CN115874328A - 玻尿酸亲肤保湿针织面料及其生产工艺 - Google Patents
玻尿酸亲肤保湿针织面料及其生产工艺 Download PDFInfo
- Publication number
- CN115874328A CN115874328A CN202211739694.1A CN202211739694A CN115874328A CN 115874328 A CN115874328 A CN 115874328A CN 202211739694 A CN202211739694 A CN 202211739694A CN 115874328 A CN115874328 A CN 115874328A
- Authority
- CN
- China
- Prior art keywords
- hyaluronic acid
- production process
- knitted fabric
- agent
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种玻尿酸亲肤保湿针织面料及其生产工艺，包括织造、定胚、烧毛、前处理、染色、缸内抗菌处理、烘干及定型整理，染料采用亨斯迈EC型活性染料实现莫代尔棉同色性佳、匀染平实，通过烧毛、缸内轻抛光协同保证面料光泽，通过玻尿酸功能整理使面料富含玻尿酸分子具有良好的保湿效果。在充分利用莫代尔/棉纤维各自的特点的基础上，再通过玻尿酸功能、吸湿排汗、手感整理，赋予面料抗菌保湿、吸湿排汗、柔软滑爽等特点，使其穿着舒适、柔软、美观大方兼优异的服用性能，尤其适用于贴身高档女装内衣、婴幼儿童服饰、其它内衣类服装面料的选择。
Description
技术领域
本发明属于纺织技术领域，具体涉及一种玻尿酸亲肤保湿针织面料及其生产工艺。
背景技术
近年来，受全球环境、碳排放、资源枯竭等趋势和影响，纺织化学合成纤维的产量将会受到越来越多的约束；人们在重视纺织品消费过程中环保性能的同时，对再生纤维素纤维的价值进行了重新认识和发掘。
莫代尔是一种新型再生纤维素纤维，它既有棉的舒适性，又有粘胶纤维的悬垂性和柔和的光泽，吸湿性好，易于染色，不易起静电，有较好的可纺性能。含氨纶的莫代尔/棉混纺织物，具有良好的光泽和悬垂感，柔软舒适，色泽鲜艳，同时具有良好的弹性，适合作高档面料。
莫代尔再生纤维素纤维和棉纤维,理论上虽然两种纤维都属于纤维素纤维，但因为两者的聚合度、聚态结构和形态结构都不同，故此导致染色性能上存在一定的差异，实际染色生产受染化料选用、处方工艺带来的上染率、固色率、染色牢度、织物品质、染色效果等等方面的影响，同浴活性染料染色时，棉和莫代尔纤维因上色性不同，普通的活性染料一般会导致两种纤维不夹色、同色性差现象，出现白星布面问题，或品质不合格、面料档次降低等问题。
另外，作为内衣面料贴身穿着，要求面料具有极佳的触感，同时要求面料吸湿排汗、抗静电性能优越。为了赋予面料极佳的亲水手感，首先需对面料布面毛羽进行处理，常规采用抛光工艺。然而，抛光对面料强力影响较大，且抛光酶对莫代尔纤维效果微乎其微，按照传统加工工艺制得的面料存在有易擦伤起毛和强力不佳等缺陷。
玻尿酸是天然中最亲水的分子之一，对人体有诸多的好处，可以改善皮肤营养代谢，使皮肤柔嫩、光滑、去皱、增加弹性、防止衰老，在保湿的同时又是良好的透皮吸收促进剂，被称之为“天然的保湿剂”。中国公开专利文献(CN109537279A)公开了一种玻尿酸丝绸面料的制作方法，包括：取完成染色工序的丝绸面料，烘干打卷后，浸轧玻尿酸，在整理机中加入工作液，工作液由柔软剂、固色剂和玻尿酸整理剂组成，采用一浸一轧的方式，带液率为100％；浸轧后的丝绸面料经烘干机烘干，同时用抗静电整理剂以喷雾法进行防静电处理，正超喂定型。但是，该整理工艺所得的玻尿酸真丝面料耐洗性不理想，刚整理后确实能获得高玻尿酸含量的面料，洗涤后面料中玻尿酸急剧流失，洗涤至5次后，面料中剩余玻尿酸含量已不足20％，丧失护肤效果。
发明内容
本发明的发明目的是提供一种玻尿酸亲肤保湿针织面料及其生产工艺，具有抗菌保湿、吸湿排汗、柔软滑爽等特点，使其穿着舒适、柔软、美观大方兼优异的服用性能，尤其适用于贴身高档女装内衣、婴幼儿童服饰、其它内衣类服装面料的选择。
为实现上述发明目的，本发明采用的技术方案是：
玻尿酸亲肤保湿针织面料的生产工艺，具体包括如下步骤：
S1、织造：采用莫代尔/棉紧密赛络纺纱线与氨纶纱按用纱量比为92-95﹕5-8纬编织造成胚布；
S2、定胚：对步骤S1的胚布先松布摆放8小时以上再进行蒸胚定型；
S3、烧毛：利用布身与绒毛升温速率不同的原理，达到只烧去胚布正反面毛羽达4级；
S4、前处理：将步骤S3烧毛后的胚布入缸进行前处理以充分去除洗净木质素、油份、蜡质及沾附的灰份杂质；
S5、染色：浴比1∶5，先加亨斯迈EC型活性染料再依次加入元明粉、纯碱和固色碱，元明粉总量为35g/l-40g/l，纯碱总量为15g/l-20g/l，固色碱为3g/l-5g/l，于60±2℃温度下保温染色40±5min；然后于80℃-85℃皂洗；
S6、缸内抗菌处理：加入抗菌剂进行缸内抗菌处理15min-20min，温度50℃-55℃；然后出布、脱水；
S7、烘干：喷涂玻尿酸整理剂，喷涂量为10g/m2-15g/m2，烘干温度为130℃-135℃；
S8、定型整理：将步骤S7烘干后的面料进行浸轧定型处理，定型液中包含2％-3％吸湿排汗剂、10％-12％亲水硅油、1％-2％亲水柔软剂和1％-2％玻尿酸整理剂，轧余率为60％-65％，定型温度155℃-160℃，车速20m/min-25m/min。
优选地，所述莫代尔/棉紧密赛络纺纱线为JM/C40S.40/60，所述氨纶纱为20D，胚布为平纹组织。
优选地，所述莫代尔/棉紧密赛络纺纱线与氨纶纱的用纱量比为95﹕5。
优选地，所述步骤S2的蒸胚定型工艺为温度为195℃-200℃，车速为25m/min-30m/min，上下超喂45％/6％。
优选地，所述步骤S3的烧毛工艺为机速为80m/min-100m/min，火力为18立方米每小时-20立方米每小时。
优选地，所述步骤S4前处理工艺具体为：胚布入缸后进50±2℃温水，加入1g/l-1.5g/l低泡精练剂SF-2和1g/l-1.5g/l低温练漂剂TF-189，保温运行4min-6min后加入2g/l-2.5g/l精炼酶1128B并保温运行8min-12min，然后以3±0.2℃/min升温至70℃，加入6g/l-7g/l双氧水和1g/l-1.5g/l除油剂TF-129K，保温运行8min-12min后升温至85℃并保温运行30min-35min，然后降温至80℃，溢流水洗，排液；加50±2℃温水，水洗6min-8min，排液；再加50±2℃温水，加入中和酸、测pH至5.5-6.0，运行6min-8min后，加入除氧酶，运行10min-14min排液。
优选地，所述步骤S5染色为浅色时，染色工艺具体为：加水升温至40±2℃，在15min-20min内加入亨斯迈EC型活性染料和少量中性抛光酶后运行10min-15min，在8min-10min内加入1/10元明粉，运行4min-6min后在8min-10min内加入余量元明粉；保温运转4min-6min后以1±0.2℃/min升温至50±2℃，保温染色15min-20min后在18min-22min内加入3/20纯碱，运行10min-15min后在18min-22min内加入17/20纯碱和固色碱XH-01；保温运转10min-15min后以1±0.2℃/min升温至60±2℃，保温运转运行40±5min，排液。
优选地，所述皂洗工艺为：加50±2℃温水，水洗6min-8min，排液；再加50±2℃温水，水洗6min-8min，排液；再加50±2℃温水，加入中和酸和皂洗粉，升温至80℃-85℃，处理10min-15min，排液；最后加50±2℃温水，水洗6min-8min，排液；浴比1∶5。
优选地，所述步骤S6中抗菌剂采用SILVADUR 930，用量以胚布重量计的3％-4％；所述步骤S7和S8的玻尿酸整理剂为TASTEXHyalu04。
本发明还提供一种由上述生产工艺制得的玻尿酸亲肤保湿针织面料。
与现有技术相比，本发明具有以下有益效果：
本发明面料采用莫代尔/棉纱为原料，面料巧妙的结合了两种纤维的特性，具有优异的吸湿透气性、柔软舒适等功能，再经优化的染整工艺，包括低温低碱前处理煮漂工艺、探讨莫代尔棉采用活性染料同浴上色不均匀工艺技术、毛羽处理工艺技术、亲水柔软整理技术及玻尿酸功能整理工艺技术等生产关键工艺技术。在充分利用莫代尔/棉纤维各自的特点的基础上，再通过玻尿酸功能、吸湿排汗、手感整理，赋予面料抗菌保湿、吸湿排汗、柔软滑爽等特点，使其穿着舒适、柔软、美观大方兼优异的服用性能，尤其适用于贴身高档女装内衣、婴幼儿童服饰、其它内衣类服装面料的选择。
本发明开发的玻尿酸功能整理工艺技术，使面料富含玻尿酸分子，通过与皮肤接触，玻尿酸分子可注入人体肌肤，具有良好的保湿效果，锁定人体肌肤水份，满足广大妇女、儿童的各种纺织服装家纺要求尤其适用于贴身内衣类服装面料选择，适用于春、夏、秋等季节的面料，穿着后给予人体亲肤保湿、柔软舒适度调节、健康卫生调节、对人体抗静电、抗起毛起球等性能的多功能面料，使人们在休闲或运动之余，得到更舒适爽悦、更卫生健康、更安全和体贴入微的体验与感受。且本发明严选SILVADUR 930抗菌剂及增加在表干时喷涂玻尿酸整理剂，利用抗菌剂中的有机聚合物粘附及缓释玻尿酸整理剂，并在抗菌层与浸轧整理层之间起架桥联结作用，一方面可以增加面料玻尿酸的初始含量，另一面可有效减缓玻尿酸在洗涤中的脱落速率，延长耐洗次数。
本发明开发增加烧毛工艺，先烧掉胚布布面毛羽，胚布毛羽效果达到4级后再落缸，避免了传统重抛光导致的胀破问题。落缸后由于长时间的摩擦会导致布面起毛，采用缸内轻抛光工艺，提高面料光洁度的同时，避免对面料强力造成损伤。因此前处理采用烧毛是本项目设计的一个亮点，不仅解决布面毛头问题，对面料强力、抗起毛起球性、各项牢度都有明显改善。
本发明采用EC型活性染料，其一氟均三嗪和乙烯砜硫酸酯基对莫代尔/棉两种纤维亲和反应能力接近，与两种纤维素纤维中羟基的结合能力更强，匀染性好且上染率和固色率高，面料纤维上染平实，避免白星、色花、布面不均等布面问题，同时结合烧毛与缸内轻抛光工艺设计协同保证面料光泽如丝绸般优雅华贵。
具体实施方式
实施例1
本实施例提供一种玻尿酸亲肤保湿针织面料的生产工艺，具体包括如下步骤：
S1、织造：采用莫代尔/棉紧密赛络纺纱线JM/C40S.40/60与20D氨纶纱通过迈耶单面机按用纱量比为95﹕5纬编织造成全衬弹力针织胚布，寸口34〞，针数28，平纹组织。
S2、定胚：对步骤S1的胚布先松布摆放8小时以上使内应力得到释放，再进一步通过蒸胚定型改善胚布克重不稳定和确保收缩平衡性，蒸胚定型工艺为温度为195℃，车速为25m/min，上下超喂45％/6％。
S3、烧毛：利用布身与绒毛升温速率不同的原理，通过气体烧毛机采用对烧方式达到只烧去胚布正反面毛羽达4级再落缸，烧毛工艺为机速为80m/min，火力为18立方米每小时。
S4、前处理：将步骤S3烧毛后的胚布入缸进行前处理以充分去除洗净木质素、油份、蜡质及沾附的灰份杂质，同时减少对纤维的损伤，保证面料的强力。具体为：胚布入缸后进50℃温水，加入1.2g/l低泡精练剂SF-2和1.5g/l低温练漂剂TF-189，保温运行5min后加入2g/l精炼酶1128B并保温运行10min，然后以3℃/min升温至70℃，加入6g/l双氧水和1g/l除油剂TF-129K，保温运行10min后升温至85℃并保温运行30min，然后降温至80℃，溢流水洗，排液；加50℃温水，水洗7min，排液；再加50℃温水，加入中和酸、测pH至6.0，运行7min后，加入除氧酶DM-8618，运行10min排液。
S5、染色：浴比1∶5，先加亨斯迈EC型活性染料再依次加入元明粉、纯碱和固色碱。中灰色染色工艺具体为：加水升温至40℃，在20min内加入亨斯迈EC型活性染料和少量中性抛光酶诺维信59000后运行10min，在10min内加入1/10元明粉，运行5min后在10min内加入余量元明粉；保温运转5min后以1℃/min升温至50℃，保温染色15min后在20min内加入3/20纯碱，运行15min后在20min内加入17/20纯碱和固色碱XH-01；保温运转15min后以1℃/min升温至60℃，保温运转运行40min，排液。
亨斯迈EC型活性染料具体为：EC-2BL活性红0.083％、EC2R活性黄0.036％、EC-R活性蓝0.088％。元明粉总量为35g/l，纯碱总量为15g/l，固色碱为3g/l。
皂洗工艺为：加50℃温水，水洗7min，排液；再加50℃温水，水洗7min，排液；再加50℃温水，加入中和酸和皂洗粉DM1508，升温至80℃，处理10min，排液；最后加50℃温水，水洗7min，排液；浴比1∶5。
S6、缸内抗菌处理：加入抗菌剂SILVADUR 930进行缸内抗菌处理20min，温度55℃，用量以胚布重量计的3％；然后出布、脱水。
S7、烘干：展布、无张力传送，在110℃温度下预烘至表干后喷涂玻尿酸整理剂TASTEX Hyalu 04，喷涂量为15g/m2，然后进烘干机烘干，烘干温度为135℃。
S8、定型整理：将步骤S7烘干后的面料进行浸轧定型处理，定型液中包含2％吸湿排汗剂QH-13、10％亲水硅油T718、1％亲水柔软剂202和1％玻尿酸整理剂TASTEX Hyalu04，一浸一轧，压力0.3MPa，轧余率为60％，定型温度160℃，车速24m/min，上下超喂30％/2％，定型后克重155g/m2。
实施例2
本实施例提供一种玻尿酸亲肤保湿针织面料的生产工艺，具体包括如下步骤：
S1、织造：采用莫代尔/棉紧密赛络纺纱线JM/C40S.40/60与20D氨纶纱通过迈耶单面机按用纱量比为95﹕5纬编织造成全衬弹力针织胚布，寸口34〞，针数28，平纹组织。
S2、定胚：对步骤S1的胚布先松布摆放8小时以上使内应力得到释放，再进一步通过蒸胚定型改善胚布克重不稳定和确保收缩平衡性，蒸胚定型工艺为温度为200℃，车速为30m/min，上下超喂45％/6％。
S3、烧毛：利用布身与绒毛升温速率不同的原理，通过气体烧毛机采用对烧方式达到只烧去胚布正反面毛羽达4级再落缸，烧毛工艺为机速为100m/min，火力为20立方米每小时。
S4、前处理：将步骤S3烧毛后的胚布入缸进行前处理以充分去除洗净木质素、油份、蜡质及沾附的灰份杂质，同时减少对纤维的损伤，保证面料的强力。具体为：胚布入缸后进50℃温水，加入1.5g/l低泡精练剂SF-2和1g/l低温练漂剂TF-189，保温运行5min后加入2.5g/l精炼酶1128B并保温运行10min，然后以3℃/min升温至70℃，加入7g/l双氧水和1.5g/l除油剂TF-129K，保温运行10min后升温至85℃并保温运行30min，然后降温至80℃，溢流水洗，排液；加50℃温水，水洗7min，排液；再加50℃温水，加入中和酸、测pH至5.5，运行7min后，加入除氧酶DM-8618，运行10min排液。
S5、染色：浴比1∶5，先加亨斯迈EC型活性染料再依次加入元明粉、纯碱和固色碱。中灰色染色工艺具体为：加水升温至40℃，在20min内加入亨斯迈EC型活性染料和少量中性抛光酶诺维信59000后运行10min，在10min内加入1/10元明粉，运行5min后在10min内加入余量元明粉；保温运转5min后以1℃/min升温至50℃，保温染色20min后在20min内加入3/20纯碱，运行15min后在20min内加入17/20纯碱和固色碱XH-01；保温运转15min后以1℃/min升温至60℃，保温运转运行40min，排液。
亨斯迈EC型活性染料具体为：EC-2BL活性红0.083％、EC2R活性黄0.036％、EC-R活性蓝0.088％。元明粉总量为40g/l，纯碱总量为15g/l，固色碱为5g/l。
皂洗工艺为：加50℃温水，水洗7min，排液；再加50℃温水，水洗7min，排液；再加50℃温水，加入中和酸和皂洗粉DM1508，升温至80℃，处理15min，排液；最后加50℃温水，水洗7min，排液；浴比1∶5。
S6、缸内抗菌处理：加入抗菌剂SILVADUR 930进行缸内抗菌处理20min，温度50℃，用量以胚布重量计的4％；然后出布、脱水。
S7、烘干：展布、无张力传送，在110℃温度下预烘至表干后喷涂玻尿酸整理剂TASTEX Hyalu 04，喷涂量为10g/m2，然后进烘干机烘干，烘干温度为130℃。
S8、定型整理：将步骤S7烘干后的面料进行浸轧定型处理，定型液中包含3％吸湿排汗剂QH-13、10％亲水硅油T718、1.5％亲水柔软剂202和2％玻尿酸整理剂TASTEX Hyalu04，一浸一轧，压力0.3MPa，轧余率为60％，定型温度160℃，车速25m/min，上下超喂30％/2％，定型后克重155g/m2。
实施例3
本实施例提供一种玻尿酸亲肤保湿针织面料的生产工艺，具体包括如下步骤：
S1、织造：采用莫代尔/棉紧密赛络纺纱线JM/C40S.40/60与20D氨纶纱通过迈耶单面机按用纱量比为95﹕5纬编织造成全衬弹力针织胚布，寸口34〞，针数28，平纹组织。
S2、定胚：对步骤S1的胚布先松布摆放8小时以上使内应力得到释放，再进一步通过蒸胚定型改善胚布克重不稳定和确保收缩平衡性，蒸胚定型工艺为温度为195℃，车速为28m/min，上下超喂45％/6％。
S3、烧毛：利用布身与绒毛升温速率不同的原理，通过气体烧毛机采用对烧方式达到只烧去胚布正反面毛羽达4级再落缸，烧毛工艺为机速为90m/min，火力为18立方米每小时。
S4、前处理：将步骤S3烧毛后的胚布入缸进行前处理以充分去除洗净木质素、油份、蜡质及沾附的灰份杂质，同时减少对纤维的损伤，保证面料的强力。具体为：胚布入缸后进50℃温水，加入1g/l低泡精练剂SF-2和1g/l低温练漂剂TF-189，保温运行5min后加入2g/l精炼酶1128B并保温运行10min，然后以3℃/min升温至70℃，加入6.5g/l双氧水和1.2g/l除油剂TF-129K，保温运行10min后升温至85℃并保温运行30min，然后降温至80℃，溢流水洗，排液；加50℃温水，水洗7min，排液；再加50℃温水，加入中和酸、测pH至5.5，运行7min后，加入除氧酶DM-8618，运行10min排液。
S5、染色：浴比1∶5，先加亨斯迈EC型活性染料再依次加入元明粉、纯碱和固色碱。中灰色染色工艺具体为：加水升温至40℃，在20min内加入亨斯迈EC型活性染料和少量中性抛光酶诺维信59000后运行10min，在10min内加入1/10元明粉，运行5min后在10min内加入余量元明粉；保温运转5min后以1℃/min升温至50℃，保温染色15min后在20min内加入3/20纯碱，运行15min后在20min内加入17/20纯碱和固色碱XH-01；保温运转15min后以1℃/min升温至60℃，保温运转运行40min，排液。
亨斯迈EC型活性染料具体为：EC-2BL活性红0.083％、EC2R活性黄0.036％、EC-R活性蓝0.088％。元明粉总量为35g/l，纯碱总量为20g/l，固色碱为3g/l。
皂洗工艺为：加50℃温水，水洗7min，排液；再加50℃温水，水洗7min，排液；再加50℃温水，加入中和酸和皂洗粉DM1508，升温至80℃，处理10min，排液；最后加50℃温水，水洗7min，排液；浴比1∶5。
S6、缸内抗菌处理：加入抗菌剂SILVADUR 930进行缸内抗菌处理20min，温度55℃，用量以胚布重量计的3％；然后出布、脱水。
S7、烘干：展布、无张力传送，在110℃温度下预烘至表干后喷涂玻尿酸整理剂TASTEX Hyalu 04，喷涂量为13g/m2，然后进烘干机烘干，烘干温度为135℃。
S8、定型整理：将步骤S7烘干后的面料进行浸轧定型处理，定型液中包含2％吸湿排汗剂QH-13、12％亲水硅油T718、2％亲水柔软剂202和1％玻尿酸整理剂TASTEX Hyalu04，一浸一轧，压力0.4MPa，轧余率为65％，定型温度155℃，车速20m/min，上下超喂30％/2％，定型后克重155g/m2。
对比例1
该对比例1与上述实施例1的区别仅在于：取消步骤S3烧毛，并在步骤S4前处理之后和S5染色之前进行步骤S4-1抛光步骤。该步骤S4-1抛光工艺具体为：加入温度处于35～60℃的温水，调整PH值处于5.5～6，然后加入胚布重量0.2％～0.5％的中性抛光酶，持续反应15min～20min。抛光完成后进行实施例1所述的染色工艺且取消使用S5染色中的中性抛光酶。
对比例2
该对比例2与上述实施例1的区别仅在于步骤S5染色不同，该对比例2的采用雅格素染料替代EC活性染料。
对比例3
该对比例3与上述实施例1的区别仅在于：取消步骤S7中的喷涂玻尿酸整理剂并将对应量的玻尿酸整理剂与S8的玻尿酸整理剂合并加在定型液中。
取上述实施例1-3和对比例1-3的针织面料进行试验检测，结果参见表1。
表1：本发明实施例1-3及对比例1-3的针织面料物性检测结果表
其中：透明质酸钠含量采用紫外可见分光光度计测试；金黄色葡萄球菌的抗菌性能采用AATCC 100-2019标准测试；耐皂洗牢度采用GB/T 3921-2008(40℃，30min)测试；耐水色牢度采用GB/T 5713-2013标准测试；吸水时间采用AATCC79-2010标准测试；水洗方法按照GB/T8629-2001《纺织品试验用家庭洗涤和干燥程序》执行。
以上显示和描述了本发明创造的基本原理和主要特征及本发明的优点，本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明创造精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内，本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (10)
1.玻尿酸亲肤保湿针织面料的生产工艺，其特征在于：具体包括如下步骤：
S1、织造：采用莫代尔/棉紧密赛络纺纱线与氨纶纱按用纱量比为92-95﹕5-8纬编织造成胚布；
S2、定胚：对步骤S1的胚布先松布摆放8小时以上再进行蒸胚定型；
S3、烧毛：利用布身与绒毛升温速率不同的原理，达到只烧去胚布正反面毛羽达4级；
S4、前处理：将步骤S3烧毛后的胚布入缸进行前处理以充分去除洗净木质素、油份、蜡质及沾附的灰份杂质；
S5、染色：浴比1∶5，先加亨斯迈EC型活性染料再依次加入元明粉、纯碱和固色碱，元明粉总量为35g/l-40g/l，纯碱总量为15g/l-20g/l，固色碱为3g/l-5g/l，于60±2℃温度下保温染色40±5min；然后于80℃-85℃皂洗；
S6、缸内抗菌处理：加入抗菌剂进行缸内抗菌处理15min-20min，温度50℃-55℃；然后出布、脱水；
S7、烘干：喷涂玻尿酸整理剂，喷涂量为10g/m2-15g/m2，烘干温度为130℃-135℃；
S8、定型整理：将步骤S7烘干后的面料进行浸轧定型处理，定型液中包含2％-3％吸湿排汗剂、10％-12％亲水硅油、1％-2％亲水柔软剂和1％-2％玻尿酸整理剂，轧余率为60％-65％，定型温度155℃-160℃，车速20m/min-25m/min。
2.根据权利要求1所述的玻尿酸亲肤保湿针织面料的生产工艺，其特征在于：所述莫代尔/棉紧密赛络纺纱线为JM/C40S.40/60，所述氨纶纱为20D，胚布为平纹组织。
3.根据权利要求1所述的玻尿酸亲肤保湿针织面料的生产工艺，其特征在于：所述莫代尔/棉紧密赛络纺纱线与氨纶纱的用纱量比为95﹕5。
4.根据权利要求1所述的玻尿酸亲肤保湿针织面料的生产工艺，其特征在于：所述步骤S2的蒸胚定型工艺为温度为195℃-200℃，车速为25m/min-30m/min，上下超喂45％/6％。
5.根据权利要求1所述的玻尿酸亲肤保湿针织面料的生产工艺，其特征在于：所述步骤S3的烧毛工艺为机速为80m/min-100m/min，火力为18立方米每小时-20立方米每小时。
6.根据权利要求1所述的玻尿酸亲肤保湿针织面料的生产工艺，其特征在于：所述步骤S4前处理工艺具体为：胚布入缸后进50±2℃温水，加入1g/l-1.5g/l低泡精练剂SF-2和1g/l-1.5g/l低温练漂剂TF-189，保温运行4min-6min后加入2g/l-2.5g/l精炼酶1128B并保温运行8min-12min，然后以3±0.2℃/min升温至70℃，加入6g/l-7g/l双氧水和1g/l-1.5g/l除油剂TF-129K，保温运行8min-12min后升温至85℃并保温运行30min-35min，然后降温至80℃，溢流水洗，排液；加50±2℃温水，水洗6min-8min，排液；再加50±2℃温水，加入中和酸、测pH至5.5-6.0，运行6min-8min后，加入除氧酶，运行10min-14min排液。
7.根据权利要求1所述的玻尿酸亲肤保湿针织面料的生产工艺，其特征在于：所述步骤S5染色为浅色时，染色工艺具体为：加水升温至40±2℃，在15min-20min内加入亨斯迈EC型活性染料和少量中性抛光酶后运行10min-15min，在8min-10min内加入1/10元明粉，运行4min-6min后在8min-10min内加入余量元明粉；保温运转4min-6min后以1±0.2℃/min升温至50±2℃，保温染色15min-20min后在18min-22min内加入3/20纯碱，运行10min-15min后在18min-22min内加入17/20纯碱和固色碱XH-01；保温运转10min-15min后以1±0.2℃/min升温至60±2℃，保温运转运行40±5min，排液。
8.根据权利要求7所述的玻尿酸亲肤保湿针织面料的生产工艺，其特征在于：所述皂洗工艺为：加50±2℃温水，水洗6min-8min，排液；再加50±2℃温水，水洗6min-8min，排液；再加50±2℃温水，加入中和酸和皂洗粉，升温至80℃-85℃，处理10min-15min，排液；最后加50±2℃温水，水洗6min-8min，排液；浴比1∶5。
9.根据权利要求1所述的玻尿酸亲肤保湿针织面料的生产工艺，其特征在于：所述步骤S6中抗菌剂采用SILVADUR 930，用量以胚布重量计的3％-4％；所述步骤S7和S8的玻尿酸整理剂为TASTEX Hyalu 04。
10.一种由权利要求1至9任一项所述的生产工艺制得的玻尿酸亲肤保湿针织面料。