CN1218990C - 淀粉与聚合物复合物的制备方法 - Google Patents
淀粉与聚合物复合物的制备方法 Download PDFInfo
- Publication number
- CN1218990C CN1218990C CN 03100424 CN03100424A CN1218990C CN 1218990 C CN1218990 C CN 1218990C CN 03100424 CN03100424 CN 03100424 CN 03100424 A CN03100424 A CN 03100424A CN 1218990 C CN1218990 C CN 1218990C
- Authority
- CN
- China
- Prior art keywords
- starch
- emulsion
- polymer
- rubber
- mixture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
Description
实施例1 | 实施例2 | 实施例3 | 实施例4 | 实施例5 | 对比例1 | 对比例2 | |
硬度 | 40 | 57 | 87 | 50 | 56 | 54 | 46 |
300%定伸应力,MPa | 2.4 | 4.9 | 19.0 | 4.9 | 6.9 | 1.8 | 3.8 |
拉伸强度,MPa | 3.8 | 7.8 | 22.4 | 19.5 | 15.6 | 2.8 | 15.4 |
断裂伸长率,% | 440 | 460 | 360 | 530 | 510 | 660 | 490 |
撕裂强度,KN/m | 18.5 | 24.1 | 56.7 | 52.3 | 58.2 | 18.7 | 48.7 |
密度,g/cm3 | 0.942 | 1.034 | 1.182 | 0.920 | 1.243 | 1.034 | 0.920 |
Claims (4)