CN1346816A - 复合金属陶瓷及其制备方法 - Google Patents
复合金属陶瓷及其制备方法 Download PDFInfo
- Publication number
- CN1346816A CN1346816A CN 01133646 CN01133646A CN1346816A CN 1346816 A CN1346816 A CN 1346816A CN 01133646 CN01133646 CN 01133646 CN 01133646 A CN01133646 A CN 01133646A CN 1346816 A CN1346816 A CN 1346816A
- Authority
- CN
- China
- Prior art keywords
- composite cermet
- vacuum
- preparation
- forming agent
- pressure
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种复合金属陶瓷及其制备方法,属于陶瓷材料及其制备方法。采取优化材料成分、改进烧结工艺、细化晶粒的手段进一步提高其强韧性,该金属陶瓷成份为:25≤Ti≤30,6≤C≤8.5,25≤Ni≤40,12≤Mo≤20,2≤N≤3,5≤W≤10,0.4≤Cr≤1.0。其制备工艺为:将单质元素Ti、C、Ni、Mo粉末混合,在氩气保护下,通过机械合金化制备包括纳米级TiCx和NiMo固溶体的混合物,再与TiN、WC、Cr3C2、C粉末一起配制成符合上述成份的混合料,加入成型剂、压制成型,在真空度高于5Pa的条件脱脂,在真空度高于1.0×10-1Pa的条件下烧结,在压力为100-150MPa,处理温度1350-1400℃的条件下进行热等静压处理。所述材料具有高硬度,高抗弯强度,HRA≥90.0,σb≥2500MPa。可用于刀具、拉丝模、压制模等。
Description
技术领域
本发明为陶瓷材料及其制造方法,特别涉及复合Ti(C,N)基金属陶瓷及其制备方法。
背景技术
Ti(C,N)基金属陶瓷不但具有较高的硬度、耐磨性、红硬性、优良的化学稳定性、与金属间极低的摩擦系数,而且还有一定的韧性和强度。如用作刀具,与通常的硬质合金相比,它在以下几个方面有明显的优势:可以允许有较高的切削速度和较大的进刀量,被加工件有较好的表面性能,刀具的耐磨性能更高。目前日本市场的主要牌号见表1,见中国建筑材料科学研究院张国军‘Ti(C,N)基金属材料’一文,机械工程材料,1990年第3期。我国八·五期间也投入大量的人力物力并已研制出一些牌号的Ti(C,N)基金属陶刀具,现正在市场上试用,但反应出的问题是性能不稳定,强韧性偏低,在较高的转速条件下,震动很大,因而这些牌号的金属陶瓷刀具至今基本上没有得到实际运用。表2为中国市场上正在试用的几种金属陶瓷的牌号和性能。因此,只有在保持其优越性的前提下,进一步提高材料的强韧性,才有可能使其在国内刀具市场上得到运用,并将其应用领域扩展到模具市场。
表1 日本市场上常用的金属陶瓷的牌号和性能
牌号 | N302 | N308 | N310 | N350 |
主要性能 | 高耐磨性 | 高韧性 | 更高韧性 | 更高韧性 |
组 成 | TiCN-WC-TaC | TiCN-WC-TaC | TiCN-WC-TaC | (Ti,W,Ta)CN |
硬度HRA | 93.0~94.0 | 91.0~92.0 | 91.0~92.0 | 92.5~92.5 |
抗弯强度/MPa | 1200~1400 | 1600~1800 | 1700~1900 | 1700~1900 |
比 重 | 6.4 | 7.0 | 7.0 | 7.0 |
表2 中国市场上正在试用的几种金属陶瓷的牌号和性能
牌号 | YN05 | TN10 | TN20 | TN30 |
主要性能 | 高耐磨性 | 与TN05性能类似,韧性提高 | 韧性,耐磨性等较好 | 韧性,耐磨性等较好 |
组 成 | TiC-Ni-Mo | Ti(CN)-Ni-Mo | Ti(CN)-Ni-Mo | Ti(CN)-Ni-Mo |
硬 度 | ≥93 | ≥92.5 | ≥91.5 | ≥90.5 |
抗弯强度 | 950 | 1200 | ≥1400 | ≥1550 |
比 重 | ≥6.2 | ≥6.5 | ≥6.8 | ≥6.8 |
发明内容
本发明的一种复合金属陶瓷及其制备方法,采取优化材料成分、改进烧结工艺、细化晶粒的手段进一步提高该金属陶瓷的强韧性,提供一种显微组织中含有10%以上的纳米晶粒,HRA≥90.0,σb≥2500MPa的Ti(C,N)基金属陶瓷,使此类材料在保持原有优越性的基础上,其强韧性得到改善。实现这一目的的Ti(C,N)基金属陶瓷,在组成成份中加入少量的Cr3C2。本发明的另一目的是提供制备上述复合金属陶瓷的方法,其特点是先进行机械合金化,制备包括纳米级TiCx和NiMo固溶体的混合物,再配制符合成份要求的混合料,依次经混料、成型、脱脂、真空烧结、热等静压处理。
本发明的一种复合金属陶瓷,其成份重量百分比为:
25≤Ti≤30,6≤C≤8.5,25≤Ni≤40,12≤Mo≤20,2≤N≤3,5≤W≤10,0.4≤Cr≤1.0。
本发明如前所述的复合金属陶瓷的制备方法,依次包括如下步骤;
(1)将单质元素Ti、C、Ni、Mo粉末混合,其成分重量配比为:25≤Ti≤28,6.5≤C≤7,25≤Ni≤40,12≤Mo≤20,用机械合金化制备包括纳米级的TiCx和NiMo固溶体的混合物,再将其与TiN、WC、Cr3C2、C粉一起配制成符合最终重量比例的混合料,
(2)加入成型剂,压制成型,脱脂,
(3)然后经真空烧结和热等静压处理而成。
所述的复合金属陶瓷的制备方法,其进一步的特征为:
(1)机械合金化在氩气保护下进行,
(2)所加入成型剂为聚乙烯醇,
(3)脱脂工序在真空炉中进行,
(4)热等静压处理在氩气保护下进行。
所述的复合金属陶瓷的制备方法,其工艺参数可以为:
(1)机械合金化过程所用氩气纯度≥99.99%、压力0.2-0.8MPa,转速为350-400rpm,时间为96-132h,
(2)成型剂加入比例为混合料的4wt%-8wt%,压制成型所用压力为250-400MPa,
(3)脱脂工序在真空度高于5Pa的条件下进行,在400-600℃之间保温6-10h。
(4)真空烧结的真空度高于1.0×10-1Pa,烧结温度为1410-1480℃,保温时间为40-80min,
(5)热等静压炉中所用的氩气压力为100-150MPa,处理温度1350-1400℃,时间为30-50min。
本发明的纳米复合Ti(C,N)基金属陶瓷,其HRA≥90.0,σb≥2500MPa,不但具有较高的硬度、耐磨性、红硬性、优良的化学稳定性、与金属间极低的摩擦系数等优点外,其强韧性也较优良,作为刀具不但可以在震动不大的先进机床上运用,还可以用于国内普通的机床,与相同硬度的硬质合金相比,其可以允许进刀量提高2-4倍,切削速度提高2倍以上。由于强韧性比较优越,其还可用来作拉丝模、压制模等模具。
具体实施方式
以下结合实例进一步说明本发明的技术效果。
表3是4种成分配方的混合料,分别采用不同的工艺参数将其制备成金属陶瓷,并分别测定其主要性能硬度和抗弯强度。
表3 4种混合料的成分配比成分 Ti C Ni Mo N W Cr1# 30 8.5 27.5 20 3 10 12# 27 7.3 35 17 3 10 0.73# 27 6.2 40 13 2.4 10 0.44# 25 7.6 40 20 2 5 0.4
实施例1:
机械合金化过程所用压力0.2MPa,转速为350rpm,时间为96h,
成型剂聚乙烯醇的加入量为4wt%,
压制成型所用压力为400MPa,
脱脂工序在真空度高于5Pa的条件下进行,保温温度为600℃,保温时间为10h。
真空烧结的真空度高于1.0×10-1Pa,烧结温度为1410℃,保温时间为40min,
热等静压炉中所用氩气压力为100MPa,处理温度1400℃,保温时间为30min。
在上述制备工艺条件下,不同成分配比的金属陶瓷的性能见表4。
表4 采用工艺1制备出的不同金属陶瓷的性能
成分 1# 2# 3# 4#
抗弯强度σb(MPa) 2512 2633 2884 2578
硬度(HRA) 91.5 90.8 90.7 90.2
实施例2:
机械合金化过程所用压力0.5MPa,转速为350rpm,时间为120h,
成型剂聚乙烯醇的加入量为6wt%,
压制成型所用压力为300MPa,
脱脂工序在真空度高于5Pa的条件下进行,保温温度为500℃,保温时间为6h。
真空烧结的真空度高于1.0×10-1Pa,烧结温度为1440℃,保温时间为60min,
热等静压炉中所用氩气压力为100MPa,处理温度1370℃,保温时间为40min。
在上述制备工艺条件下,不同成分配比的金属陶瓷的性能见表5。
表5 采用工艺2制备出的不同金属陶瓷的性能
成分 1# 2# 3# 4#
抗弯强度σb(MPa)2583 2534 2735 2628
硬度(HRA) 90.8 90.2 90.3 90.0
实施例3:
机械合金化过程所用压力0.8MPa,转速为400rpm,时间为132h,
成型剂聚乙烯醇的加入量为8wt%,
压制成型所用压力为250MPa,
脱脂工序在真空度高于5Pa的条件下进行,保温温度为400℃,保温时间为6h。
真空烧结的真空度高于1.0×10-1Pa,烧结温度为1480℃,保温时间为80min,
热等静压炉中所用氩气压力为150MPa,处理温度1350℃,保温时间为50min。
在上述制备工艺条件下,不同成分配比的金属陶瓷的性能见表6。
表6 采用工艺3制备出的不同金属陶瓷的性能成分 1# 2# 3# 4#抗弯强度σb(MPa) 2504 2572 2601 2609硬度(HRA) 91.7 90.8 90.5 90.2
Claims (4)
1、一种复合金属陶瓷,其成份重量百分比为:25≤Ti≤30,6≤C≤8.5,25≤Ni≤40,12≤Mo≤20,2≤N≤3,5≤W≤10,0.4≤Cr≤1.0。
2、一种如权利要求1所述的复合金属陶瓷的制备方法,依次包括如下步骤;(1)将单质元素Ti、C、Ni、Mo粉末混合,其成分重量配比为:25≤Ti≤28,6.5≤C≤7,25≤Ni≤40,12≤Mo≤20,用机械合金化制备包括纳米级的TiCx和NiMo固溶体的混合物,再将其与TiN、WC、Cr3C2、C粉一起配制成符合最终重量比例的混合料,(2)加入成型剂,压制成型,脱脂,(3)然后经真空烧结和热等静压处理而成。
3、如权利要求2所述的复合金属陶瓷的制备方法,其特征为:(1)机械合金化在氩气保护下进行,(2)所加入成型剂为聚乙烯醇,(3)脱脂工序在真空炉中进行,(4)热等静压处理在氩气保护下进行。
4、如权利要求3所述的复合金属陶瓷的制备方法,其特征为:(1)机械合金化过程所用氩气纯度≥99.99%、压力0.2-0.8MPa,
转速为350-400rpm,时间为96-132h,(2)成型剂加入比例为混合料的4wt%-8wt%,压制成型所用压力
为250-400MPa,(3)脱脂工序在真空度高于5Pa的条件下进行,在400-600℃之
间保温6-10h。(4)真空烧结的真空度高于1.0×10-1Pa,烧结温度为1410-
1480℃,保温时间为40-80min,(5)热等静压炉中所用氩气压力为100-150MPa,处理温度1350
-1400℃,时间为30-50min。