CN1308361C - 乙烯-三氟氯乙烯共聚物的制备方法 - Google Patents
乙烯-三氟氯乙烯共聚物的制备方法 Download PDFInfo
- Publication number
- CN1308361C CN1308361C CNB2004100580268A CN200410058026A CN1308361C CN 1308361 C CN1308361 C CN 1308361C CN B2004100580268 A CNB2004100580268 A CN B2004100580268A CN 200410058026 A CN200410058026 A CN 200410058026A CN 1308361 C CN1308361 C CN 1308361C
- Authority
- CN
- China
- Prior art keywords
- reaction
- add
- ethylene
- ethene
- copolymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
Description
实施例 | 第一步 | 反应时间(小时) | 第一步去离子水占总去离子水重量% | 反应温度℃ | |||||||||
混合单体与混合溶剂重量比 | 三氟氯乙烯占混合溶液重量% | 初始三氟氯乙烯∶乙烯 | 引发剂占总反应单体重量% | 补加三氟氯乙烯∶乙烯 | 第一次补加占总补加重量% | 初始占总单体加料重量% | 反应压力 | 第一步 | 第二步 | 第一步 | 第二步 | ||
1 | 1∶8.3 | 98.4 | 1.9∶1 | 0.57 | 1.7∶1 | 27.94 | 75.0 | 1.55 | 1.0 | 3.0 | 10 | 50-60 | 60-85 |
2 | 1∶6.0 | 96.7 | 1.2∶1 | 0.3 | 1.1∶1 | 25 | 66.7 | 1.95 | 1.5 | 3.0 | 16 | 50-60 | 60-70 |
3 | 1∶1.67 | 97.7 | 1.7∶1 | 0.236 | 1.4∶1 | 25.07 | 64.63 | 2.1 | 1.5 | 3.25 | 20 | 50-60 | 60-70 |
4 | 1∶7.1 | 95.9 | 1.9∶1 | 0.27 | 1.3∶1 | 24.7 | 64.77 | 2.1 | 1.5 | 4.5 | 12.5 | 50-60 | 60-70 |
5 | 1∶8.1 | 94.5 | 2.5∶1 | 0.25 | 1.2∶1 | 25 | 62.5 | 2.45 | 1.5 | 3.75 | 11.2 | 40-50 | 50-60 |
6 | 1∶7.9 | 94.0 | 4.6∶1 | 0.249 | 1.3∶1 | 25 | 66.7 | 2.5 | 1.5 | 5.5 | 10 | 40-50 | 50-60 |
7 | 1∶3.4 | 95.6 | 1.9∶1 | 0.017 | 1.26∶1 | 22.25 | 33.74 | 2.10 | 1.5 | 4.5 | 5.88 | 40-60 | 60-70 |
实施例 | 熔点 | 结晶焓J/g | 氟含量,% | 熔融指数g/10min | 抗拉强度Mpa | 断裂伸张率 | 耐热应力开裂 |
1 | 223.87 | 19.71 | 38.9 | 78.16 | 25.84 | 203 | 不开裂 |
2 | 221.49 | 17.64 | 39.2 | 50.24 | 27.59 | 215 | 不开裂 |
3 | 218.60 | 17.012 | 39.2 | 40.80 | 29.61 | 229 | 不开裂 |
4 | 214.77 | 14.911 | 39.3 | 36.05 | 29.29 | 251 | 不开裂 |
3 | 215.40 | 11.142 | 39.4 | 9.14 | 33.53 | 290 | 不开裂 |
6 | 212.72 | 10.829 | 39.6 | 3.14 | 33.53 | 314 | 不开裂 |
7 | 216.37 | 14.864 | 39.7 | 43.33 | 26.98 | 231 | 不开裂 |
Claims (2)