CN1473897A - 耐深冲高光泽金属涂料 - Google Patents

耐深冲高光泽金属涂料 Download PDF

Info

Publication number
CN1473897A
CN1473897A CNA021335761A CN02133576A CN1473897A CN 1473897 A CN1473897 A CN 1473897A CN A021335761 A CNA021335761 A CN A021335761A CN 02133576 A CN02133576 A CN 02133576A CN 1473897 A CN1473897 A CN 1473897A
Authority
CN
China
Prior art keywords
resin
resins
molecular
weight average
resistant high
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA021335761A
Other languages
English (en)
Other versions
CN1212359C (zh
Inventor
力 赵
赵力
曾燕
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Fenghua Zhaozhi New Material Technology Co., Ltd.
Original Assignee
SHICHUANG NEW MATERIAL CO Ltd CHENGDU
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHICHUANG NEW MATERIAL CO Ltd CHENGDU filed Critical SHICHUANG NEW MATERIAL CO Ltd CHENGDU
Priority to CN 02133576 priority Critical patent/CN1212359C/zh
Publication of CN1473897A publication Critical patent/CN1473897A/zh
Application granted granted Critical
Publication of CN1212359C publication Critical patent/CN1212359C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明提供一种耐深冲高光泽金属涂料，其原料组分按重量百分比计，主体树脂80～92，固化树脂8～20，其中，主体树脂由5～30的环氧树脂和70～95饱和线性聚酯树脂组成；固化树脂由3～35醚化三聚氰胺甲醛树脂，10～45取代基三聚氰胺树脂，5～20氨基聚氨酯树脂组成。涂料具有高光泽，光泽度达92％，涂布在金属表面固化后，具有优良的耐深冲性能，可对金属进行拉伸高度60～75mm的深冲加工。主要用于制作金属瓶盖或罐盖。

Description

耐深冲高光泽金属涂料
技术领域
本发明涉及一种涂料特别是涉及一种耐深冲高光泽金属涂料。
背景技术
传统的金属涂料不耐深冲，涂料膜抗冲拨能力差，深冲时开裂并失光。湖南湘江涂料集团有限公司生产了一种KP1420聚酯耐深冲涂料，它由聚酯树脂、氨基树脂、钛白及助剂经研磨分散调和而成。
发明内容
本发明的目的在于克服上述缺点，提供一种使用方便，光泽度达92％，且抗冲拨性能极佳的耐深冲高光泽金属涂料。
本发明耐深冲高光泽金属涂料的原料组分按重量百分比计，包括主体树脂80～92，固化树脂8～20。其中，主体树脂由5～30的环氧树脂和70～95饱和线性聚酯树脂组成；固化树脂由3～35醚化三聚氰胺甲醛树脂，10～45取代基三聚氰胺树脂，5～20氨基聚氨酯树脂组成。主体树脂中的环氧树脂是平均分子量为700～900双酚A环氧树脂、平均分子量为900～1500双酚A环氧树脂、平均分子量为1600～3500双酚A环氧树脂中的一种或一种以上。饱和线性聚酯树脂是平均分子量6000～12000饱和线性聚酯树脂、平均分子量15000～17000饱和线性聚酯树脂中的一种或两种；固化树脂中的醚化三聚氰胺甲醛树脂是甲醇醚化三聚氰胺甲醛树脂、正丁醇醚化三聚氰胺甲醛树脂、异丁醇醚化三聚氰胺甲醛树脂中的一种或一种以上。取代基三聚氰胺树脂是甲氧基三聚氰胺树脂、苯基三聚氰胺树脂中的一种或两种。氨基聚氨酯树脂是聚环氧乙烷氨基聚氨酯树脂、氨基甲基化聚醚氨基聚氨酯树脂中的一种或两种。
本发明耐深冲高光泽金属涂料的优点在于具有高光泽，光泽度达92％，且抗冲拨性能极佳，涂布在金属表面固化后具有优点的耐深冲性能，可对金属进行2～5次拉伸达高度60～75mm的深冲加工。主要用于制作金属瓶盖或罐盖。
具体实施方式
实施例1：一、原料组分按重量％计如下：
主体树脂                                              80
固化树脂                                              20二、主体树脂组分按重量％计如下：
双酚A环氧树脂                                         5
饱和线性聚酯树脂                                      95
其中，双酚A树脂组成按重量％计，由65％的平均分子量为700～900双酚A环氧树脂和35％的平均分子量为1600～3500双酚A环氧树脂组成；饱和线性树脂的组成按重量％计，由95％的平均分子量为6000～12000饱和线性聚酯树脂和5％的平均分子量为15000～17000的饱和线性聚酯树脂组成。三、固化树脂组分按重量％计如下：
醚化三聚氰胺甲醛树脂                                15
苯代三聚氰胺树脂                                    10
氨基甲基化聚醚氨基树脂                              75
其中，醚化三聚氰胺甲醛树脂的组成按重量％计，由85％的正丁醇醚化三聚氰胺甲醛树脂和15％的异丁醇醚化三聚氰胺甲醛树脂组成。
将主体树脂与固化树脂混合均匀，制得本发明耐深冲高光泽金属涂料。使用时可加入颜料、流平剂等助剂，并用稀释剂调整粘度，以满足辊涂施工要求。
实施例2：二、原料组分按重量％计如下：
主体树脂                                             92
固化树脂                                             8二、主体树脂组分按重量％计如下：
双酚A环氧树脂                                        12
饱和线性聚酯树脂                                88
其中，双酚A树脂组成按重量％计，由65％的平均分子量为700～900双酚A环氧树脂和35％的平均分子量为1600～3500双酚A环氧树脂组成；饱和线性树脂的组成按重量％计，由75％的平均分子量为6000～12000饱和线性聚酯树脂和25％的平均分子量为15000～17000的饱和线性聚酯树脂组成。三、固化树脂组分按重量％计如下：
醚化三聚氰胺甲醛树脂                             22
苯代三聚氰胺树脂                                 35
氨基甲基化聚醚氨基树脂                           43
其中，醚化三聚氰胺甲醛树脂的组成按重量％计，由85％的正丁醇醚化三聚氰胺甲醛树脂和15％的异丁醇醚化三聚氰胺甲醛树脂组成。
将主体树脂与固化树脂混合均匀，制得本发明耐深冲高光泽金属涂料。使用时可加入颜料、流平剂等助剂，并用稀释剂调整粘度，以满足辊涂施工要求。

Claims (4)

1、一种耐深冲高光泽金属涂料，其特征在于原料组分按重量百分比计，包括主体树脂80～92，固化树脂8～20，其中，主体树脂由5～30的环氧树脂和70～95饱和线性聚酯树脂组成；固化树脂由3～35醚化三聚氰胺甲醛树脂，10～45取代基三聚氰胺树脂，5～20氨基聚氨酯树脂组成。
2、如权利要求1所述的耐深冲高光泽金属涂料，其特征在于环氧树脂是平均分子量为700～900双酚A环氧树脂，平均分子量为900～1500双酚A环氧树脂、平均分子量为1600～3500双酚A环氧树脂中的一种或一种以上。
3、如权利要求1所述的耐深冲高光泽金属涂料，其特征在于饱和线性聚酯树脂是平均分子量6000～12000饱和线性聚酯树脂、平均分子量15000～17000饱和线性聚酯树脂中的一种或两种。
4、如权利要求1所述的耐深冲高光泽金属涂料，其特征在于醚化三聚氰胺甲醛树脂是甲醇醚化三聚氰胺甲醛树脂、正丁醇醚化三聚氰胺甲醛树脂、异丁醇醚化三聚氰胺甲醛树脂中的一种或一种以上；取代基三聚氰胺树脂是甲氧基三聚氰胺树脂、苯基三聚氰胺树脂中的一种或两种；氨基聚氨酯树脂是聚环氧乙烷氨基聚氨酯树脂、氨基甲基化聚醚氨基聚氨酯树脂中的一种或两种。
CN 02133576 2002-08-05 2002-08-05 耐深冲高光泽金属涂料 Expired - Fee Related CN1212359C (zh)