CN114773556B - 一种共价有机框架材料的绿色固相合成方法 - Google Patents

一种共价有机框架材料的绿色固相合成方法 Download PDF

Info

Publication number
CN114773556B
CN114773556B CN202111650887.5A CN202111650887A CN114773556B CN 114773556 B CN114773556 B CN 114773556B CN 202111650887 A CN202111650887 A CN 202111650887A CN 114773556 B CN114773556 B CN 114773556B
Authority
CN
China
Prior art keywords
monomer
tris
acid
organic
connection
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN202111650887.5A
Other languages
English (en)
Other versions
CN114773556A (zh
Inventor
张振杰
王志方
赵正峰
陈瑶
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Yaoke New Materials Suzhou Co ltd
Original Assignee
Yaoke New Materials Suzhou Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Yaoke New Materials Suzhou Co ltd filed Critical Yaoke New Materials Suzhou Co ltd
Publication of CN114773556A publication Critical patent/CN114773556A/zh
Priority to PCT/CN2022/138498 priority Critical patent/WO2023124952A1/zh
Application granted granted Critical
Publication of CN114773556B publication Critical patent/CN114773556B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及乙烯基共价有机框架泡沫、聚酰亚胺类、亚胺类、腙类或酮‑烯醇类共价有机框架（COFs）的新合成方法。该方法属于绿色合成策略：在非溶剂条件下，将含甲基的单体和醛基单体在酸酐类或羧酸类化合物的参与下，发生缩合反应制备乙烯基COFs；将多头酸酐或多头羧酸单体和氨基单体在酸酐类或羧酸类化合物的参与下，发生缩合反应制备酰胺类COFs；将醛基单体和氨基单体在酸酐类、咪唑类或羧酸类化合物的参与下，发生缩合反应制备亚胺类COFs。采用该类方法得到的COFs具有较大的比表面积、规则可调的孔道结构和较高的结晶性。该合成方法有效的避免了有机溶剂的使用和反应过程导致高压的危险，适合大规模制备COFs材料。

Description

一种共价有机框架材料的绿色固相合成方法
技术领域
本发明属于多孔有机材料领域，具体涉及一种共价有机框架材料的绿色固相合成方法。
背景技术
共价有机框架材料(COFs)是由有机单体通过共价键连接的二维(2D)或三维(3D)多孔晶态有机聚合物材料，具有密度低、比表面积大、结构规则稳定、孔径均一、易功能化等优点。通过对COFs材料进行合理的功能化设计，COFs被广泛的应用在气体吸附分离、催化、药物传输、超级电容器等领域。为了满足日益增长的需要，COFs的种类也在不断地丰富，目前已经报道的COFs种类有硼酸酯连接、亚胺键连接、腙键连接、酮-烯醇连接、聚酰亚胺连接、乙烯基连接等。其合成方法主要利用溶剂热制备，需要特殊的有机溶剂和催化剂作为反应介质，该过程既耗时又不环保。且该类溶剂热反应是在密闭的玻璃管或密闭容器中进行，其高温高压的反应条件严重阻碍了COFs的大规模生产。
随着政府对于低能耗、低污染的要求，以及人们环保意识的逐渐增加，发展绿色环保的制备方法大量合成COFs进一步满足COFs材料的实际应用，已经成为COFs材料领域亟待解决的问题。最近，离子液体合成、微波辅助合成和机械化学合成等环境友好的方法已经被应用在COFs的合成中，然而这些方法比较局限，只能实现个别COFs的合成，不具有广泛的普适性，因此，发展一种简单的、普适性高的、绿色无污染的、适合大规模生产的合成方法制备乙烯基连接、酰亚胺连接、硼酸酯连接、硼氧六元环连接、亚胺键连接、吖嗪连接、酮-烯醇连接、腙键连接或三嗪连接的COFs材料是迫切需要的，且具有实际意义。
一方面，本发明通过对COFs的有机单体和合成条件进行调控和筛选、选用适宜的催化剂，从而开发一种非溶剂参与的绿色合成方法制备高结晶性的COFs材料。另一方面，与传统的溶剂热合成相比，非溶剂的参与可以有效地避免高压的操作条件，适合COFs的大规模生产。此外，选用功能化的有机单体作为构筑单元，可以制备具有特殊功能的COFs材料。
发明内容
本发明的目的是为乙烯基连接、酰亚胺连接、硼酸酯连接、硼氧六元环连接、亚胺键连接、吖嗪连接、酮-烯醇连接、腙键连接或三嗪连接的COFs提供一种新型的、绿色的、无溶剂的合成方法。
本发明的另外一个目的，为乙烯基连接、酰亚胺连接、硼酸酯连接、硼氧六元环连接、亚胺键连接、吖嗪连接、酮-烯醇连接、腙键连接或三嗪连接COFs的合成提供更加便宜的反应单体，实现COFs的大量制备，并制备新型的COFs。
本发明的目的也是为乙烯基连接、酰亚胺连接、硼酸酯连接、硼氧六元环连接、亚胺键连接、吖嗪连接、酮-烯醇连接、腙键连接或三嗪连接COF泡沫的合成提供新方法，合成一系列新型的COFs，并说明泡沫材料在吸附分离中的优势。
本发明的其他目的对于熟悉技术者而言，直接由前述和下述的说明即可清楚。
本发明的第一方面是提供一种共价有机框架材料(COFs)的固相合成方法，其特征在于，所述共价有机框架材料为通过乙烯基连接、酰亚胺连接、硼酸酯连接、硼氧六元环连接、亚胺键连接、吖嗪连接、酮-烯醇连接、腙键连接或三嗪连接的共价有机框架材料，其具体通过如下步骤进行合成：
有机单体1和有机单体2在非溶剂、有催化剂存在的条件下，通过缩合反应获得。
优选的，所述合成方法是原位生长方法，具体为：把催化剂、有机单体1和有机单体2，通过研磨成浆糊状或研磨均匀，涂在任意基底上或直接放进密闭反应容器中中，高温聚合得到共价有机框架材料。
优选的，所述反应在非溶剂条件下进行反应，包括如下步骤：
(1)将有机单体1和有机单体2加入到反应器中，加入催化剂进行反应；
(2)反应结束后，对产物进行纯化；
(3)纯化后的产物在超临界二氧化碳中处理或真空条件下加热处理得到最终产物。
优选的，所述有机单体1为含有羧酸酐官能团的二连接单体、含有羧酸官能团的二连接单体、含醛基官能团的二连接单体或含醛基官能团的三连接单体。
进一步优选的，有机单体1为含苯硼酸的单体、含苯甲醛的单体、2,4,6-三羟基苯-1,3,5-三甲醛、含邻苯二酸酐的单体、含羟基丙烯酮的单体、含苯二酮的单体或二元酸酐单体。更优选的，所述有机单体1为含苯甲醛的二连接或三连接单体、含苯酸酐的二连接单体，含邻苯二甲酸的二连接单体，其中二连接单体的为直线分子，三连接单体夹角为120°。
优选的，有机单体2为含有氨基官能团的二连接单体、含有氨基官能团的三连接单体、含有氨基官能团的四连接单体、含活性甲基官能团的二连接单体、或含有活性甲基官能团的三连接单体。
进一步优选的，有机单体2为含邻苯二酚的单体、含苯胺的单体、含苯甲酰肼的单体、水合肼、含苯甲腈的单体、含苯乙腈的单体、二甲基吡嗪单体、含苯甲脒的单体、含邻苯二胺的单体或三胺单体；更进一步优选的，所述有机单体2为含苯胺的二连接、三连接或四连接单体、含苯甲酰肼的二连接或三连接单体、水合肼、含活性甲基的二连接或三连接单体，其中二连接单体的为直线分子，三连接单体和四连接单体的夹角为120°。
优选的，所述催化剂为含有酸酐官能团的化合物、含有羧酸官能团的化合物、含有咪唑官能团的化合物或含有羟基官能团的化合物。
进一步优选的，所述催化剂为取代或未取代的如下化合物：苯甲酸酐、4-三氟甲基苯甲酸酐、苯乙酸酐、乙酸酐、三氟乙酸酐、苯甲酸、4-氟苯甲酸、4-溴苯甲酸、丙酸、芳香酸、咪唑、苯并咪唑或苯酚。
本发明优选的方案中，所述有机单体1为对苯二甲醛、1,4-二(4-醛基苯基)苯、4,4'-联苯二甲醛、1,2-二(4'-甲酰基苯基)乙炔、4,4'-(1,3-丁二炔-1,4-二基)双苯甲醛、2,5-二甲氧基-1,4-对苯二甲醛、4,7-二(4-醛基苯基)苯并呋喃、4,7-二(4-醛基苯基)苯并噻吩、4,7-二(4-醛基苯基)苯并硒酚、1,3,5-均苯三甲醛、2-羟基-1,3,5-苯三甲醛、2,4-二羟基-1,3,5-苯三甲醛、2,4,6-三羟基-1,3,5-苯三甲醛、1,3,5-三(4'-醛基[1,1'-联苯]-4-基)苯、1,3,5-三(对甲酰基苯基)苯、4,4’,4”-[苯-1,3,5-三基三(乙炔-2,1-二基)]三苯甲醛、2,4,6-三(4-醛基苯基)-1,3,5-三嗪、4’,4”,4”’-(1,3,5-三嗪-2,4,6-三基)三(([1,1'-联苯]-4-甲醛))、2,4,6-三(4-甲酰基-联苯-4-基)-1,3,5-三嗪中的任意一种。
所述有机单体2为2,5-二甲基吡嗪、四甲基吡嗪、3,6-二甲基哒嗪、2,5-二甲基对苯二腈、2,4,6-三甲基-1,3,5-三嗪、2,4,6-三甲基吡啶、2,4,6,-三甲基-嘧啶、2,4,6,-三甲基-嘧啶-5-甲腈、2,4,6-三甲基吡啶-3,5-二甲腈、2,4,6-三氰基-1,3,5-三甲基苯、2,2'-联吡啶-5,5'-二乙腈中的任意一种。
其中，二连接的有机单体2与三连接的有机单体1组合反应，或二连接的有机单体1与三连接的有机单体2组合反应。
本发明优选的方案中，所述有机单体1为均苯四甲酸二酐(PMDA)、1,4,5,8-萘四甲酸二酐(NTCDA)、均苯四甲酸(PA)、1,4,5,8-萘四甲酸(NTA)、对苯二甲醛、1,4-二(4-醛基苯基)苯、4,4'-联苯二甲醛、1,2-二(4'-甲酰基苯基)乙炔、4,4'-(1,3-丁二炔-1,4-二基)双苯甲醛、2,5-二甲氧基-1,4-对苯二甲醛、均苯三甲醛、2-羟基-1,3,5-苯三甲醛、2,4-二羟基-1,3,5-苯三甲醛、2,4,6-三羟基-1,3,5-苯三甲醛、1,3,5-三(4'-醛基[1,1'-联苯]-4-基)苯、1,3,5-三(对甲酰基苯基)苯、4,4',4”-[苯-1,3,5-三基三(乙炔-2,1-二基)]三苯甲醛、2,4,6-三(4-醛基苯基)-1,3,5-三嗪、4',4”',4””'-(1,3,5-三嗪-2,4,6-三基)三(([1,1'-联苯]-4-甲醛))或2,4,6-三-(4-甲酰基-联苯-4-基)-1,3,5-三嗪中任意一种。
所述有机单体2为对苯二胺、2,5-二氨基吡啶、联苯胺、4,4'-二氨基三连苯、水合肼、对苯二酸二肼、2,5-二乙氧基苯-1,4-二(甲酰肼)、2,5-双(烯丙氧基)对苯二甲酰肼、1,3,5-三(4-氨苯基)苯(TAPB)、2,4,6-三(4-氨基苯基)-1,3,5-三嗪(TAPT)、三(4-氨基苯基胺)(TAPA)、5"-(4'-氨基[1,1'-联苯基]-4-基)[1,1':4',1”:3”,1”':4”',1””-五联苯]-4,4”'-二胺(TABPB)、4',4”',4””'-(1,3,5-三嗪-2,4,6-三基)三(([[1,1'-联苯]-4-胺))(TTBT)、2,7,12-三氨基-5H-二吲哚[1,2-a:1',2’-c]芴-5,10,15-三酮(TRO)、2,4,6-三(3-羟基-4-氨基苯基)-1,3,5-三嗪、1,3,5-苯三甲酰肼、N,N,N',N'-四(对氨基苯基)对苯二胺或四-(4-氨基苯)乙烯中任意一种。
其中，二连接的有机单体2与三连接有机单体1组合反应，或二连接的有机单体1与三连接或四连接的有机单体2组合反应。
优选的，共价有机框架材料(COFs)为聚酰亚胺型共价有机框架、乙烯基连接共价有机框架泡沫、亚胺键连接共价有机框架、吖嗪连接共价有机框架、腙键连接共价有机框架和酮-烯醇类共价有机框架材料。
优选的，共价有机框架材料的形态为块状、圆柱状或泡沫状。
优选的，所述共价有机框架材料的孔径为0.6-4.9nm，更有选的为1.8-4.9nm。
优选的，在反应体系中，有机单体1和有机单体2的摩尔比为1:4至4:1，更优选为1:1至1:2。
优选的，在反应体系中，催化剂和有机单体1的摩尔比为1:5至5:1，更优选为1:3至3:1。
优选的，反应体系的压强为0-1atm。
优选的，合成温度为20-200℃，更有选为150-250℃，尤其优选为180-200℃。
优选的，反应时间3-7天，更优选为5天。
优选的，所述密闭反应容器为耐高温高压的Pyrex管、需火焰封管的安瓿瓶、带有聚四氟乙烯衬里的钢制高压反应釜中的一种。
优选地，所述构筑单体和一种低熔点的有机化合物按照一定当量比放入密闭容器中，通过抽真空至容器内压力达到0.15mmHg，持续半个小时，通过火焰封管，将密封后的反应容器放入200℃烘箱中，持续3-5天，反应完毕后，将得到的固体粉末用DMF洗涤以除去未反应单体，再用CH3OH洗涤以除去过量加入的调节剂，随后将所得固体粉末在无水四氢呋喃溶剂中索氏提取12h，以除去孔道中未反应的小分子，最后将得到的固体粉末在真空高温烘箱中100℃的温度条件下加热干燥12h，以得到高结晶性的共价有机框架材料。
优选的，反应体系无需加入有机溶剂，属于固相反应体系。
另一方面，本发明提供一种COFs材料的简单的、绿色的合成方法，首先选用低熔点的苯甲酸酐、苯甲酸等作为催化剂，由2,5-二甲基吡嗪单体或2,4,6-三甲基-1,3,5-三嗪与三连接的醛(包括：1,3,5-三(4'-醛基[1,1'-联苯]-4-基)苯、1,3,5-三(对甲酰基苯基)苯、4,4',4”-[苯-1,3,5-三基三(乙炔-2,1-二基)]三苯甲醛、2,4,6-三(4-醛基苯基)-1,3,5-三嗪、4',4”',4””'-(1,3,5-三嗪-2,4,6-三基)三(([1,1'-联苯]-4-甲醛))、2,4,6-三-(4-甲酰基-联苯-4-基)-1,3,5-三嗪、均苯三甲醛)或二连接的醛(包括：对苯二甲醛、1,4-二(4-醛基苯基)苯、4,4'-联苯二甲醛、1,2-二(4'-甲酰基苯基)乙炔、4,4'-(1,3-丁二炔-1,4-二基)双苯甲醛、2,5-二甲氧基-1,4-对苯二甲醛、4,7-二(4-醛基苯基)苯并呋喃、4,7-二(4-醛基苯基)苯并噻吩、4,7-二(4-醛基苯基)苯并硒酚)在无溶剂条件下反应的得到产物。由于苯甲酸酐较低的熔点(43℃)利于COFs塑形，结合2,5-二甲基吡嗪或2,4,6-三甲基-1,3,5-三嗪单体低熔点的特性，与三醛单体在高温下反应，可以制备乙烯基COF泡沫材料。
一种绿色的无溶剂的合成方法，适用于聚酰亚胺型共价有机框架、乙烯基连接共价有机框架泡沫、亚胺键连接共价有机框架、吖嗪连接共价有机框架、腙键连接共价有机框架和酮-烯醇类共价有机框架材料的制备。在高真空度的密闭反应容器中，两种构筑单元在另一种低熔点的化合物辅助下，高温脱水缩合，制备孔径均一、高结晶度、高比表面积的共价有机框架材料。
本发明的另一方面是有关通式1的聚酰亚胺类COFs的合成
其中，有机单体1主要包括含有酸酐官能团的二连接单体，如：均苯四甲酸二酐(PMDA)，1,4,5,8-萘四甲酸二酐(NTCDA)等；或者含有羧酸官能团的四连接单体，如均苯四甲酸(PA)，1,4,5,8-萘四甲酸(NTA)等。
有机单体2主要包括含有氨基官能团的三连接单体，如：1,3,5-三(4-氨苯基)苯(TAPB)、2,4,6-三(4-氨基苯基)-1,3,5-三嗪(TAPT)、三(4-氨基苯基胺)(TAPA)、5"-(4'-氨基[1,1'-联苯基]-4-基)[1,1':4',1”:3”,1”':4”',1””-五联苯]-4,4”'-二胺(TABPB)、4',4”',4””'-(1,3,5-三嗪-2,4,6-三基)三(([[1,1'-联苯]-4-胺))(TTBT)、2,7,12-三氨基-5H-二吲哚[1,2-a:1',2’-c]芴-5,10,15-三酮(TRO)、2,4,6-三(3-羟基-4-氨基苯基)-1,3,5-三嗪、N,N,N',N'-四(对氨基苯基)对苯二胺、四-(4-氨基苯)乙烯等。
化合物3主要包括含有酸酐官能团的化合物，如苯甲酸酐(BZDA)、4-三氟甲基苯甲酸酐(TFBA)、乙酸酐(AA)等；或者含有羧酸官能团的化合物，如苯甲酸(BA)、4-氟苯甲酸(FBA)、丙酸(PA)等。
在上述提到的有机单体1和有机单体2可以随意组合，在化合物3中任意一个参与的条件下均可制备目标COFs。
本发明的另一方面是有关通式2的乙烯基类COFs的合成
有机单体1主要包括：1,3,5-三(4'-醛基[1,1'-联苯]-4-基)苯、1,3,5-三(对甲酰基苯基)苯、4,4',4”-[苯-1,3,5-三基三(乙炔-2,1-二基)]三苯甲醛、2,4,6-三(4-醛基苯基)-1,3,5-三嗪、4',4”',4””'-(1,3,5-三嗪-2,4,6-三基)三(([1,1'-联苯]-4-甲醛))、2,4,6-三-(4-甲酰基-联苯-4-基)-1,3,5-三嗪、均苯三甲醛、对苯二甲醛、1,4-二(4-醛基苯基)苯、4,4'-联苯二甲醛、1,2-二(4'-甲酰基苯基)乙炔、4,4'-(1,3-丁二炔-1,4-二基)双苯甲醛、2,5-二甲氧基-1,4-对苯二甲醛、4,7-二(4-醛基苯基)苯并呋喃、4,7-二(4-醛基苯基)苯并噻吩、4,7-二(4-醛基苯基)苯并硒酚。
有机单体2主要包括：2,4,6-三甲基-1,3,5-三嗪、2,4,6-三甲基吡啶-3,5-二甲腈、2,4,6-三氰基-1,3,5-三甲基苯、2,5-二甲基吡嗪、3,6-二甲基哒嗪、2,5-二甲基对苯二腈。
在上述提到的单体1和单体2可以随意组合，在化合物3中任意一个参与的条件下均可制备目标COFs。
本发明的另一方面是有关通式3的腙键类COFs的合成
有机单体1主要包括：1,3,5-三(4'-醛基[1,1'-联苯]-4-基)苯、1,3,5-三(对甲酰基苯基)苯、4,4',4”-[苯-1,3,5-三基三(乙炔-2,1-二基)]三苯甲醛、2,4,6-三(4-醛基苯基)-1,3,5-三嗪、4',4”',4””'-(1,3,5-三嗪-2,4,6-三基)三(([1,1'-联苯]-4-甲醛))、2,4,6-三-(4-甲酰基-联苯-4-基)-1,3,5-三嗪、均苯三甲醛。
有机单体2主要包括：对苯二酸二肼、2,5-二乙氧基苯-1,4-二(甲酰肼)、2,5-双(烯丙氧基)对苯二甲酰肼、1,3,5-苯三甲酰肼。
化合物3主要包括：苯甲酸酐、苯并咪唑、苯甲酸。
在上述提到的单体1和单体2可以随意组合，在化合物3中任意一个参与的条件下均可制备目标COFs。
本发明的另一方面是有关通式4的亚胺类COFs的合成
有机单体1主要包括：1,3,5-三(对甲酰基苯基)苯、2,4,6-三(4-醛基苯基)-1,3,5-三嗪、均苯三甲醛、2-羟基-1,3,5-苯三甲醛、2,4-二羟基-1,3,5-苯三甲醛、对苯二甲醛、4,4'-联苯二甲醛1,4-二(4-醛基苯基)苯、1,2-二(4'-甲酰基苯基)乙炔。
有机单体2主要包括：1,3,5-三(4-氨基苯基)苯、2,4,6-三(4-氨基苯基)-1,3,5-三嗪、三(4-氨基苯基)胺、对苯二胺、2,5-二氨基吡啶、联苯胺、4,4'-二氨基三连苯、水合肼。
化合物3主要包括：苯甲酸酐、苯并咪唑、苯甲酸。
上述提到的有机单体1和有机单体2可以随意组合，在化合物3中任意一个参与的条件下也可制备目标COFs，其中有机单体2为水合肼所制备的COFs为吖嗪连接的共价有机框架材料。
本发明的另一方面是有关通式5的酮-烯醇类COFs的合成
有机单体1为三醛基间苯三酚。
有机单体2主要包括：对苯二胺、2,5-二氨基吡啶、联苯胺、4,4'-二氨基三连苯、水合肼、1,3,5-三(4-氨基苯基)苯、2,4,6-三(4-氨基苯基)-1,3,5-三嗪、三(4-氨基苯基)胺。
在上述提到的有机单体1与有机单体2中的任意一种单体组合，在化合物3中任意一个参与的条件下也可制备目标COFs。
与现有技术相比，该发明有以下创新之处：
1.优化了现有的乙烯基连接、酰亚胺连接、硼酸酯连接、硼氧六元环连接、亚胺键连接、吖嗪连接、酮-烯醇连接、腙键连接或三嗪连接的共价有机框架材料的合成方法，拓展了反应单体，降低的材料成本，通过无溶剂法的合成避免了高毒性催化剂、溶剂的使用，降低了能耗，提高了共价有机框架的结晶性和比表面积具备极佳的普适性。
2.优化了现有的乙烯基连接、酰亚胺连接、硼酸酯连接、硼氧六元环连接、亚胺键连接、吖嗪连接、酮-烯醇连接、腙键连接或三嗪连接的共价有机框架材料的合成方法，通过无溶剂法的合成避免了高毒性催化剂、溶剂的使用，降低了筛选反应条件的时间。得益于固相反应易成型的优点，可以一步制备高结晶性的共价有机框架泡沫。
3.本发明选用的固催化剂如取代或未取代的如下化合物：苯甲酸酐、4-三氟甲基苯甲酸酐、苯乙酸酐、乙酸酐、三氟乙酸酐、苯甲酸、4-氟苯甲酸、4-溴苯甲酸、丙酸、芳香酸、咪唑、苯并咪唑或苯酚等为本研究领域的首次尝试，成功的避免了有机溶剂的参与，降低了反应的有效地降低了反应的风险，为共价有机框架材料的大规模生产提供了新方法。
附图说明：
图1：列举了部分本发明所用到的合成共价有机框架材料所用的有机构单体的结构式，进行示例性说明。
图2：列举了部分本发明所制备的共价有机框架材料的合成路线示意图。
图3：本发明所制备的几种代表性共价有机框架材料的粉末衍射图。
图4：本发明所制备的几种代表性共价有机框架材料的红外光谱图。
图5：本发明所制备的几种代表性共价有机框架材料的77K氮气等温吸脱附曲线图。注：由于所制备的共价有机框架材料的种类和数量较多，每种共价有机框架只提供一个材料的表征数据图。
具体实施方式：
除非本申请上下文中另有其他说明，否则本申请中所用技术术语及缩写均具有本领域技术人员所知的常规含义；除非另有说明，否则下述实施例中所用原料化合物均为商购获得。
按照本发明所提到的，聚酰亚胺型共价有机框架、乙烯基连接共价有机框架泡沫、亚胺键连接共价有机框架、腙键连接共价有机框架和酮-烯醇类共价有机框架材料的制备六种聚酰亚胺型共价有机框架材料的合成及相关性能表征测试，其具体实施方式如下。相反，下列实施例仅用于对本发明进一步解释和发明，而不应视为限制本发明的范围。
实施例1～14为聚酰亚胺型共价有机框架材料的制备方法，实施例15～17为乙烯基共价有机框架泡沫的制备方法，实施例18和19为腙键共价有机框架材料的制备方法，实施例20和21为亚胺型共价有机框架材料的制备方法，实施例22和23为酮-烯醇类共价有机框架材料的制备方法，其中每一种材料更换六种不同的酸酐类或芳酸类调节剂均可以得到结晶性高的共价有机框架材料。
实施例1：
如图1所示，称取1,4,5,8-萘四甲酸二酐(NTCDA)(0.15mmol,40.23mg)或1,4,5,8-萘四甲酸(NTA)(0.15mmol,45.63mg)中的一种,2,4,6-三(4-氨基苯基)-1,3,5-三嗪(TAPT)(0.10mmol,35.4mg)、以及苯甲酸酐(0.225mmol,50.9mg)、4-三氟甲基苯甲酸酐(0.225mmol,81.50mg)、乙酸酐(0.5mmol,51.04mg)、苯甲酸(0.6mmol,73.28mg)、4-氟苯甲酸(0.6mmol,86.47mg)或丙酸(0.6mmol,44.4mg)中的一种,小心地装入耐高温高压的厚壁玻璃管中。抽真空至管内压力达到0.15mmHg后从真空线上取下，通过氢氧机产生的火焰将玻璃管封好，以隔绝空气。将密封好的玻璃管放入250℃烘箱中反应5天。反应后得到土黄色粉末的固体粉末，将其在DMF，CH3OH中浸泡后，在四氢呋喃溶剂中索氏提取持续48h,从而得到土黄色粉末的粉末，质量在51-59mg之间，产率约为74％-84％。如图3a所示，粉末X-射线测试揭示，利用1,4,5,8-萘四甲酸二酐与2,4,6-三(4-氨基苯基)-1,3,5-三嗪在苯甲酸酐催化反应下所制备的粉末样品具有很高的结晶性，图4a红外光谱测试进一步证明该材料是酰亚胺连接COFs材料，图5a为该材料在77K条件下氮气等温吸脱附曲线，其BET表面积为894m2/g。
实施例2：
如图1所示，称取1,4,5,8-萘四甲酸二酐(NTCDA)(0.15mmol,40.23mg)或1,4,5,8-萘四甲酸(NTA)(0.15mmol,45.63mg)中的一种，三(4-氨基苯基胺)(TAPA)(0.10mmol,29.0mg)、以及苯甲酸酐(0.225mmol,50.9mg)、4-三氟甲基苯甲酸酐(0.225mmol,81.50mg)、乙酸酐(0.5mmol,51.04mg)、苯甲酸(0.6mmol,73.28mg)、4-氟苯甲酸(0.6mmol,86.47mg)或丙酸(0.6mmol,44.4mg)中的一种，其他操作与实施例1相同，得到黑色粉末，质量在51-59mg之间，产率为71％-91％。
实施例3：
如图1所示，称取1,4,5,8-萘四甲酸二酐(NTCDA)(0.2mmol,,53.6mg)或1,4,5,8-萘四甲酸(NTA)(0.2mmol,60.8mg)中的一种，N,N,N',N'-四(对氨基苯基)对苯二胺(0.1mmol,47.2mg)或四-(4-氨基苯)乙烯(0.1mmol,39.2mg)中的一种，以及苯甲酸酐(0.225mmol,50.9mg)、4-三氟甲基苯甲酸酐(0.225mmol,81.50mg)、乙酸酐(0.5mmol,51.04mg)、苯甲酸(0.8mmol,97.6mg)、4-氟苯甲酸(0.8mmol,115.29mg)或丙酸(0.8mmol,59.2mg)中的一种，其他操作与实施例1相同,得到的棕色粉末，产率约为90％
实施例4：
如图1所示，称取均苯四甲酸二酐(PMDA)(0.15mmol，32.7mg)或均苯四甲酸(PA)(0.15mmol，38.1mg)中的一种，1,3,5-三(4-氨苯基)苯(TAPB)(0.10mmol,35.1mg)，以及苯甲酸酐(0.3mmol,67.8mg)、4-三氟甲基苯甲酸酐(0.3mmol,108.67mg)、乙酸酐(0.5mmol,51.04mg)、苯甲酸(0.6mmol,73.28mg)、4-氟苯甲酸(0.6mmol,86.47mg)或丙酸(0.6mmol,44.4mg)中的一种，小心地装入耐高温高压的厚壁玻璃管中。抽真空至管内压力达到0.15mmHg后从真空线上取下，通过氢氧机产生的火焰将玻璃管封好，以隔绝空气。将密封好的玻璃管放入200℃烘箱中反应5天。反应后得到橙黄色的固体粉末，将其在DMF，CH3OH中浸泡后，在四氢呋喃溶剂中索氏提取持续48h,从而得到橙黄色的粉末，质量在44-52mg之间，产率约在77％-95％之间。
实施例5：
如图1所示，称取均苯四甲酸二酐(PMDA)(0.15mmol,32.7mg)或均苯四甲酸(PA)(0.15mmol，38.1mg)中的一种，2,4,6-三(4-氨基苯基)-1,3,5-三嗪(TAPT)(0.10mmol,35.4mg)，以及苯甲酸酐(0.3mmol,67.8mg)、4-三氟甲基苯甲酸酐(0.3mmol,108.67mg)、乙酸酐(0.5mmol,51.04mg)、苯甲酸(0.6mmol,73.28mg)、4-氟苯甲酸(0.6mmol,86.47mg)或丙酸(0.6mmol,44.4mg)中的一种，其他操作与实施例4相同，得到淡黄色的固体粉末，质量在42-59mg之间，产率约在75％-86％之间。
实施例6：
如图1所示，称取均苯四甲酸二酐(PMDA)(0.15mmol，32.7mg)或均苯四甲酸(PA)(0.15mmol，38.1mg)中的一种，三(4-氨基苯基胺)(TAPA)(0.10mmol,29.0mg)或2,4,6-三(3-羟基-4-氨基苯基)-1,3,5-三嗪(0.10mmol,40.2mg)，以及苯甲酸酐(0.3mmol,67.8mg)、4-三氟甲基苯甲酸酐(0.3mmol,108.67mg)、乙酸酐(0.5mmol,51.04mg)、苯甲酸(0.6mmol,73.28mg)、4-氟苯甲酸(0.6mmol,86.47mg)或丙酸(0.6mmol,44.4mg)中的一种，其他操作与实施例4相同，得到紫黑色的固体粉末，质量在42-52mg之间，产率约在75％-91％之间。
实施例7：
如图1所示，称取均苯四甲酸二酐(PMDA)(0.2mmol，43.6mg)或均苯四甲酸(PA)(0.2mmol，50.8mg)中的一种，N,N,N',N'-四(对氨基苯基)对苯二胺(0.1mmol,47.2mg)或四-(4-氨基苯)乙烯(0.1mmol,39.2mg)中的一种，以及苯甲酸酐(0.225mmol,50.9mg)、4-三氟甲基苯甲酸酐(0.225mmol,81.50mg)、乙酸酐(0.5mmol,51.04mg)、苯甲酸(0.8mmol,97.6mg)、4-氟苯甲酸(0.8mmol,115.29mg)或丙酸(0.8mmol,59.2mg)中的一种，其他操作与实施例4相同,得到的棕色粉末，产率约为90％。
实施例8：
如图1所示，称取1,4,5,8-萘四甲酸二酐(NTCDA)(0.15mmol,40.23mg)或1,4,5,8-萘四甲酸(NTA)(0.15mmol,45.63mg)中的一种，1,3,5-三(4-氨苯基)苯(TAPB)(0.10mmol,35.1mg)，以及苯甲酸酐(0.225mmol,50.9mg)、4-三氟甲基苯甲酸酐(0.225mmol,81.50mg)、乙酸酐(0.5mmol,51.04mg)、苯甲酸(0.6mmol,73.28mg)、4-氟苯甲酸(0.6mmol,86.47mg)或丙酸(0.6mmol,44.4mg)中的一种，小心地装入耐高温高压的厚壁玻璃管中，将该粉末抽真空至管内压力达到0.15mmHg后从真空线上取下，通过氢氧机产生的火焰将玻璃管封好，以隔绝空气。将密封好的玻璃管放入250℃烘箱中反应3天。反应后得到黑色固体粉末，将其在DMF，CH3OH中浸泡后，在四氢呋喃溶剂中索氏提取持续48h,从而得到的黑色粉末，质量在43-54mg之间，产率约为68％-83％之间。
实施例9：
如图1所示，称取均苯四甲酸二酐(PMDA)(0.15mmol，32.7mg)或均苯四甲酸(PA)(0.15mmol，38.1mg)中的一种，5"-(4'-氨基[1,1'-联苯基]-4-基)[1,1':4',1”:3”,1”':4”',1””-五联苯]-4,4”'-二胺(TABPB)(0.1mmol,57.9mg)、以及苯甲酸酐(0.225mmol,50.9mg)、4-三氟甲基苯甲酸酐(0.225mmol,81.50mg)、乙酸酐(0.5mmol,51.04mg)、苯甲酸(0.6mmol,73.28mg)、4-氟苯甲酸(0.6mmol,86.47mg)或丙酸(0.6mmol,44.4mg)中的一种，小心地装入耐高温高压的厚壁玻璃管中，将该粉末抽真空至管内压力达到0.15mmHg后从真空线上取下，通过氢氧机产生的火焰将玻璃管封好，以隔绝空气。将密封好的玻璃管放入250℃烘箱中反应3天。反应后得到黑色固体粉末，将其在DMF，CH3OH中浸泡后，在四氢呋喃溶剂中索氏提取持续48h,从而得到的黑色粉末，质量为46-53mg左右，产率约为67％-76％之间。
实施例10：
如图1所示，称取均苯四甲酸二酐(PMDA)(0.15mmol，32.7mg)或均苯四甲酸(PA)(0.15mmol，38.1mg)中的一种，4',4”',4””'-(1,3,5-三嗪-2,4,6-三基)三(([[1,1'-联苯]-4-胺))(TTBT)(0.1mmol,58.3mg)、以及苯甲酸酐(0.225mmol,50.9mg)、4-三氟甲基苯甲酸酐(0.225mmol,81.50mg)、乙酸酐(0.5mmol,51.04mg)、苯甲酸(0.6mmol,73.28mg)、4-氟苯甲酸(0.6mmol,86.47mg)或丙酸(0.6mmol,44.4mg)中的一种，其他操作与实施例9相同,得到的深黄色粉末，质量为52-68mg左右，产率约为75％-83％之间。
实施例11：
如图1所示，称取1,4,5,8-萘四甲酸二酐(NTCDA)(0.15mmol,40.23mg)或1,4,5,8-萘四甲酸(NTA)(0.15mmol,45.63mg)中的一种，5"-(4'-氨基[1,1'-联苯基]-4-基)[1,1':4',1”:3”,1”':4”',1””-五联苯]-4,4”'-二胺(TABPB)(0.1mmol,57.9mg)，以及苯甲酸酐(0.225mmol,50.9mg)、4-三氟甲基苯甲酸酐(0.225mmol,81.50mg)、乙酸酐(0.5mmol,51.04mg)、苯甲酸(0.6mmol,73.28mg)、4-氟苯甲酸(0.6mmol,86.47mg)或丙酸(0.6mmol,44.4mg)中的一种，其他操作与实施例9相同,得到的黑色粉末，质量为43-59mg左右，产率约为63％-79％之间。
实施例12：
如图1所示，称取1,4,5,8-萘四甲酸二酐(NTCDA)(0.15mmol,40.23mg)或1,4,5,8-萘四甲酸(NTA)(0.15mmol,45.63mg)中的一种，4',4”',4””'-(1,3,5-三嗪-2,4,6-三基)三(([[1,1'-联苯]-4-胺))(TTBT)(0.1mmol,58.3mg)，以及苯甲酸酐(0.225mmol,50.9mg)、4-三氟甲基苯甲酸酐(0.225mmol,81.50mg)、乙酸酐(0.5mmol,51.04mg)、苯甲酸(0.6mmol,73.28mg)、4-氟苯甲酸(0.6mmol,86.47mg)或丙酸(0.6mmol,44.4mg)中的一种，其他操作与实施例9相同,得到的黑色粉末，质量为52-63mg左右，产率约为75％-81％之间。
实施例13：
如图1所示，称取均苯四甲酸二酐(PMDA)(0.15mmol，32.7mg)或均苯四甲酸(PA)(0.15mmol，38.1mg)中的一种，2,7,12-三氨基-5H-二吲哚[1,2-a:1',2’-c]芴-5,10,15-三酮(TRO)(0.1mmol,42.9mg)，以及苯甲酸酐(0.225mmol,50.9mg)、4-三氟甲基苯甲酸酐(0.225mmol,81.50mg)、乙酸酐(0.5mmol,51.04mg)、苯甲酸(0.6mmol,73.28mg)、4-氟苯甲酸(0.6mmol,86.47mg)或丙酸(0.6mmol,44.4mg)中的一种，其他操作与实施例9相同,得到的棕色粉末，质量为47-52mg左右，产率约为63％-71％之间。
实施例14：
如图1所示，称取1,4,5,8-萘四甲酸二酐(NTCDA)(0.15mmol,40.23mg)或1,4,5,8-萘四甲酸(NTA)(0.15mmol,45.63mg)中的一种，2,7,12-三氨基-5H-二吲哚[1,2-a:1',2’-c]芴-5,10,15-三酮(TRO)(0.1mmol,42.9mg)，以及苯甲酸酐(0.225mmol,50.9mg)、4-三氟甲基苯甲酸酐(0.225mmol,81.50mg)、乙酸酐(0.5mmol,51.04mg)、苯甲酸(0.6mmol,73.28mg)、4-氟苯甲酸(0.6mmol,86.47mg)或丙酸(0.6mmol,44.4mg)中的一种，其他操作与实施例9相同,得到的棕色粉末，质量为43-55mg左右，产率约为61％-73％之间。
实施例15：
如2式所示，选取0.2mmol的2,4,6-三甲基吡啶-3,5-二甲腈(24.2mg)、2,4,6-三氰基-1,3,5-三甲基苯(39.0mg)、2,4,6-三甲基-1,3,5-三嗪(24.6mg)中的一种，与苯甲酸酐(0.6mmol135mg)或苯甲酸(0.12mmol 146.5mg)以及0.2mmol的均苯三甲醛(32.4mg)、1,3,5-三(4'-醛基[1,1'-联苯]-4-基)苯(123.8mg)、1,3,5-三(对甲酰基苯基)苯(78.1mg)、4,4',4”-[苯-1,3,5-三基三(乙炔-2,1-二基)]三苯甲醛(92.5mg)、2,4,6-三(4-醛基苯基)-1,3,5-三嗪(78.7mg)、2,4,6-三-(4-甲酰基-联苯-4-基)-1,3,5-三嗪(124.3mg)中的一种装入耐高温高压的厚壁玻璃管中，将该管抽真空至管内压力达到0.15mmHg后从真空线上取出，通过氢氧机产生的火焰将玻璃管封好，以隔绝空气。将密封好的玻璃管放入180℃烘箱中反应5天。反应后得到固体粉末，将其在DMF，CH3OH中浸泡后，在四氢呋喃溶剂中索氏提取至100℃持续48h,从而得到乳白色到橙黄色不等的的整块COF状材料，质量约为52mg，产率约在85％到95％之间。如图3b所示，粉末X-射线测试揭示，利用2,4,6-三甲基-1,3,5-三嗪与均苯三醛在苯甲酸酐催化反应下所制备的粉末样品具有很高的结晶性，图4b红外光谱测试进一步证明该材料是碳碳双键连接的COFs材料，图5b为该材料在77K条件下氮气等温吸脱附曲线，其BET表面积为536m2/g。
实施例16：
如2式所示，选取0.02mmol的2,4,6-三甲基吡啶-3,5-二甲腈(24.2mg)、2,4,6-三氰基-1,3,5-三甲基苯(39.0mg)、2,4,6-三甲基-1,3,5-三嗪(24.6mg)中的一种，与苯甲酸酐(0.6mmol135mg)或苯甲酸(1.2mmol 146.5mg)以及0.3mmol的对苯二甲醛(40.2mg)、1,4-二(4-醛基苯基)苯(85.9mg)、4,4'-联苯二甲醛(63mg)、1,2-二(4'-甲酰基苯基)乙炔(70.3mg)、4,4'-(1,3-丁二炔-1,4-二基)双苯甲醛(77.5mg)、2,5-二甲氧基苯-1,4-二甲醛(58.2mg)、4,7-二(4-醛基苯基)苯并呋喃(97.8mg)、4,7-二(4-醛基苯基)苯并噻吩(102.7mmg)、4,7-二(4-醛基苯基)苯并硒酚(116.7mg)，中的一种装入耐高温高压的厚壁玻璃管中，将该管抽真空至管内压力达到0.15mmHg后从真空线上取出，通过氢氧机产生的火焰将玻璃管封好，以隔绝空气。将密封好的玻璃管放入180℃烘箱中反应5天。反应后得到固体粉末，将其在DMF，CH3OH中浸泡后，在四氢呋喃溶剂中索氏提取至100℃持续48h,从而得到乳白色，黄色和棕红色不等的的整块COF状材料，产率约在83％到95％之间。
实施例17：
如2式所示，选取0.03mmol的单体2主要包括：2,5-二甲基吡嗪(32.4mg)、3,6-二甲基哒嗪(32.4mg)、2,5-二甲基对苯二腈(46.9mg)中的一种，与苯甲酸酐(0.6mmol135mg)或苯甲酸(1.2mmol 146.5mg)以及0.2mmol的均苯三甲醛(32.4mg)、1,3,5-三(4'-醛基[1,1'-联苯]-4-基)苯(123.8mg)、1,3,5-三(对甲酰基苯基)苯(78.1mg)、4,4',4”-[苯-1,3,5-三基三(乙炔-2,1-二基)]三苯甲醛(92.5mg)、2,4,6-三(4-醛基苯基)-1,3,5-三嗪(78.7mg)、2,4,6-三-(4-甲酰基-联苯-4-基)-1,3,5-三嗪(124.3mg)中的一种装入耐高温高压的厚壁玻璃管中，将该管抽真空至管内压力达到0.15mmHg后从真空线上取出，通过氢氧机产生的火焰将玻璃管封好，以隔绝空气。将密封好的玻璃管放入200℃烘箱中反应5天。反应后得到橙黄色的固体粉末，将其在DMF，CH3OH中浸泡后，在四氢呋喃溶剂中索氏提取至100℃持续48h,从而得到乳白色，黄色和棕红色不等的的整块COF状材料，产率约在80％到95％之间。
实施例18：
如3式所示，选取0.04mmol的单体1，主要包括：1,3,5-三(4'-醛基[1,1'-联苯]-4-基)苯(24.7mg)、1,3,5-三(对甲酰基苯基)苯(15.6mg)、2,4,6-三(4-醛基苯基)-1,3,5-三嗪(15.7mg)、4',4”',4””'-(1,3,5-三嗪-2,4,6-三基)三(([1,1'-联苯]-4-甲醛))(24.9mg)、均苯三甲醛(6.5mg)中的一种装入耐高温高压的厚壁玻璃管中；再称取0.06mmol单体2主要包括：对苯二酸二肼(11.7mg)、2,5-二乙氧基苯-1,4-二(甲酰肼)(16.9mg)、2,5-双(烯丙氧基)对苯二甲酰肼(18.4mg)中的一种装入玻璃管；再称取0.06mmol的化合物3：苯甲酸酐、苯并咪唑、苯甲酸中的一种装入玻璃管。将该管抽真空至管内压力达到0.15mmHg后从真空线上取出，通过氢氧机产生的氢气火焰将玻璃管封好，以隔绝空气。将密封好的玻璃管放入120℃烘箱中反应3天。反应后得到固体粉末，将其在DMF，CH3OH中浸泡后，在四氢呋喃溶剂中索氏提取至100℃持续48h，从而得到比较纯净的COF材料，产率约在80％到95％之间。如图3c所示，粉末X-射线测试揭示，利用均苯三甲醛与2,5-二乙氧基苯-1,4-二(甲酰肼)在苯甲酸酐催化反应下所制备的粉末样品具有很高的结晶性，图4c红外光谱测试进一步证明该材料是腙键连接的COFs材料，图5c为该材料在77K条件下氮气等温吸脱附曲线，其BET表面积为951m2/g。
实施例19：
如3式所示，选取0.04mmol的1,3,5-苯三甲酰肼(10.1mg)装入耐高温高压的厚壁玻璃管中；再称取0.06mmol有机单体1主要包括：对苯二甲醛(8mg)、1,4-二(4-醛基苯基)苯(17.2mg)、4,4'-联苯二甲醛(12.6mg)、1,2-二(4'-甲酰基苯基)乙炔(14.1mg)、4,4'-(1,3-丁二炔-1,4-二基)双苯甲醛(15.5mg)中的一种装入玻璃管，再称取0.06mmol的化合物3：苯甲酸酐、苯并咪唑、苯甲酸中的一种装入玻璃管。将该管抽真空至管内压力达到0.15mmHg后从真空线上取出，通过氢氧机产生的氢气火焰将玻璃管封好，以隔绝空气。将密封好的玻璃管放入120℃烘箱中反应3天。反应后得到固体粉末，将其在DMF，CH3OH中浸泡后，在四氢呋喃溶剂中索氏提取至100℃持续48h，从而得到比较纯净的COF材料，产率约在80％到95％之间。
实施例20：
如4式所示，选取0.04mmol有机单体1的醛类单体，主要包括：1,3,5-三(对甲酰基苯基)苯、2,4,6-三(4-醛基苯基)-1,3,5-三嗪，均苯三甲醛、2-羟基-1,3,5-苯三甲醛、2,4-二羟基-1,3,5-苯三甲醛中的一种装入耐高温高压的厚壁玻璃管中；再称取0.06mmol有机单体2的胺类单体，包括对苯二胺、2,5-二氨基吡啶、联苯胺、4,4'-二氨基三连苯，水合肼中的一种装入玻璃管；再称取0.06mmol的化合物3：苯甲酸酐、苯并咪唑、苯甲酸中的一种装入玻璃管。将该管抽真空至管内压力达到0.15mmHg后从真空线上取出，通过氢氧机产生的氢气火焰将玻璃管封好，以隔绝空气。将密封好的玻璃管放入120℃烘箱中反应3天。反应后得到固体粉末，将其在DMF，CH3OH中浸泡后，在四氢呋喃溶剂中索氏提取至100℃持续48h，从而得到比较纯净的COF材料，产率约在80％到95％之间。如图3d所示，粉末X-射线测试揭示，利用均苯三甲醛与对苯二胺在苯甲酸催化反应下所制备的粉末样品具有很高的结晶性，图4d红外光谱测试进一步证明该材料是亚胺键连接的COFs材料,图5d为该材料在77K条件下氮气等温吸脱附曲线，其BET表面积为401m2/g。
实施例21：
如4式所示，选取0.04mmol有机单体2的胺类单体，主要包括：1,3,5-三(4-氨基苯基)苯、2,4,6-三(4-氨基苯基)-1,3,5-三嗪、三(4-氨基苯基)胺中的一种装入耐高温高压的厚壁玻璃管中；再称取0.06mmol有机单体1的醛类单体，包括对苯二甲醛、4,4'-联苯二甲醛1,4-二(4-醛基苯基)苯、1,2-二(4'-甲酰基苯基)乙炔中的一种装入玻璃管；再称取0.06mmol的化合物3：苯甲酸酐、苯并咪唑、苯甲酸中的一种装入玻璃管。将该管抽真空至管内压力达到0.15mmHg后从真空线上取出，通过氢氧机产生的氢气火焰将玻璃管封好，以隔绝空气。将密封好的玻璃管放入120℃烘箱中反应3天。反应后得到固体粉末，将其在DMF，CH3OH中浸泡后，在四氢呋喃溶剂中索氏提取至100℃持续48h，从而得到比较纯净的COF材料，产率约在80％到95％之间。
实施例22：
如5式所示，选取0.04mmol的2,4,6-三羟基-1,3,5-苯三甲醛(8.4mg)装入耐高温高压的厚壁玻璃管中；再称取0.06mmol有机单体2包括对苯二胺、2,5-二氨基吡啶、联苯胺、4,4'-二氨基三连苯、水合肼中的一种装入玻璃管；再称取0.06mmol的化合物3：苯甲酸酐、苯并咪唑、苯甲酸中的一种装入玻璃管。将该管抽真空至管内压力达到0.15mmHg后从真空线上取出，通过氢氧机产生的氢气火焰将玻璃管封好，以隔绝空气。将密封好的玻璃管放入120℃烘箱中反应3天。反应后得到固体粉末，将其在DMF，CH3OH中浸泡后，在四氢呋喃溶剂中索氏提取至100℃持续48h，从而得到比较纯净的COF材料，产率约在80％到95％之间。如图3e所示，粉末X-射线测试揭示，利用2,4,6-三羟基-1,3,5-苯三甲醛与对苯二胺在苯甲酸催化反应下所制备的粉末样品具有很高的结晶性，图4e红外光谱测试进一步证明该材料是酮-烯醇类COFs材料，图5e为该材料在77K条件下氮气等温吸脱附曲线，其BET表面积为334m2/g。
实施例23：
如5式所示，选取0.04mmol的2,4,6-三羟基-1,3,5-苯三甲醛(8.4mg)装入耐高温高压的厚壁玻璃管中；再称取0.06mmol单体2包括1,3,5-三(4-氨基苯基)苯、2,4,6-三(4-氨基苯基)-1,3,5-三嗪、三(4-氨基苯基)胺中的一种装入玻璃管；再称取0.06mmol的化合物3：苯甲酸酐、苯并咪唑、苯甲酸中的一种装入玻璃管。将该管抽真空至管内压力达到0.15mmHg后从真空线上取出，通过氢氧机产生的氢气火焰将玻璃管封好，以隔绝空气。将密封好的玻璃管放入120℃烘箱中反应3天。反应后得到固体粉末，将其在DMF，CH3OH中浸泡后，在四氢呋喃溶剂中索氏提取至100℃持续48h，从而得到比较纯净的COF材料，产率约在80％到95％之间。
最后应说明的是：以上所述仅为本发明的优选实施例，并不用于对本发明做任何形式上的限制。任何熟悉本领域的研究及技术人员，在不脱离本发明的技术方案范围的情况下，利用上述内容对本发明的技术方案做出的非创新性变动和修改，例如仅更改原料试剂添加比例、反应时长和操作流程等，均应包含在本发明的保护范围之内。

Claims (10)

1.一种共价有机框架材料(COFs)的固相合成方法，其特征在于，所述共价有机框架材料为通过乙烯基连接、酰亚胺连接、硼酸酯连接、硼氧六元环连接、亚胺键连接、吖嗪连接、酮-烯醇连接、腙键连接或三嗪连接的共价有机框架材料，其具体通过如下步骤进行合成：
有机单体1和有机单体2在非溶剂、有催化剂存在的条件下，通过缩合反应获得；
其中，所述有机单体1为含有羧酸酐官能团的二连接单体、含有羧酸官能团的二连接单体、含醛基官能团的二连接单体或含醛基官能团的三连接单体；
所述有机单体2为含有氨基官能团的二连接单体、含有氨基官能团的三连接单体、含有氨基官能团的四连接单体、含活性甲基官能团的二连接单体、或含有活性甲基官能团的三连接单体；
所述催化剂为含有酸酐官能团的化合物、含有羧酸官能团的化合物、含有咪唑官能团的化合物或含有羟基官能团的化合物；
所述合成方法是原位生长方法，具体为：把催化剂、有机单体1和有机单体2，直接放进密闭反应容器中，高温聚合得到共价有机框架材料；
其中，反应体系压强为0-1atm，反应温度为120-250℃。
2.如权利要求1所述的固相合成方法，其特征在于，在非溶剂条件下进行反应，包括如下步骤：
(1)将有机单体1和有机单体2加入到反应器中，加入催化剂进行反应；
(2)反应结束后，对产物进行纯化；
(3)纯化后的产物在真空条件下加热处理得到最终产物。
3.如权利要求1-2任一项所述的固相合成方法，其特征在于，所述有机单体1为含苯硼酸的单体、含苯甲醛的单体、2,4,6-三羟基苯-1,3,5-三甲醛、含邻苯二酸酐的单体、含羟基丙烯酮的单体、含苯二酮的单体或二元酸酐单体，所述有机单体2为含邻苯二酚的单体、含苯胺的单体、含苯甲酰肼的单体、水合肼、含苯甲腈的单体、含苯乙腈的单体、二甲基吡嗪单体、含苯甲脒的单体、含邻苯二胺的单体或三胺单体。
4.如权利要求1-2任一项所述的固相合成方法，其特征在于，所述有机单体1为含苯甲醛的二连接或三连接单体、含苯酸酐的二连接单体，含邻苯二甲酸的二连接单体，其中二连接单体的为直线分子，三连接单体夹角为120°；所述有机单体2为含苯胺的二连接、三连接或四连接单体、含苯甲酰肼的二连接或三连接单体、水合肼、含活性甲基的二连接或三连接单体，其中二连接单体的为直线分子，三连接单体和四连接单体的夹角为120°。
5.如权利要求1-2任一项所述的固相合成方法，其特征在于，所述催化剂为取代或未取代的如下化合物：苯甲酸酐、4-三氟甲基苯甲酸酐、苯乙酸酐、乙酸酐、三氟乙酸酐、苯甲酸、4-氟苯甲酸、4-溴苯甲酸、丙酸、芳香酸、咪唑、苯并咪唑或苯酚。
6.如权利要求1-2任一项所述的固相合成方法，其特征在于，所述有机单体1为对苯二甲醛、1,4-二(4-醛基苯基)苯、4,4'-联苯二甲醛、4,7-二(4-醛基苯基)苯并呋喃、4,7-二(4-醛基苯基)苯并噻吩、4,7-二(4-醛基苯基)苯并硒酚、1,2-二(4'-甲酰基苯基)乙炔、4,4'-(1,3-丁二炔-1,4-二基)双苯甲醛、2,5-二甲氧基-1,4-对苯二甲醛、1,3,5-均苯三甲醛、2-羟基-1,3,5-苯三甲醛、2,4-二羟基-1,3,5-苯三甲醛、2,4,6-三羟基-1,3,5-苯三甲醛、1,3,5-三(4'-醛基[1,1'-联苯]-4-基)苯、1,3,5-三(对甲酰基苯基)苯、4,4’,4”-[苯-1,3,5-三基三(乙炔-2,1-二基)]三苯甲醛、2,4,6-三(4-醛基苯基)-1,3,5-三嗪、4’,4”,4”’-(1,3,5-三嗪-2,4,6-三基)三(([1,1'-联苯]-4-甲醛))、2,4,6-三(4-甲酰基-联苯-4-基)-1,3,5-三嗪中的任意一种；
所述有机单体2为2,5-二甲基吡嗪、四甲基吡嗪、3,6-二甲基哒嗪、2,5-二甲基对苯二腈、2,4,6-三甲基-1,3,5-三嗪、2,4,6-三甲基吡啶、2,4,6,-三甲基-嘧啶、2,4,6,-三甲基-嘧啶-5-甲腈、2,4,6-三甲基吡啶-3,5-二甲腈、2,4,6-三氰基-1,3,5-三甲基苯、2,2'-联吡啶-5,5'-二乙腈中的任意一种；
其中，二连接的有机单体2与三连接单体1组合反应，或二连接的单体1与三连接的单体2组合反应。
7.如权利要求1-2任一项所述的固相合成方法，其特征在于，所述有机单体1为均苯四甲酸二酐(PMDA)、1,4,5,8-萘四甲酸二酐(NTCDA)、均苯四甲酸(PA)、1,4,5,8-萘四甲酸(NTA)、对苯二甲醛、1,4-二(4-醛基苯基)苯、4,4'-联苯二甲醛、1,2-二(4'-甲酰基苯基)乙炔、4,4'-(1,3-丁二炔-1,4-二基)双苯甲醛、2,5-二甲氧基-1,4-对苯二甲醛、均苯三甲醛、2-羟基-1,3,5-苯三甲醛、2,4-二羟基-1,3,5-苯三甲醛、2,4,6-三羟基-1,3,5-苯三甲醛、1,3,5-三(4'-醛基[1,1'-联苯]-4-基)苯、1,3,5-三(对甲酰基苯基)苯、4,4',4”-[苯-1,3,5-三基三(乙炔-2,1-二基)]三苯甲醛、2,4,6-三(4-醛基苯基)-1,3,5-三嗪、4',4”',4””'-(1,3,5-三嗪-2,4,6-三基)三(([1,1'-联苯]-4-甲醛))或2,4,6-三-(4-甲酰基-联苯-4-
基)-1,3,5-三嗪中任意一种；
所述有机单体2为对苯二胺、2,5-二氨基吡啶、联苯胺、4,4'-二氨基三连苯、水合肼、对苯二酸二肼、2,5-二乙氧基苯-1,4-二(甲酰肼)、2,5-双(烯丙氧基)对苯二甲酰肼、1,3,5-三(4-氨苯基)苯、2,4,6-三(4-氨基苯基)-1,3,5-三嗪、三(4-氨基苯基胺)、5"-(4'-氨基[1,1'-联苯基]-4-基)[1,1':4',1”:3”,1”':4”',1””-五联苯]-4,4”'-二胺、4',4”',4””'-(1,3,5-三嗪-2,4,6-三基)三(([[1,1'-联苯]-4-胺))、2,7,12-三氨基-5H-二吲哚[1,2-a:1',2’-c]芴-5,10,15-三酮、2,4,6-三(3-羟基-4-氨基苯基)-1,3,5-三嗪、1,3,5-苯三甲酰肼、N,N,N',N'-四(对氨基苯基)对苯二胺或四-(4-氨基苯)乙烯中任意一种；
其中，二连接的有机单体2与三连接有机单体1组合反应，或二连接的有机单体1与三连接或四连接的有机单体2组合反应。
8.如权利要求1-2任一项所述的固相合成方法，其特征在于，所述共价有机框架材料(COFs)的形态为块状、圆柱状或泡沫状，孔径为1.8-4.9nm。
9.如权利要求1-2任一项所述的固相合成方法，其特征在于，所述有机单体1与有机单体2的摩尔比为1:4至4:1；催化剂和有机单体1的摩尔比为1:5至5:1。
10.如权利要求1-2任一项所述的固相合成方法，其特征在于，反应时间为3-7天。
CN202111650887.5A 2020-12-30 2021-12-30 一种共价有机框架材料的绿色固相合成方法 Active CN114773556B (zh)