CN1295282C - 环保回收式柔性石墨填料 - Google Patents
环保回收式柔性石墨填料 Download PDFInfo
- Publication number
- CN1295282C CN1295282C CNB2004100131131A CN200410013113A CN1295282C CN 1295282 C CN1295282 C CN 1295282C CN B2004100131131 A CNB2004100131131 A CN B2004100131131A CN 200410013113 A CN200410013113 A CN 200410013113A CN 1295282 C CN1295282 C CN 1295282C
- Authority
- CN
- China
- Prior art keywords
- density
- graphite
- flexible graphite
- environmental protection
- type flexible
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种环保回收式柔性石墨填料，其特征在于包括将回收的柔性石墨板材的边角余料或密度为0.09-1.5g/cm3的不合格填料产品经压缩剪切和粉碎制成石墨粒料，模压成型体积密度为1.2-1.9g/cm3。石墨粒料的尺寸不大于6×0.8×0.35mm，每批粒料密度≥1.4g/cm3的粒子不超过30%，≤0.5g/cm3的粒子不超过10%。本发明具有密封性能优良，选材要求低，对厚度、密度的要求范围广，成本低廉等特点。
Description
技术领域
本发明涉及一种石墨填料，特别是一种柔性石墨粒料组成各向同性的高膨胀率柔性石墨填料。
背景技术
目前使用的柔性石墨填料成型环的结构为：柔性石墨带材绕轴缠绕，在模腔内沿轴向压缩，成型面断面为波纹状互相粘合成型，此种产品要求尺寸精度高，而且制造的原料必须为石墨板材开条而成，对原料的要求也较严格，最大的缺点是：使用过程中内外径的膨胀率如超过3％，就会出现断裂，导致密度失效；使用石墨板材的价格昂贵，内部波纹状结构显示明显的各向异性特点，不利于填料函内密封充盈性。
发明内容
本发明的目的就是要提供一种密封性能优良，选材要求低，对厚度、密度的要求范围广，成本低廉的环保回收式柔性石墨填料。
本发明的目的是这样实现的：一种环保回收式柔性石墨填料，包括将回收的柔性石墨板材的边角余料或密度为0.09-1.5g/cm3的不合格填料产品经压缩剪切和粉碎制成石墨粒料，模压成型体积密度为1.2-1.9g/cm3。石墨粒料的尺寸不大于6×0.8×0.35mm，每批粒料密度≥1.4g/cm3的粒子不超过30％，≤0.5g/cm3的粒子不超过10％。
本发明具有密封性能优良，选材要求低，对厚度、密度的要求范围广，成本低廉等特点。可从柔性石墨生产加工板材厂家回收边角余料进行剪切粉碎加工，成本低廉，大多数厂家将这些边角余料作为垃圾处理掉，污染环境，回收利于环保。此种碎料填料环外径膨胀率可达7％，内径收缩率可达10％，传统填料环外径膨胀率超过4％就会开裂。
具体实施方式
本发明所述的密封填料，使用于各种填料函，是将各种废弃的柔性石墨板材边角料和废弃的柔性石墨填料经粉碎、剪切工艺制成的无序的石墨碎料，加工成密度为1.2-1.9g/cm3的预成型石墨填料或石墨盘根线(添加棉纱线或玻纤或碳纤维丝)。
根据成品体积测算重量，单件用天平称量，模压成型体积密度控制在1.2-1.9g/cm3以内，根据要求也可在配料时加入适量的玻纤、碳纤维、棉纱或酚醛树脂等。
经废料制成的石墨碎料密度为0.09-1.50g/cm3，碎粉的尺寸范围为：长≤6mm，宽≤0.8mm，高≤0.35mm。每批石墨碎料中密度≥1.4g/cm3的粒子不能超过30％，≤0.5g/cm3不能超过10％。
碎料成型压力应控制在120-200kgf/cm2的压力。
Claims (1)
1、一种环保回收式柔性石墨填料，其特征在于包括将回收的柔性石墨板材的边角余料或密度为0.09-1.5g/cm3的不合格填料产品经压缩剪切和粉碎制成石墨填料，模压成型体积密度为1.2-1.9g/cm3，石墨粒料的尺寸不大于6×0.8×0.35mm，每批粒料密度≥1.4g/cm3的粒子不超过30％，≤0.5g/cm3的粒子不超过10％。