CN114425353A - 渣油加氢脱金属催化剂及其制备 - Google Patents
渣油加氢脱金属催化剂及其制备 Download PDFInfo
- Publication number
- CN114425353A CN114425353A CN202011185888.2A CN202011185888A CN114425353A CN 114425353 A CN114425353 A CN 114425353A CN 202011185888 A CN202011185888 A CN 202011185888A CN 114425353 A CN114425353 A CN 114425353A
- Authority
- CN
- China
- Prior art keywords
- catalyst
- macroporous
- pore volume
- residual oil
- gel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
原料油性质 | 中东常渣 |
S,wt% | 3.8 |
Ni,μg/g | 31.9 |
V,μg/g | 99.8 |
反应温度,℃ | 380 |
反应压力,MPa | 15.0 |
体积空速,h<sup>-1</sup> | 1.0 |
氢油比,V/V | 650 |
Claims (12)