CN115055178A - 一种低碳烷烃铬系脱氢催化剂及其制备方法和应用 - Google Patents
一种低碳烷烃铬系脱氢催化剂及其制备方法和应用 Download PDFInfo
- Publication number
- CN115055178A CN115055178A CN202210806633.6A CN202210806633A CN115055178A CN 115055178 A CN115055178 A CN 115055178A CN 202210806633 A CN202210806633 A CN 202210806633A CN 115055178 A CN115055178 A CN 115055178A
- Authority
- CN
- China
- Prior art keywords
- chromium
- catalyst
- auxiliary agent
- dehydrogenation catalyst
- alkaline earth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种低碳烷烃铬系脱氢催化剂及其制备方法和应用,属于石油化工技术领域。该脱氢催化剂具有尖晶石结构,包括以干基总质量为基准计的以下质量分数的组分:氧化铬0.1~35%,第一助剂0.1~5%,第二助剂0.1~10%,第三助剂0.1~5%,其余为流化床载体。这种脱氢催化剂,通过调整载体表面的电性对催化剂中的活性中心的存在状态进行了控制,使催化剂的具有更高的脱氢活性、丙烯选择性;同时增强了催化剂整体的稳定性、强度以及磨耗,缓解了催化剂在使用过程中损耗问题。
Description
技术领域
本发明属于石油化工技术领域,具体涉及一种低碳烷烃铬系脱氢催化剂及其制备方法和应用。
背景技术
随着聚丙烯、聚丙烯腈、环氧丙烷、丙烯酸等衍生物需求的迅速增长,对丙烯的需求也逐年俱增,当前全球市场对丙烯需求的增长速度已超过了产能的增速,市场供求日趋紧张。近年来,我国丙烯需求量同样增长快速。在催化裂化、石脑油蒸汽裂解等工艺过程中会副产大量低碳烷烃,将这些烷烃经济地转化成丙烯,将有效改善市场对丙烯的需求。且相对于甲醇制烯烃工艺、煤制烯烃工艺,烷烃脱氢制烯烃工艺具有原料丰富、成本低、反应过程不需要引入水,废水量低等优点。低碳烷烃脱氢工艺可分为氧化脱氢和直接脱氢,氧化脱氢反应过程放热量高,操作过程危险,目标产物选择性差,转化率不占优势。因此烷烃直接脱氢是制烯烃的最有效方法。
目前所开发的烷烃直接脱氢工艺包括UOP公司的Oleflex工艺、Air Product&Chemical公司的Catofin工艺、Phillips公司的Star工艺、Snamprogetti&Yarsintz公司的FBD工艺、以及Linde公司的Linde工艺等。根据操作压力、温度、可连续性、生产装置的稳定操作和降低生产成本的综合比较,流化床烷烃脱氢工艺具有广泛的发展前景。流化床反应器相对于固定床反应器和移动床反应器,具有床层传热效率高、能够稳定地控制床层温度均匀、可以连续反应与再生、可以实现在较高温度下长周期稳定操作等优点。意大利Snamprogetti和俄罗斯Yarsintz公司的FBD工艺采用流化床反应器,配备反应-再生系统,目前已应用于俄罗斯1套13万吨/年异丁烯工业装置,还应用于5套异丁烷和丙烷脱氢装置。而国内同样重视流化床烷烃脱氢工艺的发展,由中国石油大学(华东)重质油国家重点实验室自主研发、中国石油工程建设公司华东设计分公司设计的新型丙烷/丁烷脱氢(ADHO)技术,已于2016年在山东恒源石油化工完成工业化试验证明,填补了国内该技术领域的空白。
在丙烷直接脱氢的反应中,副产物主要为C1和C2的轻质烃,这些轻质烃的产生源自裂解。现阶段,FBD工艺大多采用粉状Cr2O3催化剂或微球Cr2O3/Al2O3催化剂,铬系催化剂的选择性和稳定性都需要改进,传统铬系催化剂,多以氧化铝做载体,采用碱金属等元素进行改性制备得到。中国专利CN110560043、CN103769078、美国专利US20030232720提及了碱金属在脱氢催化剂中的作用,并公开了在催化剂中加入了少量的碱金属元素的方法,试图降低催化剂自身的酸性。但是由于碱金属的碱性较强,不仅降低了酸性,同时也降低了催化剂的稳定性。美国专利US8835347将部分碱金属和碱土金属加入脱氢催化剂中,以期待改变其选择性。但是,根据其催化剂的制备方法和性能表现,可以看出,该专利中加入的碱土元素的作用仅为在覆盖催化剂表面的酸性位点,提高了选择性,然而碱土元素未与固定床载体形成尖晶石结构,因此其催化剂的使用寿命并未得到增强。
相对于固定床、移动床反应器,流化床反应器能够稳定地控制床层温度均匀,传热过程几乎瞬间完成,传热传质效率高。因此,流化床反应器丙烷催化脱氢实验研究减少了温度不均引起的副反应的发生。并且流化床脱氢工艺可以连续反应与再生,可以实现在较高温度下长期稳定操作。但流化床反应器对催化剂的流化性能和耐磨性能要求较高,现阶段流化床工艺所使用催化剂丙烷转化率较低,丙烯产率较低。
但是现有的流化床脱氢工艺的催化剂,由于强度、磨耗、以及稳定性等问题,经常出现由于催化剂颗粒磨损所产生的损耗问题,一方面增加了催化剂的消耗量,另一方面对装置的旋风分离器以及颗粒回收装置也有较高的要求。因此,需要对流化床脱氢工艺的催化剂进行改进,以克服上述问题。
发明内容
为了克服现有技术中存在的“流化床脱氢工艺的催化剂强度、磨耗和稳定性不足的问题”,本发明提供一种低碳烷烃铬系脱氢催化剂及其制备方法和应用。
本发明通过以下技术方案实现:
第一方面,本发明提供一种低碳烷烃铬系脱氢催化剂,脱氢催化剂具有尖晶石结构,包括以干基总质量为基准计的以下质量分数的组分:
氧化铬0.1%~35%,第一助剂0.1%~5%,第二助剂0.1%~10%,第三助剂0.1%~5%,其余为流化床载体;
第一助剂为包含至少一种碱土金属元素的物质;
第二助剂为包含至少一种第ⅣB族元素的物质;
第三助剂为包含至少一种镧系金属元素的物质。
进一步地,在本发明较佳的实施例中,上述流化床载体的比表面积为50~300m2/g,粒度100~200μm。
进一步地,在本发明较佳的实施例中,上述流化床载体包括具有较高机械强度的氧化铝、分子筛或氧化硅。
尖晶石结构包括镁铝尖晶石结构、钙铝尖晶石结构、含钛尖晶石结构以及钙钛矿结构中的至少一种。
进一步地,在本发明较佳的实施例中,上述第一助剂包括碱土金属粉末、碱土金属卤化物、碱土金属氧化物、碱土金属硫化物、碱土金属硝酸盐,碱土金属乙酸盐以及碱土金属草酸盐中的一种或多种。
进一步地,在本发明较佳的实施例中,上述第二助剂包括第ⅣB族元素金属粉末、第ⅣB族元素卤化物、第ⅣB族元素氧化物、第ⅣB族元素硫化物、第ⅣB族元素硝酸盐、第ⅣB族元素乙酸盐以及第ⅣB族元素草酸盐中的一种或多种。
进一步地,在本发明较佳的实施例中,上述第三助剂包括镧系金属粉末、镧系金属卤化物、镧系金属氧化物、镧系金属硫化物、镧系金属碳化物、镧系金属硝酸盐、镧系金属乙酸盐以及镧系金属草酸盐中的一种或多种。
第二方面,本发明提供一种低碳烷烃铬系脱氢催化剂的制备方法,包括:
按照质量分数,将氧化铬、第一助剂、第二助剂和第三助剂混合后,得到浸渍液;
在真空条件下,将流化床载体置于浸渍液中进行浸渍处理,再陈化1~10h、干燥后,于650~950℃下焙烧2~10h。
进一步地,在本发明较佳的实施例中,上述流化床载体的粒度100~200μm,通过将氧化铝、分子筛或氧化硅在300-1000℃下煅烧2-10小时,过筛制得。
第三方面,本发明提供一种上述低碳烷烃铬系脱氢催化剂的应用,催化剂用于流化床反应器中,反应压力为0.01~0.50MPa、温度为530~660℃、体积空速800~2400h-1。
与现有技术相比,本发明至少具有如下技术效果:
相比于现有的传统流化床铬系脱氢催化剂,本发明提供的用于流化床的低碳烷烃铬系脱氢催化剂,使用碱土金属、第IVB族元素以及镧系金属元素,一方面通过调整载体表面的电性对催化剂中的活性中心的存在状态进行了控制,使催化剂的具有更高的脱氢活性、丙烯选择性;另一方面由于助剂与流化床载体会形成性能相对更加稳定的尖晶石结构,因此增强了催化剂整体的稳定性、强度以及磨耗,缓解了催化剂在使用过程中损耗问题。此外该催化剂生产原料简单易得,制备工艺简单,并可以使用现有的生产线高效,稳定,经济进行生产,可以有效的代替现有的传统铬系脱氢催化剂。
具体实施方式
下面将结合实施例对本发明的实施方案进行详细描述,但是本领域技术人员将会理解,下列实施例仅用于说明本发明,而不应视为限制本发明的范围,实施例中未注明的具体条件,按照常规条件或者制造商建议的条件进行,所用试剂或仪器未注明生产厂商者,均为可以通过市售购买获得的常规产品。
本发明的技术方案为:
为了满足流化床反应器对催化剂的流动性和耐磨性能的高要求,和解决低碳烷烃铬系脱氢催化剂存在的稳定性差,选择性低的问题,本发明提供一种用于流化床的低碳烷烃铬系脱氢催化剂。该低碳烷烃铬系脱氢催化剂具有尖晶石结构,用于流化床反应器中,反应压力为0.01~0.50MPa、温度为530~660℃、体积空速800~2400h-1。
该低碳烷烃铬系脱氢催化剂,具有尖晶石结构,包括镁铝尖晶石结构,钙铝尖晶石结构或含钛尖晶石结构中的至少一种。
该低碳烷烃铬系脱氢催化剂,包括按低碳烷烃铬系脱氢催化剂干基总质量为基准计的以下质量分数的组分:氧化铬0.1%~35%,第一助剂0.1%~5%,第二助剂0.1%~10%,第三助剂0.1%~5%,其余为流化床载体;
优选地,按干基总质量为基准计的以下质量分数的组分:氧化铬0.1~35%,第一助剂0.1~5%,第二助剂0.1~10%,第三助剂0.1~5%,其余为流化床载体;更为优选地,氧化铬1~25%,第一助剂0.5~3%,第二助剂0.5~3%,第三助剂0.5~3%,其余为流化床载体。
其中,氧化铬中的铬来源于铬酸钠,重铬酸钠,铬酸钾,重铬酸钾,重铬酸铵,铬酸,氯化铬,乙酰丙酮铬酸,硫酸铬钾,三氧化铬,过氧化铬,铬酸铅,氮化铬,硝酸铬以及氟化铬中的一种或多种。
第一助剂为包含至少一种碱土金属元素的物质,包括碱土金属粉末、碱土金属卤化物、碱土金属氧化物、碱土金属硫化物、碱土金属硝酸盐,碱土金属乙酸盐以及碱土金属草酸盐中的一种或多种。优选地,第一助剂为碱金属乙酸盐和硝酸盐,采用这种物质作为第一助剂,不易在催化剂的制备过程中引入杂质。
第二助剂为包含至少一种第ⅣB族元素的物质,包括第ⅣB族元素金属粉末、第ⅣB族元素卤化物、第ⅣB族元素氧化物、第ⅣB族元素硫化物、第ⅣB族元素硝酸盐、第ⅣB族元素乙酸盐,第IVB族元素的有机铵盐以及第ⅣB族元素草酸盐中的一种或多种。优选地,第二助剂为第IVB元素的有机铵盐和硝酸盐,采用这种物质作为第二助剂,不易在催化剂的制备过程中引入杂质。
第三助剂为包含至少一种镧系金属元素的物质,包含镧系金属粉末、镧系金属卤化物、镧系金属氧化物、镧系金属硫化物、镧系金属碳化物、镧系金属硝酸盐、镧系金属碳酸盐以及镧系金属草酸盐中的一种或多种。优选地,第三助剂为;镧系金属硝酸盐和碳酸盐,采用这种物质作为第三助剂,不易在催化剂的制备过程中引入杂质。
进一步地,流化床载体包括具有较高机械强度的氧化铝、分子筛或氧化硅。流化床载体的比表面积为50~300m2/g,粒度100~200μm。优选地,流化床载体的比表面积为80~120m2/g,粒度120~180μm。采用这种规格的流化床载体,有助于催化剂流化。
本实施方式还提供一种上述低碳烷烃铬系脱氢催化剂的制备方法,包括:
(1)按照质量分数,将氧化铬、第一助剂、第二助剂和第三助剂混合后,得到浸渍液;
(2)在真空条件下,将所述流化床载体置于浸渍液中进行浸渍处理,待表面干燥,再陈化1~10h、干燥后,于650~950℃下焙烧2~10h。
进一步地,配置所需含铬的可溶性溶液,其铬源可以使用铬的氧化物、铬的醋酸盐、铬的硝酸盐和铬的草酸盐中的一种;配置所需含钙或镁的可溶性溶液,镁源可以使用含镁硫酸盐、含镁的氯化物和含镁的硝酸盐中的一种,钙源配制时可以使用含钙的氯化物、含钙的硝酸盐和含钙的硫酸盐中的一种。
进一步地,将流化床载体与浸渍液的浸渍过程中,其真空度优选为0.2kPa-50kPa,更优选为0.2kPa-5kPa;陈化时间优选为1-5小时,更优选为2-4小时;干燥时间优选为2-8小时,更优选为2-5小时;焙烧温度优选为750-950℃,更优选为750-900℃;焙烧时间优选为2-8小时,更优选为4-6小时。
以下对本发明的具体实施方式进行详细说明。应当理解的是,此处所描述的具体实施方式仅用于说明和解释本发明,并不用于限制本发明。
实施例1
本实施例提供一种用于流化床的低碳烷烃铬系脱氢催化剂,其制备方法包括:
(1)将铝石粉烘干,以5℃/min的速度升温至900℃下,在该温度下煅烧3小时,冷却后筛分得到粒度100~200μm的流化床载体,测得其吸水量为45gH2O/100g、比表面积为110-120m2/g。
(2)称取23.8g铬酸酐、6.4g四水醋酸镁、2.2g一水草酸氧钛铵和3.2g六水硝酸镧,溶于50g水中,得到浸渍液;将100g流化床载体加入抽滤瓶中,抽真空2小时,真空度为-50kPa;将浸渍液缓慢加入抽滤瓶中,将湿润的流化床载体每10分钟进行一次搅拌,直至载体表面风干。放入110℃烘箱中烘干8小时,得到干燥的催化剂;将干燥的催化剂在马弗炉中进行焙烧,焙烧温度为800℃,焙烧时间为8小时,升温速率为5℃/min,待催化剂自然降温至200℃以下时,得到流化床催化剂1。
实施例2
本实施例提供一种用于流化床的低碳烷烃铬系脱氢催化剂,其制备方法包括:
称取33.9g铬酸酐,6.8g四水醋酸镁,1.7g八水氯化氧锆,3.4g六水硝酸镧,溶于50g水中,得到浸渍液;将实施例1中制得的100g流化床载体加入抽滤瓶中,抽真空2小时,真空度为-50kPa;将浸渍液缓慢加入抽滤瓶中,将湿润的流化床载体每10分钟进行一次搅拌,直至载体表面风干。放入110℃烘箱中烘干8小时,得到干燥的催化剂;将干燥的催化剂在马弗炉中进行焙烧,焙烧温度为650℃,焙烧时间为6小时,升温速率为5℃/min,待催化剂自然降温至200℃以下时,得到流化床催化剂2。
实施例3
本实施例提供一种用于流化床的低碳烷烃铬系脱氢催化剂,其制备方法包括:
称取33.7g铬酸酐,5.4g四水硝酸钙,1.7g八水氯化氧锆,1.6g六水硝酸铈,溶于50g水中,得到浸渍液;将实施例1中制得的100g流化床载体加入抽滤瓶中,抽真空2小时,真空度为-50kPa;将浸渍液缓慢加入抽滤瓶中,将湿润的流化床载体每10分钟进行一次搅拌,直至载体表面风干。放入110℃烘箱中烘干8小时,得到干燥的催化剂;将干燥的催化剂在马弗炉中进行焙烧,焙烧温度为750℃,焙烧时间为6小时,升温速率为5℃/min,待催化剂自然降温至200℃以下时,得到流化床催化剂3。
实施例4
本实施例提供一种用于流化床的低碳烷烃铬系脱氢催化剂,其制备方法包括:
称取29.8g铬酸酐,4g二水氯化钡,2.3g一水草酸氧钛胺,1.6g六水硝酸铈,溶于50g水中,得到浸渍液;将实施例1中制得的100g流化床载体加入抽滤瓶中,抽真空2小时,真空度为-50kPa;将浸渍液缓慢加入抽滤瓶中,将湿润的流化床载体每10分钟进行一次搅拌,直至载体表面风干。放入110℃烘箱中烘干8小时,得到干燥的催化剂;将干燥的催化剂在马弗炉中进行焙烧,焙烧温度为850℃,焙烧时间为6小时,升温速率为5℃/min,待催化剂自然降温至200℃以下时,得到流化床催化剂4。
实施例5
本实施例提供一种用于流化床的低碳烷烃铬系脱氢催化剂,其制备方法包括:
(1)以ZSM-5分子筛载体,将分子筛烘干,以5℃/min的速度升温至500℃下,在该温度下煅烧2小时,冷却后筛分得到粒度100~200μm的流化床载体,测得其吸水量为45g H2O/100g、比表面积为50~60m2/g。
(2)称取23.8g铬酸酐、6.4g四水醋酸镁、2.2g一水草酸氧钛铵和3.2g六水硝酸镧,溶于50g水中,得到浸渍液;将100g流化床载体加入抽滤瓶中,抽真空2小时,真空度为-40kPa;将浸渍液缓慢加入抽滤瓶中,将湿润的流化床载体每5分钟进行一次搅拌,直至载体表面风干。放入120℃烘箱中烘干2小时,得到干燥的催化剂;将干燥的催化剂在马弗炉中进行焙烧,焙烧温度为950℃,焙烧时间为2小时,升温速率为10℃/min,待催化剂自然降温至200℃以下时,得到流化床催化剂5。
实施例6
本实施例提供一种用于流化床的低碳烷烃铬系脱氢催化剂,其制备方法包括:
(1)以多孔氧化硅为载体,将氧化硅烘干,以5℃/min的速度升温至300℃下,在该温度下煅烧10小时,冷却后筛分得到粒度100~200μm的流化床载体,测得其吸水量为45gH2O/100g、比表面积为250~300m2/g。
(2)称取33.7g铬酸酐,5.4g四水硝酸钙,1.7g八水氯化氧锆,1.6g六水硝酸铈,溶于50g水中,得到浸渍液;将100g流化床载体加入抽滤瓶中,抽真空2小时,真空度为-100kPa;将浸渍液缓慢加入抽滤瓶中,将湿润的流化床载体每20分钟进行一次搅拌,直至载体表面风干。放入100℃烘箱中烘干5小时,得到干燥的催化剂;将干燥的催化剂在马弗炉中进行焙烧,焙烧温度为650℃,焙烧时间为10小时,升温速率为3℃/min,待催化剂自然降温至200℃以下时,得到流化床催化剂6。
对比例1
本对比例提供一种用于脱氢催化剂,其制备方法包括:
称取23.7g铬酸酐,6.4g四水醋酸镁,溶于50g水中,得到浸渍液;将100g流化床载体加入抽滤瓶中,抽真空2小时,真空度为-50kPa;将浸渍液缓慢加入抽滤瓶中,将湿润的流化床载体每10分钟进行一次搅拌,直至载体表面风干。放入110℃烘箱中烘干8小时,得到干燥的催化剂;将干燥的催化剂在马弗炉中进行焙烧,焙烧温度为650℃,焙烧时间为6小时,升温速率为5℃每分,待催化剂自然降温至200℃以下时,得到流化床对比剂1。
对比例2
本对比例提供一种用于脱氢催化剂,其制备方法包括:
称取29.8g铬酸酐,6.7g四水醋酸镁,2.3g一水草酸氧钛,溶于50g水中,得到浸渍液;将100g流化床载体加入抽滤瓶中,抽真空2小时,真空度为-50kPa;将浸渍液缓慢加入抽滤瓶中,将湿润的流化床载体每10分钟进行一次搅拌,直至载体表面风干。放入110℃烘箱中烘干8小时,得到干燥的催化剂;将干燥的催化剂在马弗炉中进行焙烧,焙烧温度为850℃,焙烧时间为6小时,升温速率为5℃每分,待催化剂自然降温至200℃以下时,得到流化床对比剂2。
为了说明本申请提供的低碳烷烃铬系脱氢催化剂的技术效果,特进行下述实验:
实验例1丙烷脱氢试验
将实施例1~4制得的流化床催化剂1-4与对比例1和2中的流化床对比剂1-2分别进行丙烷脱氢试验;
采用的工艺流程为现有的工艺流程,实施例中不作详细阐述,工艺流程中的控制参数如下:丙烷体积空速为1000h-1,通入适量氮气,保持丙烷分压为50kPa,反应体系总压力为常压;床层温度为560-610℃;结果如表1所示,
表1.
由表1可知,相比于对比例1和对比例2提供的催化剂,本发明实施例1~4提供的这种低碳烷烃铬系脱氢催化剂在600℃丙烷脱氢反应中丙烯选择性均有提高。
实验例2
实施例3提供的流化床催化剂3在不同温度下的丙烷脱氢性能试验
采用的工艺流程为现有的工艺流程,实施例中不作详细阐述,工艺流程中的控制参数如下:丙烷体积空速为1000h-1,通入适量氮气,保持丙烷分压为50kPa,反应体系总压力为常压;床层温度为560-610℃;结果如表2所示,
表2.
由表2可知,这种低碳烷烃铬系脱氢催化剂在床层温度为560-610℃范围内,随着温度上升,催化剂转化率升高,选择性降低,但副产物增加,符合丙烷脱氢催化剂的动力学规律,反应温度达到600℃时,丙烯收率高于40%,超过传统铬系脱氢催化剂的丙烯收率,由此说明,本发明制备的铬系脱氢催化剂具有较高的反应活性和稳定性。
最后应说明的是:以上所述仅为本发明的优选实施例而已,并不用于限制本发明的保护范围。凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (10)
1.一种低碳烷烃铬系脱氢催化剂,其特征在于,所述脱氢催化剂具有尖晶石结构,包括以干基总质量为基准计的以下质量分数的组分:
氧化铬0.1%~35%,第一助剂0.1%~5%,第二助剂0.1%~10%,第三助剂0.1%~5%,其余为载体;
所述第一助剂为包含至少一种碱土金属元素的物质;
所述第二助剂为包含至少一种第ⅣB族元素的物质;
所述第三助剂为包含至少一种镧系金属元素的物质。
2.根据权利要求1所述的低碳烷烃铬系脱氢催化剂,其特征在于,所述载体的比表面积为50~300m2/g,粒度100~200μm。
3.根据权利要求2所述的低碳烷烃铬系脱氢催化剂,其特征在于,所述载体包括氧化铝、分子筛和氧化硅中的至少一种。
4.根据权利要求1所述的低碳烷烃铬系脱氢催化剂,其特征在于,所述尖晶石结构包括镁铝尖晶石结构、钙铝尖晶石结构、含钛尖晶石结构以及钙钛矿结构中的至少一种。
5.根据权利要求1所述的低碳烷烃铬系脱氢催化剂,其特征在于,所述第一助剂包括碱土金属、碱土金属卤化物、碱土金属氧化物、碱土金属硫化物、碱土金属硝酸盐,碱土金属乙酸盐以及碱土金属草酸盐中的一种或多种。
6.根据权利要求1所述的低碳烷烃铬系脱氢催化剂,其特征在于,所述第二助剂包括第ⅣB族元素金属、第ⅣB族元素卤化物、第ⅣB族元素氧化物、第ⅣB族元素硫化物、第ⅣB族元素硝酸盐、第ⅣB族元素乙酸盐以及第ⅣB族元素草酸盐中的一种或多种。
7.根据权利要求1所述的低碳烷烃铬系脱氢催化剂,其特征在于,所述第三助剂包含镧系金属、镧系金属卤化物、镧系金属氧化物、镧系金属硫化物、镧系金属碳化物、镧系金属硝酸盐、镧系金属乙酸盐以及镧系金属草酸盐中的一种或多种。
8.一种如权利要求1~7任一项所述的低碳烷烃铬系脱氢催化剂的制备方法,其特征在于,包括:
按照质量分数,将所述氧化铬、所述第一助剂、所述第二助剂和所述第三助剂混合后,得到浸渍液;
在真空条件下,将所述载体置于所述浸渍液中进行浸渍处理,再陈化1~10h、干燥后,于650~950℃下焙烧2~10h。
9.根据权利要求8所述的低碳烷烃铬系脱氢催化剂的制备方法,其特征在于,所述载体的粒度为100~200μm,通过将氧化铝、分子筛或氧化硅在300-1000℃下煅烧2-10小时,过筛制得。
10.一种如权利要求1~7任一项所述的低碳烷烃铬系脱氢催化剂的应用,其特征在于,所述催化剂用于流化床反应器中,反应压力为0.01~0.50MPa、温度为530~660℃、体积空速800~2400h-1。