CN115286736A - 一种高温低剥离力的聚丙烯酸酯及其制备方法、应用 - Google Patents
一种高温低剥离力的聚丙烯酸酯及其制备方法、应用 Download PDFInfo
- Publication number
- CN115286736A CN115286736A CN202210830309.8A CN202210830309A CN115286736A CN 115286736 A CN115286736 A CN 115286736A CN 202210830309 A CN202210830309 A CN 202210830309A CN 115286736 A CN115286736 A CN 115286736A
- Authority
- CN
- China
- Prior art keywords
- polyacrylate
- parts
- force
- acrylate
- low
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高温低剥离力的聚丙烯酸酯，其原料按重量份包括：丙烯酸酯单体65‑70份、功能性单体2‑4份、含硅的丙烯酸酯单体27‑32份、引发剂0.8‑1.2份、链终止剂2‑4份。本发明还公开了上述高温低剥离力的聚丙烯酸酯的制备方法。本发明还公开了上述高温低剥离力的聚丙烯酸酯在压敏胶中的应用。本发明还公开了一种高温低剥离力的聚丙烯酸酯压敏胶。本发明经过高温处理后其剥离力稳定，容易剥离，且不易产生残胶。
Description
技术领域
本发明涉及压敏胶技术领域，尤其涉及一种高温低剥离力的聚丙烯酸酯及其制备方法、应用。
背景技术
压敏胶是一种同时具备着液体的黏性性质和固体的弹性性质的粘弹性体；这种粘弹性体同时具备着能够承受粘接的接触过程和破坏过程两方面的影响因素和性质。
工业上使用的压敏胶主要有4大类：溶剂型压敏胶、乳液型压敏胶、热熔型压敏胶和射线固化型压敏胶。压敏胶按其聚合物分成橡胶类压敏胶、聚丙烯酸酯类压敏胶、聚乙烯基醚树脂类、聚氨树脂类、聚异丁烯类等乳液型压敏胶。
丙烯酸酯类压敏胶粘剂是仅次于橡胶类，用得最多的压敏胶粘剂，丙烯酸酯类单体的主要特征如下：几乎不需要加入防老剂便具有优良的耐候性和耐热性；透明性好；良好的耐油性。
但是现有丙烯酸酯类压敏胶当其遇到高温后，丙烯酸酯类压敏胶会发生软化、黏性升高，其和被贴合物的浸润性变好，导致再剥离时，剥离力大幅升高，使其再剥离力过大。而对于一些使用情况(如光学屏幕保护膜等)，并不希望经高温处理后压敏胶的剥离力上升过大，从而引起再剥离残胶的产生。
发明内容
基于背景技术存在的技术问题，本发明提出了一种高温低剥离力的聚丙烯酸酯及其制备方法、应用，本发明经过高温处理后其剥离力上升幅度不高，容易剥离，不易产生残胶；高温时剥离力约为室温时剥离力的3倍。
本发明提出了一种高温低剥离力的聚丙烯酸酯，其原料按重量份包括：丙烯酸酯单体65-70份、功能性单体2-4份、含硅的丙烯酸酯单体27-32份、引发剂0.8-1.2份、链终止剂2-4份。
优选地，含硅的丙烯酸酯单体为3-(三甲氧基甲硅烷基)丙基丙烯酸酯。
优选地，聚丙烯酸酯的玻璃化温度Tg≤-70℃。
优选地，丙烯酸酯单体为丙烯酸异辛酯、丙烯酸异壬酯、丙烯酸癸酯、丙烯酸庚酯中的至少一种。
优选地，功能性单体为丙烯酸羟乙酯。
优选地，链终止剂为异丙醇。
上述引发剂为双二四过氧化物等。
本发明还提出了上述高温低剥离力的聚丙烯酸酯的制备方法，包括如下步骤：将丙烯酸酯单体、功能性单体、含硅的丙烯酸酯单体、第一溶剂、引发剂混匀，进行聚合反应，然后加入链终止剂继续反应，去除第一溶剂，得到高温低剥离力的聚丙烯酸酯。
优选地，聚合反应的温度为50-70℃，聚合反应的时间为10-15h。
优选地，继续反应的时间为8-12h。
优选地，第一溶剂为乙酸乙酯、甲苯、二甲苯、乙酸丁酯中的至少一种。
本发明还提出上述高温低剥离力的聚丙烯酸酯在压敏胶中的应用。
本发明还提出了一种高温低剥离力的聚丙烯酸酯压敏胶，其原料按重量份包括：原胶100份、固化剂1.5-2.5份、第二溶剂20-23份，其中，原胶为上述高温低剥离力的聚丙烯酸酯。
优选地，固化剂为异氰酸酯类固化剂。
优选地，第二溶剂为甲苯、二甲苯、乙酸乙酯、乙酸丁酯中的至少一种。
有益效果：
本发明选用合适种类的丙烯酸酯单体、功能性单体、含硅的丙烯酸酯单体，并选用合适的比例相互配合，使得本发明具有较低的玻璃化转变温度Tg，经过高温处理后，本发明所述压敏胶的黏性增加幅度不大，高温处理后其剥离力上升幅度不高，容易剥离，不易产生残胶；
本发明所述压敏胶室温时对钢板的剥离力小于100g/25mm；200℃保温2h，对钢板的剥离力小于200g/25mm；高温时剥离力约为室温时剥离力的3倍。
具体实施方式
下面，通过具体实施例对本发明的技术方案进行详细说明，但是应该明确提出这些实施例用于举例说明，但是不解释为限制本发明的范围。
实施例1
一种高温低剥离力的聚丙烯酸酯，其原料按重量份包括：丙烯酸异辛酯65g、丙烯酸羟乙酯3g、3-(三甲氧基甲硅烷基)丙基丙烯酸酯32g、双二四过氧化物1g、异丙醇3g。
上述高温低剥离力的聚丙烯酸酯的制备方法，包括如下步骤：按上述配方称取丙烯酸异辛酯、丙烯酸羟乙酯、3-(三甲氧基甲硅烷基)丙基丙烯酸酯，加入150g乙酸乙酯中混匀，然后加入双二四过氧化物混匀，于60℃聚合反应12h，然后加入异丙醇继续反应10h，去除乙酸乙酯，得到高温低剥离力的聚丙烯酸酯，其Tg为-85℃。
一种高温低剥离力的聚丙烯酸酯压敏胶，其原料按重量份包括：原胶100g、异氰酸酯类固化剂L452g、甲苯21g，其中，原胶为上述高温低剥离力的聚丙烯酸酯。
实施例2
一种高温低剥离力的聚丙烯酸酯，其原料按重量份包括：丙烯酸异辛酯70g、丙烯酸羟乙酯3g、3-(三甲氧基甲硅烷基)丙基丙烯酸酯27g、双二四过氧化物1g、异丙醇3g、乙酸乙酯150g。
上述高温低剥离力的聚丙烯酸酯的制备方法同实施例1，高温低剥离力的聚丙烯酸酯的Tg为-80℃。
一种高温低剥离力的聚丙烯酸酯压敏胶，其原料按重量份包括：原胶100g、异氰酸酯类固化剂L452g、甲苯22g，其中，原胶为上述高温低剥离力的聚丙烯酸酯。
实施例3
一种高温低剥离力的聚丙烯酸酯，其原料按重量份包括：丙烯酸庚酯69g、丙烯酸羟乙酯4g、3-(三甲氧基甲硅烷基)丙基丙烯酸酯27g、双二四过氧化物0.8g、异丙醇4g。
上述高温低剥离力的聚丙烯酸酯的制备方法，包括如下步骤：按上述配方称取丙烯酸庚酯、丙烯酸羟乙酯、3-(三甲氧基甲硅烷基)丙基丙烯酸酯，加入200g甲苯中混匀，然后加入双二四过氧化物混匀，于50℃聚合反应15h，然后加入异丙醇继续反应12h，去除甲苯，得到高温低剥离力的聚丙烯酸酯，其Tg为-82℃。
一种高温低剥离力的聚丙烯酸酯压敏胶，其原料按重量份包括：原胶100g、异氰酸酯类固化剂L452.5g、甲苯20g，其中，原胶为上述高温低剥离力的聚丙烯酸酯。
实施例4
一种高温低剥离力的聚丙烯酸酯，其原料按重量份包括：丙烯酸癸酯66g、丙烯酸羟乙酯2g、3-(三甲氧基甲硅烷基)丙基丙烯酸酯32g、双二四过氧化物1.2g、异丙醇2g。
上述高温低剥离力的聚丙烯酸酯的制备方法，包括如下步骤：按上述配方称取丙烯酸癸酯、丙烯酸羟乙酯、3-(三甲氧基甲硅烷基)丙基丙烯酸酯，加入100g乙酸丁酯混匀，然后加入双二四过氧化物混匀，于70℃聚合反应10h，然后加入异丙醇继续反应8h，去除乙酸丁酯，得到高温低剥离力的聚丙烯酸酯，其Tg为-85℃。
一种高温低剥离力的聚丙烯酸酯压敏胶，其原料按重量份包括：原胶100g、异氰酸酯类固化剂L451.5g、乙酸乙酯23g，其中，原胶为上述高温低剥离力的聚丙烯酸酯。
对比例1
一种高温低剥离力的聚丙烯酸酯，其原料按重量份包括：丙烯酸异辛酯85g、丙烯酸羟乙酯3g、3-(三甲氧基甲硅烷基)丙基丙烯酸酯12g、双二四过氧化物1g、异丙醇3g。
上述高温低剥离力的聚丙烯酸酯的制备方法同实施例1。
一种高温低剥离力的聚丙烯酸酯压敏胶，其原料按重量份包括：原胶100g、异氰酸酯类固化剂L452g、甲苯20g，其中，原胶为上述高温低剥离力的聚丙烯酸酯。
对比例2
一种高温低剥离力的聚丙烯酸酯，其原料按重量份包括：丙烯酸异辛酯80g、丙烯酸羟乙酯3g、3-(三甲氧基甲硅烷基)丙基丙烯酸酯17g、双二四过氧化物1g、异丙醇3g、乙酸乙酯150g。
上述高温低剥离力的聚丙烯酸酯的制备方法同实施例1。
一种高温低剥离力的聚丙烯酸酯压敏胶，其原料按重量份包括：原胶100g、异氰酸酯类固化剂L452g、甲苯23g，其中，原胶为上述高温低剥离力的聚丙烯酸酯。
对比例3
一种高温低剥离力的聚丙烯酸酯，其原料按重量份包括：丙烯酸异辛酯100g、丙烯酸羟乙酯3g、双二四过氧化物1g、异丙醇3g、乙酸乙酯150g。
上述高温低剥离力的聚丙烯酸酯的制备方法同实施例1。
一种高温低剥离力的聚丙烯酸酯压敏胶，其原料按重量份包括：原胶100g、异氰酸酯类固化剂L452g、甲苯21g，其中，原胶为上述高温低剥离力的聚丙烯酸酯。
取实施例1-4和对比例1-3，按照GBT2792-2014测试压敏胶180°剥离力。结果如表1所示。
表1检测结果
由表1可以看出：选用合适的原料和配比，可以使得本发明在常温时的剥离力＜100g/25mm，经高温处理后的剥离力＜200g/25mm；并且本发明高温时剥离力约为室温时剥离力的3倍，本发明高温时剥离力的上升幅度较低；本发明可抑制高温时压敏胶剥离力的上升幅度，使其经高温处理后，仍保持较低的剥离力。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。
Claims (10)
1.一种高温低剥离力的聚丙烯酸酯，其特征在于，其原料按重量份包括：丙烯酸酯单体65-70份、功能性单体2-4份、含硅的丙烯酸酯单体27-32份、引发剂0.8-1.2份、链终止剂2-4份。
2.根据权利要求1所述高温低剥离力的聚丙烯酸酯，其特征在于，含硅的丙烯酸酯单体为3-(三甲氧基甲硅烷基)丙基丙烯酸酯。
3.根据权利要求1或2所述高温低剥离力的聚丙烯酸酯，其特征在于，聚丙烯酸酯的玻璃化温度Tg≤-70℃。
4.根据权利要求1-3任一项所述高温低剥离力的聚丙烯酸酯，其特征在于，丙烯酸酯单体为丙烯酸异辛酯、丙烯酸异壬酯、丙烯酸癸酯、丙烯酸庚酯中的至少一种；优选地，功能性单体为丙烯酸羟乙酯。
5.根据权利要求1-4任一项所述高温低剥离力的聚丙烯酸酯，其特征在于，链终止剂为异丙醇。
6.一种如权利要求1-5所述高温低剥离力的聚丙烯酸酯的制备方法，其特征在于，包括如下步骤：将丙烯酸酯单体、功能性单体、含硅的丙烯酸酯单体、第一溶剂、引发剂混匀，进行聚合反应，然后加入链终止剂继续反应，去除第一溶剂，得到高温低剥离力的聚丙烯酸酯。
7.根据权利要求6所述高温低剥离力的聚丙烯酸酯的制备方法，其特征在于，聚合反应的温度为50-70℃，聚合反应的时间为10-15h；优选地，继续反应的时间为8-12h；优选地，第一溶剂为乙酸乙酯、甲苯、二甲苯、乙酸丁酯中的至少一种。
8.一种如权利要求1-5任一项所述高温低剥离力的聚丙烯酸酯在压敏胶中的应用。
9.一种高温低剥离力的丙烯酸酯压敏胶，其特征在于，其原料按重量份包括：原胶100份、固化剂1.5-2.5份、第二溶剂20-23份，其中，原胶为权利要求1-5任一项所述高温低剥离力的聚丙烯酸酯。
10.根据权利要求9所述高温低剥离力的丙烯酸酯压敏胶，其特征在于，固化剂为异氰酸酯类固化剂；优选地，第二溶剂为甲苯、二甲苯、乙酸乙酯、乙酸丁酯中的至少一种。