CN115385320B - 水热制备磷酸锰铁的方法及其应用 - Google Patents
水热制备磷酸锰铁的方法及其应用 Download PDFInfo
- Publication number
- CN115385320B CN115385320B CN202211018204.9A CN202211018204A CN115385320B CN 115385320 B CN115385320 B CN 115385320B CN 202211018204 A CN202211018204 A CN 202211018204A CN 115385320 B CN115385320 B CN 115385320B
- Authority
- CN
- China
- Prior art keywords
- manganese
- solution
- ferricyanide
- iron
- phosphate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开一种水热制备磷酸锰铁的方法及其应用，将铁氰化物溶液分别加入到铁盐溶液和锰盐溶液中进行反应，得到两种沉淀物，将两种沉淀物混合并分散于水中，持续加入磷酸溶液和硝酸溶液进行水热反应，即得所述磷酸锰铁。本发明利用铁氰化物分别与铁盐和锰盐反应，生成对应的铁氰化物盐沉淀，沉淀混合进行铁锰配比，与硝酸、磷酸进行水热反应生成磷酸锰铁，使铁锰达到共沉淀，提高了铁锰混合的均匀性。
Description
技术领域
本发明属于锂电池正极材料前驱体技术领域，具体涉及一种水热制备磷酸锰铁的方法及其应用。
背景技术
磷酸铁锂具有较为规则的橄榄石型结构，使得磷酸铁锂获得放电容量大、价格低廉、无毒性且不易对环境造成污染的优点，但由于其结构的限制，在应用于电池中时，磷酸铁锂存在电子导电率较低，锂离子扩散系数较小，材料振实密度较低的缺点，极大地限制了磷酸铁锂的应用。为了拓宽磷酸铁锂的应用，目前采用在磷酸铁锂中引入锰系化合物，形成磷酸锰铁锂固溶体，由于锰系化合物具有较高的电化学反应电压和较佳的电解质相容性，使得磷酸锰铁锂固溶体获得较佳的电容量以及循环效果。
目前磷酸锰铁锂的合成方法有很多，基本类似磷酸铁锂的合成。有纯固相法，包括直接使用磷源、铁源、锰源、锂源等原料烧结得到磷酸锰铁锂，也有先合成磷酸锰作为锰源和部分磷源，再将磷酸锰、铁源、锂源混合，烧结得到磷酸亚锰铁锂。其缺点在于不能实现锰、铁在原子层面的均匀混合，制备出来的磷酸锰铁锂的充电恒压段和倍率放电性能较差。由于磷酸锰与磷酸铁的Ksp不同，沉淀速率与pH不同，直接采用共沉淀法制取磷酸锰铁还存在锰铁难以形成共沉淀物的问题。
目前，有人采用有机相来沉淀制备磷酸锰铁，但该法产量低，易产生爆炸风险，危险性较高。且合成的磷酸锰铁中的锰多以二价锰存在，在后续与锂源烧结时，还需要另外补加磷源。而直接制备的三价锰在溶液中易发生歧化反应，生成二价锰和四价锰，产品的纯度不高。
中国专利CN105226273A公开了一种磷酸锰铁锂及其制备方法，其分别用溶胶凝胶法制备磷酸铁锂溶胶和磷酸锰锂溶胶；然后将磷酸铁锂溶胶和磷酸锰锂溶胶在惰性气氛中煅烧得到磷酸锰铁锂。该方法能够很方便的制备得到任意锰铁比例的磷酸锰铁锂，生产便利。但是，这种工艺由磷酸铁锂和磷酸锰锂共同烧结获得，难以使两种物质均匀分布，容易发生锰铁独自富集，产生分相，影响电性能的发挥。
发明内容
本发明旨在至少解决上述现有技术中存在的技术问题之一。为此，本发明提出一种水热制备磷酸锰铁的方法及其应用，该方法可制备得到锰铁分布较为均匀的磷酸锰铁前驱体，使后续烧结得到的磷酸锰铁锂具有较高的比容量和循环性能。
根据本发明的一个方面，提出了一种水热制备磷酸锰铁的方法，包括以下步骤：
S1：将铁氰化物溶液分别加入到铁盐溶液和锰盐溶液中进行反应，得到锰的铁氰化物沉淀和铁的铁氰化物沉淀；所述铁盐溶液中的铁盐选自二价铁盐或三价铁盐中的至少一种；
S2：按照目标产物的铁锰比，将所述锰的铁氰化物沉淀和铁的铁氰化物沉淀混合并分散于水中，持续加入磷酸溶液和硝酸溶液，在密封环境下进行水热反应；
S3：步骤S2所述水热反应结束后，固液分离，所得固体进行干燥，即得所述磷酸锰铁。
在本发明的一些实施方式中，步骤S1中，所述铁氰化物溶液为包含亚铁氰化钠、亚铁氰化钾、铁氰化钠或铁氰化钾中的至少一种的溶液。
在本发明的一些实施方式中，步骤S1中，所述铁盐溶液中的铁盐选自硫酸铁、硫酸亚铁、硝酸铁、硝酸亚铁、氯化铁或氯化亚铁中的至少一种。优选的，所述铁盐溶液为二价铁盐溶液。
在本发明的一些实施方式中，步骤S1中，所述锰盐溶液中的锰盐选自硫酸锰、硝酸锰或氯化锰中的至少一种。
在本发明的一些实施方式中，步骤S1中，所述铁氰化物溶液的浓度为0.01-1mol/L；所述铁盐溶液的浓度为0.01-1mol/L；所述锰盐溶液的浓度为0.01-1mol/L。
在本发明的一些实施方式中，步骤S1中，所述铁氰化物溶液加入的流速为25-50mL/h。
在本发明的一些实施方式中，步骤S2中，所述目标产物的铁锰比≥0.5。优选的，所述目标产物的铁锰比为(0.5-4)：1。
在本发明的一些实施方式中，步骤S2中，所述搅拌的转速为50-150r/min。
在本发明的一些实施方式中，步骤S2中，所述水热反应的温度为140-150℃。进一步地，所述水热反应的时间为12-18h。
在本发明的一些实施方式中，步骤S2中，所述磷酸溶液的浓度为0.5-1.0mol/L，所述硝酸溶液的浓度为0.5-1.0mol/L，控制磷酸与硝酸加入的摩尔量之比为1：(2.2-3.0)，控制水热反应的pH为1.8-2.0。
在本发明的一些实施方式中，步骤S3中，所述干燥为真空干燥，所述干燥的温度为120-150℃下，干燥的时间为2-4h。
本发明还提供所述的方法在制备磷酸锰铁锂或锂离子电池中的应用。
根据本发明的一种优选的实施方式，至少具有以下有益效果：
1、本发明首先利用铁氰化物分别与亚铁盐/铁盐和锰盐反应，生成对应的亚铁/铁氰化物盐沉淀(Mn2[Fe(CN)6]、Fe2[Fe(CN)6]、Mn3[Fe(CN)6]2、Fe3[Fe(CN)6]2等)，经简单洗涤后即可得到较为纯净的沉淀化合物；通过将对应的沉淀化合物混合进行铁锰配比后，与硝酸、磷酸进行水热反应，生成对应的磷酸锰铁、二氧化碳、氮气和水，整个水热反应无其它杂质离子的产生，得到磷酸锰铁具有较高的纯度。反应原理如下：
沉淀制备反应方程式如下：
[Fe(CN)6]4-+2Mn2+→Mn2[Fe(CN)6]↓；
[Fe(CN)6]4-+2Fe2+→Fe2[Fe(CN)6]↓；
2[Fe(CN)6]3-+3Mn2+→Mn3[Fe(CN)6]2↓；
2[Fe(CN)6]3-+3Fe2+→Fe3[Fe(CN)6]2↓；
水热反应方程式如下：
5Mn2[Fe(CN)6]+33NO3 -+15PO4 3-+78H+→10MnPO4↓+5FePO4↓+30CO2↑+31.5N2↑+39H2O；
5Fe2[Fe(CN)6]+33NO3 -+15PO4 3-+78H+→15FePO4↓+30CO2↑+31.5N2↑+39H2O；
5Mn3[Fe(CN)6]2+63NO3 -+25PO4 3-+138H+→15MnPO4↓+10FePO4↓+60CO2↑+61.5N2↑+69H2O；
5Fe3[Fe(CN)6]2+63NO3 -+25PO4 3-+138H+→25FePO4↓+60CO2↑+61.5N2↑+69H2O；
5Fe4[Fe(CN)6]3+93NO3 -+35PO4 3-+198H+→35FePO4↓+90CO2↑+91.5N2↑+99H2O；
Fe[Fe(CN)6]+6NO3 -+2PO4 3-+12H+→2FePO4↓+6CO2↑+6N2↑+6H2O。
2、本发明在制备磷酸锰铁时，一方面，铁与锰均以正三价态与磷酸根共沉淀，形成磷酸锰铁，避免了后续因二价阳离子沉淀导致磷源不足，而需另外补加磷源的问题，提高了磷锰铁的分布均匀性；另一方面，通过利用铁氰化盐抑制了三价铁离子、磷酸根的直接沉淀，采用硝酸与磷酸混合进行破氰反应，减缓了磷酸铁的沉淀速率，使铁锰达到共沉淀，提高了铁锰混合的均匀性，为提高磷酸锰铁锂正极材料的比容量及循环性能奠定了基础。
附图说明
下面结合附图和实施例对本发明做进一步的说明，其中：
图1为本发明实施例1制备的磷酸锰铁SEM图。
具体实施方式
以下将结合实施例对本发明的构思及产生的技术效果进行清楚、完整地描述，以充分地理解本发明的目的、特征和效果。显然，所描述的实施例只是本发明的一部分实施例，而不是全部实施例，基于本发明的实施例，本领域的技术人员在不付出创造性劳动的前提下所获得的其他实施例，均属于本发明保护的范围。
实施例1
本实施例制备了一种磷酸锰铁，具体过程为：
步骤1，配制浓度为0.5mol/L的亚铁氰化钠溶液；
步骤2，配制浓度为0.5mol/L的硫酸亚铁溶液；
步骤3，配制浓度为0.5mol/L的硫酸锰溶液；
步骤4，将步骤1配制的溶液按照35mL/h的流速分别加入到步骤2和步骤3配制的溶液中，至没有沉淀产生，得到对应的两种沉淀物；
步骤5，分别离心收集沉淀物，并采用去离子水分别对沉淀物进行洗涤；
步骤6，按照铁锰比为1:1将两种沉淀物混合后，加入到密闭反应釜中；
步骤7，向反应釜中加入纯水至漫过沉淀物，启动反应釜搅拌，控制搅拌转速为100r/min；
步骤8，将反应釜密封进行水热反应，控制反应温度为145℃，并持续向反应釜中加入浓度为1.0mol/L的磷酸溶液和浓度为1.0mol/L的硝酸溶液，控制磷酸与硝酸的加入量之比为1:2.2，控制釜内pH为1.8-2.0，反应时间15h；
步骤9，反应结束后，固液分离，将固体产物置于135℃下真空干燥3h，即得磷酸锰铁产品。
实施例2
本实施例制备了一种磷酸锰铁，具体过程为：
步骤1，配制浓度为1mol/L的铁氰化钾溶液；
步骤2，配制浓度为1mol/L的氯化亚铁溶液；
步骤3，配制浓度为1mol/L的氯化锰溶液；
步骤4，将步骤1配制的溶液按照25mL/h的流速分别加入到步骤2和步骤3配制的溶液中，至没有沉淀产生，得到对应的两种沉淀物；
步骤5，分别离心收集沉淀物，并采用去离子水分别对沉淀物进行洗涤；
步骤6，按照铁锰比为1:1将两种沉淀物混合后，加入到密闭反应釜中；
步骤7，向反应釜中加入纯水至漫过沉淀物，启动反应釜搅拌，控制搅拌转速为50r/min；
步骤8，将反应釜密封进行水热反应，控制反应温度为140℃，并持续向反应釜中加入浓度为0.5mol/L的磷酸溶液和浓度为0.5mol/L的硝酸溶液，控制磷酸与硝酸的加入量之比为1:2.52，控制釜内pH为1.8-2.0，反应时间18h；
步骤9，反应结束后，固液分离，将固体产物置于150℃下真空干燥2h，即得磷酸锰铁产品。
实施例3
本实施例制备了一种磷酸锰铁，具体过程为：
步骤1，配制浓度均为0.01mol/L的亚铁氰化钠溶液和铁氰化钠溶液；
步骤2，配制浓度为0.01mol/L的硫酸亚铁溶液；
步骤3，配制浓度为0.01mol/L的硫酸锰溶液。
步骤4，将步骤1配制亚铁氰化钠溶液按照50mL/h的流速加入到步骤2配制的溶液中，将步骤1配制铁氰化钠溶液按照50mL/h的流速加入到步骤3配制的溶液中，至没有沉淀产生，得到对应的两种沉淀物；
步骤5，分别离心收集沉淀物，并采用去离子水分别对沉淀物进行洗涤；
步骤6，按照铁锰比为1:1将两种沉淀物混合后，加入到密闭反应釜中；
步骤7，向反应釜中加入纯水至漫过沉淀物，启动反应釜搅拌，控制搅拌转速为150r/min；
步骤8，将反应釜密封进行水热反应，控制反应温度为150℃，并持续向反应釜中加入浓度为1.0mol/L的磷酸溶液和浓度为1.0mol/L的硝酸溶液，控制磷酸与硝酸的加入量之比为1:2.44，控制釜内pH为1.8-2.0，反应时间12h；
步骤9，反应结束后，固液分离，将固体产物置于120℃下真空干燥4h，即得磷酸锰铁产品。
对比例1
本对比例制备了一种磷酸锰铁，与实施例1的区别在于，不加入亚铁氰化钠制备沉淀物，直接进行水热反应，具体过程为：
步骤1，配制浓度为0.5mol/L的硫酸亚铁溶液；
步骤2，配制浓度为0.5mol/L的硫酸锰溶液；
步骤3，按照铁锰比为1:1将两种溶液混合后，加入到密闭反应釜中；
步骤4，启动反应釜搅拌，控制搅拌转速为100r/min；
步骤5，将反应釜密封进行水热反应，控制反应温度为145℃，并持续向反应釜中加入浓度为1.0mol/L的磷酸溶液和浓度为1.0mol/L的过氧化氢溶液，控制磷酸与过氧化氢的加入量之比为1:2.2，控制釜内pH为1.8-2.0，反应时间15h；
步骤6，反应结束后，固液分离，将固体产物置于135℃下真空干燥3h，即得磷酸锰铁产品。
对比例2
本实施例制备了一种磷酸锰铁，与实施例2的区别在于，不加入铁氰化钾制备沉淀物，直接进行水热反应，具体过程为：
一种水热制备磷酸锰铁的方法，包括如下步骤：
步骤1，配制浓度为1mol/L的氯化亚铁溶液；
步骤2，配制浓度为1mol/L的氯化锰溶液；
步骤3，按照铁锰比为1:1将两种溶液混合后，加入到密闭反应釜中；
步骤4，启动反应釜搅拌，控制搅拌转速为50r/min；
步骤5，将反应釜密封进行水热反应，控制反应温度为140℃，并持续向反应釜中加入浓度为0.5mol/L的磷酸溶液和浓度为0.5mol/L的过氧化氢溶液，控制磷酸与过氧化氢的加入量之比为1:2.52，控制釜内pH为1.8-2.0，反应时间18h；
步骤6，反应结束后，固液分离，将固体产物置于150℃下真空干燥2h，即得磷酸锰铁产品。
对比例3
本实施例制备了一种磷酸锰铁，与实施例3的区别在于，不加入亚铁氰化钠制备沉淀物，直接进行水热反应，具体过程为：
步骤1，配制浓度为0.01mol/L的硫酸亚铁溶液；
步骤2，配制浓度为0.01mol/L的硫酸锰溶液。
步骤3，按照铁锰比为1:1将两种溶液混合后，加入到密闭反应釜中；
步骤4，启动反应釜搅拌，控制搅拌转速为150r/min；
步骤5，将反应釜密封进行水热反应，控制反应温度为150℃，并持续向反应釜中加入浓度为1.0mol/L的磷酸溶液和浓度为1.0mol/L的过氧化氢溶液，控制磷酸与过氧化氢的加入量之比为1:2.44，控制釜内pH为1.8-2.0，反应时间12h；
步骤6，反应结束后，固液分离，将固体产物置于120℃下真空干燥4h，即得磷酸锰铁产品。
对实施例1-3和对比例1-3所得磷酸锰铁产品的主元素含量进行ICP检测，结果如表1所示。
表1
| 杂质S或Cl(ppm) | Fe/％ | Mn/％ | P/％ | Fe:Mn:P | 计算化学式 | |
| 实施例1 | 未检出 | 18.566 | 18.270 | 20.601 | 0.5:0.5:1 | Fe0.5Mn0.5PO4 |
| 实施例2 | 未检出 | 18.565 | 18.271 | 20.600 | 0.5:0.5:1 | Fe0.5Mn0.5PO4 |
| 实施例3 | 未检出 | 18.568 | 18.267 | 20.603 | 0.5:0.5:1 | Fe0.5Mn0.5PO4 |
| 对比例1 | 4378 | 37.084 | 0.0023 | 20.529 | 1:0:1 | FePO4 |
| 对比例2 | 5726 | 37.081 | 0.0021 | 20.528 | 1:0:1 | FePO4 |
| 对比例3 | 3438 | 37.082 | 0.0012 | 20.528 | 1:0:1 | FePO4 |
由表1的检测结果可知，对比例1-3几乎不会生成磷酸锰沉淀，且得到的产物中具有较高的杂质S/Cl含量。这是由于磷酸锰与磷酸铁的Ksp不同，沉淀速率不同，普通的水热反应难以形成锰铁共沉淀物，且水热反应的介质为硫酸盐或氯化盐溶液，使沉淀物易掺杂S或Cl。
试验例
按照摩尔比(Fe+Mn):Li:碳源＝1:1.1:0.4，将实施例1-3和对比例1-3所得产品分别与氢氧化锂、葡萄糖混合后，并加入总质量25％的去离子水，混合均匀后进行喷雾干燥；在惰性气体的保护下、750℃煅烧16h，自然冷却至室温，得到磷酸锰铁锂正极材料成品。
以实施例和对比例得到的磷酸锰铁锂正极材料，乙炔黑为导电剂，PVDF为粘结剂，按质量比8:1:1进行混合，并加入一定量的有机溶剂NMP，搅拌后涂覆于铝箔上制成正极片，负极采用金属锂片；隔膜为Celgard2400聚丙烯多孔膜；电解液中溶剂为EC、DMC和EMC按质量比1:1:1组成的溶液，溶质为LiPF6，LiPF6的浓度为1.0mol/L；在手套箱内组装2023型扣式电池。对电池进行充放电循环性能测试，在截止电压2.2～4.3V范围内，测试0.2C、1C放电比容量，测试电化学性能结果表2所示。
表2
由表2可见实施例的电化学性能明显优于对比例，表明与磷酸铁相比，本发明制备的磷酸锰铁烧结得到的磷酸锰铁锂具有更高的比容量和循环性能。
上面结合附图对本发明实施例作了详细说明，但是本发明不限于上述实施例，在所属技术领域普通技术人员所具备的知识范围内，还可以在不脱离本发明宗旨的前提下作出各种变化。此外，在不冲突的情况下，本发明的实施例及实施例中的特征可以相互组合。
Claims (8)
1.一种水热制备磷酸锰铁的方法，其特征在于，包括以下步骤：
S1：将铁氰化物溶液分别加入到铁盐溶液和锰盐溶液中进行反应，得到锰的铁氰化物沉淀和铁的铁氰化物沉淀；所述铁盐溶液中的铁盐选自二价铁盐或三价铁盐中的至少一种；所述铁氰化物溶液为包含亚铁氰化钠、亚铁氰化钾、铁氰化钠或铁氰化钾中的至少一种的溶液；
S2：按照目标产物的铁锰比，将所述锰的铁氰化物沉淀和铁的铁氰化物沉淀混合并分散于水中，持续加入磷酸溶液和硝酸溶液，在密封环境下进行水热反应；所述水热反应的温度为140-150℃；
S3：步骤S2所述水热反应结束后，固液分离，所得固体进行干燥，即得所述磷酸锰铁。
2.根据权利要求1所述的方法，其特征在于，步骤S1中，所述铁盐溶液中的铁盐选自硫酸铁、硫酸亚铁、硝酸铁、硝酸亚铁、氯化铁或氯化亚铁中的至少一种。
3.根据权利要求1所述的方法，其特征在于，步骤S1中，所述锰盐溶液中的锰盐选自硫酸锰、硝酸锰或氯化锰中的至少一种。
4.根据权利要求1所述的方法，其特征在于，步骤S1中，所述铁氰化物溶液的浓度为0.01-1mol/L；所述铁盐溶液的浓度为0.01-1mol/L；所述锰盐溶液的浓度为0.01-1mol/L。
5.根据权利要求1所述的方法，其特征在于，步骤S1中，所述铁氰化物溶液加入的流速为25-50mL/h。
6.根据权利要求1所述的方法，其特征在于，步骤S2中，所述目标产物的铁锰比≥0.5。
7.根据权利要求1所述的方法，其特征在于，步骤S2中，所述磷酸溶液的浓度为0.5-1.0mol/L，所述硝酸溶液的浓度为0.5-1.0mol/L，控制磷酸与硝酸加入的摩尔量之比为1：（2.2-3.0），控制水热反应的pH为1.8-2.0。
8.如权利要求1-7任一项所述的方法在制备磷酸锰铁锂或锂离子电池中的应用。