CN1323919A - 耐海水腐蚀镍基多元合金的酸性化学镀液 - Google Patents

耐海水腐蚀镍基多元合金的酸性化学镀液 Download PDF

Info

Publication number
CN1323919A
CN1323919A CN 01112670 CN01112670A CN1323919A CN 1323919 A CN1323919 A CN 1323919A CN 01112670 CN01112670 CN 01112670 CN 01112670 A CN01112670 A CN 01112670A CN 1323919 A CN1323919 A CN 1323919A
Authority
CN
China
Prior art keywords
nickel
sea water
plating
corrosion
chemical plating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 01112670
Other languages
English (en)
Other versions
CN1156606C (zh
Inventor
蔡珣
聂书红
陈秋龙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Jiaotong University
Original Assignee
Shanghai Jiaotong University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Jiaotong University filed Critical Shanghai Jiaotong University
Priority to CNB011126701A priority Critical patent/CN1156606C/zh
Publication of CN1323919A publication Critical patent/CN1323919A/zh
Application granted granted Critical
Publication of CN1156606C publication Critical patent/CN1156606C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

耐海水腐蚀镍基多元合金的酸性化学镀液配方是:每升溶液中含:硫酸镍8-12g/L,次亚磷酸钠38-45g/L,柠檬酸三钠15-20g/L,乳酸10-12mlL,乙酸钠15-20g/L,硫酸铜0.5-1g/L,氯化铬8-15g/L,钼酸钠0.4-0.8g/L,聚乙二醇0.15-0.30g/L,稳定剂0.5-1mg/L,余量为蒸馏水,其中稳定剂为碘化钾或/和硫脲。

Description

耐海水腐蚀镍基多元合金的酸性化学镀液
本发明涉及的是一种酸性化学镀镍液,特别是一种耐海水腐蚀镍基多元合金的酸性化学镀液,属于金属热处理类化学镀领域。
化学镀镍磷合金的耐蚀性取决于镀层的致密度与镀层的成分。现有化学镀方法镀覆的多元合金镀层的耐蚀性均不能满足“代替电镀镉层”的耐海水腐蚀的要求。如:中国专利申请号为89104018,发明人为:沈伟等,发明名称为:化学镀覆高耐蚀性非晶态镍磷合金的溶液及方法。该发明考虑了镀层的磷含量和镀层致密度,得到了具一定耐蚀性能的镍磷合金镀层,但其耐蚀性能仍不能完全满足抗海水腐蚀的要求。
本发明的目的在于克服现有技术中的不足,提供一种耐海水腐蚀镍基多元合金的酸性化学液。
本发明的技术方案和实施情况如下:本发明的配方是:每升溶液中含:硫酸镍8-12g/L,次亚磷酸钠38-45g/L,柠檬酸三钠15-20g/L,乳酸10-12mlL,乙酸钠15-20g/L,硫酸铜0.5-1g/L,氯化铬8-15g/L,钼酸钠0.4-0.8g/L,聚乙二醇0.15-0.30g/L,稳定剂0.5-1mg/L,余量为蒸馏水,其中稳定剂为碘化钾或/和硫脲
镀液的配制方法为:先用蒸馏水或去离子水分别溶解上述药品,然后在搅拌条件下把硫酸铜、柠檬酸三钠、乙酸钠、乳酸、聚乙二醇、次亚磷酸钠、稳定剂、氯化铬、钼酸钠依次加入硫酸镍溶液中,稀释到接近要求浓度,用氨水调整化学镀镍溶液的PH值至4.6-6.0,再稀释到接近要求浓度,在室温下静置10小时,然后过滤,便完成了整个镀液的配制过程。
用该溶液在82-90℃温度条件下采用间断清除镀层氢气的方法施镀。
以下进一步提供实例:
一、按下述配方称取药品:硫酸镍8g,次亚磷酸钠38g,柠檬酸三钠15g,乳酸10ml,乙酸钠15g,硫酸铜0.5g,氯化铬8g,钼酸钠0.4g,聚乙二醇0.15g,碘化钾0.75mg,余量为蒸馏水。先将上述组分分别用少量蒸镏水溶解,然后在搅拌条件下把硫酸铜、柠檬酸三钠、乙酸钠、乳酸、聚乙二醇、次亚磷酸钠、稳定剂、氯化铬、钼酸钠依次加入硫酸镍溶液中,稀释到接近要求浓度,用氨水调整化学镀镍溶液的PH值至4.6,再稀释到接近要求浓度,在室温下静置10小时,然后过滤,取镀液100ml于烧杯中,将烧杯放入水浴锅中升温至82.61℃,然后将表面积为3立方厘米的合金钢板经砂纸打磨、碱性除油、清水彻底冲洗、15%盐酸中酸洗30秒、清水彻底冲洗、1.5%盐酸中活化30秒,蒸馏水冲洗后,立即放入上述溶液中施镀20分钟,取出放入含聚乙二醇与柠檬酸三钠的60℃蒸馏水溶液中清洗三分钟,浸泡一分钟,立即放入镀液中再施镀20分钟,如此反复四次,在低碳钢板上得到16微米的均匀、致密、光滑的镍磷多元合金镀层,将镀层在5%Nacl溶液中浸泡30天后,观察不到腐蚀,用称重法测腐蚀实验前后的重量,失重为零。
二、按下述配方称取药品:硫酸镍10g,次亚磷酸钠41g,柠檬酸三钠17.5g,乳酸11ml,乙酸钠17.5g,硫酸铜0.75g,氯化铬11.5g,钼酸钠0.6g,聚乙二醇0.225g,碘化钾1mg,余量为蒸馏水。先将上述药品分别用少量蒸镏水溶解,然后在搅拌条件下把硫酸铜、柠檬酸三钠、乙酸钠、乳酸、聚乙二醇、次亚磷酸钠、稳定剂、氯化铬、钼酸钠依次加入硫酸镍溶液中,稀释到接近要求浓度,用氨水调整化学镀镍溶液的PH值至4.8,再稀释到接近要求浓度,在室温下静置10小时,然后过滤,取镀液100ml于烧杯中,将烧杯放入水浴锅中升温至86℃,然后将表面积为3立方厘米的合金钢板经砂纸打磨、碱性除油、清水彻底冲洗、15%盐酸中酸洗30秒、清水彻底冲洗、1.5%盐酸中活化30秒,蒸馏水冲洗后,立即放入上述溶液中施镀20分钟,取出放入含乙二醇与柠檬酸三钠的60℃蒸馏水溶液中清洗三分钟,浸泡一分钟,立即放入镀液中再施镀20分钟,如此反复四次,在低碳钢板上得到16微米的均匀、致密、光滑的镍磷多元合金镀层,将镀层在5%Nacl溶液中浸泡30天后,观察不到腐蚀,用称重法测腐蚀实验前后的重量,失重为零。
三、按下述配方称取药品:硫酸镍12g,次亚磷酸钠45g,柠檬酸三钠20g,乳酸12ml,乙酸钠20g,硫酸铜1g,氯化铬15g,钼酸钠0.8g,聚乙二醇0.30g,碘化钾0.4mg和硫脲0.1mg,余量为蒸馏水。先将上述药品分别用少量蒸镏水溶解,然后在搅拌条件下把硫酸铜、柠檬酸三钠、乙酸钠、乳酸、聚乙二醇、次亚磷酸钠、稳定剂、氯化铬、钼酸钠依次加入硫酸镍溶液中,稀释到接近要求浓度,用氨水调整化学镀镍溶液的PH值至6.0,再稀释到要求的浓度,在室温下静置10小时,然后过滤,取镀液100ml于烧杯中,将烧杯放入水浴锅中升温至90℃,然后将表面积为3立方厘米的合金钢板经砂纸打磨、碱性除油、清水彻底冲洗、15%盐酸中酸洗30秒、清水彻底冲洗、1.5%盐酸中活化30秒,蒸馏水冲洗后,立即放入上述溶液中施镀20分钟,取出放入含乙二醇与柠檬酸三钠的60℃蒸馏水溶液中清洗三分钟,浸泡一分钟,立即放入镀液中再施镀20分钟,如此反复四次,在低碳钢板上得到16微米的均匀、致密、光滑的镍磷多元合金镀层,将镀层在5%Nacl溶液中浸泡30天后,观察不到腐蚀,用称重法测腐蚀实验前后的重量,失重为零。
本发明具有实质性特点和显著进步,本发明获得的化学镀镍层为非晶态的均匀、光亮、平滑致密、结合力强的镀层。镀层的脆性较镍磷二元合金得到改善。镀液稳定性好,镀层致密度高,镀层中较高的铜含量可以使镀层免遭海生物的吸附。镀层在海水中的耐蚀性优于铜基合金,克服了其他方法制备的镍基合金的易点蚀的缺点。在海水腐蚀环境下,镀层的耐蚀性优于电镀锌镍层,是一种理想的替代电镀镉层的化学镀层。

Claims (1)

1、一种耐海水腐蚀镍基多元合金的酸性化学镀液,其特征在于配方是:每升溶液中含:硫酸镍8-12g/L,次亚磷酸钠38-45g/L,柠檬酸三钠15-20g/L,乳酸10-12mlL,乙酸钠15-20g/L,硫酸铜0.5-1g/L,氯化铬8-15g/L,钼酸钠0.4-0.8g/L,聚乙二醇0.15-0.30g/L,稳定剂0.5-1mg/L,余量为蒸馏水,其中稳定剂为碘化钾或/和硫脲。
CNB011126701A 2001-04-19 2001-04-19 耐海水腐蚀镍基多元合金的酸性化学镀液 Expired - Fee Related CN1156606C (zh)