CN1632020A - 树脂涂料 - Google Patents

树脂涂料 Download PDF

Info

Publication number
CN1632020A
CN1632020A CN 200310122102 CN200310122102A CN1632020A CN 1632020 A CN1632020 A CN 1632020A CN 200310122102 CN200310122102 CN 200310122102 CN 200310122102 A CN200310122102 A CN 200310122102A CN 1632020 A CN1632020 A CN 1632020A
Authority
CN
China
Prior art keywords
resin
polyamide resin
modified rosin
softening point
solvent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 200310122102
Other languages
English (en)
Inventor
葛祥利
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 200310122102 priority Critical patent/CN1632020A/zh
Publication of CN1632020A publication Critical patent/CN1632020A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种树脂涂料，旨在提供一种附着力好、耐刮擦、耐蒸煮、不粘连，转印率高的树脂涂料。它按照重量百分比包括下列组分：聚酰胺树脂10－15％、改性松香树脂6－9％、聚乙烯蜡3－7％、填料7－23％、颜料9－11％、分散剂0.1－0.5％。聚酰胺树脂为热塑性，在50％乙醇溶液中，软化点在80－180℃，粘度25℃，胺值不大于10。改性松香树脂的软化点在100－150℃，酸值小于20。

Description

树脂涂料
                                 技术领域
本发明涉及一种涂料，更具体地说是涉及一种标示碳带的涂料。
                                 背景技术
目前市场上销售的碳带其树脂涂层不能在适当的温度下受烫后完全转印到承印载体上，墨层对承印载体附着力差，耐刮擦、耐蒸煮性比较差。
                                 发明内容
本发明是为了克服现有技术中的不足之处，提供一种墨层热烫印性能好，转印率高，温度适应广泛，对承印物载体PP、PE、PVC、铝箔、纸张化纤等都有很好的附着力，耐磨擦、耐蒸煮，与辅助涂层有很好的结合力的标示碳带的涂料。
本发明通过下述技术方案实现：一种树脂涂料，其特征是，按重量百分比包括下列组分，聚酰胺树脂10-15％、改性松香树脂6-9％、聚乙烯蜡3-7％、填料7-23％、颜料9-11％、流平剂0.1-0.3％。
所述的聚酰胺树脂为热塑性，在50％乙醇溶液中，软化点在80-180℃，粘度25℃，胺值不大于10。
所述的改性松香树脂的软化点在100-150℃，酸值小于20。。
本发明的树脂涂料能在受烫后完全转印到承印载体上，墨层对承印载体有广泛的适应性，附着力好、耐刮擦、耐蒸煮、不粘连，转印率高。
                                具体实施方式
实例1：本实施例聚酰胺树脂选用劳特公司的P-1155，改性松香脂可采用遂川树脂的210，聚乙烯蜡可选用巴斯夫公司LumaxAL3，填料可选用超细碳酸钙和立德粉，颜料即碳黑选用卡博特公司Cabet800，分散剂选用毕克K-163，流平剂选用道康宁公司的产品，代码5T，溶剂为按重量百分比为二甲苯70％，异丙醇30％。按如下配方备料，先把树脂加热溶解在溶剂中，再按顺序加入其他组份，通过研磨机使体系分散均匀，粒径在10μm以下即可。
聚酰胺树脂  15g
改性松香树脂  7g
聚乙烯蜡Luwax AL3  5g
碳酸钙  20g
立德粉  3g
碳黑  11g
分散剂  0.5g
流平剂  0.3g
溶剂  38.2g
实例2：本实施例聚酰胺树脂选用劳特公司的P-1155，改性松香脂可采用遂川树脂的210，聚乙烯蜡可选用巴斯夫公司LumaxAL3，填料可选用超细碳酸钙和立德粉，颜料即碳黑选用卡博特公司Cabet800，分散剂选用毕克K-163，流平剂选用道康宁公司的产品，代码5T，溶剂按重量百分比为二甲苯60％，异丙醇40％。按如下配方备料，先把树脂加热溶解在溶剂中，再按顺序加入其他组份，通过研磨机使体系分散均匀，粒径在10μm以下即可。
按如下配方备料，先把树脂加热溶解在溶剂中，再按顺序加入其他组份，通过研磨机使体系分散均匀，粒经在10μm以下即可。
聚酰胺树脂 10g
改性松香树脂 9g
聚乙烯蜡Luwax AL3 5g
碳酸钙 12g
立德粉 3g
碳黑 11g
分散剂 0.5g
流平剂 0.3g
溶剂 49.2g
实施例3：本实施例聚酰胺树脂选用劳特公司的P-1155，改性松香脂可采用遂川树脂的210，聚乙烯蜡可选用巴斯夫公司LumaxAL3，填料可选用超细碳酸钙和立德粉，颜料即碳黑选用卡博特公司Cabet800，分散剂选用毕克K-163，流平剂选用道康宁公司的产品，代码5T，溶剂为按重量百分比为二甲苯70％，异丙醇30％。按如下配方，先把树脂加热溶解在溶剂中，再按顺序加入其他组份，通过研磨机使体系分散均匀，粒经在10μm以下即可。
聚酰胺树脂 12g
改性松香树脂 6g
聚乙烯蜡Luwax AL3 6g
碳酸钙 12g
立德粉 3g
碳黑 11g
分散剂 0.5g
流平剂 0.3g
溶剂 49.2g
实施例4：本实施例聚酰胺树脂选用劳特公司的P-1155，改性松香脂可采用遂川树脂的210，聚乙烯蜡可选用巴斯夫公司LumaxAL3，填料可选用超细碳酸钙和立德粉，颜料即碳黑选用卡博特公司Cabet800，分散剂选用毕克K-163，流平剂选用道康宁公司的产品，代码5T，溶剂为按重量百分比为二甲苯70％，异丙醇30％。按如下配方，先把树脂加热溶解在溶剂中，再按顺序加入其他组份，通过研磨机使体系分散均匀，粒经在10μm以下即可。
聚酰胺树脂 12g
改性松香树脂 7g
聚乙烯蜡Luwax AL3 3g
碳酸钙 12g
立德粉 3g
碳黑 11g
分散剂 0.5g
流平剂 0.3g
溶剂 51.2g

Claims (3)

1.一种树脂涂料，其特征是，按重量百分比包括下列组分，聚酰胺树脂10-15％、改性松香树脂6-9％、聚乙烯蜡3-7％、填料7-23％、颜料9-11％、流平剂0.1-0.3％。
2.根据权利要求1所述的树脂涂料，其特征是，所述的聚酰胺树脂为热塑性，在50％乙醇溶液中，软化点在80-180℃，粘度25℃，胺值不大于10。
3.根据权利要求1所述的树脂涂料，其特征是，所述的改性松香树脂的软化点在100-150℃，酸值小于20。
CN 200310122102 2003-12-24 2003-12-24 树脂涂料 Pending CN1632020A (zh)