CN115124090A - 一种低硫高比表面积三元正极前驱体材料的制备方法 - Google Patents
一种低硫高比表面积三元正极前驱体材料的制备方法 Download PDFInfo
- Publication number
- CN115124090A CN115124090A CN202210829321.7A CN202210829321A CN115124090A CN 115124090 A CN115124090 A CN 115124090A CN 202210829321 A CN202210829321 A CN 202210829321A CN 115124090 A CN115124090 A CN 115124090A
- Authority
- CN
- China
- Prior art keywords
- precursor material
- materials
- positive electrode
- low
- alkali
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种低硫高比表面积三元正极前驱体材料的制备方法，属于锂离子电池材料领域。本发明采用带喷淋装置的连续式过滤机对反应物料进行提浓，能够在反应阶段均匀地去除硫杂质，且对反应环境和生产效率没有影响，也不会引入新的杂质；通过负压抽滤的方式去除母液，可使物料均匀受控地被氧化，均匀地提高了所述三元正极前驱体材料的比表面积，使烧结时锂离子更容易进入三元正极前驱体材料的颗粒内部，从而发挥出更高的容量；本发明喷淋中所用碱液可循环使用，减少了洗涤用水、用碱和废水排放。
Description
技术领域
本发明涉及锂离子电池材料领域，具体涉及一种低硫高比表面积三元正极前驱体材料的制备方法。
背景技术
随着近几年社会对能源问题的日益关注，各类高科技电子产品迅猛发展，储能材料的开发也进入了高速发展的时期。目前在电动及储能领域应用最广泛的是锂离子电池，而锂离子电池中的正极材料市场占有率最大的是镍钴锰三元材料。
目前市面上的镍钴锰三元材料多采用共沉淀法生产，即将金属硫酸盐、沉淀剂、络合剂并流加入反应釜中并控制一定的工艺条件进行结晶沉淀，然后经过洗涤、烘干等工序得到氢氧化物固体粉末。该制备方法采用硫酸盐作为原料，会使反应体系中的硫酸根浓度过高，在沉淀过程中硫酸根会吸附在沉淀物颗粒表面，并随着颗粒的长大而富集在三元正极前驱体材料的内部和表面，影响三元材料的电性能。
针对此问题，目前常规的处理方法是在洗涤工序段进行碱洗或碱浸，但这样仅能降低产品表面的硫。CN112582605A公开了在沉淀过程中，当颗粒生长到一定粒径时停止进料，将沉淀物进行洗涤，然后返回反应釜继续生长，这样虽然能阶段性地去除不同壳层的硫杂质，但停止进料会降低生产效率，且只能去除特定半径球壳的杂质，造成硫杂质在球体中不均匀富集。CN110817975A和CN103342395A公开了通过置换反应过程中的母液来降低反应环境中的硫酸根浓度，从而达到降低硫杂质的目的；但这种方式需要维持反应环境的稳定，且需要精准补充硫酸盐原料、沉淀剂和络合剂，还要精准控制补充液的温度等参数，控制繁琐且精细化要求高，操作难度大，同时补液工艺会增加单位产品的水耗，提高了生产成本。CN109279661A公开了在沉淀过程中加入添加剂和表面活性剂的方法来降低沉淀物表面能，以此降低产物颗粒对硫杂质的吸附，但添加剂和表面活性剂也会残留在产物的内部和表面，导致新杂质的引入。
因此，开发一种可从源头上降低硫杂质的引入，且不引入其他新杂质、不降低生产效率的镍钴锰三元材料的制备方法是目前研究的热点。
发明内容
本发明的目的在于克服上述现有技术的不足而提供一种降低硫杂质引入的三元正极前驱体材料的制备方法，该方法制备得到的三元正极前驱体材料不仅具有较低的硫含量，还具有较高的比表面积。
为实现上述目的，本发明采取的技术方案为：一种低硫高比表面积三元正极前驱体材料的制备方法，包含以下步骤：
S1、将镍、钴、锰混合金属的可溶性盐溶液、碱液和络合剂按照所需比例混合，并在反应釜中进行搅拌；
S2、采用带喷淋装置的连续式过滤机对反应釜中的物料进行提浓，先将物料中的母液进行负压抽滤形成滤饼，再将热碱液通过喷淋装置喷洒至滤饼，并使滤饼与氧气接触，最后刮下滤饼，再次将物料返回反应釜继续生长；
S3、待物料生长至所需粒径后停止进料，对物料进行陈化、水洗、干燥、筛分和除磁，即得所述低硫高比表面积三元正极前驱体材料。
本发明在连续式过滤机上安装喷淋装置，并采用带喷淋装置的连续式过滤机对反应釜中的物料进行提浓，连续式过滤机的前段先通过负压抽滤的方式去除母液，可以使物料均匀受控的被氧化，增大氧气与物料的接触面积，使氧化效率提高，避免反应釜内通氧化剂引入杂质和造成氧化不可控，均匀提高了所述三元正极前驱体材料的比表面积，使所述三元材料在烧结时锂离子更容易进入颗粒内部，从而发挥出更高容量；后段将热碱通过与滤带等宽的喷淋装置均匀地喷洒在滤饼上，可去除物料颗粒表面和及一定深度的SO4 2-，同时负压抽滤可收集滤液循环使用，并控制滤饼上方的气氛使一定量的氧气与滤饼层均匀接触，通过控制氧化量提高沉淀物的比表面。
本发明在物料生长的过程中进行喷淋，使物料一边生长一边碱洗，克服了传统热碱洗涤只能去除表面和最外层1-2μm的硫杂质的缺陷，在源头上降低了硫杂质的引入。
优选地，所述步骤S1中，可溶性盐溶液为硫酸盐溶液。
更优选地，所述步骤S1中，可溶性盐溶液中镍、钴、锰混合金属的离子浓度为1-3mol/L。
优选地，所述步骤S1中，碱液为氢氧化钠溶液或氢氧化钾溶液。
更优选地，所述步骤S1中，碱液的浓度为30％-35％，碱液浓度过低，溶液中水分增多，会使喷淋效率降低。
优选地，所述步骤S1中，络合剂为氨水、水合肼或乙二胺四乙酸(EDTA)。
优选地，所述步骤S1中，镍、钴、锰混合金属的可溶性盐溶液和碱液的体积比为(66-200):(34-40)。
需要说明的是，本发明中镍、钴、锰混合金属的可溶性盐溶液和碱液的体积比由镍、钴、锰混合金属的离子浓度和碱液的浓度决定，且镍、钴、锰混合金属离子与碱液中氢氧根离子的摩尔比为2:1。
优选地，所述步骤S1中，镍、钴、锰混合金属的可溶性盐溶液和络合剂的体积比为100:5-10。
需要说明的是，本发明中镍、钴、锰混合金属离子与络合剂中络合离子的摩尔比为0.01：0.5。
优选地，所述步骤S1中，反应釜的温度为50-70℃。
优选地，所述步骤S1中，搅拌速度为200-500rpm。
优选地，所述步骤S2中，滤饼厚度＜10cm，滤饼厚度过大会影响热碱喷淋的效率。
优选地，所述步骤S2中，提浓时物料的进料速度为8-12m/h。
优选地，所述步骤S2中，氧气浓度为15％-25％。
优选地，所述步骤S3中，物料生长粒径为10-15μm。
需要说明的是，物料生长的粒径根据实验需要确定，本发明为10-15μm。
优选地，所述步骤S3中，热碱液的温度为65-85℃，浓度为1％-5％，喷淋速度为0.5-3m2/h。
本发明的有益效果在于：本发明提供了一种低硫高比表面积三元正极前驱体材料的制备方法，采用带喷淋装置的连续式过滤机对反应物料进行提浓，能够在反应阶段均匀地去除硫杂质，且对反应体系环境和生产效率几乎没有影响，也不会引入新的杂质；通过负压抽滤的方式去除母液，可以使物料均匀受控地被氧化，均匀地提高了所述三元正极前驱体材料的比表面积，使所述三元材料在烧结时锂离子更容易进入颗粒内部，从而发挥出更高的容量；本发明喷淋中所用碱液可循环使用，且三元正极前驱体材料后续洗涤也不需要再次用碱洗涤，减少了洗涤用水、用碱和废水排放。
附图说明
图1为本发明所述带喷淋装置的连续式过滤机各部分功能示意图；1、滤布传动轴，2、母液滤盘，3、气氛补充，4、热碱喷，5、氧分压仪，6、碱液滤，7、外罩，8、碱液回收，9、母液回收。
图2为实施例1中低硫高比表面积三元正极前驱体材料的SEM图。
具体实施方式
为更好地说明本发明的目的、技术方案和优点，下面将结合具体实施例对本发明作进一步说明。
实施例1
本发明所述一种低硫高比表面积三元正极前驱体材料的制备方法的一种实施例，本实施例所述低硫高比表面积三元正极前驱体材料的制备方法为：
S1、将2mol/L的镍、钴、锰混合金属的硫酸盐溶液、32％的氢氧化钠、20％的氨水以100:37:8体积比并流加入反应釜中，在60℃的温度下以300rpm的速度进行搅拌；
S2、将反应釜溢流出的物料通过泵输送到图1所示的过滤机中，先将物料中的母液进行负压抽滤，调节挡板控制滤饼的厚度为7cm，进料速度为10m/h，滤饼上方的氧气浓度18％，热碱温度为80℃，热碱浓度为2％，热碱喷淋速度为1m3/h，物料输送至过滤机末端由刮刀刮下，经过对辊破碎后再返回反应釜液面下方；
S3、待反应釜物料生长至15μm后停止进料，对物料进行离心机水洗、盘干机烘干，即得到所述低硫高比表面积三元正极前驱体材料。
实施例2
本实施例与实施例1的区别仅在于：步骤S1中，镍、钴、锰混合金属的硫酸盐溶液、氢氧化钠、氨水的体积比为100:37:6，步骤S2中，滤饼上方氧气浓度20％，步骤S3中，待反应釜物料生长至10μm后停止进料。
实施例3
本实施例与实施例1的区别仅在于：步骤S1中，镍、钴、锰混合金属的硫酸盐溶液的摩尔浓度为1mol/L。
实施例4
本实施例与实施例1的区别仅在于：步骤S1中，镍、钴、锰混合金属的硫酸盐溶液的摩尔浓度为3mol/L。
实施例5
本实施例与实施例1的区别仅在于：步骤S1中，镍、钴、锰混合金属的硫酸盐溶液和氨水的体积比为100:5。
实施例6
本实施例与实施例1的区别仅在于：步骤S1中，镍、钴、锰混合金属的硫酸盐溶液和氨水的体积比为10:1。
对比例1
本对比例与实施例1的区别仅在于：步骤S2中，未使用热碱喷淋。
对比例2
本对比例与实施例1的区别仅在于：步骤S2中，未使用热碱喷淋，且在步骤S3离心机洗涤阶段增加热碱洗涤。
对比例3
本对比例与实施例1的区别仅在于：步骤S2中，未通入空气，而是采用氮气与滤饼接触。
对比例4
本对比例与实施例1的区别在于：所述步骤S2中，反应釜物料溢流到通用的微孔浓缩机进行提浓，且在步骤S3离心机洗涤阶段增加热碱洗涤。
效果例
将上述实施例1-6、对比例1-4的三元正极前驱体材料的硫含量进行测定，并采用BET测试法对比表面积进行测试，结果如下表1所示。
表1
| 编号 | S含量(wt％) | BET(m<sup>2</sup>/g) |
| 实施例1 | 0.035 | 16.7 |
| 实施例2 | 0.030 | 18.5 |
| 实施例3 | 0.032 | 17.2 |
| 实施例4 | 0.047 | 16.3 |
| 实施例5 | 0.038 | 17.6 |
| 实施例6 | 0.032 | 15.9 |
| 对比例1 | 0.280 | 14.3 |
| 对比例2 | 0.195 | 14.8 |
| 对比例3 | 0.055 | 10.2 |
| 对比例4 | 0.205 | 9.7 |
结果如表1所示，实施例1-6中在物料生长过程中采用喷淋热碱液的方式去除硫杂质，除硫效果显著，硫含量均较低，且可以从源头去除硫杂质，且在滤饼上方控制氧气含量，对物料进行氧化，可以使晶须明显细化，使所述三元正极前驱体材料形貌均匀，显著提高了三元正极前驱体材料的比表面积；而对比例1由于未采用热碱喷淋的方式，硫含量较高，对比例2虽采用热碱洗涤，但是是在步骤S3洗料阶段进行常规碱洗，只能去除约30％的硫杂质，硫含量高达0.195％；对比例3由于未对物料进行氧化，使最终三元正极前驱体材料的比表面积较低；对比例4由于未采用负压抽滤和热碱喷淋，且在步骤S3洗料阶段进行常规碱洗，最终三元正极前驱体材料的硫含量较高，比表面积也较低。
综上，本发明所述三元正极前驱体材料的制备方法可以在不影响生产效率的前提下制备出低硫高比表面的高品质三元正极前驱体材料，且降低了制备过程中的水耗、碱耗和废水排放，具有明显的成本优势。
最后应当说明的是，以上实施例仅用以说明本发明的技术方案而非对本发明保护范围的限制，尽管参照较佳实施例对本发明作了详细说明，本领域的普通技术人员应当理解，可以对本发明的技术方案进行修改或者等同替换，而不脱离本发明技术方案的实质和范围。
Claims (10)
1.一种低硫高比表面积三元正极前驱体材料的制备方法，其特征在于，包含以下步骤：
S1、将镍、钴、锰混合金属的可溶性盐溶液、碱液和络合剂按照所需比例混合，并在反应釜中进行搅拌；
S2、采用带喷淋装置的连续式过滤机对反应釜中的物料进行提浓，先将物料中的母液进行负压抽滤形成滤饼，再将热碱液通过喷淋装置喷洒至滤饼，并使滤饼与氧气接触，最后刮下滤饼，再次将物料返回反应釜继续生长；
S3、待物料生长至所需粒径后停止进料，对物料进行陈化、水洗、干燥、筛分和除磁，即得所述低硫高比表面积三元正极前驱体材料。
2.如权利要求1所述低硫高比表面积三元正极前驱体材料的制备方法，其特征在于，所述步骤S1中，可溶性盐溶液为硫酸盐溶液。
3.如权利要求1所述低硫高比表面积三元正极前驱体材料的制备方法，其特征在于，所述步骤S1中，可溶性盐溶液中镍、钴、锰混合金属的离子浓度为1-3mol/L。
4.如权利要求1所述低硫高比表面积三元正极前驱体材料的制备方法，其特征在于，所述步骤S1中，碱液为氢氧化钠溶液或氢氧化钾溶液。
5.如权利要求1所述低硫高比表面积三元正极前驱体材料的制备方法，其特征在于，所述步骤S1中，碱液的浓度为30％-35％。
6.如权利要求1所述低硫高比表面积三元正极前驱体材料的制备方法，其特征在于，所述步骤S1中，镍、钴、锰混合金属的可溶性盐溶液和碱液的体积比为(66-200):(34-40)。
7.如权利要求1所述低硫高比表面积三元正极前驱体材料的制备方法，其特征在于，所述步骤S1中，镍、钴、锰混合金属的可溶性盐溶液和络合剂的体积比为100:5-10。
8.如权利要求1所述低硫高比表面积三元正极前驱体材料的制备方法，其特征在于，所述步骤S1中，反应釜的温度为50-70℃，搅拌速度为200-500rpm。
9.如权利要求1所述低硫高比表面积三元正极前驱体材料的制备方法，其特征在于，所述步骤S2中，滤饼厚度＜10cm。
10.如权利要求1所述低硫高比表面积三元正极前驱体材料的制备方法，其特征在于，所述步骤S3中，热碱液的温度为65-85℃，浓度为1％-5％，喷淋速度为0.5-3m2/h。