CN1243844A - 一种用于生产建筑材料或成形件的材料 - Google Patents

一种用于生产建筑材料或成形件的材料 Download PDF

Info

Publication number
CN1243844A
CN1243844A CN98103468A CN98103468A CN1243844A CN 1243844 A CN1243844 A CN 1243844A CN 98103468 A CN98103468 A CN 98103468A CN 98103468 A CN98103468 A CN 98103468A CN 1243844 A CN1243844 A CN 1243844A
Authority
CN
China
Prior art keywords
materials
construction
described material
mixture
thermoplastic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN98103468A
Other languages
English (en)
Inventor
罗尔夫·亨里希
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ROLPHM PLASTIC GmbH
Original Assignee
ROLPHM PLASTIC GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to DE29703078U priority Critical patent/DE29703078U1/de
Priority to FR9715194A priority patent/FR2760018B3/fr
Priority to GB9725983A priority patent/GB2322375B/en
Priority to EP98102658A priority patent/EP0860474A1/de
Priority to US09/028,237 priority patent/US6255391B1/en
Priority to ZA9806294A priority patent/ZA986294B/xx
Priority to AU76287/98A priority patent/AU7628798A/en
Priority to CZ19982290A priority patent/CZ9802290A3/cs
Priority to JP10208173A priority patent/JP2000044731A/ja
Application filed by ROLPHM PLASTIC GmbH filed Critical ROLPHM PLASTIC GmbH
Priority to CN98103468A priority patent/CN1243844A/zh
Priority to HU9801786A priority patent/HUP9801786A2/hu
Priority to CA002279820A priority patent/CA2279820A1/en
Publication of CN1243844A publication Critical patent/CN1243844A/zh
Pending legal-status Critical Current

Abstract

一种用于生产建筑材料或成形件的材料,其中所述材料包括热塑性材料和橡胶材料的熔融混合物。

Description

一种用于生产建筑材料或成形件的材料
本发明涉及一种用于生产建筑材料或成形件的材料，还涉及由这种材料制得的建筑材料及成形件，例如片材，本发明还涉及生产建筑材料和成形件的方法。
1976年公开的德国专利No.2159735描述了使用把旧的车辆轮胎磨碎成粉得到的橡胶粉(“橡胶细粒”)和/或粗橡胶粉(“粗橡胶细粒”)生产离子交换剂。
德国公开No.1086437描述了一种生产阴离子选择性薄膜(膜片)的方法，使用该方法使含有25-70％的芳香族单乙烯基化合物和脂肪族共轭二烯化合物的混聚物形成膜状薄膜，这种薄膜经过环化或硫化处理后不溶，随后对这种薄膜进行氯-脂环基化，并且最终使其具有活性。
在德国专利No.2159735中，它说明根据德国专利No.1086437的方法，其原材料是一种由芳香族部分和脂肪族部分组成的限定化合物，即一种混聚物，而根据德国专利No.2159735，橡胶粉和/或粗橡胶粉是碳(碳黑)填充的硫化橡胶。
在德国专利No.2159735中，还说明了和根据德国公开No.1086473的先有技术的又一个不同之处，即后一文献描述的是薄膜的生产，而在专利2159735的产品中，没有确定的形状。
在本发明的说明书中，对橡胶粉(“橡胶细粒”)或粗橡胶粉(“粗橡胶细粒”)的内容的定义和德国专利No.2159735中使用的定义相同。
德国专利No.2159735中描述的其它现有技术在此也被包括作为参考。
本发明的一个方面提供了一种用于生产建筑材料或成形件的材料，其中所述材料包括热塑性材料和橡胶材料的熔融混合物。
本发明的另一个方面提供了一种用于熔融形成建筑材料或成形件的混合物，所述混合物包括一种和橡胶材料混合的热塑性材料。
本发明的基础在于橡胶材料和热塑性材料的混合物特别易于形状变形，形成建筑材料或成形件，例如利用挤压，特别是在高温下挤压，以便形成片状产品。
最好是提供一种橡胶粉和/或粗橡胶粉与粉状或由分离的微粒组成的热塑性材料的混合物，该混合物中可能还含有适于这些原材料的填料，或者还含有象玻璃丝和/或金属丝之类的嵌入材料。这样，混合物最终可具有附加的混合填料和/或嵌入材料。
最好，通过机械作用和/或加热和/或压力和/或辐照使处于特定产品或制品形状的橡胶材料和热塑性材料结合在一起。
本发明的另一个方面提供了一种生产建筑材料或成形件的方法，该方法包括把热塑性材料和橡胶材料混合，加热所述混合物以形成熔融混合物，并且使所述熔融混合物形成所述建筑材料或所述成形件的要求形状。
一种最佳生产方法包括机械混合粒状原材料，随后利用挤压设备获得想要的形状，例如薄片形状。
粗橡胶粉特别适于作为橡胶原材料。
粉状聚乙烯特别适于作为热塑性成分的原材料，从而最好使用回收的旧聚乙烯，例如聚乙烯瓶。
特别地，根据本发明的材料可被制成片材，用于屋面，并且本发明的材料具有优良的化学和物理性能。这些片材具有很好的抗老化性及热稳定性；例如对使用本发明片材的屋面的测试结果表明，片材可抵抗-20℃到+80℃的温度，而不会受到任何破坏。
这种片材的另一个优点是极不易燃。
根据本发明的片材及根据本发明的其它形状材料还可以常规已知方式用作地板材料或隔声材料。
根据本发明的混合物还可以所谓的熔融混合物的形式供给，随后进一步处理该熔融混合物制得成品。
根据本发明的材料还可用作尺寸任意的隔热板和/或层面底层片材。
除了聚乙烯外，聚丙烯、热塑性聚氨基甲酸酯及聚乙烯化合物可作为根据本发明的材料混合物的热塑性成分。
由根据本发明的材料制得的片材的断裂应变为190％到200％。
根据本发明的材料的密度为1.2到1.3克/立方厘米。
根据本发明的材料的肖氏A型硬度为90-100。
如果必需的话，根据本发明的材料可含有附加的材料(添加剂)和/或填料，例如带有闭孔和/或带有开孔的颗粒泡沫材料，例如聚苯乙烯颗粒。
此外，根据本发明的材料还可含有丝状物，例如玻璃丝和/或金属丝和/或碳纤维。
根据本发明的材料还可含有作为增白剂的颜料，例如二氧化钛。
此外，对根据本发明的材料进行了照射实验，该实验表明这些材料具有很高的抗紫外线性能。
下面借助实施例进一步说明本发明。实施例
粒径为3毫米的25千克聚乙烯粉和粒径为1毫米的粗橡胶粉在180℃混合10分钟。
需要的话，热塑性混合物中还可加入已知的添加剂。
以一种已知的方法使混合物的一部分再成为粒状。所得到的颗粒形成可用于市场的材料。
以一种已知的方法通过真空吸引把所得混合物的另一部分输送到挤压机，并被挤压成片材建筑材料。
这样可制得隔声材料，该材料可耐-20℃到+85℃的温度。此外，该片状材料防水，耐磨并且不易破裂。
根据本发明的材料可取代石板瓦用作屋面瓦，还可用作鞋底、石膏座及所谓的“折皱”，也就是片材厚度达到约5毫米时。
可用任意已知方法使用及处理根据本发明制得的片材，例如采用切削及刨削；也可通过加热形成任意希望的形状；此外这种材料易于熔合(焊接)。
根据本发明的材料在被进一步处理前，可为片状。
除橡胶粉或粗橡胶粉之外，特别适宜的热塑性成分有聚乙烯、聚丙烯、聚氨基甲酸酯及聚乙烯化合物，例如聚苯乙烯(注本句有问题)。
材料成分的结合主要由所谓的范德瓦键实现，其结果是产生熔融混合物，范德瓦键由压力(熔融-压力)和/或加热和/或辐照引起。
根据一个最佳实施例，橡胶材料及热塑性材料均为粉状。
作为例子，下面列出了熔融挤压热塑性材料和橡胶材料的粉状混合物，随后冷却后得到的片材的测试物理性能：
1.密度(标准：DIN 53479)：1.23克/立方厘米
2. 220℃及250巴条件下的冲击弯曲强度(标准：摆锤式冲击结构)：测试片材未断裂。
3.-40℃条件下的冲击弯曲强度，其生产和测试条件与测试号2相同：测试片材未断裂。
4.常温下的冲击弯曲强度，其生产和测试条件与测试号3相同：测试片材未断裂。
5.抗拉强度，其生产和测试条件与测试号2相同，测试标准：DIN53444/3/3，测试结果：抗拉强度为8.7Mpa。
6.材料拉伸失效时的应变，生产和测试条件与测试号5相同，测试标准：DIN 53455/3/3，测试结果：应变大于100％。
7.肖氏A型硬度：95

Claims (15)

1、一种用于生产建筑材料或成形件的材料，其特征在于所述材料包含热塑性材料和橡胶材料的熔融混合物。
2、按照权利要求1所述的材料，其特征在于橡胶材料和热塑性材料以分离的颗粒形式存在，通过机械作用和/或加热和/或辐照使这些颗粒结合在一起。
3、按照权利要求2所述的材料，其特征在于所述材料由熔融挤压形成。
4、按照权利要求1、2或3所述的材料，其特征在于橡胶材料包括粗橡胶粉。
5、按照前述任一权利要求所述的材料，其特征在于热塑性材料为粉状。
6、按照前述任一权利要求所述的材料，其特征在于所述材料中含有填料。
7、按照权利要求6所述的材料，其特征在于所述填料包括带有开孔的泡沫材料和/或带有闭孔的泡沫材料和/或丝状物。
8、按照前述任一权利要求所述的材料，其特征在于所述材料为片状。
9、一种使用前述任一权利要求所述的材料制得的建筑材料。
10、一种使用权利要求1-8任一所述的材料制得的成形件。
11、一种生产建筑材料或成形件的方法，其特征在于：该方法包括混合一种热塑性材料和一种橡胶材料，加热所述混合物形成熔融混合物，并使所述熔融混合物形成所述建筑材料或所述成形件的要求形状。
12、一种包含热塑性材料和橡胶材料的物理混合物的片状材料。
13、按照权利要求12所述的片状材料，其特征在于包括填料，特别是膨胀填料。
14、按照权利要求12或13所述的片状材料，其特征在于所述材料由熔融挤压形成。
15、按照权利要求12、13或14所述的片状材料，其特征在于它是屋面底层片材。
CN98103468A 1997-02-21 1998-08-03 一种用于生产建筑材料或成形件的材料 Pending CN1243844A (zh)