CN1488596A - 一种铜绿结晶釉及其制作方法 - Google Patents

一种铜绿结晶釉及其制作方法 Download PDF

Info

Publication number
CN1488596A
CN1488596A CNA031247482A CN03124748A CN1488596A CN 1488596 A CN1488596 A CN 1488596A CN A031247482 A CNA031247482 A CN A031247482A CN 03124748 A CN03124748 A CN 03124748A CN 1488596 A CN1488596 A CN 1488596A
Authority
CN
China
Prior art keywords
glaze
verdigris
crystalline
cuo
zno
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA031247482A
Other languages
English (en)
Other versions
CN100381384C (zh
Inventor
易艳军
廖志坚
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HUNAN TAIXIN CERAMICS CO Ltd
Original Assignee
HUNAN TAIXIN CERAMICS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HUNAN TAIXIN CERAMICS CO Ltd filed Critical HUNAN TAIXIN CERAMICS CO Ltd
Priority to CNB031247482A priority Critical patent/CN100381384C/zh
Publication of CN1488596A publication Critical patent/CN1488596A/zh
Application granted granted Critical
Publication of CN100381384C publication Critical patent/CN100381384C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

一种铜绿结晶釉及其制作方法，在普通的基础釉料中，加入适量的ZnO、TiO2为引晶剂，加入适量MnO2、CuO为发色剂。将引晶剂和发色剂按配比加入基础釉料中，球磨过250目筛，筛余＜0.3％，再将加有引晶剂和发色剂的釉料施于坯体上；然后，将上有釉料的坯体置于窑炉内，用1150－1120℃进行焙烧，在烧成时高温釉面冲泡，冷却时析晶，即制出呈铜绿色，晶花类似铜钱色，大小为4－12mm的铜绿结晶釉。本发明有效地提出了一种新型的艺术结晶釉，为众多的釉面艺术提供了一种新的，具有别具一格艺术美感的釉面，满足了市场新的需求。

Description

一种铜绿结晶釉及其制作方法
技术领域
本发明属于一种陶瓷制品的釉面制作方法，特别是指一种与施釉结合的釉面焙烧方法，主要用于在陶瓷的表面制作出一种铜绿结晶釉及其制作方法。
技术背景
在陶瓷制品的表面上着色、上釉是一种增加陶瓷制品质感和美感的有效手段，而且每一种釉色或花色所起的艺术效果是不同的，目前市场上有着各种各样的釉色、花色或者其结合，这主要是根据市场的需求进行开发。当前市场上有着一种返古归真，追求自然的风气，许多东西讲究的是一种质朴、大方的艺术效果。对于陶瓷行业自然也不例外。铜绿色能给人的一种远古、悠久、大方、质朴的感觉，如果将其图案通过釉彩的形式在陶瓷器具的表面制作出来，是会令消费者感到具有很浓的返古之味，但在检索中未发现有此类文献报道。
发明内容
本发明的目的在于，提出一种新型艺术结晶釉及其制作方法，且此结晶釉具有铜绿色的艺术感，以满足人们对艺术爱好的各种追求。
根据本发明的目的，所提出的技术实施方案是：在普通的基础釉料中，加入适量的ZnO、、、TiO2为引晶剂，加入适量MnO2、、、、CuO为发色剂。其与基础釉料的配比如下：
ZnO   4-10％    MnO2、4-10％
TiO2 2-10％     CuO    8-18％
其余量为基础釉料制作方法是：
1、将引晶剂和发色剂按配比加入基础釉料中，球磨过250目筛，筛余＜0.3％。
2、将加有引晶剂和发色剂的釉料施于坯体上；
3、将上有釉料的坯体置于窑炉内，用1150-1120℃进行焙烧，在烧成时高温釉面冲泡，冷却时析晶，即制出呈铜绿色，晶花类似铜钱色，大小为4-12mm的铜绿结晶釉。
本发明有效地提出了一种新型的艺术结晶釉，为众多的釉面艺术提供了一种新的，具有别具一格艺术美感的釉面，满足了市场新的需求。
具体实施方式
实施例一
1、配料
选ZnO、TiO2、为引晶剂，MnO2、CuO为发色剂，加入基础釉料中，具体配比如下：
ZnO   4％    TiO2   10％
MnO2 4％     CuO     18％
基础釉料  64％
2、制作方法
A、将引晶剂、发色剂按配比加入基础釉料中，球磨至一定细度，过250目筛，筛余＜0.3％；
B、将搅拌好的釉料施于待上釉的坯体上；
C、将上好釉的坯料置于窑炉中，用1150-1220℃的变温焙烧3-4小时；
D、焙烧完后，让窑炉自然冷却，出炉便形成具有铜绿色品花的结晶釉面的陶瓷器具制品。
实施例二
1、配料
ZnO    10％    TiO2   2％
MnO2  10％     CuO     8％
基础釉料  70％
2、制作方法
制作方法与实施例一一样，由于配比不一样，所制出的铜绿色结晶釉色彩有所不同颜色较浅。
实施例三
1、配料
ZnO    6％    MnO2   8％
TiO2  7％     CuO     15％
基础釉料  64％
2、制作方法：
制作方法与实施例一一样，按此种配比制作出的铜绿结晶釉，色彩中等，品花约3mm。

Claims (5)

1、一种铜绿结晶釉，在普通的基础釉料中，加入适量的ZnO、、、TiO2为引晶剂，加入适量  MnO2、、、、CuO为发色剂，引晶剂和发色剂与基础釉料的配比如下：
ZnO   4-10％    MnO2、 4-10％
TiO2 2-10％     CuO     8-18％
其余量为基础釉料
2、如权利要求1所述的一种铜绿结晶釉，其特征在于：所述铜绿结晶釉的引晶剂和发色剂与基础釉料的配比如下：
ZnO   4％    TiO210％
MnO2 4％     CuO  18％
基础釉料     64％
3、如权利要求1所述的一种铜绿结晶釉，其特征在于：所述铜绿结晶釉的引晶剂和发色剂与基础釉料的配比如下：
ZnO   10％    TiO2 2％
MnO2 10％     CuO   8％
基础釉料 70％
4、如权利要求1所述的一种铜绿结晶釉，其特征在于：所述铜绿结晶釉的引晶剂和发色剂与基础釉料的配比如下：
ZnO   6％    MnO2 8％
TiO2 7％     CuO   15％
基础釉料 64％
5、如权利要求1所述的一种铜绿结晶釉的制作方法，其特征在于：所述铜绿结晶釉的制作方法是：
A、引晶剂和发色剂按配比加入基础釉料中，球磨过250目筛，筛余＜0.3％。
B、加有引晶剂和发色剂的釉料施于坯体上；
C、将上有釉料的坯体置于窑炉内，用1150-1120℃进行焙烧，在烧成时高温釉面冲泡，冷却时析晶，即制出呈铜绿色，晶花类似铜钱色，大小为4-12mm的铜绿结晶釉。
CNB031247482A 2003-08-21 2003-08-21 一种铜绿结晶釉及其制作方法 Expired - Fee Related CN100381384C (zh)