一种工艺简单、生产成本低、效率高并能脱出游离氯的虫胶快速漂白及脱氯的方法。
本发明通过下列技术方案实现：一种虫胶快速漂白及脱氯的方法，其特征在于包括下列工艺步骤：
A、在虫胶中加入纯碱及水后加热至75～95℃，使之溶解成浓度小于25％质量比的虫胶碱溶液，过滤弃渣，并恒温在75～95℃；
B、按50-90r/min的速度对所得的温度保持在75～95℃的虫胶碱溶液进行搅拌，同时加入含氯漂白剂，使有效氯含量为15～22％的质量比，搅拌30-40min，得漂白胶液；
C、将上述漂白胶液升温至85～95℃，并按50-90r/min的速度搅拌3～8min，使次氯酸钠受热分解，得脱氯胶液；
D、将上述脱氯胶液进行脱蜡、加酸中和、过滤洗涤得粒状漂白胶，再经过压片、干燥后，即得漂白虫胶产品。
所述D步骤的脱蜡、加酸中和、过滤洗涤，压片、干燥均为现有技术中的工艺过程。
所述含氯漂白剂为市售的次氯酸钠，或者氯气，或者液氯，或者二氧化氯，或者双氧水。
所述虫胶为市售的颗粒虫胶或片胶或未经漂白过的虫胶。
本发明提供的方法，对普通漂白胶以及精制漂白虫胶都适用。
本发明与现有技术相比具有下列优点和效果：采用上述方案，缩短了50％的漂白时间，并实现了生产工艺的连续性，而且经过加热脱氯后，产品氯含量在1％以下，20℃条件下贮存期大于18个月，比现有工艺生产的产品的贮存期延长了8个月，而且次氯酸钠不必稀释为有效氯含量为5％，可以直接按次氯酸钠商品固有的有效氯含量进行漂白，省去了稀释次氯酸钠的稀释设备，因此，是一项工艺流程短，漂白时间短，节省设备投资，产品质量稳定，保质期长的虫胶漂白与脱氯工艺，用该工艺生产的漂白虫胶在使用时不会改变或影响使用对象的颜色，并具有优越的绝缘性能、粘度和水溶性等特点，从而有效增加了漂白虫胶在各行业中的应用范围。
具体实施方式
下面结合实施例对本发明做进一步描述。
实施例1
A、取虫胶，并加水，按足以中和虫胶酸的量加入碱，搅拌并加热至75℃，使虫胶溶解成浓度为25％质量比以下的虫胶碱溶液，用粗筛进行粗滤，弃渣得粗滤胶液，再用细筛进行细滤，弃渣得细滤胶液，并使胶液恒温在80℃；
B、将上述恒温在80℃的胶液，按50r/min的速度进行搅拌，同时加入市售的次氯酸钠，使有效氯含量为15％的质量比，搅拌40min后，即完成虫胶的漂白而得漂白胶液；
C、将上述所得漂白虫胶液升温至85℃，并按90r/min的速度搅拌3min，使次氯酸钠受热分解，即完成漂白虫胶的脱氯而得脱氯胶液；
D、将上述脱氯胶液用现有工艺方法进行脱蜡、加酸中和、过滤洗涤得粒状漂白胶，再经过压片、干燥后，即得漂白虫胶产品。
实施例2
A、取虫胶，并加水，按足以中和虫胶酸的量加入碱，搅拌并加热至80℃，使虫胶溶解成浓度为25％质量比以下的虫胶碱溶液，用粗筛进行粗滤，弃渣得粗滤胶液，再用细筛进行细滤，弃渣得细滤胶液，并使胶液恒温在80℃；
B、按90r/min的速度对所得的温度保持在80℃的虫胶碱溶液进行搅拌，同时加入二氧化氯漂白剂，使有效氯含量为22％的质量比，搅拌30min，得漂白胶液；
C、将上述漂白胶液升温至80℃，并按50r/min的速度搅拌8min，使二氧化氯受热分解，得脱氯胶液；
D、将上述脱氯胶液进行脱蜡、加酸中和、过滤洗涤得粒状漂白胶，再经过压片、干燥后，即得漂白虫胶产品。
实施例3
A、取虫胶，并加水，按足以中和虫胶酸的量加入碱，搅拌并加热至90℃，使虫胶溶解成浓度为25％质量比以下的虫胶碱溶液，用粗筛进行粗滤，弃渣得粗滤胶液，再用细筛进行细滤，弃渣得细滤胶液，并使胶液恒温在90℃；
B、按70r/min的速度对所得的温度保持在90℃的虫胶碱溶液进行搅拌，同时加入液氯漂白剂，使有效氯含量为22％的质量比，搅拌35min，得漂白胶液；
C、将上述漂白胶液升温至95℃，并按80r/min的速度搅拌5min，使液氯受热分解，得脱氯胶液；
D、将上述脱氯胶液进行脱蜡、加酸中和、过滤洗涤得粒状漂白胶，再经过压片、干燥后，即得漂白虫胶产品。

Claims (4)

1、一种虫胶快速漂白及脱氯的方法，其特征在于包括下列工艺步骤：
A、在虫胶中加入纯碱及水后加热至75～95℃，使之溶解成浓度小于25％质量比的虫胶碱溶液，过滤弃渣，并恒温在75～95℃；
B、按50-90r/min的速度对所得的温度保持在75～95℃的虫胶碱溶液进行搅拌，同时加入含氯漂白剂，使有效氯含量为15～22％的质量比，搅拌30-40min，得漂白胶液；
C、将上述漂白胶液升温至85～95℃，并按50-90r/min的速度搅拌3～8min，使次氯酸钠受热分解，得脱氯胶液；
D、将上述脱氯胶液进行脱蜡、加酸中和、过滤洗涤得粒状漂白胶，再经过压片、干燥后，即得漂白虫胶产品。
2、根据权利要求1所述的方法，其特征在于所述D步骤的脱蜡、加酸中和、过滤洗涤，压片、干燥均为现有技术中的工艺过程。
3、根据权利要求1所述的方法，其特征在于所述含氯漂白剂为市售的次氯酸钠，或者氯气，或者液氯，或者二氧化氯，或者双氧水。
4、根据权利要求1所述的方法，其特征在于所述虫胶为市售的颗粒虫胶或片胶或未经漂白过的虫胶。
CNB2004100795679A 2004-11-18 2004-11-18 虫胶快速漂白及脱氯的方法 Expired - Fee Related CN100345926C (zh)