CN1560207A - 纳米有机钼抗磨剂 - Google Patents
纳米有机钼抗磨剂 Download PDFInfo
- Publication number
- CN1560207A CN1560207A CNA2004100236082A CN200410023608A CN1560207A CN 1560207 A CN1560207 A CN 1560207A CN A2004100236082 A CNA2004100236082 A CN A2004100236082A CN 200410023608 A CN200410023608 A CN 200410023608A CN 1560207 A CN1560207 A CN 1560207A
- Authority
- CN
- China
- Prior art keywords
- molybdenum
- organic
- agent
- organic molybdenum
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种纳米有机钼抗磨剂,由有机钼和润滑油基础油所组成,其特征在于所述的有机钼所占重量百分数为0.4-0.9%,所述的有机钼为纳米级有机钼。本发明克服了现有有机钼普遍存在的颗粒沉淀问题,能完全油溶;也解决了使用中对设备强腐蚀性的问题;本发明的产品多项性能指标优于现有产品,其最大摩擦系数为0.055-0.065,极压抗磨试验值中的最大无卡咬负荷PB为893-990N,烧结负荷PD为3187-3300N,综合磨损值ZMZ为393-410N,节省燃油9-12%,换油周期25000公里以上。
Description
技术领域
本发明涉及一种抗磨剂,特别是涉及一种纳米有机钼抗磨剂。
背景技术
在交通运输、汽车、机械等多种领域都使用润滑油和抗磨剂。目前有一种有机钼抗磨剂,它由有机钼和润滑油基础油所组成,其中有机钼所占的重量百分数为5-10%。所述的有机钼有二烷基二硫代磷酸氧钼、己基二硫代磷酸钼、磷酸酯钼、氨基甲酸钼、环烷酸钼。此外,还有人用有机铜钼、有机硼钼等。现有的有机钼抗磨剂有许多缺点,首先抗磨剂中的有机金属钼粒子没有纳米化,因此,它的物理、化学性能不能充分发挥出来,限制了产品性能的提高。
有些成分如铜、锌、硼等,虽已加工成纳米级颗粒,但这些颗粒在润滑油中的分散性、稳定性并未真正得到解决。不仅大大降低了产品性能,还有因沉淀导致使用中产生机械故障的现象。现有的有机钼化合物在使用过程中,大多对设备有较强的腐蚀性。因此,直接使用有机钼做抗磨剂是有害的。现有的有机钼性能:加入汽油机油中获得的最大摩擦系数为0.072-0.080,极压抗磨试验值PB为760-880 N,PD为2550-2990N,ZMZ为280-310 N,能节省燃油6-8%,换油周期为20000公里左右.
发明内容
本发明的目的是提供一种纳米有机钼抗磨剂,它能克服现有技术的上述缺点。
一种纳米有机钼抗磨剂,由有机钼和润滑油基础油所组成,其特征在于所述的有机钼所占的重量百分数为0.4-0.9%,所述有机钼为纳米级有机钼。
一种纳米有机钼抗磨剂的制备方法,包括将有机钼溶在润滑油基础油中,其特征在于所述的有机钼先制成纳米级有机钼。
本发明克服了现有有机钼普遍存在的颗粒沉淀问题,能完全油溶;也解决了使用中对设备强腐蚀性的问题;本发明的产品多项性能指标优于现有产品,其最大摩擦系数为0.055-0.065,极压抗磨试验值中的最大无卡咬负荷PB为893-990N,烧结负荷PD为3187-3300N,综合磨损值ZMZ为393-410N,节省燃油9-12%,换油周期25000公里以上。
具体实施方式
制备本发明的产品时,先在1立升四口烧瓶中加入仲戊醇176克和2-乙基己醇260克,搅拌,再分批慢加五硫化二磷220克,控温88±2℃,恒温3.5小时。反应生成的H2S气体导入装有178克36%(重量百分浓度,下同)的NaOH水溶液的吸收瓶,反应完毕转化为Na2S+NaHS混合液212克备用。烧瓶内产物冷却后过滤,得到仲戊基异辛基二硫代磷酸,重612克,收率为98.1%,酸值为146mgKOH/g,硫(S)的重量百分含量为19.84%,磷(P)的含量为9.85%。然后向另一烧瓶中加入三氧化钼86.4克、自来水500ml和正丁醇100ml,导入氮气,搅拌升温,达60℃时,滴加95.3克Na2S+NaHS混合液(Mo与Na的当量比为1∶2),搅拌30分钟,降温至40℃,滴加浓度为45%的硫酸34克,15分钟后,滴加仲戊基异锌基二硫代硫酸374.4克,同时升温回流反应4小时,转移反应混合液至分液漏斗中,分去下层蓝色水相,然后,加入同体积石油醚(70-80℃)稀释,再以等体积水洗2-3次,切净水后,减压蒸溜去溶剂,即获得有机钼产物434克,收率为96.4%,酸值为99.82mgKOH/g,Mo的重量百分含量为10.81%,S的含量为19.87%,P为7.53%。取上述反应物350克加入35克噻二唑衍生物减活剂,升温至73℃,搅拌1小时,制得仲戊基异辛基二硫代磷酸硫化氧钼的固体粉剂,采用对撞式气流磨并添加表面活性剂十二烷基硫酸钠,制成纳米级有机钼。将该纳米级有机钼溶在润滑油基础油中即为本发明的产品,其中有机钼的含量为0.4-0.9%。
本实施例中的表面活性剂十二烧基硫酸钠可改用十二醇聚氧乙烯醚硫酸钠、氯化十二烷基三甲基胺、C12-18脂肪醇聚氯乙烯(10.20)、十二烷基二甲基甜菜碱(PS-12)或二苯甲烷双马来酰亚胺)。
本发明产品亦称为森鹿-80纳米抗磨节能剂。该产品已经国家石油产品质量监督检验中心检认,并申办了产品条码。
Claims (5)
1、一种纳米有机钼抗磨剂,由有机钼和润滑油基础油所组成,其特征在于所述的有机钼所占重量百分数为0.4-0.9%,所述的有机钼为纳米级有机钼。
2、如权利要求1所述的抗磨剂,其特征在于所述的有机钼为仲戊基异辛基二硫代磷酸硫化氧钼。
3、一种纳米有机钼抗磨剂的制备方法,包括将有机钼溶于润滑油基础油中,其特征在于所述的有机钼先制成纳米级有机钼。
4、如权利要求3所述的制备方法,其特征在于所述的纳米有机钼的制备采用对撞式气流磨并添加表面活性剂。
5、如权利要求4的制备方法,其特征在于所述的表面活性剂为十二烷基硫酸钠、十二醇聚氧乙烯醚硫酸钠、氯化十二烷基三甲基胺、
C12-18脂肪醇聚氯乙烯、十二烷基二甲基甜菜碱或二苯甲烷双马来酰亚胺。