CN1693400A - 复膜铝箔胶带及其制造方法 - Google Patents

复膜铝箔胶带及其制造方法 Download PDF

Info

Publication number
CN1693400A
CN1693400A CN 200510074539 CN200510074539A CN1693400A CN 1693400 A CN1693400 A CN 1693400A CN 200510074539 CN200510074539 CN 200510074539 CN 200510074539 A CN200510074539 A CN 200510074539A CN 1693400 A CN1693400 A CN 1693400A
Authority
CN
China
Prior art keywords
layer
line
aluminium foil
glue
thickness
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200510074539
Other languages
English (en)
Other versions
CN1312242C (zh
Inventor
李盈峰
郑炳恩
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
FENGYOU ADHESIVE PROTECTS Co Ltd XIAMEN
Original Assignee
FENGYOU ADHESIVE PROTECTS Co Ltd XIAMEN
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by FENGYOU ADHESIVE PROTECTS Co Ltd XIAMEN filed Critical FENGYOU ADHESIVE PROTECTS Co Ltd XIAMEN
Priority to CNB2005100745392A priority Critical patent/CN1312242C/zh
Publication of CN1693400A publication Critical patent/CN1693400A/zh
Application granted granted Critical
Publication of CN1312242C publication Critical patent/CN1312242C/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

复膜铝箔胶带及其制造方法，涉及一种铝箔胶带，尤其是涉及一种采用复膜的铝箔胶带及其制造方法。提供一种改进的铝箔胶带及其制造方法。设有塑料薄膜层和铝箔层，在塑料薄膜层与铝箔层之间为中间胶层，在铝箔层的底面设底层胶层。其步骤为：在塑料薄膜层上表面涂胶，形成中间胶层；在中间胶层上复上铝箔层；在铝箔层的下表面涂胶，形成底层胶层，即制成复膜铝箔胶带。具有优良的防腐、抗拉、易撕断、初粘性和持粘性好的特性，使用既方便又广泛，成本低，利用率高，减少了资源浪费。

Description

复膜铝箔胶带及其制造方法
技术领域
本发明涉及一种铝箔胶带，尤其是涉及一种采用复膜的铝箔胶带及其制造方法。
背景技术
已有的铝箔胶带，例如厦门长天塑化有限公司出品的铝箔胶带为三层结构，由铝箔层和隔离纸层叠合，在铝箔层与隔离纸层之间涂一层胶。其主要缺点是需用较厚的隔离纸层，浪费资源，成本高，1卷铝箔胶带的实际长度较短，利用率低，隔离纸容易吸潮霉变。其产品长期以来得不到很好解决。ZL01265953.3号专利提供一种导电铝箔胶带，包括绝缘层，其表面涂覆有胶粘剂，其特殊之处在于：所述胶粘剂是其内混有均布导电粒子的导电胶粘剂，该导电胶粘剂与绝缘层间涂覆有底胶。
发明内容
本发明的目的在于针对已有铝箔胶带浪费资源、成本高、利用率低等不足，提供一种改进的铝箔胶带及其制造方法。为此本发明主要采用以复膜代替隔离纸的技术方案。
本发明所说的复膜铝箔胶带设有塑料薄膜层和铝箔层，在塑料薄膜层与铝箔层之间为中间胶层，在铝箔层的底面设底层胶层，所说的塑料薄膜层选自聚酯(PET)薄膜层，聚氯乙烯(PVC)薄膜层、苯二甲酸(PTA)薄膜层、乙二醇(EG)薄膜层、聚乙稀(PE)薄膜层等、聚丙烯双向拉伸(BOPP)薄膜层或聚丙烯(PP)薄膜层等，所说的中间胶层选自水性胶层、油性胶层、压敏胶层、油性复膜胶层或水性复膜胶层等，中间胶层最好选自油性胶层或水性复膜胶层。所说的底层胶层选自水性胶层、油性胶层、压敏胶层、油性复膜胶层或水性复膜胶层等，底层胶层最好选自水性胶层、油性胶层或压敏胶层等。铝箔层的厚度为4～40μm，优选10～25μm；塑料薄膜层的厚度为4～40μm，优选10～25μm；中间胶层的厚度为4～40μm，优选4～10μm；底层胶层的厚度为4～40μm，优选15～30μm。
本发明所说的复膜铝箔胶带的制造方法其步骤为：
1)在塑料薄膜层上表面涂胶，形成中间胶层；
2)在中间胶层上复上铝箔层；
3)在铝箔层的下表面涂胶，形成底层胶层，即制成复膜铝箔胶带。
在塑料薄膜层上表面涂胶时，可采用上胶辊筒涂胶，后经5～10m烘道，烘道温度为80～100℃，再经预压辊后到压力辊，压力辊的温度为80～100℃，速度为10～30m/min，形成中间胶层。
可将复膜铝箔胶带加工成复膜铝箔胶带卷。
与已有的铝箔胶带相比，本发明具有优良的防腐、抗拉、易撕断、初粘性和持粘性好的特性，使用既方便又广泛，成本低，利用率高，减少了资源浪费。
附图说明
图1为本发明实施例的结构示意图。
具体实施方式
实施例1
如图1所示，本发明所说的复膜铝箔胶带设有塑料薄膜层1和铝箔层2，在塑料薄膜层1上表面涂油性胶，采用上胶辊筒涂胶，后经5m烘道，烘道温度为80℃，再经预压辊后到压力辊，压力辊的温度为80℃，速度为10m/min，形成中间胶层3。在中间胶层3上复上铝箔层2，在铝箔层2的底面涂水性胶，形成底层胶层4，即制成复膜铝箔胶带。将复膜铝箔胶带加工成复膜铝箔胶带卷。
铝箔层2的厚度为4μm；塑料薄膜层1的厚度为10μm；中间胶层3的厚度为10μm，底层胶层4的厚度为4μm。
实施例2
与实施例1类似，其区别在于加工复膜铝箔胶带的步骤为：在塑料薄膜层1上表面涂水性复膜胶，采用上胶辊筒涂胶，后经8m烘道，烘道温度为90℃，再经预压辊后到压力辊，压力辊的温度为90℃，速度为30m/min，形成中间胶层3。在中间胶层3上复上铝箔层2，在铝箔层2的底面涂油性胶，形成底层胶层4，即制成复膜铝箔胶带。将复膜铝箔胶带加工成复膜铝箔胶带卷。
铝箔层的厚度为10μm；塑料薄膜层的厚度为25μm；中间胶层的厚度为15μm，底层胶层的厚度为10μm。
实施例3
与实施例1类似，其区别在于加工复膜铝箔胶带的步骤为：在塑料薄膜层1上表面涂水性胶，采用上胶辊筒涂胶，后经10m烘道，烘道温度为100℃，再经预压辊后到压力辊，压力辊的温度为100℃，速度为25m/min，形成中间胶层3。在中间胶层3上复上铝箔层2，在铝箔层2的底面涂压敏胶，形成底层胶层4，即制成复膜铝箔胶带。将复膜铝箔胶带加工成复膜铝箔胶带卷。
铝箔层的厚度为15μm；塑料薄膜层的厚度为4μm；中间胶层的厚度为4μm，底层胶层的厚度为20μm。
实施例4
与实施例1类似，其区别在于加工复膜铝箔胶带的步骤为：在塑料薄膜层1上表面涂压敏胶，采用上胶辊筒涂胶，后经10m烘道，烘道温度为85℃，再经预压辊后到压力辊，压力辊的温度为95℃，速度为20m/min，形成中间胶层3。在中间胶层3上复上铝箔层2，在铝箔层2的底面涂油性复膜胶，形成底层胶层4，即制成复膜铝箔胶带。将复膜铝箔胶带加工成复膜铝箔胶带卷。
铝箔层的厚度为20μm；塑料薄膜层的厚度为35μm；中间胶层的厚度为25μm，底层胶层的厚度为25μm。
实施例5
与实施例1类似，其区别在于加工复膜铝箔胶带的步骤为：在塑料薄膜层1上表面涂油性复膜胶，采用上胶辊筒涂胶，后经6m烘道，烘道温度为100℃，再经预压辊后到压力辊，压力辊的温度为85℃，速度为25m/min，形成中间胶层3。在中间胶层3上复上铝箔层2，在铝箔层2的底面涂水性胶，形成底层胶层4，即制成复膜铝箔胶带。将复膜铝箔胶带加工成复膜铝箔胶带卷。
铝箔层的厚度为25μm；塑料薄膜层的厚度为40μm；中间胶层的厚度为35μm，底层胶层的厚度为30μm。
实施例6
与实施例1类似，其区别在于加工复膜铝箔胶带的步骤为：在塑料薄膜层1上表面涂水性复膜胶，采用上胶辊筒涂胶，后经7m烘道，烘道温度为100℃，再经预压辊后到压力辊，压力辊的温度为100℃，速度为20m/min，形成中间胶层3。在中间胶层3上复上铝箔层2，在铝箔层2的底面涂水性胶，形成底层胶层4，即制成复膜铝箔胶带。将复膜铝箔胶带加工成复膜铝箔胶带卷。
铝箔层的厚度为30μm；塑料薄膜层的厚度为10μm；中间胶层的厚度为20μm，底层胶层的厚度为15μm。
实施例7
与实施例1类似，其区别在于加工复膜铝箔胶带的步骤为：在塑料薄膜层1上表面涂油性胶，采用上胶辊筒涂胶，后经8m烘道，烘道温度为95℃，再经预压辊后到压力辊，压力辊的温度为85℃，速度为15m/min，形成中间胶层3。在中间胶层3上复上铝箔层2，在铝箔层2的底面涂油性胶，形成底层胶层4，即制成复膜铝箔胶带。将复膜铝箔胶带加工成复膜铝箔胶带卷。
铝箔层的厚度为35μm；塑料薄膜层的厚度为30μm；中间胶层的厚度为40μm，底层胶层的厚度为35μm。
实施例8
与实施例1类似，其区别在于加工复膜铝箔胶带的步骤为：在塑料薄膜层1上表面涂水性复膜胶，采用上胶辊筒涂胶，后经10m烘道，烘道温度为80℃，再经预压辊后到压力辊，压力辊的温度为90℃，速度为15m/min，形成中间胶层3。在中间胶层3上复上铝箔层2，在铝箔层2的底面涂压敏胶，形成底层胶层4，即制成复膜铝箔胶带。将复膜铝箔胶带加工成复膜铝箔胶带卷。
铝箔层的厚度为40μm；塑料薄膜层的厚度为20μm；中间胶层的厚度为10μm，底层胶层的厚度为40μm。

Claims (10)

1、复膜铝箔胶带，其特征在于设有塑料薄膜层和铝箔层，在塑料薄膜层与铝箔层之间为中间胶层，在铝箔层的底面设底层胶层。
2、如权利要求1所述的复膜铝箔胶带，其特征在于所说的塑料薄膜层选自聚酯薄膜层，聚氯乙烯薄膜层、苯二甲酸薄膜层、乙二醇薄膜层、聚乙稀薄膜层等、聚丙烯双向拉伸薄膜层或聚丙烯薄膜层。
3、如权利要求1所述的复膜铝箔胶带，其特征在于所说的中间胶层选自水性胶层、油性胶层、压敏胶层、油性复膜胶层或水性复膜胶层，优选油性胶层或水性复膜胶层。
4、如权利要求1或3所述的复膜铝箔胶带，其特征在于所说的底层胶层选自水性胶层、油性胶层、压敏胶层、油性复膜胶层或水性复膜胶层，优选水性胶层、油性胶层或压敏胶层等。
5、如权利要求1所述的复膜铝箔胶带，其特征在于铝箔层的厚度为4～40μm，优选10～25μm；塑料薄膜层的厚度为4～40μm，优选10～25μm；中间胶层的厚度为4～40μm，优选4～10μm；底层胶层的厚度为4～40μm，优选15～30μm。
6、复膜铝箔胶带的制造方法，其特征在于其步骤为：
1)在塑料薄膜层上表面涂胶，形成中间胶层；
2)在中间胶层上复上铝箔层；
3)在铝箔层的下表面涂胶，形成底层胶层，即制成复膜铝箔胶带。
7、如权利要求6所述的复膜铝箔胶带的制造方法，其特征在于在塑料薄膜层上表面涂胶时，采用上胶辊筒涂胶，后经5～10m烘道，烘道温度为80～100℃，再经预压辊后到压力辊，压力辊的温度为80～100℃，速度为10～30m/min，形成中间胶层。
8、如权利要求6所述的复膜铝箔胶带的制造方法，其特征在于所说的塑料薄膜层选自聚酯薄膜层，聚氯乙烯薄膜层、苯二甲酸薄膜层、乙二醇薄膜层、聚乙稀薄膜层、聚丙烯双向拉伸薄膜层或聚丙烯薄膜层。
9、如权利要求6所述的复膜铝箔胶带的制造方法，其特征在于所说的中间胶层和底层胶层选自水性胶层、油性胶层、压敏胶层、油性复膜胶层或水性复膜胶层；所说的中间胶层优选油性胶层或水性复膜胶层，所说的底层胶层优选水性胶层、油性胶层或压敏胶层。
10、如权利要求6所述的复膜铝箔胶带的制造方法，其特征在于铝箔层的厚度为4～40μm，优选10～25μm；塑料薄膜层的厚度为4～40μm，优选10～25μm；中间胶层的厚度为4～40μm，优选4～10μm；底层胶层的厚度为4～40μm，优选15～30μm。
CNB2005100745392A 2005-05-26 2005-05-26 复膜铝箔胶带及其制造方法 Active CN1312242C (zh)